In suit constructing S-scheme FeOOH/MgIn2S4 heterojunction with boosted interfacial charge separation and redox activity for efficiently eliminating antibiotic pollutant

Photocatalytic elimination of antibiotic pollutant is an appealing avenue in response to the water contamination, but it still suffers from sluggish charge detachment, limited redox capacity as well as poor visible light utilization. Herein, a particular S-scheme FeOOH/MgIn₂S₄ heterojunction with wide visible light absorption was triumphantly constructed by in-situ growth of MgIn₂S₄ nanoparticles onto the surface of FeOOH nanorods, and employed as a high-efficiency visible light driven photocatalyst for removing tetracycline (TC). Conspicuously, the as-obtained FeOOH(15 wt%)/MgIn₂S₄ elucidated the optimal TC removal rate of 0.01258 min^-1 after 100 min of visible light illumination, which was almost 33.1 and 6.6 times larger than those of neat FeOOH and MgIn₂S₄, separately. The exceptional degradation performance was principally put down to the establishment of S-scheme heterojunction between FeOOH and MgIn₂S₄, which could not merely accelerate the detachment of photogenerated carriers, but also retain the powerful reducing ability of photoinduced electrons for MgIn₂S₄ and high oxidizing capacity of photoexcited holes for FeOOH, strongly driving the generation of plentiful active species including holes, superoxide and hydroxyl radicals. Additionally, the possible degradation mechanism and pathways of TC were also speculated. This work offers a valuable perspective for constructing high-efficiency S-scheme heterojunction photocatalysts for eradicating antibiotics.

Atomically Thin Materials for Next-Generation Rechargeable Batteries

Atomically thin materials (ATMs) with thicknesses in the atomic scale (typically <5 nm) offer inherent advantages of large specific surface areas, proper crystal lattice distortion, abundant surface dangling bonds, and strong in-plane chemical bonds, making them ideal 2D platforms to construct high-performance electrode materials for rechargeable metal-ion batteries, metal-sulfur batteries, and metal-air batteries. This work reviews the synthesis and electronic property tuning of state-of-the-art ATMs, including graphene and graphene derivatives (GE/GO/rGO), graphitic carbon nitride (g-C₃N₄), phosphorene, covalent organic frameworks (COFs), layered transition metal dichalcogenides (TMDs), transition metal carbides, carbonitrides, and nitrides (MXenes), transition metal oxides (TMOs), and metal-organic frameworks (MOFs) for constructing next-generation high-energy-density and high-power-density rechargeable batteries to meet the needs of the rapid developments in portable electronics, electric vehicles, and smart electricity grids. We also present our viewpoints on future challenges and opportunities of constructing efficient ATMs for next-generation rechargeable batteries.

Recent advances in amphiphilic block copolymer templated mesoporous metal-based materials: assembly engineering and applications

Mesoporous metal-based materials (MMBMs) have received unprecedented attention in catalysis, sensing, and energy storage and conversion owing to their unique electronic structures, uniform mesopore size and high specific surface area. In the last decade, great progress has been made in the design and application of MMBMs; in particular, many novel assembly engineering methods and strategies based on amphiphilic block copolymers as structure-directing agents have also been developed for the "bottom-up" construction of a variety of MMBMs. Development of MMBMs is therefore of significant importance from both academic and practical points of view. In this review, we provide a systematic elaboration of the molecular assembly methods and strategies for MMBMs, such as tuning the driving force between amphiphilic block copolymers and various precursors (i.e., metal salts, nanoparticles/clusters and polyoxometalates) for pore characteristics and physicochemical properties. The structure-performance relationship of MMBMs (e.g., pore size, surface area, crystallinity and crystal structure) based on various spectroscopy analysis techniques and density functional theory (DFT) calculation is discussed and the influence of the surface/interfacial properties of MMBMs (e.g., active surfaces, heterojunctions, binding sites and acid-base properties) in various applications is also included. The prospect of accurately designing functional mesoporous materials and future research directions in the field of MMBMs is pointed out in this review, and it will open a new avenue for the inorganic-organic assembly in various fields.

Substrate-induced hydrothermal synthesis of hematite superstructures and their Fischer–Tropsch synthesis performance

Fe foam substrates with different pore densities are used to fabricate versatile α-Fe₂O₃ nanostructures with different Fischer–Tropsch synthesis performance.

Synergy between nanomaterials and volatile organic compounds for non-invasive medical evaluation

This article is an overview of the present and ongoing developments in the field of nanomaterial-based sensors for enabling fast, relatively inexpensive and minimally (or non-) invasive diagnostics of health conditions with follow-up by detecting volatile organic compounds (VOCs) excreted from one or combination of human body fluids and tissues (e.g., blood, urine, breath, skin). Part of the review provides a didactic examination of the concepts and approaches related to emerging sensing materials and transduction techniques linked with the VOC-based non-invasive medical evaluations. We also present and discuss diverse characteristics of these innovative sensors, such as their mode of operation, sensitivity, selectivity and response time, as well as the major approaches proposed for enhancing their ability as hybrid sensors to afford multidimensional sensing and information-based sensing. The other parts of the review give an updated compilation of the past and currently available VOC-based sensors for disease diagnostics. This compilation summarizes all VOCs identified in relation to sickness and sampling origin that links these data with advanced nanomaterial-based sensing technologies. Both strength and pitfalls are discussed and criticized, particularly from the perspective of the information and communication era. Further ideas regarding improvement of sensors, sensor arrays, sensing devices and the proposed workflow are also included.

Morphology-Controlled Synthesis of Hematite Nanocrystals and Their Optical, Magnetic and Electrochemical Performance

A series of α-Fe₂O₃ nanocrystals (NCs) with fascinating morphologies, such as hollow nanoolives, nanotubes, nanospindles, and nanoplates, were prepared through a simple template-free hydrothermal synthesis process. The results showed that the morphologies could be easily controlled by SO₄2- and H₂PO₄-. Physical property analysis showed that the α-Fe₂O₃ NCs exhibited shape- and size-dependent ferromagnetic and optical behaviors. The absorption band peak of the α-Fe₂O₃ NCs could be tuned from 320 to 610 nm. Furthermore, when applied as electrode material for supercapacitor, the hollow olive-structure exhibited the highest capacitance (285.9 F·g-1) and an excellent long-term cycling stability (93% after 3000 cycles), indicating that it could serve as a candidate electrode material for a supercapacitor.

Co3O4–SnO2 nanobox sensor with a PN junction and semiconductor–conductor transformation for high selectivity and sensitivity detection of H2S

Uniform Co₃O₄–SnO₂ nanoboxes have been synthesized successfully by a facile annealing treatment.

Role of [FeOx(OH)y] surface sites on the adsorption of β-lactamic antibiotics on Al2O3 supported Fe oxide

In this work, [FeOx(OH)y]/Al2O3 composites with different Fe oxyhydroxy contents, i.e. 10, 20 and 50wt% treated at 150, 200, 300 and 450°C were investigated as adsorbents of β-lactamic antibiotics, i.e. cephalexin, ceftriaxone and especially amoxicillin, from aqueous solutions. The obtained results showed that the nature of the surface Fe(3+) species play a fundamental role on the adsorption process. The most efficient adsorption was obtained for the sample 150Fe50A (50% [FeOx(OH)y] supported in Al2O3 treated at 150°C) whereas the thermal treatment at higher temperatures caused a strong decrease on the adsorption capacity. Mössbauer, XRD, FTIR, Raman, TG-MS, SEM, CHN and BET of the composite 150Fe50A suggested an approximate composition of FeO0.65(OH)1.7 whereas at 450°C strong dehydroxylation process takes place to form FeO1.4(OH)0.21. These results combined with competitive adsorption using amoxicillin mixed with phosphate or H2O2 suggest that the antibiotic molecules adsorb by complexation on surface sites likely based on FeOx(OH)y by the replacement of the labile OH ligands.

Wide bandgap mesoporous hematite nanowire bundles as a sensitive and rapid response ethanol sensor

In this study, α-Fe2O3 nanowires were synthesized using mesoporous SBA-15 silica as the hard templates with the nanocasting method, and then mesoporous α-Fe2O3 nanowire bundles (NWBs) were separated from the well-dispersed α-Fe2O3 nanowires (NWs) by the centrifugation technique. Both samples were characterized by x-ray diffraction, transmission electron microscopy (TEM), nitrogen adsorption/desorption isotherm and UV-vis spectra. All results indicated that the α-Fe2O3 NWBs with mesoporous structure presented a higher BET surface area (95 m(2) g(-1)) and wider bandgap (2.08 eV) than those of α-Fe2O3 NWs (32 m(2) g(-1) and 1.91 eV). The bandgap of α-Fe2O3 NWBs was in accordance with the bulk α-Fe2O3, while the BET surface area was much higher. The results from the gas-sensing measurement revealed that the α-Fe2O3 NWBs based gas sensor exhibited a high sensitivity of 21.7, fast response-recovery of 7.5 s and 1 s, and good selectivity to ethanol at 340 °C. The sensitivity (21.7) for ethanol of α-Fe2O3 NWBs was much better than that of the α-Fe2O3 NWs (12.2), which should be attributed to the higher BET surface area and wider bandgap of α-Fe2O3 NWBs.

Hierarchical core–shell structured Fe3O4@NiSiO3 magnetic microspheres: preparation, characterization, and adsorption of methylene blue from aqueous solution

Core–shell structured Fe₃O₄@NiSiO₃ magnetic microspheres are synthesised and possess high porosity and magnetic properties, which allow the microspheres to exhibit efficient adsorption of methylene blue and convenient separation from wastewater.

α-Fe2O3 nanopillar arrays fabricated by electron beam evaporation for the photoassisted degradation of dyes with H2O2

Vertically aligned α-Fe₂O₃ nanopillar arrays (NPAs) were fabricated by thermally oxidizing Fe NPAs on Si, quartz and F-doped SnO₂ (FTO) substrates prepared by glancing angle e-beam deposition (GLAD).

A high-performance dual-function material: self-assembled super long α-Fe2O3 hollow tubes with multiple heteroatom (C-, N- and S-) doping

Flow diagram of the synthesis of nitrogen doped α-Fe₂O₃ nanorods into super long hollow tubes.

Ethanol Gas Detection Using a Yolk-Shell (Core-Shell) α-Fe2O3 Nanospheres as Sensing Material

Three-dimensional (3D) nanostructures of α-Fe2O3 materials, including both hollow sphere-shaped and yolk-shell (core-shell)-shaped, have been successfully synthesized via an environmentally friendly hydrothermal approach. By expertly adjusting the reaction time, the solid, hollow, and yolk-shell shaped α-Fe2O3 can be selectively synthesized. Yolk-shell α-Fe2O3 nanospheres display outer diameters of 350 nm, and the interstitial hollow spaces layer is intimately sandwiched between the inner and outer shell of α-Fe2O3 nanostructures. The possible growth mechanism of the yolk-shell nanostructure is proposed. The results showed that the well-defined bilayer interface effectively enhanced the sensing performance of the α-Fe2O3 nanostructures (i.e., yolk-shell α-Fe2O3@α-Fe2O3), owing predominantly to the unique nanostructure, thus facilitated the transport rate and augmented the adsorption quantity of the target gas molecule under gas detection.

TiO2 Fibers Supported β-FeOOH Nanostructures as Efficient Visible Light Photocatalyst and Room Temperature Sensor

Hierarchical heterostructures of beta-iron oxyhydroxide (β-FeOOH) nanostructures on electrospun TiO₂ nanofibers were synthesized by a facile hydrothermal method. This synthesis method proves to be versatile to tailoring of β-FeOOH structural design that cuts across zero-dimensional particles (TF-P), one-dimensional needles (TF-N) to two-dimensional flakes (TF-F). In addition, synthesizing such oxyhyroxide nanostructures presents the advantage of exhibiting similar functional performances to its oxides counterpart however, without the need to undergo any annealing step which leads to undesirable structural collapse or sintering. The as-prepared hierarchical heterostructures possess high surface area for dye adsorptivity, efficient charge separation and visible photocatalytic activity. Also, for the first time, hydrogen gas sensing has been demonstrated on β-FeOOH nanostructures at room temperature. The reported hierarchical heterostructures of β-FeOOH on TiO₂ nanofibers afford multiple functions of photocatalysis and sensing which are highly promising for environment monitoring and clean up applications.

The mechanistic insight into the biomilling of goethite (α-FeO(OH)) nanorods using the yeast Saccharomyces cerevisiae

Proteins react with the Fe³⁺ ions on goethite surface, form Fe³⁺–protein complexes which get disassociated, and results into fresh Fe³⁺ ions on the surface. This process of complexation–dissociation leads to biomilling.

Eco-friendly synthesis and photodegradation of hierarchical nanostructures of β-FeOOH and α-Fe2O3

β-FeOOH and α-Fe₂O₃ with different morphologies were synthesized via a facile method using urea or saccharide as the organic matrix.

Facile synthesis of single-crystalline hollow α-Fe2O3 nanospheres with gas sensing properties

High-quality single-crystalline hollow α-Fe₂O₃ nanospheres were prepared, using ZnS–CHA nanohybrid as additive with gas sensing property.

Ultrahigh sensitivity of Au/1D α-Fe2O3 to acetone and the sensing mechanism

Hematite (α-Fe(2)O(3)) is a nontoxic, stable, versatile material that is widely used in catalysis and sensors. Its functionality in sensing organic molecules such as acetone is of great interest because it can result in potential medical applications. In this report, microwave irradiation is applied in the preparation of one-dimensional (1D) α-FeOOH, thereby simplifying our previous hydrothermal method and reducing the reaction time to just a few minutes. Upon calcination, the sample was converted to porous α-Fe(2)O(3) nanorods, which were then decorated homogeneously by fine Au particles, yielding Au/1D α-Fe(2)O(3) at nominally 3 wt % Au. After calcination, the sample was tested as a potential sensor for acetone in the parts per million range and compared to a similarly loaded Pt sample and the pure 1D α-Fe(2)O(3) support. Gold addition results in a much enhanced response whereas Pt confers little or no improvement. From tests on acetone in the 1-100 ppm range in humid air, Au/1D α-Fe(2)O(3) has a fast response, short recovery time, and an almost linear response to the acetone concentration. The optimum working temperature was found to be 270 °C, which was judged to be a compromise between the thermal activation of lattice oxygen in hematite and the propensity for acetone adsorption. The surface reaction was investigated by diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS), and a possible sensing mechanism is proposed. The presence of Au nanoparticles is believed to promote the dissociation of molecular oxygen better in replenishing O vacancies, thereby increasing the instantaneous supply of lattice oxygen to the oxidation of acetone (to H(2)O and CO(2)), which proceeds through an adsorbed acetate intermediate. This work contributes to the development of next-generation sensors, which offer ultrahigh detection capabilities for organic molecules.

Low-cost synthesis of flowerlike α-Fe2O3 nanostructures for heavy metal ion removal: adsorption property and mechanism

Flowerlike α-Fe(2)O(3) nanostructures were synthesized via a template-free microwave-assisted solvothermal method. All chemicals used were low-cost compounds and environmentally benign. These flowerlike α-Fe(2)O(3) nanostructures had high surface area and abundant hydroxyl on their surface. When tested as an adsorbent for arsenic and chromium removal, the flowerlike α-Fe(2)O(3) nanostructures showed excellent adsorption properties. The adsorption mechanism for As(V) and Cr(VI) onto flowerlike α-Fe(2)O(3) nanostructures was elucidated by X-ray photoelectron spectroscopy and synchrotron-based X-ray absorption near edge structure analysis. The results suggested that ion exchange between surface hydroxyl groups and As(V) or Cr(VI) species was accounted for by the adsorption. With maximum capacities of 51 and 30 mg g(-1) for As(V) and Cr(VI), respectively, these low-cost flowerlike α-Fe(2)O(3) nanostructures are an attractive adsorbent for the removal of As(V) and Cr(VI) from water.

Probing the morphology-device relation of Fe₂O₃ nanostructures towards photovoltaic and sensing applications

A lot of research on nanomaterials has been carried out in recent years. However, there is still a lack of nanostructures that have a combination of superior properties; both efficient electron transport and high surface area. Here, the authors have tried to develop hybrid α-Fe(2)O(3) flower-like morphology which exhibits both superior electron transport and high surface area. Intrigued by the unique properties of Fe(2)O(3) at the nanoscale and its abundance in nature, we have demonstrated a facile template-free solution based synthesis of hybrid α-Fe(2)O(3) comprising nanopetals nucleating radially from a 3D core. Due to its simplicity, the synthesis process can be easily reproduced and scaled up. We carried out in-depth studies on gas sensing and dye-sensitized solar cell (DSSC) device characterization so as to gain an understanding of how surface area and transport properties are affected by variation in morphology. The hybrid α-Fe(2)O(3) nanostructures are studied as potential candidates for gas sensors and for the first time as a working electrode for DSSC.