In-situ catalytic upgrading of bio-oil from rapid pyrolysis of biomass over hollow HZSM-5 with mesoporous shell

To solve the issue of narrow micropores in traditional protonic type Zeolite Socony Mobil-5 (HZSM-5) catalysts in the restricting of large-molecular reactants/products diffusion, hollow HZSM-5 with a mesoporous shell was prepared using a hydrothermal method combined with a tetrapropylammonium hydroxide (TPAOH) treatment process. Applying for in-situ catalyst upgrading of bio-oil from rapid pyrolysis of biomass, the obtained most efficient catalyst of Hollow(30)-TP resulted in aromatic hydrocarbon yields in the range of 78.49-78.67% for cellulose and hemicellulose, which is much greater than those using the traditional HZSM-5 (61.06-68.26%). Furthermore, in the case using real biomass (cedar) with an optimal biomass/catalyst weight ratio of 1:2, the aromatic hydrocarbon yield reached up to 80.16%. In addition, this catalyst exhibited excellent reusability and regeneration property due to the increased accessibility to the acid sites in the hollow HZSM-5 for the improving of the reaction rate as well as the reducing of coking.

Reducing the dosage of the organic structure-directing agent in the crystallization of pure silica zeolite MFI (silicalite-1) for volatile organic compounds (VOCs) adsorption

Zeolite silicalite-1 (MFI) was synthesized with a lower amount of TPA⁺ but an appropriate amount of seed.

State of the Art and Perspectives of Hierarchical Zeolites: Practical Overview of Synthesis Methods and Use in Catalysis

Microporous zeolites have proven to be of great importance in many chemical processes. Yet, they often suffer from diffusion limitations causing inefficient use of the available catalytically active sites. To address this problem, hierarchical zeolites have been developed, which extensively improve the catalytic performance. There is a multitude of recent literature describing synthesis of and catalysis with these hierarchical zeolites. This review attempts to organize and overview this literature (of the last 5 years), with emphasis on the most important advances with regard to synthesis and application of such zeolites. Special attention is paid to the most common and important 10- and 12-membered ring zeolites (MTT, TON, FER, MFI, MOR, FAU, and *BEA). In contrast to previous reviews, the research per zeolite topology is brought together and discussed here. This allows the reader to instantly find the best synthesis method in accordance to the desired zeolite properties. A summarizing graph is made available to enable the reader to select suitable synthesis procedures based on zeolite acidity and mesoporosity, the two most important tunable properties.

A Comprehensive Review of the Applications of Hierarchical Zeolite Nanosheets and Nanoparticle Assemblies in Light Olefin Production

Light olefins including ethylene, propylene and butylene are important building blocks in petrochemical industries to produce various chemicals such as polyethylene, polypropylene, ethylene oxide and cumene. Traditionally, light olefins are produced via a steam cracking process operated at an extremely high temperature. The catalytic conversion, in which zeolites have been widely used, is an alternative pathway using a lower temperature. However, conventional zeolites, composed of a pure microporous structure, restrict the diffusion of large molecules into the framework, resulting in coke formation and further side reactions. To overcome these problems, hierarchical zeolites composed of additional mesoporous and/or macroporous structures have been widely researched over the past decade. In this review, the recent development of hierarchical zeolite nanosheets and nanoparticle assemblies together with opening up their applications in various light olefin productions such as catalytic cracking, ethanol dehydration to ethylene, methanol to olefins (MTO) and other reactions will be presented.

Seed-induced synthesis of multilamellar ZSM-5 nanosheets directed by amphiphilic organosilane

Multilamellar ZSM-5 nanosheets formed by the transformation of ordered MCM-41-like mesophases.