Tensile strength of restorative resins

The Influence of Low-Molecular-Weight Monomers (TEGDMA, HDDMA, HEMA) on the Properties of Selected Matrices and Composites Based on Bis-GMA and UDMA

Bisphenol A-glycidyl methacrylate (bis-GMA) and urethane dimethacrylate (UDMA) are usually combined with low-viscosity monomers to obtain more desirable viscosity, handling characteristics and general properties. The present study determined the flexural strength (FS), flexural modulus (FM), diametral tensile strength (DTS), and hardness (HV) of five matrices and composites based on these resins. The polymerization shrinkage stress (PSS) was also studied for the composites. The polymer matrices were formed using bis-GMA and UDMA. TEGDMA, HEMA and HDDMA acted as co-monomers. The composites had 45 wt.% of filler content. The highest FS and FM were obtained from the UDMA/bis-GMA/TEGDMA/HEMA matrix and the composite (matrix + filler). The best DTS values were obtained from the UDMA/bis-GMA/HEMA matrix and the composite. One of the lowest values of FS, FM, and DTS was obtained from the UDMA/bis-GMA/HDDMA matrix and the composite. All the composites demonstrated similar hardness values. The lowest polymerization shrinkage stress was observed for the UDMA/bis-GMA/TEGDMA/HEMA composite, and the highest PSS was observed for the UDMA/bis-GMA/TEGDMA/HDDMA composite. The addition of HEMA had a positive effect on the properties of the tested materials, which may be related to the improved mobility of the bis-GMA and UDMA monomers.

An Evaluation of the Properties of Urethane Dimethacrylate-Based Dental Resins

Most of the dental materials available on the market are still based on traditional monomers such as bisphenol A-glycidyl methacrylate (Bis-GMA), urethane dimethacrylate (UDMA), triethyleneglycol dimethacrylate (TEGDMA), and ethoxylated bisphenol-A dimethacrylate (Bis-EMA). The interactions that arise in the monomer mixture and the characteristics of the resulting polymer network are the most important factors, which define the final properties of dental materials. The use of three different monomers in proper proportions may create a strong polymer matrix. In this paper, fourteen resin materials, based on urethane dimethacrylate with different co-monomers such as Bis-GMA or Bis-EMA, were evaluated. TEGDMA was used as the diluting monomer. The flexural strength (FS), diametral tensile strength (DTS), and hardness (HV) were determined. The impacts of material composition on the water absorption and dissolution were evaluated as well. The highest FS was 89.5 MPa, while the lowest was 69.7 MPa. The median DTS for the tested materials was found to range from 20 to 30 MPa. The hardness of the tested materials ranged from 14 to 16 HV. UDMA/TEGDMA matrices were characterized by the highest adsorption values. The overall results indicated that changes in the materials' properties are not strictly proportional to the material's compositional changes. The matrices showed good properties when the composite contained an equal mixture of Bis-GMA/Bis-EMA and UDMA or the content of the UDMA monomer was higher.