The effects on bone cells of metal ions released from orthopaedic implants. A review

Influence of obesity on load-transfer mechanism, contact mechanics, and longevity of cemented acetabular cup

Objective

This investigation aimed to assess the impact of obesity on the load-transfer mechanism, longevity, and contact mechanics of cemented acetabular cups.

Methods

Three obesity scenarios were considered: obese case-I (100-110 kg), obese case-II (120-130 kg), and obese case-III (140-150 kg). Utilising six finite element models, the effects of different bodyweights on load transfer, contact mechanics, and cup longevity during normal walking conditions were assessed. Muscle forces and hip joint reaction forces were adjusted and linearly calibrated based on obesity cases.

Results

Elevated stresses in cortical and cancellous bones, as well as the cement mantle, were observed in obese cases, suggesting a heightened risk of loosening and failure of the cemented fixation of the acetabular cup. Additionally, increased contact pressure and micromotion between articulating surfaces were noted in obese individuals, with a gradual escalation from obese case-I to obese case-III.

Conclusions

These findings highlight the significant negative impact of obesity on the performance of cemented acetabular cups, emphasizing the importance of considering bodyweight variations in the design and assessment of orthopaedic implants for optimal functionality and durability.

Hypoallergenic Knee Implant Usage and Clinical Outcomes: Are They Safe and Effective?

Background

One of the most debated topics in modern total knee arthroplasty (TKA) is the impact of metal hypersensitivity (MH) as a potential cause of prosthesis failure. Implanting hypoallergenic prostheses to avoid potential problems in suspected cases of MH is one treatment option that can be used in such cases. However, their long-term clinical safety and efficacy are not well proven.

Methods

All literature relevant to modern hypoallergenic implants were reviewed and summarized to provide a comprehensive synopsis. In addition, a detailed literature search was performed on PUBMED, MEDLINE, and Google Scholar to identify all the clinical studies reporting outcomes for hypoallergenic knee implants. Our search was confined to those studies published as full manuscripts in the English language from July 2018 to July 2023.

Results

To minimize the risk of MH, new implant variants have been developed which are either under clinical evaluation or in routine clinical use. These include conventional metal implants with protective coatings (mono- or multilayer) and metal-free implants. However, there is insufficient clinical data to confirm the rationale and effectiveness of using these "hypoallergenic" TKA implants.

Conclusions

Published studies and arthroplasty registry data analyses indicate no significant differences between hypoallergenic and standard TKAs with overall good survival rates. In the future, further high-quality studies are needed to better understand the complexity of this subject.

Interfaces between Cranial Bone and AISI 304 Steel after Long-Term Implantation: A Case Study of Cranial Screws

Interfaces between AISI 304 stainless steel screws and cranial bone were investigated after long-term implantation lasting for 42 years. Samples containing the interface regions were analyzed using state-of-the-art analytical techniques including secondary ion mass, Fourier-transform infrared, Raman, and X-ray photoelectron spectroscopies. Local samples for scanning transmission electron microscopy were cut from the interface regions using the focused ion beam technique. A chemical composition across the interface was recorded in length scales covering micrometric and nanometric resolutions and relevant differences were found between peri-implant and the distant cranial bone, indicating generally younger bone tissue in the peri-implant area. Furthermore, the energy dispersive spectroscopy revealed an 80 nm thick steel surface layer enriched by oxygen suggesting that the AISI 304 material undergoes a corrosion attack. The attack is associated with transport of metallic ions, namely, ferrous and ferric iron, into the bone layer adjacent to the implant. The results comply with an anticipated interplay between released iron ions and osteoclast proliferation. The interplay gives rise to an autocatalytic process in which the iron ions stimulate the osteoclast activity while a formation of fresh bone resorption sites boosts the corrosion process through interactions between acidic osteoclast extracellular compartments and the implant surface. The autocatalytic process thus may account for an accelerated turnover of the peri-implant bone.

Prosthetic Metals: Release, Metabolism and Toxicity

The development of metallic joint prostheses has been ongoing for more than a century alongside advancements in hip and knee arthroplasty. Among the materials utilized, the Cobalt-Chromium-Molybdenum (Co-Cr-Mo) and Titanium-Aluminum-Vanadium (Ti-Al-V) alloys are predominant in joint prosthesis construction, predominantly due to their commendable biocompatibility, mechanical strength, and corrosion resistance. Nonetheless, over time, the physical wear, electrochemical corrosion, and inflammation induced by these alloys that occur post-implantation can cause the release of various metallic components. The released metals can then flow and metabolize in vivo, subsequently causing potential local or systemic harm. This review first details joint prosthesis development and acknowledges the release of prosthetic metals. Second, we outline the metallic concentration, biodistribution, and elimination pathways of the released prosthetic metals. Lastly, we discuss the possible organ, cellular, critical biomolecules, and significant signaling pathway toxicities and adverse effects that arise from exposure to these metals.

Surface Topography Steer Soft Tissue Response and Antibacterial Function at the Transmucosal Region of Titanium Implant

Metallic dental implants have been extensively used in clinical practice due to their superior mechanical properties, biocompatibility, and aesthetic outcomes. However, their integration with the surrounding soft tissue at the mucosal region remains challenging and can cause implant failure due to the peri-implant immune microenvironment. The soft tissue integration of dental implants can be ameliorated through different surface modifications. This review discussed and summarized the current knowledge of topography-mediated immune response and topography-mediated antibacterial activity in Ti dental implants which enhance soft tissue integration and their clinical performance. For example, nanopillar-like topographies such as spinules, and spikes showed effective antibacterial activity in human salivary biofilm which was due to the lethal stretching of bacterial membrane between the nanopillars. The key findings of this review were (I) cross-talk between surface nanotopography and soft tissue integration in which the surface nanotopography can guide the perpendicular orientation of collagen fibers into connective tissue which leads to the stability of soft tissue, (II) nanotubular array could shift the macrophage phenotype from pro-inflammatory (M1) to anti-inflammatory (M2) and manipulate the balance of osteogenesis/osteoclasia, and (III) surface nanotopography can provide specific sites for the loading of antibacterial agents and metallic nanoparticles of clinical interest functionalizing the implant surface. Silver-containing nanotubular topography significantly decreased the formation of fibrous encapsulation in per-implant soft tissue and showed synergistic antifungal and antibacterial properties. Although the Ti implants with surface nanotopography have shown promising in targeting soft tissue healing in vitro and in vivo through their immunomodulatory and antibacterial properties, however, long-term in vivo studies need to be conducted particularly in osteoporotic, and diabetic patients to ensure their desired performance with immunomodulatory and antibacterial properties. The optimization of product development is another challenging issue for its clinical translation, as the dental implant with surface nanotopography must endure implantation and operation inside the dental microenvironment. Finally, the sustainable release of metallic nanoparticles could be challenging to reduce cytotoxicity while augmenting the therapeutic effects.

The activity of monocyte-derived macrophages after stimulation with platelet-rich and platelet-poor concentrates. Study on an ovine model of insertion of a tibial implant coated with silicon-doped diamond-like carbon

Introduction

Macrophages are crucial immune cells that play a role in tissue repair and can exhibit pro- or anti-inflammatory behaviour based on environmental stimulation. Their functional phenotype can be affected by platelet-derived products as determined by those products' composition. When the inflammatory response caused by implantation is excessive, it can lead to rejection of the implant. Therefore, a thorough evaluation of implant haemocompatibility is necessary to minimise undesirable consequences.

Material and Methods

In an in vitro study, monocyte-derived macrophages (MDMs) were obtained from the whole blood of sheep after a silicon-doped diamond-like carbon-coated implant insertion. These MDMs were then exposed to autologous platelet-derived products for functional marker analysis.

Results

Platelet-poor plasma (PPP) and pure platelet-rich plasma (P-PRP) stimulation increased arginase-1 activity, while leukocyte-rich PRP stimulation produced a mixed response involving higher O2- (6.49 ± 2.43 nM vs non-stimulated 3.51 ± 1.23 nM, P-value < 0.05) and NO (3.28 ± 1.38 μM vs non-stimulated 2.55 ± 0.32μM, P-value < 0.05) generation.

Conclusion

Using PPP and P-PRP stimulation in post-implantation procedures may contribute to the polarisation of macrophages towards the M2-like pro-resolving phenotype, thereby accelerating wound healing. This would also prevent implant degradation due to an excessive inflammatory process.

Metal ions: the unfading stars of bone regeneration-from bone metabolism regulation to biomaterial applications

In recent years, bone regeneration has emerged as a remarkable field that offers promising guidance for treating bone-related diseases, such as bone defects, bone infections, and osteosarcoma. Among various bone regeneration approaches, the metal ion-based strategy has surfaced as a prospective candidate approach owing to the extensive regulatory role of metal ions in bone metabolism and the diversity of corresponding delivery strategies. Various metal ions can promote bone regeneration through three primary strategies: balancing the effects of osteoblasts and osteoclasts, regulating the immune microenvironment, and promoting bone angiogenesis. In the meantime, the complex molecular mechanisms behind these strategies are being consistently explored. Moreover, the accelerated development of biomaterials broadens the prospect of metal ions applied to bone regeneration. This review highlights the potential of metal ions for bone regeneration and their underlying mechanisms. We propose that future investigations focus on refining the clinical utilization of metal ions using both mechanistic inquiry and materials engineering to bolster the clinical effectiveness of metal ion-based approaches for bone regeneration.

Optimization of the Manufacturing Process and Mechanical Evaluation of a Functionally Graded Biodegradable Composite Screw for Orthopedic Applications

Background

Metal screws are commonly used for fracture fixations. However, the high modulus of elasticity relative to bones and releasing metallic ions by the metal screw needed a second surgery to remove the implant after the healing period. Furthermore, the removal of metal screws following the healing of the bone is a serious problem that can lead to refracture due to the presence of holes in the screw. Bioresorbable screws can overcome most of the problems associated with metallic screws which motivated research on manufacturing nonmetallic screws.

Methods

In this study, three-layer poly L-lactic acid/bioactive glass composite screws were manufactured according to functionally graded material theory, by the forging process. All of the physical and chemical parameters in the manufacturing stages from making composite layers to the forging process were optimized to obtain suitable mechanical properties and durability off the screw in load-bearing positions.

Results

The tri-layer composite screw with unidirectional, ±20° angled, and random fibers orientation from core to shell shows a flexural load of 661.5 ± 20.3 (N) with a decrease about 31% after 4-week degradation. Furthermore, its pull-out force was 1.8 ± 0.1 (N) which is considerably more than the degradable polymeric screws. Moreover, the integrity of the composite screws was maintained during the degradation process.

Conclusions

By optimizing the manufacturing process and composition of the composite and crystallinity, mechanical properties (flexural, torsion, and pull-out) were improved and making it a perfect candidate for load-bearing applications in orthopedic implants. Improving the fiber/matrix interface through the use of a coupling agent was also considered to preserve the initial mechanical properties. The manufactured screw is sufficiently robust enough to replace metals for orthopedic load-bearing applications.

Inflammatory Impact on Tissues Surrounding the Dental Implant of Singular Abutments Bonded onto Titanium Base - A Randomized Controlled Trial

Introduction

In dental implants, the biochemical connection between titanium (ti) and bony tissue has been well established. The properties of dental implants such as osseointegration and stability depend upon composition, design of the implant, connection, and design of the abutment, and additional removal of abutments. Recently, laser-generated micro-grooved surface (LSS) and TI abutments are the main focus of preventing peri-implant inflammation.

Objectives

To assess the inflammatory impact of singular abutments bonded onto titanium bases on tissues surrounding the dental implant.

Methods

Twenty subjects were enrolled. Only those subjects were enrolled who were scheduled to undergo prosthetic rehabilitation of missing teeth. Random division of subjects was done. Group A: Test abutment group and Group B: Control abutment group. The test abutments comprised Computer-Aided Design/Computer-Aided Manufacturing (CAD/CAM) titanium abutments bonded onto titanium abutments. However, control abutments were customized and only one-piece CAD/CAM titanium abutments were enrolled.On 6 months and 12 months of follow-up, the clinical and radiographic examination was done. Assessment of the bone level changes, clinical variables, and IL-1b levels was assessed.

Results

Mean IL-1b levels in Group A subjects at baseline, 6 months, and 12 months were 1.52 pg/mL, 1.69 pg/mL, and 1.55 pg/mL, respectively. Mean IL-1b levels among the patients of group B at baseline, 6 months, and 12 months were 1.56 pg/mL, 1.71 pg/mL, and 1.54 pg/mL, respectively.

Conclusion

Within the limitation of the study, it can be concluded that the impact on the inflammatory condition of surrounding tissues of dental implant does not vary significantly between single abutments bonded onto Titanium bases and singular abutments.

Therapeutic activity of lipoxin A4 in TiO2-induced arthritis in mice: NF-κB and Nrf2 in synovial fluid leukocytes and neuronal TRPV1 mechanisms

Background

Lipoxin A4 (LXA4) has anti-inflammatory and pro-resolutive roles in inflammation. We evaluated the effects and mechanisms of action of LXA4 in titanium dioxide (TiO2) arthritis, a model of prosthesis-induced joint inflammation and pain.

Methods

Mice were stimulated with TiO2 (3mg) in the knee joint followed by LXA4 (0.1, 1, or 10ng/animal) or vehicle (ethanol 3.2% in saline) administration. Pain-like behavior, inflammation, and dosages were performed to assess the effects of LXA4 in vivo.

Results

LXA4 reduced mechanical and thermal hyperalgesia, histopathological damage, edema, and recruitment of leukocytes without liver, kidney, or stomach toxicity. LXA4 reduced leukocyte migration and modulated cytokine production. These effects were explained by reduced nuclear factor kappa B (NFκB) activation in recruited macrophages. LXA4 improved antioxidant parameters [reduced glutathione (GSH) and 2,2-azino-bis 3-ethylbenzothiazoline-6-sulfonate (ABTS) levels, nuclear factor erythroid 2-related factor 2 (Nrf2) mRNA and Nrf2 protein expression], reducing reactive oxygen species (ROS) fluorescent detection induced by TiO2 in synovial fluid leukocytes. We observed an increase of lipoxin receptor (ALX/FPR2) in transient receptor potential cation channel subfamily V member 1 (TRPV1)+ DRG nociceptive neurons upon TiO2 inflammation. LXA4 reduced TiO2-induced TRPV1 mRNA expression and protein detection, as well TRPV1 co-staining with p-NFκB, indicating reduction of neuronal activation. LXA4 down-modulated neuronal activation and response to capsaicin (a TRPV1 agonist) and AITC [a transient receptor potential ankyrin 1 (TRPA1) agonist] of DRG neurons.

Conclusion

LXA4 might target recruited leukocytes and primary afferent nociceptive neurons to exert analgesic and anti-inflammatory activities in a model resembling what is observed in patients with prosthesis inflammation.

Biocompatibility of a Zr-Based Metallic Glass Enabled by Additive Manufacturing

The present work explored the use of the selective laser melting (SLM) technique to develop a Zr-based bulk metallic glass (BMG) and investigate the influence of the process parameters on obtaining different levels of surface roughness. Moreover, the potential of the additively manufactured BMG Zr_59.3Cu_28.8Al_10.4Nb_1.5 (trade name AMLOY-ZR01) as an implant material was studied by evaluating the osteoblastic cell response to the alloy and its stability under simulated biological environments. The materials were characterized in terms of degree of crystallinity, surface roughness, and morphology, followed by a systematic investigation of the response of the MC3T3-E1 preosteoblastic cell line to the as-printed samples. The materials supported cell proliferation and differentiation of the preosteoblastic cells, with results comparable to the reference material Ti-6Al-4V. The surface microroughness and surface morphology (porous or groove-type laser tracks) investigated in this study did not have a significant effect on modulating the cell response. Ion release experiments showed a large increase in ion release under inflammatory conditions as compared to regular physiological conditions, which could be attributed to the increased local corrosion under inflammatory conditions. The findings in this work showed that the surface roughness of the additively manufactured BMG AMLOY-ZR01 can be tailored by controlling the laser power applied during the SLM process. The favorable cell response to the as-printed AMLOY-ZR01 represents of a significant advancement of the investigation of additively manufactured BMGs for orthopedic applications, while the results of the ion release study highlights the effect that inflammatory conditions could have on the degradation of the alloy.

Insight into synergetic effects of serum albumin and glucose on the biodegradation behavior of WE43 alloy in simulated body fluid

The biodegradation rate of Mg alloy medical devices, such as screws and plates for temporary bone fracture fixation or coronary angioplasty stents, is an increasingly important area of study.In vitromodels of the corrosion behavior of these devices use revised simulated body fluid (m-SBF) based on a healthy individual's blood chemistry. Therefore, model outputs have limited application to patients with altered blood plasma glucose or protein concentrations. This work studies the biodegradation behavior of Mg alloy WE43 in m-SBF modified with varying concentrations of glucose and bovine serum albumin (BSA) to (1) mimic a range of disease states and (2) determine the contributions of each biomolecule to corrosion. Measurements include the Mg ion release rate, electrolyte pH, the extent of hydrogen evolution (as a proxy for corrosion rate), surface morphology, and corrosion product composition and effects. BSA (0.1 g l^-1) suppresses the rate of hydrogen evolution (about 30%) after 24 h and-to a lesser degree-Mg²⁺release in both the presence and absence of glucose. This effect gets more pronounced with time, possibly due to BSA adsorption on the Mg surface. Electrochemical studies confirm that adding glucose (2 g l^-1) to the solution containing BSA (0.1 g l^-1) caused a decrease in corrosion resistance (by around 40%), and concomitant increase in the hydrogen evolution rate (from 10.32 to 11.04 mg cm^-2d^-1) to levels far beyond the tolerance limits of live tissues.

Ultrasound evaluations and guided procedures of the painful joint arthroplasty

The purpose of this article is to describe the use of ultrasound for the diagnosis and treatment of painful joint arthroplasty. Ultrasound plays a crucial role in the diagnosis of the painful joint arthroplasty, especially given its unique dynamic capabilities, convenience, and high resolution. Ultrasound guidance is also instrumental for procedures in both diagnosing and in select cases, treating the painful joint arthroplasty. Topics to be discussed in this article include trends in arthroplasty placement, benefits of the use of ultrasound overall, and ultrasound evaluation of periprosthetic joint infections. We will also review the sonographic findings with dissociated/displaced components and adverse reaction to metallic debris including metallosis, trunnionosis, and metal-on-metal pseudotumors. Additionally, we will discuss ultrasound evaluation of tendon pathologies with arthroplasties, including dynamic maneuvers to evaluate for tendon impingement/snapping. Finally, we will cover ultrasound-guided joint arthroplasty injection indications and precautions. KEY POINTS: • Ultrasound is preferred over MRI in patients with joint arthroplasty and plays a crucial role in diagnosis, especially given its unique dynamic capabilities, convenience and high resolution. • It is especially beneficial for US-guided aspiration in periprosthetic joint infections; effectively used to evaluate periprosthetic fluid collections, facilitating differentiation between abscesses and aseptic collections, and tracking sinus tracts. • Recently, the diagnosis of periprosthetic joint infections has shifted focus to biomarkers in the periprosthetic fluid, specifically α-defensin, which has a high sensitivity and specificity for diagnosing infection. • Cutibacterium acnes is a major pathogen responsible for shoulder arthroplasty infections, often presenting with normal laboratory values and since slow growing, must be kept for a minimum of 14 days.

Hypersensitivity Reaction to Metal: A Bibliometric Study

Background: To delineate the scientific publications on metal hypersensitivity. Methods: Scopus database from 1946 to 2020, written in English, Spanish, or Portuguese. This is a bibliometric study, with a descriptive and quantitative approach. For data analysis, we used RStudio® and VOSviewer® and bibliometric packages-bibliometrix and biblioshiny. Results: Of the 804 articles retrieved, most of the publications come from European, Asian, and American countries, with Germany, Japan, and United States leading. Published articles and keywords refer to orthopedic, dermatological, and orthodontic specialties. Conclusion: Scientific production is scarce with slight oscillations in the studied period, authored predominantly by researchers in North America and Europe. Articles were mostly published in scientific journals in the fields of dermatology, dentistry, and orthopedics, which indicated the need for greater investments in the research development on the topic.

Psychiatric Disorders and Genotoxicity Following Primary Metal on Polyethylene Total Hip Arthroplasty and Their Correlation to Cobalt/Chromium Levels

Introduction

Hip arthroplasty (HA) using implantable metal components is among the commonest orthopedic interventions. However, it can be followed by several complications following corrosion and the release of metal ions. Several studies proved that damaged genomic DNA may contribute to the pathophysiology of mental disorders.

Aim

The current work aims to evaluate the psychiatric disorders in metal on polyethylene hip arthroplasty (MOP-HA) patients and its correlation to cobalt/chromium (Co/Cr) levels and genotoxicity.

Methods

The work was a longitudinal follow-up study including 34 adults with unilateral primary MOP-HA meeting the inclusion and exclusion criteria. Preoperatively, 6, 12-months-postoperatively, patients were examined for cognitive impairment using mini-mental-state-examination (MMSE), depression using major-depressive-inventory (MDI), and blood samples were collected for estimation of Co/Cr, detection of genotoxicity by single-cell-gel-electrophoresis (comet assay) and serum 8-hydroxy-2'-deoxyguanosine (8-OHdG).

Results

Cognitive impairment was reported in 18.5% and 14.8% at 6-months, and 12-months postoperative, respectively. Depressive disorder was recorded in 22.2% at 6-months and 14.8% at 12-months postoperative. The marginal homogeneity tests proved a non-significant difference. There was a non-significant difference in preoperative, 6-months, 12-months postoperative MMSE, and MDI scores. There were significantly increased Co/Cr levels at 6-months postoperative. The levels decreased at 12-months postoperative, however, still significantly higher than preoperative values. There was a significant increase in serum 8-OHdG and the levels were positively correlated to cobalt levels at both 6 and 12-months-postoperative. There was a non-significant difference among preoperative, 6-months, and 12-months postoperative comet assay measurements.

Conclusion

From previous findings, we can conclude that will-functioning MOP hip arthroplasty can induce increased ion levels and positively correlated increase in biochemical markers of genotoxicity (8-OHdG).

Effects of Zinc, Magnesium, and Iron Ions on Bone Tissue Engineering

Large-sized bone defects are a great challenge in clinics and considerably impair the quality of patients' daily life. Tissue engineering strategies using cells, scaffolds, and bioactive molecules to regulate the microenvironment in bone regeneration is a promising approach. Zinc, magnesium, and iron ions are natural elements in bone tissue and participate in many physiological processes of bone metabolism and therefore have great potential for bone tissue engineering and regeneration. In this review, we performed a systematic analysis on the effects of zinc, magnesium, and iron ions in bone tissue engineering. We focus on the role of these ions in properties of scaffolds (mechanical strength, degradation, osteogenesis, antibacterial properties, etc.). We hope that our summary of the current research achievements and our notifications of potential strategies to improve the effects of zinc, magnesium, and iron ions in scaffolds for bone repair and regeneration will find new inspiration and breakthroughs to inspire future research.

The Abundance of Trace Elements in Human Bone Relative to Bone Type and Bone Pathology

As the global population ages and the proportion of individuals afflicted with musculoskeletal disease spirals upward, there is an increasing interest in understanding and preventing bone-related diseases. Bone diseases, such as osteoporosis and osteoarthritis, are known to be influenced by a variety of factors including age, gender, nutrition, and genetics, but are also inherently linked to the human body's ability to produce biominerals of suitable quality. Because the crystal lattice structure and mineralogy of bone hydroxyapatite is surprisingly analogous to geological hydroxyapatite, trace element levels and exposure have long been proposed to influence the structure of biominerals as they do geological minerals (e.g., strontium substitution changes the crystal lattice of bone minerals, while toxic lead disrupt bone cellular processes leading to bone disease). Here, we explore the distribution of trace elements in human bones to evaluate the distribution of these elements with respect to bone type (cortical vs. trabecular) and bone disease (osteoarthritis vs. osteoporosis). We find higher concentrations of many metabolically active transition metals, as well as lead, in cortical bone compared to trabecular bone. When compared to patients who have osteoarthritis, and thus presumably normal bone minerals, osteoporosis patients have higher concentrations of scandium and chromium (Cr) in trabecular bone, and Cr and lead in cortical bone. Lower concentrations of barium and titanium are associated with osteoporotic trabecular bone. This survey is an exploratory cross-sectional geochemical examination of several trace element concentrations previously understudied in human bone minerals.

Metallic Implants Used in Lumbar Interbody Fusion

Over the last decade, pedicle fixation systems have evolved and modifications in spinal fusion techniques have been developed to increase fusion rates and improve clinical outcomes after lumbar interbody fusion (LIF). Regarding materials used for screw and rod manufacturing, metals, especially titanium alloys, are the most popular resources. In the case of pedicle screws, that biomaterial can be also doped with hydroxyapatite, CaP, ECM, or tantalum. Other materials used for rod fabrication include cobalt-chromium alloys and nitinol (nickel-titanium alloy). In terms of mechanical properties, the ideal implant used in LIF should have high tensile and fatigue strength, Young's modulus similar to that of the bone, and should be 100% resistant to corrosion to avoid mechanical failures. On the other hand, a comprehensive understanding of cellular and molecular pathways is essential to identify preferable characteristics of implanted biomaterial to obtain fusion and avoid implant loosening. Implanted material elicits a biological response driven by immune cells at the site of insertion. These reactions are subdivided into innate (primary cellular response with no previous exposure) and adaptive (a specific type of reaction induced after earlier exposure to the antigen) and are responsible for wound healing, fusion, and also adverse reactions, i.e., hypersensitivity. The main purposes of this literature review are to summarize the physical and mechanical properties of metal alloys used for spinal instrumentation in LIF which include fatigue strength, Young's modulus, and corrosion resistance. Moreover, we also focused on describing biological response after their implantation into the human body. Our review paper is mainly focused on titanium, cobalt-chromium, nickel-titanium (nitinol), and stainless steel alloys.

Prodigiosin-Loaded Poly(lactic acid) to Combat the Biofilm-Associated Infections

Poly(lactic acid) (PLA) is an emerging biobased implant material. Despite its biocompatibility and the aseptic procedures followed during orthopedic surgery, bacterial infection remains an obstacle to implementing PLA-based implants. To tackle this issue, prodigiosin-incorporated PLA has been developed, which possesses improved hydrophobicity with a contact angle of 111 ± 1.5°. The degradation temperature of the prodigiosin is 215 °C, which is more than the melting temperature of PLA, which supports the processability and sterilization of the PLA-based implants without any toxic gases. Further, prodigiosin improves the transparency of PLA and acts as a nucleation site. The spherulite density increases three times compared to that of neat PLA. The inherent methoxy group of prodigiosin is an active site responsible for the inhibition of bacterial attack and biofilm formation. The in vitro study on biofilm formation shows excellent inhibition activity against implant-associated pathogens such as Klebsiella aerogenes and Staphylococcus aureus.

Bio-Inspired Nanostructured Ti-6Al-4V Alloy: The Role of Two Alkaline Etchants and the Hydrothermal Processing Duration on Antibacterial Activity

Inspired by observations that the natural topography observed on cicada and dragonfly wings may be lethal to bacteria, researchers have sought to reproduce these nanostructures on biomaterials with the goal of reducing implant-associated infections. Titanium and its alloys are widely employed biomaterials with excellent properties but are susceptible to bacterial colonisation. Hydrothermal etching is a simple, cost-effective procedure which fabricates nanoscale protrusions of various dimensions upon titanium, depending on the etching parameters used. We investigated the role of etching time and the choice of cation (sodium and potassium) in the alkaline heat treatment on the topographical, physical, and bactericidal properties of the resulting modified titanium surfaces. Optimal etching times were 4 h for sodium hydroxide (NaOH) and 5 h for potassium hydroxide (KOH). NaOH etching for 4 h produced dense, but somewhat ordered, surface nanofeatures with 75 nanospikes per µm². In comparison, KOH etching for 5 h resulted sparser but nonetheless disordered surface morphology with only 8 spikes per µm². The NaOH surface was more effective at eliminating Gram-negative pathogens, while the KOH surface was more effective against the Gram-positive strains. These findings may guide further research and development of bactericidal titanium surfaces which are optimised for the predominant pathogens associated with the intended application.

Effect of Copper and Selenium Supplementation on the Level of Elements in Rats' Femurs under Neoplastic Conditions

A study was conducted to determine the effect of long-term supplementation with selenium and copper, administered at twice the level used in the standard diet of rats, on the content of selected elements in the femoral bones of healthy rats and rats with implanted LNCaP cancer cells. After an adaptation period, the animals were randomly divided into two experimental groups. The rats in the experimental group were implanted with prostate cancer cells. The rats in the control group were kept in the same conditions as those in the experimental group and fed the same diet, but without implanted cancer cells. The cancer cells (LNCaP) were intraperitoneally implanted in the amount of 1 × 106 (in PBS 0.4 mL) at the age of 90 days. The content of elements in the samples was determined by a quadrupole mass spectrometer with inductively coupled plasma ionization (ICP-MS). In the femoral bones of rats with implanted LNCaP cells, in the case of the standard diet and the copper-enriched diet, there was a marked decreasing trend in the content of the analysed elements relative to the control rats. This may indicate slow osteolysis taking place in the bone tissue. Contrasting results were obtained for the diet enriched with selenium; there was no significant reduction in the level of these elements, and there was even an increase in the concentrations of Fe and K in the bones of rats with implanted LNCaP cells. Particularly, numerous changes in the mineral composition of the bones were generated by enriching the diet with copper. The elements that most often underwent changes (losses) in the bones were cobalt, iron, manganese and molybdenum. The changes observed, most likely induced by the implantation of LNCaP cells, may indicate a disturbance of mineral homeostasis.

The Application of an Allogenic Bone Screw for Stabilization of a Modified Chevron Osteotomy: A Prospective Analysis

Background: Distal first metatarsal osteotomies are commonly performed operative procedures for hallux valgus deformity, and usually involve fixation with a metal screw. However, various bioabsorbable osteosynthesis materials have been in use for a number of years. One recent innovation is the Shark Screw®, a human cortical bone allograft. This study aimed to evaluate the efficacy and safety of this allogeneic screw in the stabilization of Reversed L-Shaped osteotomy, a modified Chevron osteotomy. Methods: In a prospective study, 15 patients underwent a Reversed L-Shaped osteotomy stabilized with the allogenic bone screw Radiological data on osteointegration of the screw and correction of the intermetatarsal angle were recorded. Furthermore, each follow-up examination included the collection of clinical data, the American Orthopedic Foot and Ankle Society (AOFAS) score, evaluation of pain level, and patient’s overall satisfaction. Results: Full osseous fusion of the osteotomy was seen in all patients. The bone screws were radiographically integrated after approximately 6.5 (±2.6) months. Neither nonunion nor failure occurred in any of our cases. Furthermore, we did not find any potential graft reaction. The AOFAS score improved significantly from 51.6 (±15.2) points to 90.9 (±10.3) (p < 0.001). The preoperative hallux valgus angle and intermetatarsal angle decreased significantly from 24.8 (±4.9) degrees to 7.2 (±4.4) degrees (p < 0.001) and 12.6 (±3.2) degrees to 4.8 (±1.3) degrees (p < 0.001), respectively. Conclusions: With this study, we demonstrated the efficiency of the allogenic bone screw (Shark Screw®) in regard to clinical and radiological short-term outcomes.

Success Factors of Additive Manufactured Root Analogue Implants

Dental implantation is an effective method for the treatment of loose teeth, but the threaded dental implants used in the clinic cannot match with the tooth extraction socket. A root analogue implant (RAI) has the congruence shape, which reduces the damage to bone and soft tissue. Additive manufacturing (AM) technologies have the advantages of high precision, flexibility, and easy operation, becoming the main manufacturing method of RAI in basic research. The purpose of this systematic review is to summarize AM technologies used for RAI manufacturing as well as the factors affecting successful implantation. First, it introduces the AM technologies according to different operating principles and summarizes the advantages and disadvantages of each method. Then the influences of materials, structure design, surface characteristics, implant site, and positioning are discussed, providing reference for designers and dentists. Finally, it addresses the gap between basic research and clinical application for additive manufactured RAIs and discusses the current challenges and future research directions for this field.

Mesenchymal Stem Cell-Immune Cell Interaction and Related Modulations for Bone Tissue Engineering

Critical bone defects and related delayed union and nonunion are still worldwide problems to be solved. Bone tissue engineering is mainly aimed at achieving satisfactory bone reconstruction. Mesenchymal stem cells (MSCs) are a kind of pluripotent stem cells that can differentiate into bone cells and can be used as one of the key pillars of bone tissue engineering. In recent decades, immune responses play an important role in bone regeneration. Innate immune responses provide a suitable inflammatory microenvironment for bone regeneration and initiate bone regeneration in the early stage of fracture repair. Adaptive immune responses maintain bone regeneration and bone remodeling. MSCs and immune cells regulate each other. All kinds of immune cells and secreted cytokines can regulate the migration, proliferation, and osteogenic differentiation of MSCs, which have a strong immunomodulatory ability to these immune cells. This review mainly introduces the interaction between MSCs and immune cells on bone regeneration and its potential mechanism, and discusses the practical application in bone tissue engineering by modulating this kind of cell-to-cell crosstalk. Thus, an in-depth understanding of these principles of bone immunology can provide a new way for bone tissue engineering.

Effects of the secondary shot in the double shot peening process on the residual compressive stress distribution of Ti-6Al-4V

Double shot peening is the development of shot peening by shooting large media as a first shot and re-shooting again with smaller media as a second shot in order to achieve high residual compressive stress and hardness at the surface, while the in-depth effect can still be maintained. This research aims to examine the effect of media type and media size when used in the second shot of double shot peening on hardness, roughness, and residual stress to identify the suitable conditions and compare them with single shot peening, such as conventional shot peening and fine shot peening, which was used as the first shot and second shot. Ti–6Al–4V was used as the substrate material, while various diameter sizes of silica and SUS304 media were selected as the media for the second shot in the process. The results showed that in the case of the larger size of silica media in the second shot of double shot peening, the hardness and residual compressive stress on the surface clearly increased more than with the smaller media due to the higher Almen intensity, which affected impact energy. On the other hand, when shooting with SUS304 media as a second shot, the increment of residual compressive stress and hardness, including roughness reduction on the surface, showed less effect than was the case for silica media, due to the lower Almen intensity, which affected the impact energy transfer. This research found that the condition of shooting with 80 μm of silica media as the second shot could generate the highest hardness and residual compressive stress on the surface, which increased by 14% and 53%, respectively, while roughness was decreased by 20% when compared with single shot peening.

The application of an allogeneic bone screw for osteosynthesis in hand and foot surgery: a case series

INTRODUCTION

The allogeneic bone screw transplant is a new osteosynthesis device making the use of foreign fixation material obsolete for various kinds of indications. Moreover, it is integrated into the recipient bone by natural bone remodeling without harming the surrounding tissue. The aim of this study was to determine the efficacy and safety of the transplant for osteotomy and arthrodesis in hand and foot surgery and to evaluate the clinical importance of the device.

MATERIALS AND METHODS

A single-surgeon case series of 32 patients who had undergone hand or foot surgery with the application of an allogeneic bone screw with an average follow-up time of 1 year is reported. Clinical data were reviewed to evaluate the pain levels and satisfaction of the patients and the frequency and type of complications occurring during the healing process. Routine radiography and computed tomography were reviewed to determine the fusion rate, the ingrowth behavior of the transplant and the possible occurrence of transplant failure.

RESULTS

High patient satisfaction was paired with low postoperative pain levels and a low complication rate. 97% of the patients were free of pain at the timepoint of the second follow-up examination, the mean time of recovery of full mobility was 50.1 ± 26.1 days after surgery. Wound healing disturbance occurred only in two cases. Bony consolidation of the osteotomy or arthrodesis gap as well as osseointegration of the transplant was seen in all cases. No transplant failure or transplant loosening occurred.

CONCLUSIONS

The application of the allogeneic bone screw resulted in a 100% fusion rate while the patient burden was low. The transplant is safe and suited for various kinds of osteosynthesis in hand and foot surgery.

Benefits of Residual Aluminum Oxide for Sand Blasting Titanium Dental Implants: Osseointegration and Bactericidal Effects

OBJECTIVES

The purpose of this work was to determine the influence of residual alumina after sand blasting treatment in titanium dental implants. This paper studied the effect of alumina on physico-chemical surface properties, such as: surface wettability, surface energy. Osseointegration and bacteria adhesion were determined in order to determine the effect of the abrasive particles.

MATERIALS AND METHODS

Three surfaces were studied: (1) as-received, (2) rough surface with residual alumina from sand blasting on the surface and (3) with the same roughness but without residual alumina. Roughness was determined by white light interferometer microscopy. Surface wettability was evaluated with a contact angle video-based system and the surface free energy by means of Owens and Wendt equation. Scanning electron microscopy equipped with microanalysis was used to study the morphology and determine the chemical composition of the surfaces. Bacteria (Lactobacillus salivarius and Streptococcus sanguinis) were cultured in each surface. In total, 110 dental implants were placed into the bone of eight minipigs in order to compare the osseointegration. The percentage of bone-to-implant contact was determined after 4 and 6 weeks of implantation with histometric analysis.

RESULTS

The surfaces with residual alumina presented a lower surface free energy than clean surfaces. The in vivo studies demonstrated that the residual alumina accelerated bone tissue growth at different implantation times, in relation to clean dental implants. In addition, residual alumina showed a bactericidal effect by decreasing the quantity of bacteria adhering to the titanium.

CONCLUSIONS

It is possible to verify the benefits that the alumina (percentages around 8% in weight) produces on the surface of titanium dental implants.

CLINICAL RELEVANCE

Clinicians should be aware of the benefits of sand-blasted alumina due to the physico-chemical surface changes demonstrated in in vivo tests.

Conductive Scaffolds for Bone Tissue Engineering: Current State and Future Outlook

Bone tissue engineering strategies attempt to regenerate bone tissue lost due to injury or disease. Three-dimensional (3D) scaffolds maintain structural integrity and provide support, while improving tissue regeneration through amplified cellular responses between implanted materials and native tissues. Through this, scaffolds that show great osteoinductive abilities as well as desirable mechanical properties have been studied. Recently, scaffolding for engineered bone-like tissues have evolved with the use of conductive materials for increased scaffold bioactivity. These materials make use of several characteristics that have been shown to be useful in tissue engineering applications and combine them in the hope of improved cellular responses through stimulation (i.e., mechanical or electrical). With the addition of conductive materials, these bioactive synthetic bone substitutes could result in improved regeneration outcomes by reducing current factors limiting the effectiveness of existing scaffolding materials. This review seeks to overview the challenges associated with the current state of bone tissue engineering, the need to produce new grafting substitutes, and the promising future that conductive materials present towards alleviating the issues associated with bone repair and regeneration.

Recent Advances in the Evaluation of Antimicrobial Materials for Resolution of Orthopedic Implant-Associated Infections In Vivo

While orthopedic implant-associated infections are rare, revision surgeries resulting from infections incur considerable healthcare costs and represent a substantial research area clinically, in academia, and in industry. In recent years, there have been numerous advances in the development of antimicrobial strategies for the prevention and treatment of orthopedic implant-associated infections which offer promise to improve the limitations of existing delivery systems through local and controlled release of antimicrobial agents. Prior to translation to in vivo orthopedic implant-associated infection models, the properties (e.g., degradation, antimicrobial activity, biocompatibility) of the antimicrobial materials can be evaluated in subcutaneous implant in vivo models. The antimicrobial materials are then incorporated into in vivo implant models to evaluate the efficacy of using the material to prevent or treat implant-associated infections. Recent technological advances such as 3D-printing, bacterial genomic sequencing, and real-time in vivo imaging of infection and inflammation have contributed to the development of preclinical implant-associated infection models that more effectively recapitulate the clinical presentation of infections and improve the evaluation of antimicrobial materials. This Review highlights the advantages and limitations of antimicrobial materials used in conjunction with orthopedic implants for the prevention and treatment of orthopedic implant-associated infections and discusses how these materials are evaluated in preclinical in vivo models. This analysis serves as a resource for biomaterial researchers in the selection of an appropriate orthopedic implant-associated infection preclinical model to evaluate novel antimicrobial materials.

Collagen 2A Type B Induction after 3D Bioprinting Chondrocytes In Situ into Osteoarthritic Chondral Tibial Lesion

OBJECTIVE

Large cartilage defects and osteoarthritis (OA) cause cartilage loss and remain a therapeutic challenge. Three-dimensional (3D) bioprinting with autologous cells using a computer-aided design (CAD) model generated from 3D imaging has the potential to reconstruct patient-specific features that match an articular joint lesion.

DESIGN

To scan a human OA tibial plateau with a cartilage defect, retrieved after total knee arthroplasty, following clinical imaging techniques were used: (1) computed tomography (CT), (2) magnetic resonance imaging (MRI), and (3) a 3D scanner. From such a scan, a CAD file was obtained to generate G-code to control 3D bioprinting in situ directly into the tibial plateau lesion.

RESULTS

Highest resolution was obtained using the 3D scanner (2.77 times more points/mm² than CT), and of the 3 devices tested, only the 3D scanner was able to detect the actual OA defect area. Human chondrocytes included in 3D bioprinted constructs produced extracellular matrix and formed cartilage tissue fragments after 2 weeks of differentiation and high levels of a mature splice version of collagen type II (Col IIA type B), characteristic of native articular cartilage and aggrecan (ACAN). Chondrocytes had a mean viability of 81% in prints after day 5 of differentiation toward cartilage and similar viability was detected in control 3D pellet differentiation of chondrocytes (mean viability 72%).

CONCLUSION

Articular cartilage can be formed in 3D bioprints. Thus, this 3D bioprinting system with chondrocytes simulating a patient-specific 3D model provides an attractive strategy for future treatments of cartilage defects or early OA.

3D Bioprinted Implants for Cartilage Repair in Intervertebral Discs and Knee Menisci

Cartilage defects pose a significant clinical challenge as they can lead to joint pain, swelling and stiffness, which reduces mobility and function thereby significantly affecting the quality of life of patients. More than 250,000 cartilage repair surgeries are performed in the United States every year. The current gold standard is the treatment of focal cartilage defects and bone damage with nonflexible metal or plastic prosthetics. However, these prosthetics are often made from hard and stiff materials that limits mobility and flexibility, and results in leaching of metal particles into the body, degeneration of adjacent soft bone tissues and possible failure of the implant with time. As a result, the patients may require revision surgeries to replace the worn implants or adjacent vertebrae. More recently, autograft - and allograft-based repair strategies have been studied, however these too are limited by donor site morbidity and the limited availability of tissues for surgery. There has been increasing interest in the past two decades in the area of cartilage tissue engineering where methods like 3D bioprinting may be implemented to generate functional constructs using a combination of cells, growth factors (GF) and biocompatible materials. 3D bioprinting allows for the modulation of mechanical properties of the developed constructs to maintain the required flexibility following implantation while also providing the stiffness needed to support body weight. In this review, we will provide a comprehensive overview of current advances in 3D bioprinting for cartilage tissue engineering for knee menisci and intervertebral disc repair. We will also discuss promising medical-grade materials and techniques that can be used for printing, and the future outlook of this emerging field.

Osteoblast Cell Response on Polycrystalline Diamond-Coated Additively Manufactured Scaffolds

Additive manufacturing of metals using selective laser melting can create customized parts with various degrees of complexity and geometry for medical implants. However, challenges remain in accepting orthopedic implants due to the bio-inert surface of metal scaffolds, resulting in a lack of osseointegration. Here, we show that polycrystalline diamond (PCD) coatings on selective laser melted titanium (SLM-Ti) scaffolds can improve the cell-to-material interaction of osteoblasts. The results show that by controlling the uniformity of the diamond coatings, we can mediate the biological response of osteoblasts, such as cell adhesion, proliferation, and spreading. The osteoblasts show favorable cell adhesion and spreading on non-planar PCD-coated scaffolds compared to the un-coated SLM-Ti scaffold. This study plays an important role in understanding the key physicochemical behavior of bone cell growth on customized orthopedic implant materials.

Recent Advances in the Treatment of Bone Metastases and Primary Bone Tumors: An Up-to-Date Review

In the last decades, the treatment of primary and secondary bone tumors has faced a slow-down in its development, being mainly based on chemotherapy, radiotherapy, and surgical interventions. However, these conventional therapeutic strategies present a series of disadvantages (e.g., multidrug resistance, tumor recurrence, severe side effects, formation of large bone defects), which limit their application and efficacy. In recent years, these procedures were combined with several adjuvant therapies, with different degrees of success. To overcome the drawbacks of current therapies and improve treatment outcomes, other strategies started being investigated, like carrier-mediated drug delivery, bone substitutes for repairing bone defects, and multifunctional scaffolds with bone tissue regeneration and antitumor properties. Thus, this paper aims to present the types of bone tumors and their current treatment approaches, further focusing on the recent advances in new therapeutic alternatives.

The Expression Levels of Toll-like Receptors after Metallic Particle and Ion Exposition in the Synovium of a Murine Model

To date, the exact role of specific Toll-like receptors (TLRs) in regulating immune reactivity to metallic byproducts of orthopedic implants has not been fully clarified. In light of the situation, our objective in this investigation was to assess the expression levels of surface TLRs after metallic particle and ion exposure in an established animal model. Ten female BALB/c mice in each group received intra-articular injections of phosphate buffer (PBS) (control), metallic particles (MP), and metallic ions (MI), respectively. Seven days later, immunohistochemical staining was undertaken in the synovial layer of the murine knee joints using anti-TLR 1, 2, 4, 5, and 6 polyclonal antibodies. In addition to increased cellular infiltrates and a hyperplastic synovial membrane, the MP group showed significantly elevated TLR expression compared to the control group and had higher TLR 1-, 4-, and 6-positive cells than the MI group (p < 0.0167). TLR 4- and TLR 6-positive cells were significantly augmented for the MI group compared to the control group (p < 0.0167). Additionally, greenish corrosion particles found in the necrotic tissue suggested that metallic particles might release a certain level of locally toxic metallic ions in vivo.

Refractory Metal Coated Alumina Foams as Support Material for Stem Cell and Fibroblasts Cultivation

Ceramics are widely used as implant materials; however, they are brittle and may emit particles when used in these applications. To overcome this disadvantage, alumina foams, which represent a 3D cellular structure comparable to that of human trabecular bone structures, were sputter coated with platinum, tantalum or titanium and modified with fibronectin or collagen type I, components of the extracellular matrix (ECM). To proof the cell material interaction, the unmodified and modified materials were cultured with (a) mesenchymal stem cells being a perfect indicator for biocompatibility and releasing important cytokines of the stem cell niche and (b) with fibroblasts characterized as mediators of inflammation and therefore an important cellular component of the foreign body reaction and inflammation after implantation. To optimize and compare the influence of metal surfaces on cellular behavior, planar glass substrates have been used. Identified biocompatible metal surface of platinum, titanium and tantalum were sputtered on ceramic foams modified with the above-mentioned ECM components to investigate cellular behavior in a 3D environment. The cellular alumina support was characterized with respect to its cellular/porous structure and niche accessibility and coating thickness of the refractory metals; the average cell size was 2.3 mm, the average size of the cell windows was 1.8 mm, and the total foam porosity was 91.4%. The Pt, Ti and Ta coatings were completely dense covering the entire alumina foam surface. The metals titanium and tantalum were colonized very well by the stem cells without a coating of ECM components, whereas the fibroblasts preferred components of the ECM on the alumina foam surface.

Three-dimensional printing technology for patient-matched instrument in treatment of cubitus varus deformity: A case report

BACKGROUND

Recently, medical three-dimensional printing technology (3DPT) has demonstrated potential benefits for the treatment of cubitus varus deformity (CVD) by improving accuracy of the osteotomy through the use of an osteotomy guide, with or without a patient-mated plate. Here, we present an interesting CVD case, involving a patient who was treated with corrective biplanar chevron osteotomy using an innovative customized osteotomy guide and a newly designed patient-matched monoblock crosslink plate created with 3DPT.

CASE SUMMARY

A 32-year-old female presented with a significant CVD from childhood injury. A computer simulation was processed using images from computerized tomography scans of both upper extremities. The biplanar chevron osteotomy was designed to create identical anatomy between the mirror image of the contralateral distal humerus and the osteotomized distal humerus. Next, the customized osteotomy guide and patient-matched monoblock crosslink plate were designed and printed. A simulation osteotomy was created for the real-sized bone model, and the operation was performed using the posterior paratricipital approach with k-wire positioning from the customized osteotomy guide as a predrilled hole for screw fixation to achieve immediate control of the reduction after osteotomy. Our method allowed for successful treatment of the CVD case, significantly improving the patient’s radiographic and clinical outcomes, with satisfactory result.

CONCLUSION

3DPT-created patient-matched osteotomy guide and instrumentation provides accurate control during CVD correction.

Medical Device Industry Approaches for Addressing Sources of Failing Cytotoxicity Scores

To ensure patient safety, medical device manufacturers are required by the Food and Drug Administration and other regulatory bodies to perform biocompatibility evaluations on their devices per standards, such as the AAMI-approved ISO 10993-1:2018 (ANSI/AAMI/ISO 10993-1:2018).However, some of these biological tests (e.g., systemic toxicity studies) have long lead times and are costly, which may hinder the release of new medical devices. In recent years, an alternative method using a risk-based approach for evaluating the toxicity (or biocompatibility) profile of chemicals and materials used in medical devices has become more mainstream. This approach is used as a complement to or substitute for traditional testing methods (e.g., systemic toxicity endpoints). Regardless of the approach, the one test still used routinely in initial screening is the cytotoxicity test, which is based on an in vitro cell culture system to evaluate potential biocompatibility effects of the final finished form of a medical device. However, it is known that this sensitive test is not always compatible with specific materials and can lead to failing cytotoxicity scores and an incorrect assumption of potential biological or toxicological adverse effects. This article discusses the common culprits of in vitro cytotoxicity failures, as well as describes the regulatory-approved methodology for cytotoxicity testing and the approach of using toxicological risk assessment to address clinical relevance of cytotoxicity failures for medical devices. Further, discrepancies among test results from in vitro tests, use of published half-maximal inhibitory concentration data, and the derivation of their relationship to tolerable exposure limits, reference doses, or no observed adverse effect levels are highlighted to demonstrate that although cytotoxicity tests in general are regarded as a useful sensitive screening assays, specific medical device materials are not compatible with these cellular/in vitro systems. For these cases, the results should be analyzed using more clinically relevant approaches (e.g., through chemical analysis or written risk assessment).

Use of Plasma Technologies for Antibacterial Surface Properties of Metals

Bacterial infections of medical devices present severe problems connected with long-term antibiotic treatment, implant failure, and high hospital costs. Therefore, there are enormous demands for innovative techniques which would improve the surface properties of implantable materials. Plasma technologies present one of the compelling ways to improve metal's antibacterial activity; plasma treatment can significantly alter metal surfaces' physicochemical properties, such as surface chemistry, roughness, wettability, surface charge, and crystallinity, which all play an important role in the biological response of medical materials. Herein, the most common plasma treatment techniques like plasma spraying, plasma immersion ion implantation, plasma vapor deposition, and plasma electrolytic oxidation as well as novel approaches based on gaseous plasma treatment of surfaces are gathered and presented. The latest results of different surface modification approaches and their influence on metals' antibacterial surface properties are presented and critically discussed. The mechanisms involved in bactericidal effects of plasma-treated surfaces are discussed and novel results of surface modification of metal materials by highly reactive oxygen plasma are presented.

Chemical Evaluation of Energy Dispersive X-ray Spectroscopy Analysis of Different Failing Dental Implant Surfaces: A Comparative Clinical Trial

The aim of the present study is to compare two different implant surface chemistries of failing dental implants. Sixteen patients (mean age: 52 ± 8.27 with eight females and eight males) and 34 implants were included in the study. Group-I implants consisted of a blasted/etched surface with a final process surface, while Group-II implants consisted of the sandblasted acid etching (SLA) method. The chemical surface analysis was performed by the energy dispersive X-ray spectroscopy (EDX) method from coronal, middle, and apical parts of each implant. Titanium (Ti) element values were found to be 20.22 ± 15.7 at.% in Group I and 33.96 ± 13.62 at.% in Group-II in the middle of the dental implants. Aluminum (Al) element values were found to be 0.01 ± 0.002 in Group-I and 0.17 ± 0.28 at.% in Group II in the middle of the dental implants, and statistically significant differences were found between the groups for the Al and Ti elements in the middle of the dental implants (p < 0.05). There was a statistically significant difference for the Ti, Al, O, Ca, Fe, P, and Mg elements in the coronal, middle, and apical parts of the implants in the intragroup evaluation (p < 0.05). It is reported that different parts of the implants affected by peri-implant inflammation show different surface chemistries, from coronal to apical, but there is no difference in the implants with different surfaces.

Mixed oxide nanotubes in nanomedicine: A dead-end or a bridge to the future?

Nanomedicine has seen a significant rise in the development of new research tools and clinically functional devices. In this regard, significant advances and new commercial applications are expected in the pharmaceutical and orthopedic industries. For advanced orthopedic implant technologies, appropriate nanoscale surface modifications are highly effective strategies and are widely studied in the literature for improving implant performance. It is well-established that implants with nanotubular surfaces show a drastic improvement in new bone creation and gene expression compared to implants without nanotopography. Nevertheless, the scientific and clinical understanding of mixed oxide nanotubes (MONs) and their potential applications, especially in biomedical applications are still in the early stages of development. This review aims to establish a credible platform for the current and future roles of MONs in nanomedicine, particularly in advanced orthopedic implants. We first introduce the concept of MONs and then discuss the preparation strategies. This is followed by a review of the recent advancement of MONs in biomedical applications, including mineralization abilities, biocompatibility, antibacterial activity, cell culture, and animal testing, as well as clinical possibilities. To conclude, we propose that the combination of nanotubular surface modification with incorporating sensor allows clinicians to precisely record patient data as a critical contributor to evidence-based medicine.

A Review on Recent Advancements of Graphene and Graphene-Related Materials in Biological Applications

Graphene is the most outstanding material among the new nanostructured carbonaceous species discovered and produced. Graphene’s astonishing properties (i.e., electronic conductivity, mechanical robustness, large surface area) have led to a deep change in the material science field. In this review, after a brief overview of the main characteristics of graphene and related materials, we present an extensive overview of the most recent achievements in biological uses of graphene and related materials.

Key Properties of a Bioactive Ag-SiO2/TiO2 Coating on NiTi Shape Memory Alloy as Necessary at the Development of a New Class of Biomedical Materials

Recent years have seen the dynamic development of methods for functionalizing the surface of implants using biomaterials that can mimic the physical and mechanical nature of native tissue, prevent the formation of bacterial biofilm, promote osteoconduction, and have the ability to sustain cell proliferation. One of the concepts for achieving this goal, which is presented in this work, is to functionalize the surface of NiTi shape memory alloy by an atypical glass-like nanocomposite that consists of SiO2-TiO2 with silver nanoparticles. However, determining the potential medical uses of bio(nano)coating prepared in this way requires an analysis of its surface roughness, tribology, or wettability, especially in the context of the commonly used reference coat-forming hydroxyapatite (HAp). According to our results, the surface roughness ranged between (112 ± 3) nm (Ag-SiO2)-(141 ± 5) nm (HAp), the water contact angle was in the range (74.8 ± 1.6)° (Ag-SiO2)-(70.6 ± 1.2)° (HAp), while the surface free energy was in the range of 45.4 mJ/m2 (Ag-SiO2)-46.8 mJ/m2 (HAp). The adhesive force and friction coefficient were determined to be 1.04 (Ag-SiO2)-1.14 (HAp) and 0.247 ± 0.012 (Ag-SiO2) and 0.397 ± 0.034 (HAp), respectively. The chemical data showed that the release of the metal, mainly Ni from the covered NiTi substrate or Ag from Ag-SiO2 coating had a negligible effect. It was revealed that the NiTi alloy that was coated with Ag-SiO2 did not favor the formation of E. coli or S. aureus biofilm compared to the HAp-coated alloy. Moreover, both approaches to surface functionalization indicated good viability of the normal human dermal fibroblast and osteoblast cells and confirmed the high osteoconductive features of the biomaterial. The similarities of both types of coat-forming materials indicate an excellent potential of the silver-silica composite as a new material for the functionalization of the surface of a biomaterial and the development of a new type of functionalized implants.

Titanium for Orthopedic Applications: An Overview of Surface Modification to Improve Biocompatibility and Prevent Bacterial Biofilm Formation

Titanium and its alloys have emerged as excellent candidates for use as orthopedic biomaterials. Nevertheless, there are often complications arising after implantation of orthopedic devices, most notably prosthetic joint infection and aseptic loosening. To ensure that implanted devices remain functional in situ, innovation in surface modification has attracted much attention in the effort to develop orthopedic materials with optimal characteristics at the biomaterial-tissue interface. This review will draw together metallurgy, surface engineering, biofilm microbiology, and biomaterial science. It will serve to appreciate why titanium and its alloys are frequently used orthopedic biomaterials and address some of the challenges facing these biomaterials currently, including the significant problem of device-associated infection. Finally, the authors shall consolidate and evaluate surface modification techniques employed to overcome some of these issues by offering a unique perspective as to the direction in which research is headed from a broad, interdisciplinary point of view.

Comparison of the Physicochemical Properties of Carboxylic and Phosphonic Acid Self-Assembled Monolayers Created on a Ti-6Al-4V Substrate

This study compared the tribological properties in nano- and millinewton load ranges of Ti‑6Al-4V surfaces that were modified using self-assembled monolayers (SAMs) of carboxylic and phosphonic acids. The effectiveness of the creation of SAMs with the use of the liquid phase deposition (LPD) technique was monitored by the contact angle measurement, the surface free energy (SFE) calculation, X-ray photoelectron spectroscopy (XPS), and Fourier-transform infrared spectroscopy (FTIR) measurements. The obtained results indicated that more stable and well-ordered layers, which were characterized by the lowest values of the coefficient of friction, adhesion, and wear rate, were obtained using phosphonic acid as a surface modifier. Based on the obtained results, it was found that the Ti-6Al-4V alloy modified by phosphonic acid would be the most advantageous for practical applications, especially in micro- and nanoelectromechanical systems (MEMS/NEMS).

Comprehensive Survey on Nanobiomaterials for Bone Tissue Engineering Applications

One of the most important ideas ever produced by the application of materials science to the medical field is the notion of biomaterials. The nanostructured biomaterials play a crucial role in the development of new treatment strategies including not only the replacement of tissues and organs, but also repair and regeneration. They are designed to interact with damaged or injured tissues to induce regeneration, or as a forest for the production of laboratory tissues, so they must be micro-environmentally sensitive. The existing materials have many limitations, including impaired cell attachment, proliferation, and toxicity. Nanotechnology may open new avenues to bone tissue engineering by forming new assemblies similar in size and shape to the existing hierarchical bone structure. Organic and inorganic nanobiomaterials are increasingly used for bone tissue engineering applications because they may allow to overcome some of the current restrictions entailed by bone regeneration methods. This review covers the applications of different organic and inorganic nanobiomaterials in the field of hard tissue engineering.

Metal-Specific Biomaterial Accumulation in Human Peri-Implant Bone and Bone Marrow

Metallic implants are frequently used in medicine to support and replace degenerated tissues. Implant loosening due to particle exposure remains a major cause for revision arthroplasty. The exact role of metal debris in sterile peri-implant inflammation is controversial, as it remains unclear whether and how metals chemically alter and potentially accumulate behind an insulating peri-implant membrane, in the adjacent bone and bone marrow (BM). An intensively focused and bright synchrotron X-ray beam allows for spatially resolving the multi-elemental composition of peri-implant tissues from patients undergoing revision surgery. In peri-implant BM, particulate cobalt (Co) is exclusively co-localized with chromium (Cr), non-particulate Cr accumulates in the BM matrix. Particles consisting of Co and Cr contain less Co than bulk alloy, which indicates a pronounced dissolution capacity. Particulate titanium (Ti) is abundant in the BM and analyzed Ti nanoparticles predominantly consist of titanium dioxide in the anatase crystal phase. Co and Cr but not Ti integrate into peri-implant bone trabeculae. The characteristic of Cr to accumulate in the intertrabecular matrix and trabecular bone is reproducible in a human 3D in vitro model. This study illustrates the importance of updating the view on long-term consequences of biomaterial usage and reveals toxicokinetics within highly sensitive organs.

The gut microbiota may be a novel pathogenic mechanism in loosening of orthopedic implants in rats

Particles released from implants cause inflammatory bone loss, which is a key factor in aseptic loosening, the most common reason for joint replacement failure. With the anticipated increased incidence of total joint replacement in the next decade, implant failure will continue to burden patients. The gut microbiome is increasingly recognized as an important factor in bone physiology, however, its role in implant loosening is currently unknown. We tested the hypothesis that implant loosening is associated with changes in the gut microbiota in a preclinical model. When the particle challenge caused local joint inflammation, decreased peri-implant bone volume, and decreased implant fixation, the gut microbiota was affected. When the particle challenge did not cause this triad of local effects, the gut microbiota was not affected. Our results suggest that cross-talk between these compartments is a previously unrecognized mechanism of failure following total joint replacement.

Calcium Phosphate Based Bioactive Ceramic Layers on Implant Materials Preparation, Properties, and Biological Performance

Calcium phosphate based bioactive ceramics (CPCs) can be successfully applied as implant coatings since they are chemically similar to the inorganic constituent of hard tissues (bones, teeth). Nowadays, in orthopedic surgeries, it is still common to use metallic implants. However, the biological response of the human body to these foreign materials can be adverse, causing the failure of implant materials. This disadvantage can be avoided by bioactive coatings on the surface of implants. CPCs can be prepared by different routes that provide coatings of different quality and properties. In our paper, we compared the morphological, chemical, and biological properties of CPC coatings prepared by the pulse current electrochemical method. The size and thickness of the pulse current deposited platelets largely depended on the applied parameters such as the length of ton and the current density. The decrease in the ton/toff ratio resulted in thinner, more oriented platelets, while the increase in current density caused a significant decrease in grain size. The higher pH value and the heat treatment favored the phase transformation of CPCs from monetite to hydroxyapatite. The contact angle measurements showed increased hydrophilicity of the CPC sample as well as better biocompatibility compared to the uncoated implant material.