Effect of Adding Different Concentrations of Silver Nanoparticles on Flexural Strength and Microhardness of Different Denture Base Materials

AIM

This study aimed to evaluate the effect of adding different concentrations of silver nanoparticles (AgNPs) on the flexural strength and microhardness of various denture base materials.

MATERIALS AND METHODS

For this study, a total of 60 specimens were used and divided into equal groups. The first group consisted of heat-cured acrylic resin (Vertex-Germany), while the second group consisted of thermoplastic resin (Breflex 2nd edition, Germany). The samples were created using a split brass mold with dimensions of 65 × 10 × 2.5 mm, in accordance with the specifications of the American Dental Association (specifically No. 12 for flexural and microhardness). Following this, the samples were divided into three groups (A, B, and C) based on different concentrations of AgNPs (0, 2, and 5%). The flexural and microhardness of the samples were assessed using a universal testing machine and the Vickers hardness test, respectively. The data were gathered, organized, and analyzed using statistical methods.

RESULTS

The flexural strength findings showed a significant difference between the two groups. Also, there was a considerable decrease in the average value of the acrylic group as the concentrations of AgNPs rose, while the flexural strength of the thermoplastic group notably improved. Regarding microhardness, the results showed a significant difference between the two groups. It showed that the mean value of both groups increased with increasing concentrations of AgNPs.

CONCLUSION

Within the limitations of laboratory testing conditions of this study, it was discovered that AgNPs negatively impact the flexural strength of acrylic resins. Furthermore, an increase in the concentration of AgNPs was found to be directly related to the flexural strength of thermoplastic resin and the microhardness of both groups.

CLINICAL SIGNIFICANCE

The concentration of AgNPs has a significant impact on certain mechanical properties of denture base materials, but it is important to consider their potential toxicity. How to cite this article: El-Hussein IG. Effect of Adding Different Concentrations of Silver Nanoparticles on Flexural Strength and Microhardness of Different Denture Base Materials. J Contemp Dent Pract 2024;25(5):417-423.

Multifunctional 58S Bioactive Glass/Silver/Cerium Oxide-Based Biocomposites with Effective Antibacterial, Cytocompatibility, and Mechanical Properties

58S bioactive glass (BG) has effective biocompatibility and bioresorbable properties for bone tissue engineering; however, it has limitations regarding antibacterial, antioxidant, and mechanical properties. Therefore, we have developed BGAC biocomposites by reinforcing 58S BG with silver and ceria nanoparticles, which showed effective bactericidal properties by forming inhibited zones of 2.13 mm (against Escherichia coli) and 1.96 mm (against Staphylococcus aureus; evidenced by disc diffusion assay) and an increment in the antioxidant properties by 39.9%. Moreover, the elastic modulus, hardness, and fracture toughness were observed to be increased by ∼84.7% (∼51.9 GPa), ∼54.5% (∼3.4 GPa), and ∼160% (∼1.3 MPam1/2), whereas the specific wear rate was decreased by ∼55.2% (∼1.9 × 10-11 m3/Nm). X-ray diffraction, high-resolution transmission electron microscopy, and field emission scanning electron microscopy confirmed the fabrication of biocomposites and the uniform distribution of the nanomaterials in the BG matrix. The addition of silver nanoparticles in the 58S BG matrix (in BGA) increased mechanical properties by composite strengthening and bactericidal properties by damaging the cytoplasmic membrane of bacterial cells. The addition of nanoceria in 58S BG (BGC) increased the antioxidant properties by 44.5% (as evidenced by the 2,2-diphenyl-1-picrylhydrazyl assay). The resazurin reduction assay and MTT assay confirmed the effective cytocompatibility for BGAC biocomposites against mouse embryonic fibroblast cells (NIH3T3) and mouse bone marrow stromal cells. Overall, BGAC resulted in mechanical properties comparable to those of cancellous bone, and its effective antibacterial and cytocompatibility properties make it a good candidate for bone healing.

Performance of Biocomposite Materials Reinforced by Hydroxyapatite and Seashell Nanoparticles for Bone Replacement

Bone defects and disorders include trauma, osteonecrosis, osteoporosis, bone tumours, arthritis rheumatoid, osteosarcoma, and iatrogenic injury. Obtaining a composite material with characteristics that mimic what bones in the human body have is a vital target for the purpose of replacing or repairing damaged bones. The key objective of this study was to develop a composite having mechanical and biological properties that resemble to a large extent native bone features. Highly biocompatible epoxy resin was reinforced by various weight fractions of seashell nanoparticles. The morphologies of the pristine bioepoxy, seashell-bioepoxy, and hydroxyapatite-bioepoxy composites were observed by scanning electron microscopy. Moreover, the mechanical properties were examined by the means of tension and Izod impact tests. Besides, the influence of seashell and hydroxyapatite nanoparticles on the bioepoxy chemical structure and thermal properties was also evaluated using Fourier transform infrared spectroscopy and differential scanning calorimetry technique, respectively. The tensile strength, modulus of elasticity, and impact strength of the seashell nanoparticle-reinforced bioepoxy were revealed to be higher than those of the unmodified bioepoxy and were significantly depended on the filler content. When the mass fraction of the reinforcement was 7 wt%, the improvement in the tensile strength, modulus of elasticity, and impact strength was around 46.7%, 37%, and 57%, respectively, compared to that of blank bioepoxy. In addition, these properties were higher for the composites loaded with seashell nanoparticles than those filled with commercially available hydroxyapatite nanoparticles. An enhancement in glass transition temperature for the bioepoxy after modification with both of these nanofillers was also achieved. All these features make these kinds of composites a promising option that could be used in the orthopaedic field. Furthermore, the use of seashell nanoparticles may reduce the cost of the resulted composite and alleviate the negative consequences of large quantity by-product waste seashells on the environment.