Evaluation of the physical and antifungal effects of chlorhexidine diacetate incorporated into polymethyl methacrylate

Microbiological, physicomechanical, and surface evaluation of an experimental self-curing acrylic resin containing halloysite nanotubes doped with chlorhexidine

OBJECTIVE

The objective was to synthesize halloysite nanotubes loaded with chlorhexidine (HNT/CHX) and evaluate the antimicrobial activity, microhardness, color change, and surface characteristics of an experimental self-curing acrylic resin containing varying concentrations of the synthesized nanomaterial.

METHODS

The characterization of HNT/CHX was carried out by calculating incorporation efficiency, morphological and compositional, chemical and thermal evaluations. SAR disks were made containing 0 %, 3 %, 5 %, and 10 % of HNT/CHX. Specimens (n = 3) were immersed in distilled water and spectral measurements were carried out using UV/Vis spectroscopy to evaluate the release of CHX for up to 50 days. The antimicrobial activity of the composite against Candida albicans and Streptococcus mutans was evaluated by disk-diffusion test. Microhardness, color analyses (ΔE), and surface roughness (Ra) (n = 9) were performed before and after 30 days of immersion. Data were analyzed using ANOVA/Bonferroni. {Results.} The incorporation efficiency of CHX into HNT was of 8.15 %. All test groups showed controlled and cumulative CHX release up to 30 or 50 days. Significant antimicrobial activity was verified against both microorganisms (p < 0.001). After the 30-day immersion period, the 10 % HNT/CHX group showed a significant increase in hardness (p < 0.05) and a progressive color change (p < 0.001). At T0, the 5 % and 10 % groups exhibited Ra values similar to the control group (p > 0.05), while at T30, all groups showed similar roughness values (p > 0.05). {Significance.} The modification of a SAR with HNT/CHX provides antimicrobial effect and controlled release of CHX, however, the immediate surface roughness in the 3 % group was compromised when compared to the control group.

Evaluation of polymethyl-methacrylate and acetal denture base resins processed by two different techniques before and after nano-chlorohexidine surface treatment

BACKGROUND

Flexible denture base polymers have gained popularity in modern dentistry however, their biofilm formation tendency, adversely affecting the oral tissue heath, remains a concern. Consequently, this study aimed to evaluate surface roughness and biofilm formation tendency of two types of denture base resins manufactured with two techniques before and after surface coating with chlorohexidine (CHX) NPs.

MATERIALS AND METHODS

Acetal (AC) and Polymethyl-methacrylate (PMMA) resins manufactured by conventional and CAD/CAM methods were shaped into disk (10 X 10 X 1 mm). They were dipped for 8 h and 24 h in colloidal suspension prepared by mixing aqueous solution of CHX digluconate and hexa-metaphosphate (0.01 M). Surface roughness, optical density (OD) of microbial growth media and biofilm formation tendency were evaluated directly after coating. Elutes concentrations of released CHX were evaluated for 19 days using spectrophotometer. Three-way ANOVA and Tukey's post-hoc statistical analysis were used to assess the outcomes.

RESULTS

AC CAD/CAM groups showed statistically significant higher roughness before and after coating (54.703 ± 4.32 and 77.58 ± 6.07 nm, respectively). All groups showed significant reduction in OD and biofilm formation tendency after surface coating even after 19 days of CHX NPs release.

CONCLUSIONS

Biofilm formation tendency was highly relevant to surface roughness of tested resins before coating. After CHX NPs coating all tested groups showed significant impact on microbial growth and reduction in biofilm formation tendency with no relation to surface roughness. Significant antimicrobial effect remained even after 19 days of NPs release and specimens storage.

Evaluation of the flexural strength of orthodontic acrylic resin incorporated with propolis nanoparticles: an in vitro study

AIM

Nanopropolis has become the subject of interest in medicine and dentistry as a natural product due to its outstanding properties, particularly antimicrobial activity. This study aimed at investigating the effect of nanopropolis on flexural strength of polymethyl methacrylate (PMMA).

Highlights on Drug and Ion Release and Recharge Capacity of Antimicrobial Removable Prostheses

This article aimed to review the ion and drug release, recharge abilities, and antimicrobial properties of drug/ion-releasing removable prostheses, and to assess their capability in preventing and inhibiting denture stomatitis as well preventing caries and reversing carious lesions. Data was collected from published scientific papers listed in PubMed database from January 1975 to December 2021. English full-text articles, involving clinical or in vitro studies, focusing on removable prostheses and are concerned with drug/ion release and rechargeability as a way to prevent or inhibit denture stomatitis or dental caries were included. The relevant articles reported that ion- or drug-modified polymethylmethacrylate acts as a reservoir for these ions and drugs and is capable of releasing significant amounts with sustained release effect. Recharging of modified resin resulted in greater sustainability of ion and drug release, thus improving the long-term effects of protection against demineralization and reducing the adhesion of Streptococcus mutans and Candida albicans. Modifications of removable prostheses with rechargeable ions and drugs enhance remineralization, hinder demineralization, and reduce microbial adhesion in difficult-to-access areas. Selection of denture base for clinical use will consider its ability to act as an ion/drug reservoir that is capable of release and recharge.

Evaluation of drug release, monomer conversion and surface properties of resin composites containing chlorhexidine-loaded mesoporous and nonporous hydroxyapatite nanocarriers

The aim of this study was to evaluate drug release, degree of conversion (DC), and surface properties of resin composites containing chlorhexidine (CHX)-loaded mesoporous (mHAP) and nonporous hydroxyapatite (HAP) nanocarrier. CHX loaded mHAP and HAP, or CHX without nanocarrier was added into the resin composite in 1% and 5% concentrations. After characterization of experimental materials with XRD, EDX, FT-IR, and SEM, the CHX release on the 1st, 7th, 30th, and 120th days were evaluated by UV-vis spectroscopy. DC, surface roughness, and surface hardness of the samples were also evaluated. The data was statistically analyzed. While mHAP groups released significantly higher CHX on the 30th day (p < .05), there was no statistically significant difference between the HAP and mHAP groups on the 120th day (p > .05). DCs of all groups were similar (p > .05). While mHAP and HAP groups containing 5% CHX showed significantly higher roughness than the other groups (p < .05), no statistically significant difference was observed between the other groups (p > .05). The 1% and 5% CHX groups without nanocarrier showed significantly lower surface hardness (p < .05). However, no statistically significant difference was observed between the other groups in terms of surface hardness (p > .05). A controlled CHX release was achieved by mHAP and HAP nanocarriers for 120 days. The nanocarrier addition up to 5% did not negatively affect the DC and the surface hardness which is one of the surface properties of the resin composites. Although the addition of 5% nanocarrier to the resin composite increased the surface roughness, while adding 1% of these nanocarriers did not change.

Prospects on Tuning Bioactive and Antimicrobial Denture Base Resin Materials: A Narrative Review

Denture base resin (DBR) materials are used in dentistry in constructing removable dentures and implant-supported prostheses. A plethora of evidence has demonstrated that DBR materials are associated with a high risk of denture stomatitis, a clinical complication where the soft oral tissues underneath the resin-based material are inflamed. The prevalence of denture stomatitis among denture wearers is high worldwide. Plaque accumulation and the infiltration of oral microbes into DBRs are among the main risk factors for denture stomatitis. The attachment of fungal species, mainly Candida albicans, to DBRs can irritate the underneath soft tissues, leading to the onset of the disease. As a result, several attempts were achieved to functionalize antimicrobial compounds and particles into DBRs to prevent microbial attachment. This review article explored the advanced approaches in designing bioactive and antimicrobial DBR materials. It was reported that using monomer mixtures, quaternary ammonium compounds (QACs), and organic and inorganic particles can suppress the growth of denture stomatitis-related pathogens. This paper also highlighted the importance of characterizing bioactive DBRs to be mechanically and physically sustainable. Future directions may implement a clinical translational model to attempt these materials inside the oral cavity.

How Effective Are Antimicrobial Agents on Preventing the Adhesion of Candida albicans to Denture Base Acrylic Resin Materials? A Systematic Review

Denture stomatitis is a common oral infection caused by Candid albicans. It occurs under removable dentures due to several causative and contributing factors. If not treated, it can lead to fatal systemic candida infections. Different materials and techniques have been used to treat denture stomatitis; however, no single treatment has succeeded. The purpose of this study was to review novel techniques for incorporating antimicrobial and protein repellent agents into denture acrylic resin materials and their effect on the adhesion of Candida albicans to denture base acrylic resin materials to prevent and/or treat denture stomatitis. A systematic review was conducted in which an electronic search was undertaken using different databases and relevant keywords. The literature search revealed numerous studies describing different antifungal materials incorporated into different denture acrylic resin materials. The investigated materials showed significant antimicrobial activity with slight or no effect on the physical and mechanical properties; however, the optical properties were particularly affected with higher concentrations. The incorporation of antimicrobial agents to reduce or prevent Candida albicans biofilm formation on acrylic resin proved to be very effective, and this effect was found to be proportional to the percentage of the material used. The latter should be considered carefully not to alter the physical, mechanical or optical characteristics of the denture base material.

Antifungal Polymeric Materials and Nanocomposites

Rising global populations due to medicinal advancements increases the patient population susceptible to superficial and severe fungal infections. Fungi often implicated in these diseases includes the dermatophytes (Microsporum spp., Epidermophtyon spp., Trichophyton spp.) as well as species of the Candida spp., Aspergillosis spp. and Cryptococcus spp. genera. In addition, increasing global populations leads to increasing agricultural demands. Thus, fungal infections of preharvested crops and stored food by plant pathogens such as Magnaporthe oryzae and Fusarium oxysporum can have detrimental socioeconomic effects due to food insecurity. Current antifungal strategies are based mainly on small molecule antifungal drugs. However, these drugs are limited by poor solubility and bioavailability. Furthermore, antifungal resistance against these drugs are on the rise. Thus, antimicrobial polymers offer an alternative antifungal strategy. Antifungal polymers are characterised by cationic and hydrophobic regions where the cationic regions have been shown to interact with microbial phospholipids and membranes. These polymers can be synthetic or natural and demonstrate distinct antifungal mechanisms ranging from fungal cell membrane permeabilisation, cell membrane depolarisation or cell entry. Although the relative importance of such mechanisms is difficult to decipher. Due to the chemical properties of these polymers, they can be combined with other antimicrobial compounds including existing antifungal drugs, charcoals, lipids and metal ions to elicit synergistic effects. In some cases, antifungal polymers and nanocomposites show better antifungal effects or reduced toxicity compared to the widely used small molecule antifungal drugs. This review provides an overview of antimicrobial polymers and nanocomposites with antifungal activity and the current understanding of their antifungal mechanisms.