Bonding efficiency and durability: current possibilities

Light-curable urushiol enhanced bisphenol A glycidyl dimethacrylate dentin bonding agent

OBJECTIVES

The low durability of composite resin restorations can be attributed to the degradation of the resin dentin bonding interface. Owing to the presence of hydrophilic components in the adhesive, the integrity of the resin dentin bonding interface is easily compromised, which, in turn, leads to a reduction in bond strength. The hydrophilic nature of the adhesive leads to water sorption, phase separation, and leaching of the resin component. Therefore, hydrophobic adhesives could effectively be used to stabilize the integrity and durability of the resin dentin bonding interface.

METHODS

We synthesized a novel hydrophobic dentin adhesive by partially replacing bisphenol A glycidyl dimethacrylate (Bis-GMA) with a light-curable urushiol monomer. The properties of the produced adhesive, including the degree of conversion, viscosity, contact angle, water sorption/solubility, and mechanical strength, were comprehensively examined and compared to those of the commercially adhesive Adper Single Bond2 as a positive control. The adhesive properties were determined using microtensile bond strength measurements, laser confocal microscopy, scanning electron microscopy observations, and nanoleakage tests. Finally, the novel adhesive was subjected to biocompatibility testing to determine its potential cytotoxicity.

RESULTS

At a light-curable urushiol content of 20 %, the synthesized adhesive exhibited high degrees of conversion and hydrophobicity, low cytotoxicity, good mechanical properties, and outstanding adhesive strength.

CONCLUSIONS

The introduction of the light-curable urushiol into dentin adhesives can significantly enhance their hydrophobic, mechanical, and bonding properties, demonstrating potential to significantly improve restoration longevity.

CLINICAL SIGNIFICANCE

The integration of light-curable urushiol has endowed the experimental adhesives with several enhanced functionalities. These notable benefits underscore the suitability of this monomer for expanded applications in clinical practice.

Internal Adaptation of Composite Fillings Made Using Universal Adhesives-A Micro-Computed Tomography Analysis

This study aimed to evaluate internal tooth-filling interfaces of composite fillings made using universal adhesives using micro-computed tomography (µCT). Sixty class V cavities were randomly assigned into six groups: Peak Universal etch and rinse (PER), Peak Universal self-etch (PSE), Adhese Universal etch and rinse (AER), and Adhese Universal self-etch (ASE). Two further adhesives considered gold standards were used as control groups: OptiBond FL (OER) for the etch and rinse technique and Clearfil SE for the self-etch technique (CSE). All teeth were subjected to thermomechanical loading and four-year water storage. Next, they were analyzed using µCT to investigate the internal tooth-filling interfaces. The proportions between the gap volume (GV) at the tooth-filling interface and the volume of applied composite filling (FV), between the gap and cavity volumes (CV), and between the gap volumes at the tooth-filling interface of the external (EGV) and internal (IGV) parts were calculated. Adhese Universal achieved the significantly lowest gap-to-filling- and gap-to-cavity-volume ratios for both types of etching techniques comparing to those of the Peak Universal and control groups. Significant differences between the gaps in external and internal parts of the tooth-filling interface were only noted in the control groups. Internal gap formation and development at the tooth-filling interface depend on the material as well as the type of its application.

The cross-linking and protective effect of artemisinin and its derivatives on collagen fibers of demineralized dentin surface

OBJECTIVE

To investigate the cross-linking and protective effect of artemisinin (ART), dihydroartemisinin (DHA), and artesunate (AST) on collagen fibers of demineralized dentin surface.

METHODS

Molecular docking was used to predict potential interactions of ART, DHA, and AST with dentin type I collagen. Human third molars without caries were completely demineralized and treated with different solutions for 1 min. The molecular interactions and cross-linking degree of ART and its derivatives with dentin collagen were evaluated by FTIR spectroscopy, total extractable protein content, and a ninhydrin assay. Scanning electron microscopy, hydroxyproline release, and ultimate microtensile strength tests (μUTS) were employed to confirm the mechanical properties and anti-collagenase degradation properties of dentin collagen fibers.

RESULTS

ART, DHA, and AST combined with dentin type I collagen mainly through hydrogen bonding and hydrophobic interactions, and the cross-linking reaction sites were mainly C=O and CN functional groups. Compared to the control group, ART and its derivatives significantly increased the degree of cross-linking. Additionally, significant increases were observed in resistance to enzymatic digestion and mechanical properties of the artemisinin and its derivatives group.

CONCLUSION

ART, DHA, and AST could cross-link with demineralized dentin collagen, through improving the mechanical properties and anti-collagenase degradation properties.

CLINICAL SIGNIFICANCE

The study endorses the potential use of ART and its derivatives as a prospective collagen cross-linking agent for degradation-resistant and long-period dentin bonding in composite resin restorations.

Comparative evaluation of effect of chlorhexidine application on dentin bond strength with two different adhesives after ER, CR: YSGG phototherapy: an in vitro study

This study aimed to assess the efficacy of phototherapy with an Er, Cr:YSGG laser on the bond strength of dentin using two different adhesive systems after chlorhexidine (CHX) application. Twenty-four non-carious human molar teeth were separated into three main groups: negative control Group A (Group A), CHX and phototherapy with an Er, Cr:YSGG laser (Group PC), and CHX with conventional diamond bur (no phototherapy) (Group C). These groups were divided into two subgroups based on adhesives: Clearfil Universal Quick Bond and Clearfil SE Bond. To evaluate the microtensile bond strength, the occlusal enamel surfaces of the teeth were removed with a low-speed, water-cooled diamond bur to expose hard dentin tissue. The teeth within Group PC were treated with Er, Cr:YSGG phototherapy. The surfaces were then disinfected with 0.2% chlorhexidine gluconate. Subgroups were applied according to the manufacturer's instructions using the adhesive systems mentioned above. Following adhesive application, the teeth were restored with composite resin. A microtensile bond strength test was performed on the test sticks obtained from the teeth using a universal test device. Data were analyzed using variance analysis (ANOVA) at a significance level of p < 0.05. Among all groups, the highest bond strength was achieved with Clearfil SE Bond with CHX + phototherapy (45.6 ± 4.2), while the lowest was achieved with Clearfil Universal Quick Bond without phototherapy (control group) (27.0 ± 6.7) (p < 0.05). Phototherapy with Er, Cr: YSGG following chlorhexidine application enhanced the bond strength of both the bond systems (p < 0.05).

Effect of irradiance and exposure time on the adhesive properties of universal adhesives after 2 years of storage

OBJECTIVE

This study aims to evaluate the effects of exposure time and irradiance on the dentin bonding properties (microtensile bond strength (μTBS) and nanoleakage (NL)) of the Clearfil Universal Bond Quick (CUQ) adhesive and Scotchbond Universal Adhesive (SBU) immediately and after 2 years of water storage.

MATERIAL AND METHODS

Hence, 128 human molars were randomly assigned to 16 groups based on adhesive strategy, irradiance/exposure times, and storage time for each universal adhesive tested. The adhesives were applied using the etch-and-rinse and self-etch strategies and were light-cured using four different irradiance/exposure times: 1400 mW/cm2 for 5 s (1400 × 5), 1400 mW/cm2 for 10 s (1400 × 10), 3200 mW/cm2 for 5 s (3200 × 5), and 3200 mW/cm2 for 10 s (3200 × 10). Then, each sample was restored and sectioned into a resin-dentin bonded stick to be tested for μTBS and NL (immediately and after 2 years of water storage). The mean μTBS and NL of all resin-dentin bonded sticks from the same hemi-tooth (factor time) were statistically analyzed using a three-way ANOVA and Tukey's test (a = 0.05).

RESULTS

Despite a significant decrease in the μTBS values for all groups after 2 years of water storage, the 3200 × 5 group showed higher μTBS values, whereas the 3200 × 10 group showed lower μTBS values for both universal adhesives tested. Although a significant increase in the NL values was observed for all groups after 2 years of water storage, the 3200 × 10 group showed higher NL values than the other groups (p < 0.001).

CONCLUSION

Results indicate that light-curing the adhesive layer with 14-16 J/cm2 led to an improvement in the stability of the resin-dentin adhesive interface. A longer exposure time (10 s) coupled with a higher irradiance (3200 mW/cm2) resulted in a greater degree of degradation of the adhesive interface.

CLINICAL SIGNIFICANCE

To guarantee better stability of the adhesive interface, clinicians could be preferred a light-cured universal adhesive layer with 14-16 J/cm2. Higher irradiances should be avoided.

Eighteen-month clinical evaluation of a new universal adhesive applied in the "no-waiting" technique: a randomized clinical trial

OBJECTIVE

The aim of this double-blind, randomized clinical trial was to evaluate the 6- and 18-month clinical performances of a new universal adhesive applied in the "no-waiting" (NW) technique to non-carious cervical lesions (NCCLs) using two evaluation criteria.

MATERIALS AND METHODS

One hundred and seventy-six restorations were assigned to four groups according to the adhesive system, adhesive strategy, and application mode: Prime&Bond Active (PB) applied using the etch-and-rinse (ER) and self-etch (SE) strategies with 20 s applications and Clearfil Universal Bond Quick (CQ) applied using the ER and SE strategies with the NW technique. The composite resin restorations were evaluated at baseline and after 6 and 18 months using the World Dental Federation (FDI) and US Public Health Service (USPHS) criteria. The Friedman repeated measures analysis of variance and Wilcoxon test were used for statistical analyses (α = 0.05).

RESULTS

No significant differences were observed among any of the groups or criteria after 6 months (p > 0.05). After 18 months, 10 restorations were lost (p > 0.05) (2 with PB-ER [95.5%; 95%CI: 92-100%], 4 with PB-SE [90.9%; 95%CI: 82-98%], 0 with CQ-ER [100%; 95%CI: 92-100%], and 4 with CQ-SE [90.9%; 82-98%]). The restorations performed with the SE strategy showed more marginal discrepancies than those performed with the ER strategy, mainly when the FDI criteria were used (p < 0.05). Those that used the PB-SE showed fewer marginal discrepancies than those that used the CQ-SE (FDI; p < 0.05). A few restorations showed marginal discrepancies after the USPHS analysis (p > 0.05).

CONCLUSIONS

The results when using the CQ-SE and -ER strategies with the NW technique were similar to those when using the PB-SE and -ER strategies in standard applications to non-carious cervical lesions after 6 and 18 months of clinical evaluation.

CLINICAL RELEVANCE

After 6 and 18 months, the application of Clearfil Universal Bond Quick with the "no-waiting" technique showed similar clinical performance compared to the standard application of Prime & Bond Active applied using the standard application time (20 s).

TRIAL REGISTRATION

ClinicalTrials.gov identifier RBR-5f9gps.

Comparison of collagen features of distinct types of caries-affected dentin

OBJECTIVES

To compare the biodegradability, mechanical behavior, and physicochemical features of the collagen-rich extracellular matrix (ECM) of artificial caries-affected dentin (ACAD), natural caries-affected dentin (NCAD) and sound dentin (SD).

METHODS

Dentin specimens from human molars were prepared and assigned into groups according to the type of dentin: ACAD, NCAD, or SD. ACAD was produced by incubation of demineralized SD with Streptococcus mutans in a chemically defined medium (CDM) with 1% sucrose for 7 days at 37 °C under anaerobic conditions. Specimens were assessed to determine collagen birefringence, biodegradability, mechanical behavior, and chemical composition. Data were individually processed and analyzed by ANOVA and post-hoc tests (α = 0.05).

RESULTS

CDM-based biofilm challenge reduced loss, storage, and complex moduli in ACAD (p < 0.001), while the damping capacity remained unaffected (p = 0.066). Higher red and lower green birefringence were found in ACAD and NCAD when compared with SD (p < 0.001). Differently to ACAD, SD and NCAD presented higher biodegradability to exogenous proteases (p = 0.02). Chemical analysis of the integrated areas of characteristic bands that assess mineral quality (carbonate/phosphate and crystallinity index), mineral to matrix (phosphate/amide I) and post-translational modifications (amide III/CH₂, pentosidine/CH₂, and pentosidine/amide III) (p<0.05) showed that NCAD was significantly different from SD while ACAD exhibited intermediate values.

CONCLUSIONS

CDM-based biofilm challenge produced a dentin ECM with decreased mechanical properties and increased collagen maturity. The compositional and structural conformation of the ACAD suggested that CDM-based biofilm challenge showed potential to produce artificial lesions by revealing a transitional condition towards mimicking critical features of NCAD.

CLINICAL SIGNIFICANCE

This study highlights the importance of developing a tissue that mimics the features of natural caries-affected dentin ECM for in vitro studies. Our findings suggested the potential of a modified biofilm challenge protocol to produce and simulate a relevant substrate, such as caries-affected dentin.

Secondary caries and marginal adaptation of ion-releasing versus resin composite restorations: a systematic review and meta-analysis of randomized clinical trials

This systematic review was aimed to evaluate occurrence of secondary caries and marginal adaptation in ion-releasing materials versus resin composite. Electronic search of PubMed, Scopus, and Open Grey databases with no date or language restrictions until May 21st, 2021, was conducted. Randomized clinical trials that compared ion-releasing restorations versus resin composite were included. For quantitative analysis, a random-effects meta-analysis with risk difference as an effect measure and a 95% confidence interval was used. Quality of evidence was assessed using The Grading of Recommendations, Assessment, Development, and Evaluation criteria. The risk of bias was evaluated using the Cochran Collaboration Risk of Bias tool. The inclusion criteria were met by 22 studies, and 10 studies were included in the meta-analysis. Three follow-up periods (1 year, 18 months-2 years, and 3 years) were evaluated. The overall quality of evidence for secondary caries and marginal adaptation outcomes was low. The results of the meta-analysis showed no significant difference (p > 0.05) in both outcomes between ion-releasing materials and resin composite. The occurrence of secondary caries was not dependent on the nature of the restorative material. It is more likely a complex process that involves the same risk factors as primary carious lesions.

Influence of Irradiance and Exposure Times on the Mechanical and Adhesive Properties of Universal Adhesives with Dentin

OBJECTIVES

This study evaluated the influence of irradiance/exposure time on the Knoop hardness (KHN) and polymer cross-linking density (PCLD), as well as microtensile bond strength (μTBS), nanoleakage (NL), and in situ degree of conversion (DC) of universal adhesives.

METHODS AND MATERIALS

Two universal adhesive systems, Clearfil Universal Bond Quick (CUQ) and Scotchbond Universal Adhesive (SBU), were light-cured using various irradiance/exposure times: 1400 mW/cm2 for 5 s (1400*5); 1400 mW/cm2 for 10 s (1400*10); 3200 mW/cm2 for 5 s (3200*5); and 3200 mW/cm2 for 10 s (3200*10). Adhesive disks from each group were used to measure PCLD by KHN. One hundred and twenty-eight human molars were randomly assigned to 16 groups according to the following variables: adhesive system vs adhesive strategies vs radiance/exposure times. After restoration, specimens were sectioned into resin-dentin sticks and tested for μTBS, NL, and DC. The data from PCLD (%), KHN, μTBS (MPa), NL (%), and DC (%) data were subjected to ANOVA and Tukey's test (α=0.05).

RESULTS

Significant reductions in KHN, μTBS, and DC (p=0.00001) values and an increase in NL and PCLD (p=0.00001) values were observed for 3200*10 when compared with other groups. Higher KHN, μTBS, and DC (p=0.000001) values were observed for 3200*5 in comparison with the other groups. The 1400*5 (7 J/cm2) and 1400*10 (14 J/cm2) groups showed intermediate values (p=0.000001).

CONCLUSION

Although similar results in terms of hardness, polymer cross-linking density and nanoleakage were observed when 5 seconds at 3200 mW/cm2 and 10 seconds at 1400 mW/cm2 groups were compared, the use of higher irradiance (3200 mW/cm2) for only 5 seconds showed better results in terms of bond strength and degree of conversion for both universal adhesives to dentin. The prolonged exposure time (10 seconds) at the higher irradiance (3200 mW/cm2) showed the worst results.

Gelatinolytic activity after dentin pretreatment with dimethyl sulfoxide (DMSO) combined to dental bonding systems: Perspectives for biological responses

Endogeneous proteolytic responses in dentin bonding interface have addressing to strategies to preventive and therapeutic approaches of clinical use of dentin bonding systems (DBSs), but still present limitations. The aim of this study was to examine the gelatinolytic profile by means of in situ zymography regarding the use of 1% dimethyl sulfoxide (DMSO) as an aprotic solvent. Sound human third molars were prepared and randomized in 10 groups, following the factors 1- DBS: Adper™ Scotchbond Multipurpose [MP], Adper™ Single Bond 2 [SB], Clearfil™ SE Bond [CSE] and Adper™ Scotchbond Universal - Etch-and-rinse [SU-ER] mode and self-etch mode [SU-SE], 2- dentin pretreatment: Control - Water [C], 2% CHX and 1% DMSO and 3- time: Initial-24 h [I], 6 months [6M] and 30 months [30M]. Pretreatments were applied before primer application for 30s. After restoration, specimens were cut into slices, in which one third were incubated with fluorescein-conjugated gelatin for 24h at 37 °C and analyzed by confocal laser scanning microscopy. The other two-thirds were stored for 6 or 30 months at 37 °C. Fluorescence was quantified using Image J and data was subjected for two-way ANOVA followed by Tukey test (p<0.05). Neither DMSO nor CHX affected initial analyses for any tested conditions. After 6 months, it was observed increased fluorescence for MP using both pretreatments and for SB using only DMSO. Regardless time and pretreatment, CSE and SU-SE showed stabilized gelatinolytic pattern. For SU-ER, both CHX and DMSO were able to maintain a lower fluorescence compared to control group after 6 months. 30-month performance states the susceptibility of degradation for all etched-dentin systems. DMSO pretreatment can be promising to reduce gelatinolytic activity combined with an universal adhesive system under etch-and-rinse mode. For self-etching strategies, DMSO was successful to stabilize the gelatinolytic reactions.

Micro Push-Out Bond Strength of Resin Composite to Dentin in Primary Dentition Using Three Universal Adhesives with Different pH: An In Vitro Study

To evaluate the bond strength of different universal adhesives on deciduous tooth dentineand their relationship with the composition and potential of hydrogen (pH). Methods: An in vitromicro push-out test on 150 samples (n = 50) per group per adhesive, namely, Adhese Universal(ADH; Ivoclar Vivadent), Futurabond U (FUT; Voco GmbH) (Test), and Scotchbond Universal withpre-conditioning (SCO; 3M) (Control), to record bond strength (BS) and type of adhesive failure.Results: The results of the different adhesives (megapascals (MPa)) varied, showing no statisticalsignificance. The corresponding averages are in MPa: ADH, 13.66 2.81; FUT, 14.48 2.88; SCO,14.98 3.96. Additionally, the frequency of type of failure was as follows: mixed (60.7%), adhesive(27.3%), and cohesive (12%). Conclusions: SCO, with a pH of 2.7, showed greater resistance tofracture, while FUT, with a pH of 2.3 and no pre-conditioning, approached the same values, being aone-step adhesive. No relationship was found between failure and type of adhesive.

Dentin Bond Integrity of Filled and Unfilled Resin Adhesive Enhanced with Silica Nanoparticles-An SEM, EDX, Micro-Raman, FTIR and Micro-Tensile Bond Strength Study

The objective of this study was to synthesize and assess unfilled and filled (silica nanoparticles) dentin adhesive polymer. Methods encompassing scanning electron microscopy (SEM)-namely, energy dispersive X-ray spectroscopy (EDX), micro-tensile bond strength (µTBS) test, Fourier transform infrared (FTIR), and micro-Raman spectroscopy-were utilized to investigate Si particles' shape and incorporation, dentin bond toughness, degree of conversion (DC), and adhesive-dentin interaction. The Si particles were incorporated in the experimental adhesive (EA) at 0, 5, 10, and 15 wt. % to yield Si-EA-0% (negative control group), Si-EA-5%, Si-EA-10%, and Si-EA-15% groups, respectively. Teeth were set to form bonded samples using adhesives in four groups for µTBS testing, with and without aging. Si particles were spherical shaped and resin tags having standard penetrations were detected on SEM micrographs. The EDX analysis confirmed the occurrence of Si in the adhesive groups (maximum in the Si-EA-15% group). Micro-Raman spectroscopy revealed the presence of characteristic peaks at 638, 802, and 1300 cm^-1 for the Si particles. The µTBS test revealed the highest mean values for Si-EA-15% followed by Si-EA-10%. The greatest DC was appreciated for the control group trailed by the Si-EA-5% group. The addition of Si particles of 15 and 10 wt. % in dentin adhesive showed improved bond strength. The addition of 15 wt. % resulted in a bond strength that was superior to all other groups. The Si-EA-15% group demonstrated acceptable DC, suitable dentin interaction, and resin tag formation.

A novel dentin bonding scheme based on extrafibrillar demineralization combined with covalent adhesion using a dry-bonding technique

Dentin bonding is a dynamic process that involves the penetration of adhesive resin monomers into the extrafibrillar and intrafibrillar demineralized collagen matrix using a wet-bonding technique. However, adhesive resin monomers lack the capacity to infiltrate the intrafibrillar space, and the excess water that is introduced by the wet-bonding technique remains at the bonding interface. This imperfectly bonded interface is inclined to hydrolytic degradation, severely jeopardizing the longevity of bonded clinical restorations. The present study introduces a dentin bonding scheme based on a dry-bonding technique, combined with the use of extrafibrillar demineralization and a collagen-reactive monomer (CRM)-based adhesive (CBA). Selective extrafibrillar demineralization was achieved using 1-wt% high-molecular weight (MW) carboxymethyl chitosan (CMCS) within a clinically acceptable timeframe to create a less aggressive bonding substance for dentin bonding due to its selectively extrafibrillar demineralization capacity. CMCS demineralization decreased the activation of in situ collagenase, improved the shrinking resistance of demineralized collagen, and thus provided stronger and more durable bonding than traditional phosphoric acid etching. The new dentin bonding scheme that contained CMCS and CBA and used a dry-bonding technique achieved an encouraging dentin bonding strength and durability with low technical sensitivity. This bonding scheme can be used to improve the stability of the resin-dentin interface and foster the longevity of bonded clinical restorations.

Aging Methods-An Evaluation of Their Influence on Bond Strength

Objectives  To evaluate the effect of different artificial aging methods on the bond strength of a resin composite associated with a universal adhesive (Scotchbond Universal) used under two etching approaches (self-etch [SE] or etch-and-rinse [ER]) to enamel and dentin substrates.

Materials and Methods  A total of 96 noncarious human third molars were prepared and randomly divided according to three factors ( n = 6): substrate (enamel and dentin), adhesive approach (SE and ER), and aging method (water storage for 24 hours, 6 months, or 1 year; subjected to 10,000, 20,000, or 30,000 thermal cycles; and sodium hypochlorite [NaOCl] storage for 1 or 5 hours).

Statistical Analysis  Microshear bond strength tests were conducted, and the collected data (MPa) were subjected to three-way analysis of variance (ANOVA) with post hoc Bonferroni tests ( p < 0.05) and Weibull analysis. The failure pattern was also evaluated.

Results  Three-way ANOVA revealed that the factors “substrate” ( p = 0.00) and “aging method” ( p = 0.00) had a significant effect on the bond strength, but the factor “adhesive approach” did not ( p = 0.84). The bond strength in the enamel group for the SE approach was negatively affected under 20,000 and 30,000 thermal cycles. Weibull presented the highest m in the NaOCl storage for the 5 hours group to enamel using the SE and to dentin using ER approaches. Adhesive/mixed failures were predominant for all groups.

Conclusion  Thermocycling aging (20,000 and 30,000 cycles) significantly reduced the bond strength to enamel using the SE approach. On the contrary, storage with the NaOCl method proved to increase bond strength under the evaluated conditions.

MDP-based universal adhesive system irradiated with Er,CR:YSGG: Analysis of its performance up to 6 months

This study aimed to analyze the interaction of a MDP-based universal dentin bonding system (DBS) with Er, Cr: YSGG laser irradiation, measuring the microtensile bond strength to dentin over a six-month period. The experimental design involved three factors: DBS (Adper Scotchbond Universal; Clearfil SE Bond, Adper Scotchbond Multipurpose and Adper Single Bond 2), laser (Control and Er, Cr: YSGG), and time (initial- 7 days and 6 months). Eighty dentin samples from molars were prepared (n=10) with laser irradiation after primer and DBS application. After 7 days, were subjected to micro tensile bond strength test. The data were analyzed by three-way ANOVA and Tukey tests (p<0.05). Both DBS and laser significantly affected the bonding performance and their interaction was statistically significant (p=0.0194). The self-etching mode of the MDP-based universal DBS maintained the bond strength on dentin irradiated with ER, Cr: YSGG after 6 months, while bonding with all other DBS deteriorated.

In Vitro Analysis of Quality of Dental Adhesive Bond Systems Applied in Various Conditions

Introduction: There are several methods of reducing a microleakage, and one of them is choosing appropriate adhesive material. The aim of the work was the in vitro analysis of 4 bonds: 3M ESPE “Single bond”, Dentsply “Prime and Bond Active”, Coltene “One Coat 7 Universal”, and Kuraray “Clearfil Universal Bond Quick”. Material and methods: 136 healthy molar teeth were collected and randomly split into 4 groups and Vth Class cavities were prepared. Chosen adhesives were used in four groups of teeth with the same composite. Teeth were the thermocycled, sealed, covered with lacquer, and submerged in 1% methylene blue solution for 24 h. After the thermocycling, the vertices of each tooth were sealed using dental wax. Each tooth was then fully covered with lacquer. All teeth were then submerged into 1% methylene blue solution for 24 h in room temperature. In the next step they were transversely cut through a center of restoration. The Olympus BX43 microscope was used to photograph each cut tooth. With the usage of Olympus stream software, measurement of the dye’s leakage was performed. Results. The statistical analysis proved that the most effective material when applied to ideally prepared cavity surface was Dentsply “Prime and Bond Active”. The second material was 3M ESPE “Single Bond”, third—Coltene “One Coat 7 Universal” and fourth—Kuraray “Clearfil Universal Bond Quick”. The most effective material applied to a too-dry surface was Dentsply “Prime and Bond Active”, second—3M ESPE “Single Bond”, third—Coltene “One Coat 7 Universal” and fourth—Kuraray “Clearfil Universal Bond Quick”. When it comes to too damp surfaces the best results were obtained with Dentsply “Prime and Bond Active” then Coltene “One Coat 7 Universal”, 3M ESPE “Single Bond” and Kuraray “Clearfil Universal Bond Quick”. Conclusion: The level of cavity dampness influences the quality of adhesives. Better results are obtained with over-dried surfaces than over-damp, which is connected with the dilution of the material.

Effect of thermo-mechanical cycling and chlorhexidine on the bond strength of universal adhesive system to dentin

OBJECTIVES

This study evaluated the influence of thermo-mechanical cycling (TMC) on the bond strength (BS) of a universal adhesive system (UAS - Adper Single Bond Universal, 3M ESPE) to dentin treated or not with 0.2% chlorhexidine (CHX).

METHODS

Eighty human molars were flattened until reach the dentin and separated into 4 groups according to the bonding protocol: ENR Group: 37% phosphoric acid + 3-step etch-and-rinse adhesive system (ENR); UAS Group: UAS in self-etch mode; ENR + CHX Group: 37% phosphoric acid + CHX + ENR; UAS + CHX Group: CHX + UAS in self-etch mode. After treatments, teeth were restored (Filtek Z350, 3M ESPE). Samples (n = 10) were submitted to aging process: stored in distilled water at 37°C/30 days or TMC (ERIOS - 98N/1.6Hz + thermal cycling 5/37/55 °C - 1,200,000 cycles). Specimens were sectioned into sticks (1.0 mm2) and submitted to the microtensile test (Mechanical Test Machine - 0.5 mm/min). Fracture patterns and hybrid layer integrity were analyzed under Stereomicroscope and Scanning Electron Microscopy (SEM).

RESULTS

The BS results (3-way ANOVA, Bonferroni's test, α = 5%) showed that groups treated with CHX presented higher BS values than control groups; significant in all cases (p < .05), except for ENR submitted to TMC (p > .05). When CHX was applied and samples were cycled, UAS revealed higher BS (p < .05) than ENR. After TMC, cohesive fractures increased for UAS, regardless of CHX application. SEM analysis demonstrated different hybridization patterns for the adhesive systems tested.

CONCLUSION

The performance of the universal adhesive system used in self-etch mode was better than that of the 3-step etch-and-rinse adhesive system.

CLINICAL SIGNIFICANCE

Universal adhesive systems have been developed in order to simplify the dentin hybridization protocol. It is important to determine the longevity of the adhesive interface using these bonding materials after chewing.

Evaluation of gap formation at the composite resin-tooth interface after using universal adhesives: In vitro SEM study using the replica technique

The aim of this study was to evaluate gap formation after using two universal adhesives, Peak Universal Bond (P), which contains chlorhexidine and Adhese Universal (A), which contains 10-MDP monomer, and to compare them with two gold standard adhesives. The adhesives were tested in different etching modes, etch-and-rinse (ER) or self-etch (SE), and under thermomechanical loading (TML). Two identical Class V cavities were prepared in each of 30 human third molar teeth, and resin-composite restorations were made. Before and after TML, replicas of the restorations were prepared. Gap formation and their frequency according to the modified classification of Blunck and Zaslansky and the width of the maximum marginal gap (MG) were separately evaluated in enamel and dentin. Gap frequency did not differ significantly only in the enamel before TML, despite the use of different adhesives or etching modes. At both timepoints, the highest MG values were obtained with the Peak Universal Bond self-etch (PSE) group in enamel (6.2 μm before TML, 12.2 μm after TML) and the Peak Universal Bond etch-and-rinse (PER) group in dentine (21.3 μm before TML, 35.5 μm after TML). After TML, there was a significant increase of gap frequency for Adhese universal self-etch (ASE) group and MG values for PER, PSE, ASE groups at the resin-enamel interface, and gap frequency and MG values for all groups at the resin-dentin interface. Universal adhesive with 10-MDP monomer have beneficial effect on the resin-dentin interface, while chlorhexidine may reduce the resistance of the universal adhesive system to oral cavity conditions.

18-month clinical evaluation of a copper-containing universal adhesive in non-carious cervical lesions: A double-blind, randomized controlled trial

OBJECTIVE

This study aimed to evaluate the addition of copper nanoparticles (CuNp) on the clinical performance of a universal adhesive system used as etch-and-rinse (ER) and self-etch (SE).

METHODS

216 restorations were randomly placed in 36 subjects according to the following groups: ERcu = etch-and-rinse with 0.1% CuNp; ERct = etch-and-rinse without CuNp; SEcu = self-etch with 0.1% CuNp; SEct = self-etch without CuNp. Resin composite was placed incrementally and light-cured. The restorations were evaluated at baseline and 6, 12 and 18 months using the FDI and USPHS criteria. Statistical analyses were performed using appropriate tests (α = 0.05).

RESULTS

The addition of CuNp did not increase the clinical performance (FDI / USPHS) of the universal adhesive tested after 18-month when applied in the ER mode (p > 0.05). The addition of CuNp in SE restorations increased the retention rate significantly and decreased the marginal discrepancies after 18 months (p < 0.05).

CONCLUSION

The clinical performance of universal adhesive was significantly increased when applied in the SE mode with the addition of copper nanoparticles.

CLINICAL RELEVANCE

This is the first study that demonstrates a slight improvement in the clinical performance of universal adhesive systems in non-carious cervical lesions when added CuNp in lower concentration.

Universal dental adhesives: Current status, laboratory testing, and clinical performance

Increasing demand for simplified and user-friendly adhesive systems has led to the development of a new class of adhesives termed as Universal Adhesives (UAs). The term "Universal" reflects manufacturers' claims that these adhesives can be applied with any adhesion strategy and offer the versatility of use with a variety of direct and indirect restorative materials. The aim of this review was to synthesize the literature regarding the current status of UAs, their adhesion potential to various substrates and their performance in different restorative situations. In vitro studies, clinical trials and systematic reviews were identified utilizing controlled vocabulary and keyword searches in Medline and EMBASE databases. About 282 studies (272 in vitro studies; 11 clinical studies) were included. Available laboratory and clinical evidence does not support the claim that UAs can be used with any adhesive strategy. Although, they can chemically bond to various tooth and direct/indirect restorative substrates, the stability of this bond is material-dependent and subject to hydrolytic degradation. Hence, additional measures are still needed to ensure long-term durability. which undermines the versatility of UAs. The lack of long-term data regarding the clinical performance of UAs further complicates clinical decision-making. © 2019 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 2121-2131, 2019.

Clinical Evaluation of Microhybrid Composite and Glass lonomer Restorative Material in Permanent Teeth

AIM

The aim of this study was to clinically compare glass ionomer cement (GIC) with microhybrid composite resin used in class I cavities on permanent teeth over a period of 9 months.

MATERIALS AND METHODS

A total of 40 teeth with class I cavities were divided into two groups (n = 20) and restored with GIC (EQUIA; GC) and microhybrid resin composite (Amelogen Plus; Ultradent). Restorations were evaluated at ×4.5 magnification using the United States Public Health Service (USPHS) criteria every 3 months. Statistical analysis was performed using the Fisher's exact test (a < 0.05).

RESULTS

The data obtained reported no statistical significance difference between both groups in regard to anatomical shape, color, postoperative sensitivity, secondary caries, material handling, adaptation, and marginal staining.

CONCLUSION

The results of this clinical study showed that GIC (EQUIA; GC) can be used for the restoration of permanent teeth and may be more appropriate for certain clinical situations than the resin composite material.

CLINICAL SIGNIFICANCE

EQUIA (GIC) is a viable alternative to resin composite in restoring class I cavities in permanent teeth.