Influence of incorporation of ZrO2 nanoparticles on the repair strength of polymethyl methacrylate denture bases

Mapping the research landscape of nanoparticles and their use in denture base resins: a bibliometric analysis

BACKGROUND

Nanoparticles are increasingly used in dentistry for various applications, including enhancing the mechanical properties of denture base resins. This study aimed to comprehensively review and analyze the research landscape of nanoparticles and their effect on the flexural strength of denture base resins to identify key research areas and trends and to highlight the importance of collaboration between authors and institutions.

METHODS

A Bibliometric Analysis was conducted using the Keywords "Nanoparticle*" AND "Denture*" OR "CAD/CAM." The literature search from the WOS database was restricted to the publication years 2011 to 2022.

RESULTS

Key findings encompass an increase in research publications but a decline in citations. Saudi Arabia, China, and Iraq led this research, with specific institutions excelling. Notable journals with high impact factors were identified. Authorship patterns show variations in citation impact. Additionally, keyword analysis revealed that current research trends offer insights into influential authors and their networks.

CONCLUSIONS

The analysis of nanoparticles and denture base resins reveals a dynamic and evolving landscape that emphasizes the importance of collaboration, staying current with research trends, and conducting high-quality research in this ever-evolving domain.

Composite Nanomaterials Based on Polymethylmethacrylate Doped with Carbon Nanotubes and Nanoparticles: A Review

Composite polymer materials have high strength and lightness, which makes them attractive for use in a variety of structures and products. The present article contains an overview of modern works devoted to the production of composite materials based on poly(methyl methacrylate) (PMMA) with improved characteristics. The possibility of obtaining such materials can be a key area for creating more efficient and durable products in various industries. Various methods were considered to improve the characteristics of PMMA by doping the polymer matrix with carbon nanotubes (CNTs), graphite, nanohydroxyapatite particles, micro-zirconia nanoparticles, titanium dioxide, etc. The possibilities of using the obtained composite materials in various industries such as aviation, automotive, construction, medical and others are discussed. This article also presents the results of our own research on the mechanisms of interaction of PMMA with single-layer CNTs, leading to the creation of a composite polymer system "PMMA+CNT", achieved using the modern quantum chemical method DFT. This article presents a review of the recent research on the effect of CNTs on the mechanical and electrically conductive properties of nanocomposite materials. The outcomes of this study can be important for the development of science and technology in various fields, from fundamental chemistry to applied scientific research.

A 3D-simulation study of the deformation, tension, and stress of 3D-printed and conventional denture base materials after immersion in artificial saliva

INTRODUCTION

The worldwide application of digital technology has presented dentistry with transformative opportunities. The concept of digital dentures, incorporating computer-aided design (CAD) and computer-aided manufacturing (CAM) techniques, holds the promise of improved precision, customization, and overall patient satisfaction. However, the shift from traditional dentures to their digital counterparts should not be taken lightly, as the intricate interplay between oral physiology, patient comfort, and long-term durability requires thorough examination.

Influence of Novel SrTiO3/MnO2 Hybrid Nanoparticles on Poly(methyl methacrylate) Thermal and Mechanical Behavior

While dental poly methyl methacrylate(PMMA) possesses distinctive qualities such as ease of fabrication, cost-effectiveness, and favorable physical and mechanical properties, these attributes alone are inadequate to impart the necessary impact strength and hardness. Consequently, pure PMMA is less suitable for dental applications. This research focused on the incorporation of Strontium titanate (SrTiO3-STO) and hybrid filler STO/Manganese oxide (MnO2) to improve impact resistance and hardness. The potential of STO in reinforcing PMMA is poorly investigated, while hybrid filler STO/MnO2 has not been presented yet. Differential scanning calorimetry is conducted in order to investigate the agglomeration influence on the PMMA glass transition temperature (Tg), as well as the leaching of residual monomer and volatile additives that could pose a threat to human health. It has been determined that agglomeration with 1 wt% loading had no influence on Tg, while the first scan revealed differences in evaporation of small molecules, in favor of composite PMMA-STO/MnO2, which showed the trapping potential of volatiles. Investigations of mechanical properties have revealed the significant influence of hybrid STO/MnO2 filler on microhardness and total absorbed impact energy, which were increased by 89.9% and 145.4%, respectively. Results presented in this study revealed the reinforcing potential of hybrid nanoparticles that could find application in other polymers as well.

3D printed denture base material: The effect of incorporating TiO2 nanoparticles and artificial ageing on the physical and mechanical properties

OBJECTIVES

To evaluate the physical and mechanical properties of three-dimensional (3D) printed denture base resin incorporating TiO2 nanoparticles (NPs), subjected to a physical ageing process.

METHODS

Acrylic denture base samples were prepared by a Stereolithography (SLA) 3D printing technique reinforced with different concentrations (0.10, 0.25, 0.50, and 0.75) of silanated TiO2 NPs. The resulting nanocomposite materials were characterized in terms of degree of conversion (DC), and sorption/solubility flexural strength, impact strength, Vickers hardness and Martens hardness and compared with unmodified resin and conventional heat-cured (HC) material. The nanocomposites were reassessed after subjecting them to ageing in artificial saliva. A fractured surface was studied under a scanning electron microscope (SEM).

RESULTS

The addition of TiO2 NPs into 3D-printed resin significantly improved flexural strength/modulus, impact strength, Vickers hardness, and DC, while also slightly enhancing Martens hardness compared to the unmodified resin. Sorption values did not show any improvements, while solubility was reduced significantly. The addition of 0.10 wt% NPs provided the highest performance amongst the other concentrations, and 0.75 wt% NPs showed the lowest. Although ageing degraded the materials' performance to a certain extent, the trends remained the same. SEM images showed a homogenous distribution of the NPs at lower concentrations (0.10 and 0.25 wt%) but revealed agglomeration of the NPs with the higher concentrations (0.50 and 0.75 wt%).

SIGNIFICANCE

The outcomes of this study suggested that the incorporation of TiO2 NPs (0.10 wt%) into 3D-printed denture base material showed superior performance compared to the unmodified 3D-printed resin even after ageing in artificial saliva. The nanocomposite has the potential to extend service life of denture bases in future clinical use.

Influence of inorganic nanoparticles on dental materials' mechanical properties. A narrative review

Inorganic nanoparticles have been widely incorporated in conventional dental materials to help in improving their properties. The literature has shown that incorporating nanoparticles in dental materials in different specialties could have a positive effect on reinforcing the mechanical properties of those materials; however, there was no consensus on the effectiveness of using nanoparticles in enhancing the mechanical properties of dental materials, due to the variety of the properties of nanoparticles itself and their effect on the mechanical properties. This article attempted to analytically review all the studies that assessed the effect of different types of inorganic nanoparticles on the most commonly used dental materials in dental specialties such as polymethyl methacrylate, glass ionomer cement, resin composite, resin adhesive, orthodontic adhesive, and endodontic sealer. The results had shown that those inorganic nanoparticles demonstrated positive potential in improving those mechanical properties in most of the dental materials studied. That potential was attributed to the ultra-small sizes and unique physical and chemical qualities that those inorganic nanoparticles possess, together with the significant surface area to volume ratio. It was concluded from this comprehensive analysis that while a definitive recommendation cannot be provided due to the variety of nanoparticle types, shapes, and incorporated dental material, the consensus suggests using nanoparticles in low concentrations less than 1% by weight along with a silane coupling agent to minimize agglomeration issues and benefit from their properties.

The germicidal effect, biosafety and mechanical properties of antibacterial resin composite in cavity filling

In recent years, dental resin materials have become increasingly popular for cavity filling. However, these materials can shrink during polymerization, leading to microleakages that enable bacteria to erode tooth tissue and cause secondary caries. As a result, there is great clinical demand for the development of antibacterial resins. The principle of antibacterial resin includes contact killing and filler-release killing of bacteria. For contact killing, quaternary ammonium salts (QACs) and antibacterial peptides (AMPs) can be added. For filler-release killing, chlorhexidine (CHX) and nanoparticles are used. These antibacterial agents are effective against gram-positive bacteria, gram-negative bacteria, fungi, and more. Among them, QACs has a lasting antibacterial effect, and silver nanoparticles even have a certain ability to kill viruses. Biocompatibility-wise, QACs, AMPs, and CHX have low cytotoxicity to cells when added into the resin. However, nanoparticles with smaller particle sizes have higher cytotoxicity. In terms of mechanical properties, QACs, AMPs, and CHX do not negatively affect the resin. However, the addition of magnesium oxide can have a negative impact. This paper reviews the types and antibacterial principles of commonly used antibacterial resins in recent years, evaluates their antibacterial effect, biological safety, and mechanical properties, and provides references for selecting clinical filling materials.

Effect of treated zirconium dioxide nanoparticles on the flexural properties of autopolymerized resin for interim fixed restorations: An in vitro study

STATEMENT OF PROBLEM

Fractures of interim fixed restorations are a common complication. The autopolymerized polymethyl methacrylate resin materials used for interim fixed restorations have limited mechanical properties, but whether adding treated zirconium dioxide nanoparticles improves mechanical properties is unclear.

PURPOSE

The purpose of this in vitro study was to evaluate the effect of treated zirconium dioxide nanoparticles on the flexural strength and elastic modulus of autopolymerized polymethyl methacrylate resin.

MATERIAL AND METHODS

A split-metal mold (60×10×3.3 mm) was used to fabricate 40 autopolymerized acrylic resin specimens. The specimens were divided into 4 groups (n=10) according to zirconium dioxide nanoparticle concentration: control (unmodified resin) and zirconium dioxide nanoparticle contents of 1, 2.5, and 5 wt%. The specimens were mixed and polymerized according to the manufacturer's instructions and stored in distilled water for 48 ±2 hours at 37 °C. The flexural strength and elastic modulus were evaluated based on the 3-point bend test where data were analyzed by using 1-way analysis of variance and Tukey post hoc tests (α=.05).

RESULTS

The flexural strength of the 1-wt% zirconium dioxide nanoparticle specimens was significantly higher than that of the control group (P<.001) but did not significantly increase further with the higher nanoparticle content (P>.05). Elastic modulus significantly decreased with 2.5-wt% zirconium dioxide nanoparticles (P=.019), while no significant changes were found with other test groups (P>.05).

CONCLUSIONS

The addition of treated zirconium dioxide nanoparticles at low concentrations increased the flexural strength of autopolymerized polymethyl methacrylate resins used in fixed interim restorations.

Analyses of Experimental Dental Adhesives Based on Zirconia/Silver Phosphate Nanoparticles

This study aimed to evaluate the incorporation of zirconia/silver phosphate nanoparticles to develop experimental dental adhesives and to measure their physical and mechanical properties. The nanoparticles were synthesized by the sonication method, and the phase purity, morphological pattern, and antibacterial properties with Staphylococcus aureus and Pseudomonas aeruginosa were assessed. The silanized nanoparticles were incorporated (0, 0.15, 0.25, and 0.5 wt.%) into the photoactivated dimethacrylate resins. The degree of conversion (DC) was assessed, followed by the micro-hardness and flexural strength/modulus test. Long-term color stability was investigated. The bond strength with the dentin surface was conducted on days 1 and 30. The transmission electron microscopy and X-ray diffractogram confirmed the nano-structure and phase purity of the particles. The nanoparticles showed antibacterial activities against both strains and inhibited biofilm formation. The DC range of the experimental groups was 55-66%. The micro-hardness and flexural strength increased with the concentration of nanoparticles in the resin. The 0.5 wt.% group showed significantly high micro-hardness values, whereas a non-significant difference was observed between the experimental groups for flexural strength. The bond strength was higher on day 1 than on day 30, and a significant difference was observed between the two periods. At day 30, the 0.5 wt.% showed significantly higher values compared to other groups. Long-term color stability was observed for all the samples. The experimental adhesives showed promising results and potential to be used for clinical applications. However, further investigations such as antibacterial, penetration depth, and cytocompatibility are required.

Evaluation and Comparison of Mechanical Properties of Heat Polymerized Acrylic Resin After Reinforcement of Different Fibers in Different Patterns: An In Vitro Study

INTRODUCTION

Most denture fractures occur within the mouth due to resin flexural fatigue. For example, the deep labial notch at the high labial frenum causes denture breakage, as can deep scratches and generated processing stresses. The rising cost of annual prosthetic repairs is evidence that the problem of total denture fracture has not been solved. The purpose of this investigation was to evaluate the relative improvement in flexural strength between heat-cured polymethyl methacrylate (PMMA) resin reinforced with glass fibers (GF) and basalt fibers (BF) of varied orientations.

MATERIAL AND METHODS

A total of 150 heat-cured acrylic resin specimens of 65x10x3 mm dimension were prepared, 30 of which were left unreinforced (Group A), 30 of which were reinforced with GF in transverse pattern (Group B), 30 of which were reinforced with GF in meshwork pattern (Group C), 30 of which were reinforced with BF in transverse pattern (Group D), and 30 of which were reinforced with BF in meshwork pattern (Group E). All of the samples were put through flexural strength testing on the universal testing machine. One-way ANOVA and the Tukey-Kramer various correlation test (= 0.05) were used in SPSS for Windows to look at the facts.

RESULTS

The mean flexural strength for Group A was 46.26±2.26 MPa, 64.98±1.53 MPa for Group B, 76.45±2.67 MPa for Group C, 54.22±2.24 MPa for Group D, and 59.02±2.38 MPa for Group E. Flexural strength was impacted by both the kind of BF and GF reinforcement (F = 768.316, P = 0.001).

CONCLUSION

Within the limitation of the current research, BF reinforcement outperforms GF reinforcement and unreinforced heat-cured acrylic resin in terms of flexural strength.

Advanced materials and technologies for oral diseases

Oral disease, as a class of diseases with very high morbidity, brings great physical and mental damage to people worldwide. The increasing burden and strain on individuals and society make oral diseases an urgent global health problem. Since the treatment of almost all oral diseases relies on materials, the rapid development of advanced materials and technologies has also promoted innovations in the treatment methods and strategies of oral diseases. In this review, we systematically summarized the application strategies in advanced materials and technologies for oral diseases according to the etiology of the diseases and the comparison of new and old materials. Finally, the challenges and directions of future development for advanced materials and technologies in the treatment of oral diseases were refined. This review will guide the fundamental research and clinical translation of oral diseases for practitioners of oral medicine.

Prospects on Tuning Bioactive and Antimicrobial Denture Base Resin Materials: A Narrative Review

Denture base resin (DBR) materials are used in dentistry in constructing removable dentures and implant-supported prostheses. A plethora of evidence has demonstrated that DBR materials are associated with a high risk of denture stomatitis, a clinical complication where the soft oral tissues underneath the resin-based material are inflamed. The prevalence of denture stomatitis among denture wearers is high worldwide. Plaque accumulation and the infiltration of oral microbes into DBRs are among the main risk factors for denture stomatitis. The attachment of fungal species, mainly Candida albicans, to DBRs can irritate the underneath soft tissues, leading to the onset of the disease. As a result, several attempts were achieved to functionalize antimicrobial compounds and particles into DBRs to prevent microbial attachment. This review article explored the advanced approaches in designing bioactive and antimicrobial DBR materials. It was reported that using monomer mixtures, quaternary ammonium compounds (QACs), and organic and inorganic particles can suppress the growth of denture stomatitis-related pathogens. This paper also highlighted the importance of characterizing bioactive DBRs to be mechanically and physically sustainable. Future directions may implement a clinical translational model to attempt these materials inside the oral cavity.

Antibacterial Effect of Zirconia Nanoparticles on Polyethyl Methacrylate Resin for Provisional Crowns

Objective

Mid-to-long term use of provisional crowns in the oral cavity is associated with bacterial adhesion and biofilm formation, thus necessitating provisional crowns exhibiting antibacterial properties to prevent the occurrence of gingivitis and periodontal disease. This study aimed to evaluate the antibacterial effect of zirconia nanoparticle-containing polyethyl methacrylate (PEMA) resin for provisional restorations.

Methods

Zirconia nanoparticles were added to the monomer of PEMA resin for provisional restorations, and the mixture was stirred for 2 h using a magnetic stirrer. Disk-shaped specimens were prepared by mixing the polymer with the nanoparticle solution. The control group contained pure PEMA resin samples, and the experimental groups Group Z2, Group Z4, and Group Z8 included PEMA resin specimens containing 2, 4, and 8% w/v zirconia nanoparticles, respectively. After analyzing the sample surfaces, the antibacterial effect of the specimens was evaluated using Streptococcus mutans. Statistical analysis was performed using Tukey's test and Mann-Whitney U-test, according to the normality result in the Shapiro-Wilk test.

Results

FE-SEM and EDX analyses revealed the successful addition of zirconia nanoparticles. Results showed no significant difference in the measured values for surface roughness and contact angle between the experimental and control groups; however, adhesion and biofilm thickness of S. mutans were significantly decreased in Group Z2, Group Z4, and Group Z8 compared to the control group (P < 0.05, P < 0.01, P < 0.01, respectively).

Conclusion

The addition of zirconia nanoparticles can lower the incidence of adhesion and biofilm thickness of S. mutans on PEMA resin used for provisional crowns. Thus, incorporating zirconia nanoparticles in repair materials for provisional crowns and PEMA resin can produce an antibacterial effect and prevent gingivitis, periodontal disease, and dental caries.

Influence of ZrO2 Nanoparticle Addition on the Optical Properties of Denture Base Materials Fabricated Using Additive Technologies

This study investigated the translucency of 3D-printed denture base resins modified with zirconium dioxide nanoparticles (ZrO₂NPs) under thermal cycling. A total of 110 specimens were fabricated and divided into 3 groups according to the materials, i.e., heat-polymerized resin, and 3D-printed resins (NextDent, and ASIGA). The 3D-printed resins were modified with 0, 0.5, 1, 3, and 5 wt.% of ZrO₂NPs. All the specimens were subjected to 5000 thermal cycles. The translucency was measured using a spectrophotometer. The results showed that the heat-polymerized resin had considerably higher translucency than the 3D-printed resins. Compared to the unmodified group, the translucency decreased significantly after adding 5% ZrO₂NPs to NextDent and 3% ZrO₂NPs to ASIGA resins. The highest translucency was achieved for NextDent by adding 0.5% ZrO₂NPs and for ASIGA without any ZrO₂NPs. It was found that the average concentration level in ASIGA was significantly higher than that in NextDent. These findings revealed that 3D-printed resins have lower translucency than heat-polymerized acrylic resin, and adding ZrO₂NPs at low concentrations did not affect the translucency of the 3D-printed resins. Therefore, in terms of translucency, 3D-printed nanocomposite denture base resins could be considered for clinical applications when ZrO₂NPs are added at low concentrations.

The Mechanical and Antibacterial Properties of Boron Nitride/Silver Nanocomposite Enhanced Polymethyl Methacrylate Resin for Application in Oral Denture Bases

The introduction of nanomaterials into polymethyl methacrylate (PMMA) resin has been effective for mechanically reinforcing PMMA for application in oral denture bases. However, these methods cannot simultaneously improve the mechanical and antibacterial properties, which limits widespread clinical application. Here, we self-assembled binary nanocomposites of boron nitride nanosheets (h-BNNs) and silver nanoparticles (AgNPs) as nanofillers and incorporated the nanofillers into PMMA. The aim of this study was to achieve antibacterial effects while significantly improving the mechanical properties of PMMA and provide a theoretical basis for further clinical application. We employed scanning electron microscopy (SEM), X-ray diffraction (XRD), Raman spectroscopy (Raman), Ultraviolet visible spectrum (UV) and atomic force microscopy (AFM) to investigate the microscopic morphology and composition of PMMA containing nanocomposites with different mass fraction. In addition, the content of the h-BNNs/AgNPs was 1 wt%, and the compressive strength and flexural strength of pure PMMA were improved by 53.5% and 56.7%, respectively. When the concentration of the nanocomposite in the PMMA resin was 1.4 wt%, the antibacterial rate was 92.1%. Overall, synergistically reinforcing PMMA composite resin with a multi-dimensional nanocomposite structure provided a new perspective for expanding not only the application of resins in clinical settings but also the research and development of new composite resins.

Synthesis and Biomedical Applications of Zirconium Nanoparticles: Advanced Leaps and Bounds in the Recent Past

Many synthetic routes manufacture zirconium nanoparticles in metal oxide, nitride, and other combination forms. Coupled with other variables such as concentration, pH, and form of precursor used, the various synthetic methods support synthesizing the zirconium metal oxide nanoparticles with changed features. Various synthetic methods were studied, such as sol-gel, hydrothermal, laser ablation, and precipitation. All have different synthetic routes, different precursors and solvents were sued, and the product was characterized by SEM, TEM, photo luminance spectroscopy, UV-absorption spectroscopy, and powder X-ray diffraction. X-ray diffraction determined the crystal structure by identifying the crystal shape, arrangement of atoms, and spacing between them. SEM and TEM studied the particle size and morphology of nanoparticles. UV-visible absorption spectroscopy and PL spectroscopy were used for the determination of optical properties of nanoparticles. Zirconium oxide nanoparticles have many applications in the medical field. The review study primarily focuses on the efficient combination of zirconium dioxide with other additive materials and functionalization techniques used to improve the material's properties, assisting the use of the material in hip arthroplasty and bone tissue applications. The development of sophisticated near-infrared (NIR) absorbing small molecules for useful phototheranostic applications was discussed in this paper.

Influence of Incorporating 5% Weight Titanium Oxide Nanoparticles on Flexural Strength, Micro-Hardness, Surface Roughness and Water Sorption of Dental Self-Cured Acrylic Resin

Background: Polymethyl methacrylate (PMMA) is used in fabricating acrylic denture bases. Repairing a fractured acrylic denture base can be done by self-cured PMMA, yet this is still a weak point after repair. The aim of this study was to evaluate the effect of incorporating 5% weight titanium oxide nanoparticles (TiO₂) to self-cured PMMA on flexural strength, surface micro-hardness, roughness, and water sorption. Methods: A total of 160 acrylic–resin specimens were used in this study. They were divided in two main groups; (a) control group, prepared by mixing self-cured PMMA powder to its liquid monomer, (b) treated group, prepared by blending 5% weight TiO₂ nanoparticles to self-cured PMMA powder then this blend was mixed with the liquid monomer. Flexure strength, surface micro-hardness, roughness, and water sorption were evaluated. Data were analyzed using independent sample t-tests (p ≤ 0.05). Results: There was a significant increase in the flexural strength of PMMA of the treated group after the addition of TiO₂ (137.6 MPa) compared with the control (75.4 MPa) (p ≤ 0.001). No significant difference between the two groups in terms of micro-hardness (p = 0.385) and surface roughness (p = 0.269). Water sorption showed a significant reduction in the treated group (p ≤ 0.001). Conclusions: Addition of 5% weight TiO₂ nanoparticles to the self-cured acrylic resin improved its flexural strength and reduced its water-sorption without impairing the surface micro-hardness and roughness.

PMMA-Based Nanocomposites for Odontology Applications: A State-of-the-Art

Polymethyl methacrylate (PMMA), a well-known polymer of the methacrylate family, is extensively used in biomedicine, particularly in odontological applications including artificial teeth, dentures and denture bases, obturators, provisional or permanent crowns, and so forth. The exceptional PMMA properties, including aesthetics, inexpensiveness, simple manipulation, low density, and adjustable mechanical properties, make it a perfect candidate in the field of dentistry. However, it presents some deficiencies, including weakness regarding hydrolytic degradation, poor fracture toughness, and a lack of antibacterial activity. To further enhance its properties and solve these drawbacks, different approaches can be performed, including the incorporation of nanofillers. In this regard, different types of metallic nanoparticles, metal oxide nanofillers, and carbon-based nanomaterials have been recently integrated into PMMA matrices with the aim to reduce water absorption and improve their performance, namely their thermal and flexural properties. In this review, recent studies regarding the development of PMMA-based nanocomposites for odontology applications are summarized and future perspectives are highlighted.

Photocatalytic effect-assisted antimicrobial activities of acrylic resin incorporating zinc oxide nanoflakes

To overcome the deficiency of the antimicrobial effect of polymer, zinc oxide nanoparticles have been widely utilized as advanced nanofillers due to their antimicrobial and photocatalytic activity. However, the underlying antimicrobial mechanism has not been fully understood apart from topological and physical characteristics. In this study, we prepared zinc oxide nanoparticles-based acrylic resin to explore its antimicrobial mechanism under controlled mechanophysical conditions by using silane-treated zinc oxide nanoflakes (S-ZnNFs). S-ZnNFs incorporated acrylic resin (poly(methyl methacrylate), PMMA) composites up to 2 wt% were selected based on comparable mechanophysical properties (e.g., roughness, wettability, strength and hardness), possibly affecting antimicrobial properties beyond the zinc oxide nanoparticle effect, to bare PMMA. Antimicrobial adhesion results were still observed in 2 wt% S-ZnNFs incorporated PMMA using Candida albicans (C. albicans), one of the fungal infection species. In order to confirm the antimicrobial effects by photocatalysis, we pre-exposed the UV light on 2 wt% S-ZnNF composites before cell seeding, revealing synergetic antimicrobial effect via additional reactive oxygen species (ROS) generation to C. albicans over zinc oxide nanoparticle-induced one. RNA-seq analysis revealed distinguished cellular responses between zinc oxide nanoparticles and UV-mediated photocatalytic effect, but both linked to generation of intracellular ROS. Thus, the above data suggest that induction of high intracellular ROS of C. albicans was the main antimicrobial mechanism under controlled mechanophysical parameters and synergetic ROS accumulation can be induced by photocatalysis, recapitulating a promising use of a S-ZnNFs or possibly zinc oxide nanoparticles as intracellular-ROS-generating antimicrobial nanofillers in acrylic composite for biomedical applications.

3D-Printed Nanocomposite Denture-Base Resins: Effect of ZrO2 Nanoparticles on the Mechanical and Surface Properties In Vitro

Due to the low mechanical performances of 3D-printed denture base resins, ZrO2 nanoparticles (ZrO2NPs) were incorporated into different 3D-printed resins and their effects on the flexure strength, elastic modulus, impact strength, hardness, and surface roughness were evaluated. A total of 286 specimens were fabricated in dimensions per respective test and divided according to materials into three groups: heat-polymerized as a control group and two 3D-printed resins (NextDent and ASIGA) which were modified with 0.5 wt.%, 1 wt.%, 3 wt.%, and 5 wt.% ZrO2NPs. The flexure strength and elastic modulus, impact strength, hardness, and surface roughness (µm) were measured using the three-point bending test, Charpy’s impact test, Vickers hardness test, and a profilometer, respectively. The data were analyzed by ANOVA and Tukey’s post hoc test (α = 0.05). The results showed that, in comparison to heat-polymerized resin, the unmodified 3D-printed resins showed a significant decrease in all tested properties (p < 0.001) except surface roughness (p = 0.11). In between 3D-printed resins, the addition of ZrO2NPs to 3D-printed resins showed a significant increase in flexure strength, impact strength, and hardness (p < 0.05) while showing no significant differences in surface roughness and elastic modulus (p > 0.05). Our study demonstrated that the unmodified 3D-printed resins showed inferior mechanical behavior when compared with heat-polymerized acrylic resin while the addition of ZrO2NPs improved the properties of 3D-printed resins. Therefore, the introduced 3D-printable nanocomposite denture-base resins are suitable for clinical use.

Impact of Nanoparticles Additions on the Strength of Dental Composite Resin

Objective

This study aimed to evaluate the effect of nanoparticles, zirconium dioxide (ZrO₂), titanium dioxide (TiO₂), and silicon dioxide (SiO₂), on flexural strength (FS), hardness, and wear resistance of light cured dental composite resin.

Materials and Methods

210 rectangular and disc-shaped composite resin specimens were fabricated with dimensions (25 × 2 × 2 ± 0.03 mm) and (6×4 ± 0.03 mm) for FS, hardness, and wear resistance, respectively (70/test). Specimens of each test were divided according to nanofillers into four groups, unmodified as control, ZrO₂ (Z), TiO₂ (T), and SiO₂ (S) groups; each one was further subdivided into two subgroups according to nanoparticles concentration, 3wt.% and 7wt.% (Z3, Z7, T3, T7, S3, and S7), 10 specimens of each subgroup. A3-point bending test and Vickers hardness test were used for FS and hardness measurements, respectively. Wear resistance was evaluated by the differences in surface roughness of tested specimens before and after wear test. Two-way and 1-way ANOVA and Bonferroni's post hoc tests were done for data analysis (α = 0.05).

Results

Two-way ANOVA for FS and wear resistance showed that there was a significant interaction between type of nanoparticles and concentration of nanoparticles (p < 0.001) while two-way ANOVA for hardness showed that both type of nanoparticles and concentration of nanoparticles had a significant effect (p < 0.001), while the effect of their interaction was not statistically significant (p=0.142). 1-way-ANOVA test showed significant increase in FS and wear resistance for all tested groups (p < 0.001 and p < 0.001, respectively) except T7 and S7. Also, there was a significant enhancement in hardness for all tested groups (p < 0.001).

Conclusion

Modification of light cured composite resin with certain amounts of nanoparticles (3% and 7% of ZrO₂ and 3% of TiO₂ and SiO₂) can be beneficial in improving flexural strength and wear resistance while hardness of composite resin was increased with all NPs additions.

Development of Synthesis and Application of High Molecular Weight Poly(Methyl Methacrylate)

Poly(methyl methacrylate) (PMMA) is widely used in aviation, architecture, medical treatment, optical instruments and other fields because of its good transparency, chemical stability and electrical insulation. However, the application of PMMA largely depends on its physical properties. Mechanical properties such as tensile strength, fracture surface energy, shear modulus and Young’s modulus are increased with the increase in molecular weight. Consequently, it is of great significance to synthesize high molecular weight PMMA. In this article, we review the application of conventional free radical polymerization, atom transfer radical polymerization (ATRP) and coordination polymerization for preparing high molecular weight PMMA. The mechanisms of these polymerizations are discussed. In addition, applications of PMMA are also summarized.

Comparative Effect of Incorporation of ZrO2, TiO2, and SiO2 Nanoparticles on the Strength and Surface Properties of PMMA Denture Base Material: An In Vitro Study

Objective

This study aimed to investigate the effects of nanoparticles (zirconium dioxide (ZrO₂), titanium dioxide (TiO₂), and silicon dioxide (SiO₂)) on the flexural strength, impact strength, hardness, and wear resistance of the acrylic resin denture base material.

Materials and Methods

Acrylic resin specimens were fabricated in dimensions according to American Dental Association (ADA) specifications per test. Specimens were divided according to nanofiller into four groups; unmodified as control, ZrO₂ (Z), TiO₂, (T), and SiO₂ (S) groups. Each one was subdivided into two subgroups according to nanoparticle concentrations; 3% and 7% (Z3, Z7, T3, T7, S3, and S7). A 3-point bending test, Charpy impact test, and Vickers hardness test were used for flexural strength, impact strength, and hardness measurements, respectively. Wear resistance was measured by the differences in surface roughness of tested specimens before and after the wear test. A scanning electron microscope was used to assess nanoparticle specifications and distributions and for fracture surfaces analysis. ANOVA, Bonferroni's post hoc test, and the Kruskal–Wallis test were applied for data analysis (α = 0.05).

Results

Regarding the flexural and impact strength, there was a statistically remarkable increase for all tested groups compared with the control group, except for the T7 and S7 groups (P value <0.001, effect size = 0.893) and (P value <0.001, effect size = 0.759), respectively. There was a statistically significant improvement in the hardness of all tested groups compared with the control group (P value <0.001, effect size = 0.67) except T3 and S3. Regarding wear, a statistically significant enhancement was noticed in the wear resistance of all tested groups (P value <0.001, effect size = 0.685), except for the T7 and S7 groups.

Conclusion

The flexural strength, impact strength, and wear resistance improved with both concentrations of ZrO₂ and low TiO₂ and SiO₂ concentrations. The hardness increased with both concentrations of ZrO₂ and high TiO₂ and SiO₂ concentrations.

The Effect of Salinized Nano ZrO2 Particles on the Microstructure, Hardness, and Wear Behavior of Acrylic Denture Tooth Nanocomposite

The wear of acrylic denture teeth is a serious problem that can change the vertical dimensions of dentures. This study evaluates the effect of adding salinized nano ZrO₂ particles on the microstructure, hardness, and wear resistance of acrylic denture teeth. Heat polymerizing polymethyl methacrylate resin was mixed with salinized ZrO₂ at concentrations of 5 wt.% and 10 wt.%. Acrylic resin specimens without filler addition were used as a control group. SEM/EDS analyses were performed and the Vickers’ hardness was evaluated. Two-body wear testing was performed using a chewing simulator with a human enamel antagonist. After subjecting the samples to 37,500 cycles, both height loss and weight loss were used to evaluate the wear behavior. The microstructural investigation of the reinforced-denture teeth indicates sound nanocomposite preparation using the applied regime without porosity or macro defects. The addition of zirconium oxide nanofillers to PMMA at both 5% and 10% increased the microhardness, with values of up to 49.7 HV. The wear mechanism in the acrylic base material without nanoparticle addition was found to be fatigue wear; a high density of microcracks were found. The addition of 5 wt.% ZrO₂ improved the wear resistance. Increasing the nanoparticles to 10 wt.% ZrO₂ further improved the wear resistance, with no microcracks found.

Polymethylmethacrylate Incorporating Nanodiamonds for Denture Repair: In Vitro Study on the Mechanical Properties

OBJECTIVE

 This study aimed to evaluate the effect of nanodiamond (ND) addition to repair resin with repair gap modifications on the flexural and impact strength of repaired polymethylmethacrylate denture base.

MATERIALS AND METHODS

 Heat-polymerized acrylic resin specimens (N = 100/test) were prepared and sectioned to half creating two repair gaps: 2.5- and 0 mm with 45 degrees beveling. They were further divided into subgroups (n = 20) according to ND concentration (control, 0.25%ND, and 0.50%ND), thermocycling (500 cycles) was done to half the specimens in each subgroup. Flexural strength was tested using 3-point bending test and impact strength was tested by Charpy's impact test. Analysis of variance and post-hoc Tukey's tests were performed for data analysis (α = 0.05). Scanning electron microscope was employed for fracture surface analysis and ND distribution.

RESULTS

 Before and after thermocycling, the addition of ND significantly increased the flexural strength and elastic modulus in comparison to control group (p ˂ 0.001), while 0 mm repair gap showed insignificant difference between ND-reinforced groups (p ˃ 0.05). Regarding impact strength, ND addition increased the impact strength with 0 mm gap in comparison to control and 2.5 mm with ND (p˂0.001), while later groups showed no significant in between (p ˃ 0.05). Comparing thermocycling effect per respective concentration and repair gap, thermocycling adversely affected all tested properties except elastic modulus with 0 mm-0.25 and 0 mm-0.5% and impact strength with 2.5 mm, 2.5 mm-0.25%, 2.5 mm- 0.5% (p ˃ 0.05).

CONCLUSION

 ND addition combined with decreased repair gap improved the flexural strength, elastic modulus, and impact strength of repaired denture resin, while thermocycling has a negative effect on denture repair strength.

The impact of nanoparticles-modified repair resin on denture repairs: a systematic review

This study aimed to evaluate the effect of nanoparticles on the mechanical properties of acrylic denture repairs. The review was designed following PRISMA (Preferred Reporting Items for Systematic Reviews and Meta-Analysis) guidelines. Database search was conducted involving articles published from 2000 to 2020 using the following keywords: PMMA/nanoparticles, denture repair/nanoparticles, and repair strength/nanoparticles. PubMed/MEDLINE, Embase, Google Scholar, Scopus, and EBSCOhost were used to find only those studies used repair resin reinforced with nanoparticles for denture repairs. Due to variations between nanoparticles types, sizes, and testing properties, the quantitative statistical meta-analysis couldn't be conducted. Therefore, a descriptive data analysis was applied. Out of 379 articles, 8 articles were included; three nanoparticles, zirconium oxide (nano-ZrO2), silicon oxide (nano-SiO2), and aluminum oxide (nano-Al2O3) nanoparticles were used as reinforcements to repair resin. Seven studies investigated the effects of 0.25-7.5 wt.% nano-ZrO2 on the mechanical properties of repaired denture bases and reported positive effects with high concentrations. Two studies study investigated 0.25-0.75 wt% nano-SiO2 and found that low % nano-SiO2 concentrations improved repair strength while, one study showed that 1 and 1.5 wt.% nano-Al2O3 increased the flexural strength. Although nanoparticles offer positive effects on the properties of denture repair, inadequate studies exist. Therefore, further investigations are required. Scientific field of dental Science: Prosthodontics.

New lignin-based hybrid materials as functional additives for polymer biocomposites: From design to application

Within this study, the ZrO₂/lignin and ZrO₂-SiO₂/lignin hybrid materials were obtained for the first time. The mechanical grinding method was used for this purpose. In order to determine the properties of obtained lignin-based hybrids and the components used to produce them, as well as to evaluate the efficiency of their preparation, the authors used such research techniques as scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), elemental analysis, porous structure analysis and thermal stability assessment (TGA/DTG). The next step involved using the components and produced hybrid materials as polymer fillers for poly(methyl methacrylate) (PMMA). The obtained lignin-based hybrid biocomposites have then been thoroughly characterized using gel permeation chromatography (GPC), differential scanning calorimetry (DSC), dynamic mechanical analysis (DMA) and hardness testing. All the conducted tests confirm the possibility of using the obtained bio-based products in practice, within the widely understood construction industry, for producing durable building facades or noise barriers, among others.

Sol-Gel Synthesis and Characterization of YSZ Nanofillers for Dental Cements at Different Temperatures

BACKGROUND

Yttria-stabilized zirconia nanoparticles can be applied as fillers to improve the mechanical and antibacterial properties of luting cement. The aim of this study was to synthesize yttria-stabilized zirconia nanoparticles by the sol-gel method and to investigate their composition, structure, morphology and biological properties.

METHODS

Nanopowders of ZrO₂ 7 wt% Y₂O₃ (nY-ZrO) were synthesized by the sol-gel method and were sintered at three different temperatures: 800, 1000 and 1200 °C, and their composition, size and morphology were investigated. The biocompatibility was investigated with human gingival fibroblasts (hGFs), while reactive oxygen species (ROS) production was evaluated through fluorescence analysis.

RESULTS

All synthesized materials were composed of tetragonal zirconia, while nanopowders sintered at 800 °C and 1000 °C additionally contained 5 and 20 wt% of the cubic phase. By increasing the calcination temperature, the crystalline size of the nanoparticles increased from 12.1 nm for nY-ZrO800 to 47.2 nm for nY-ZrO1200. Nano-sized particles with good dispersion and low agglomeration were received. Cell culture studies with human gingival fibroblasts verified the nanopowders' biocompatibility and their ROS scavenging activity.

CONCLUSIONS

the obtained sol-gel derived nanopowders showed suitable properties to be potentially used as nanofillers for dental luting cement.

Effect of Nanostructures on the Properties of Glass Ionomer Dental Restoratives/Cements: A Comprehensive Narrative Review

Overall perspective of nanotechnology and reinforcement of dental biomaterials by nanoparticles has been reported in the literature. However, the literature regarding the reinforcement of dental biomaterials after incorporating various nanostructures is sparse. The present review addresses current developments of glass ionomer cements (GICs) after incorporating various metallic, polymeric, inorganic and carbon-based nanostructures. In addition, types, applications, and implications of various nanostructures incorporated in GICs are discussed. Most of the attempts by researchers are based on the laboratory-based studies; hence, it warrants long-term clinical trials to aid the development of suitable materials for the load bearing posterior dentition. Nevertheless, a few meaningful conclusions are drawn from this substantial piece of work; they are as follows: (1) most of the nanostructures are likely to enhance the mechanical strength of GICs; (2) certain nanostructures improve the antibacterial activity of GICs against the cariogenic bacteria; (3) clinical translation of these promising outcomes are completely missing, and (4) the nanostructured modified GICs could perform better than their conventional counterparts in the load bearing posterior dentition.

Influence of Reinforcing Agents on the Mechanical Properties of Denture Base Resin: A Systematic Review

Knowledge about the influence of fillers in denture base resin is vague. This systematic review aimed to report the reinforcing effect of fillers on the mechanical properties of denture base resin by following PRISMA guidelines. Two electronic databases (Pubmed/Medline & Web of Science) were searched for articles using the keywords: fibers in denture base, fillers in denture base, and reinforcement of denture base. Laboratory studies complying with the inclusion criteria were reviewed according to the set protocol. The established focus question was: "Do reinforcing fillers positively influence the mechanical properties of polymethyl methacrylate (PMMA) heat polymerized denture base material?" A total of twenty-nine relevant papers qualified for final inclusion. Of these, 24 were determined to have a moderate risk of bias. Micron or nano-sized metal/metal oxides particles and glass fibers were the frequently used reinforcing agents. The trend of evaluating fractural strength (FS) was common. Most of the studies limited the use of reinforcing agents up to 5 wt.%. FS, fracture toughness (FT), and impact strength (IS) tend to increase if the fillers are chemically bonded and well-dispersed in denture base resin. Though fillers with a higher elastic modulus increase the hardness of the reinforced denture base resin, they compromise other mechanical properties. Well-dispersed lower filler loading PMMA denture base resin can enhance the FS, FT, and other related mechanical properties.

Impact of ZrO2 nanoparticles addition on flexural properties of denture base resin with different thickness

PURPOSE

This study aimed to evaluate the effect of incorporating zirconium oxide nanoparticles (nano-ZrO₂) in polymethylmethacrylate (PMMA) denture base resin on flexural properties at different material thicknesses.

MATERIALS AND METHODS

Heat polymerized acrylic resin specimens (N = 120) were fabricated and divided into 4 groups according to denture base thickness (2.5 mm, 2.0 mm, 1.5 mm, 1.0 mm). Each group was subdivided into 3 subgroups (n = 10) according to nano-ZrO₂ concentration (0%, 2.5%, and 5%). Flexural strength and elastic modulus were evaluated using a three-point bending test. One-way ANOVA, Tukey's post hoc, and two-way ANOVA were used for data analysis (α = .05). Scanning electron microscopy (SEM) was used for fracture surface analysis and nanoparticles distributions.

RESULTS

Groups with 0% nano-ZrO₂ showed no significant difference in the flexural strength as thickness decreased (P = .153). The addition of nano-zirconia significantly increased the flexural strength (P < .001). The highest value was with 5% nano-ZrO₂ and 2 mm-thickness (125.4 ± 18.3 MPa), followed by 5% nano-ZrO₂ and 1.5 mm-thickness (110.3 ± 8.5 MPa). Moreover, the effect of various concentration levels on elastic modulus was statistically significant for 2 mm thickness (P = .001), but the combined effect of thickness and concentration on elastic modulus was insignificant (P = .10).

CONCLUSION

Reinforcement of denture base material with nano-ZrO₂ significantly increased flexural strength and modulus of elasticity. Reducing material thickness did not decrease flexural strength when nano-ZrO₂ was incorporated. In clinical practice, when low thickness of denture base material is indicated, PMMA/nano-ZrO₂ could be used with minimum acceptable thickness of 1.5 mm.

Nanoparticles in Dentistry: A Comprehensive Review

In recent years, nanoparticles (NPs) have been receiving more attention in dentistry. Their advantageous physicochemical and biological properties can improve the diagnosis, prevention, and treatment of numerous oral diseases, including dental caries, periodontal diseases, pulp and periapical lesions, oral candidiasis, denture stomatitis, hyposalivation, and head, neck, and oral cancer. NPs can also enhance the mechanical and microbiological properties of dental prostheses and implants and can be used to improve drug delivery through the oral mucosa. This paper reviewed studies from 2015 to 2020 and summarized the potential applications of different types of NPs in the many fields of dentistry.

Closed Repair Technique: Innovative Surface Design for Polymethylmethacrylate Denture Base Repair

PURPOSE

This study aimed to evaluate the repair strength of a newly introduced repair technique involving zero-gap repair width.

MATERIALS AND METHODS

A total of 36 rectangular prism specimens with dimensions of 64 × 10 × 3.3 mm were prepared from heat-polymerized acrylic resin. Nine specimens were kept intact. The other specimens were sectioned into halves and modified to create repair gaps of 2.5-mm beveled (2.5B) as control, 0-mm beveled (ZB), and 0-mm inverse bi-beveled (ZIBB). The ZIBB group was prepared with a V-shaped internal groove on both halves (repair tunnel), while the intaglio and cameo surfaces were kept intact except for two small holes at the cameo surface for repair resin injection. The 2.5B and ZB groups were repaired conventionally while the ZIBB group was repaired by injecting repair resin into the tunnel through one of the holes until excess material oozed from the other hole. Repaired specimens were thermally cycled at 5 and 55°C for 10,000 cycles with 1 min dwell time. A 3-point bending test was conducted using a universal testing machine for flexural strength and elastic modulus measurement. Kruskal-Wallis/Mann-Whitney tests and ANOVA/post hoc Tukey tests were applied for data analysis (α = 0.05).

RESULTS

The flexural strength of repaired specimens was substantially lower than that of intact specimens, and significant differences were present between repaired groups (p ˂ 0.05). ZB and ZIBB had higher flexural strength (p ˂ 0.001) and elastic modulus (p ˂ 0.05) than 2.5B. Among the ZB and ZIBB groups, ZB showed the highest flexural strength, and ZIBB had the highest elastic modulus.

CONCLUSION

The closed repair technique improved the flexural strength and elastic modulus of repaired acrylic denture base.

Chemical Characterisation of Silanised Zirconia Nanoparticles and Their Effects on the Properties of PMMA-Zirconia Nanocomposites

Objectives: The objective of this study was to investigate the mechanical properties of high-impact (HI) heat-cured acrylic resin (PMMA) reinforced with silane-treated zirconia nanoparticles. Methods: Forty-five PMMA specimens reinforced with zirconia were fabricated and divided into three groups: Pure HI PMMA (control group), PMMA reinforced with 3 wt.% of non-silanised zirconia nanoparticles and PMMA reinforced with 3 wt.% of silanised zirconia nanoparticles. Silanised and non-silanised zirconia nanoparticles were analysed with Fourier Transform Infrared (FTIR) Spectroscopy. For measuring the flexural modulus and strength, a Zwick universal tester was used, and for surface hardness, a Vickers hardness tester were used. Furthermore, raw materials and fractured surfaces were analysed using Scanning Electron Microscopy (SEM). A one-way ANOVA test followed by a post-hoc Bonferroni test was employed to analyse the data. Results: The results showed that the mean values for flexural strength (83.5 ± 6.2 MPa) and surface hardness (20.1 ± 2.3 kg/mm²) of the group containing 3 wt.% treated zirconia increased significantly (p < 0.05) in comparison to the specimens in the group containing non-treated zirconia (59.9 ± 7.1 MPa; 15.0 ± 0.2 kg/mm²) and the control group (72.4 ± 8.6 MPa; 17.1 ± 0.9 kg/mm²). However, the group with silanised zirconia showed an increase in flexural modulus (2313 ± 161 MPa) but was not significantly different (p > 0.05) from the non-silanised group (2207 ± 252 MPa) and the control group (1971 ± 235 MPa). Conclusion: Silane-treated zirconia nano-filler improves the surface hardness and flexural strength of HI PMMA-zirconia nanocomposites, giving a potentially longer service life of the denture base.

In Vitro Assessment of Artificial Aging on the Antifungal Activity of PMMA Denture Base Material Modified with ZrO2 Nanoparticles

The antifungal effect of zirconium dioxide nanoparticles (ZrO₂NPs) incorporated into denture base material has been inadequately investigated; additionally, to the authors' knowledge, no studies have assessed the influence of artificial aging on the antifungal activity of these particles. Methodology. Heat-polymerized acrylic resin disks were fabricated and divided into four groups (0%, 1%, 2.5%, and 5% ZrO₂NPs by weight). Antifungal activity was assessed using the direct culture and disk diffusion methods. Surface roughness and contact angles were measured using a profilometer and a goniometer, respectively. The artificial aging procedure was performed by repeating all tests at 7, 14, and 30 days following 2 rounds of thermocycling. Data were analyzed using ANOVA and Tukey's post-hoc test (p < 0.05). Results. The addition of ZrO₂NPs significantly decreased the adhesion of Candida albicans with and without artificial aging procedures (p < 0.001), while the disk diffusion methods did not reveal inhibition zones. ZrO₂NP-modified specimens displayed significantly higher surface roughness compared to specimens in the control group (p < 0.05) and showed the same behaviors with artificial aging procedures. The contact angle was significantly decreased in all modified groups in comparison to the control group (p < 0.05). Conclusion. The addition of ZrO₂NPs to polymethylmethacrylate denture base material reduced the adhesion of Candida albicans with a long-term antifungal effect. With the addition of ZrO₂NPs, contact angles were decreased and surface roughness was increased; 1% was the most appropriate concentration. Clinical significance. The addition of ZrO₂NPs to denture base material confers a long-term antifungal effect and could be used as a possible method for preventing and treating denture stomatitis.

Electron Momentum Density of Nanoparticles ZrO2: A Compton Profile Study

This work investigates the electronic momentum density (EMD) distribution in nanosize zirconia (ZrO2) using the technique of Compton scattering. The ZrO2 nanoparticles (11.2[Formula: see text]nm) are synthesized of mechanical milling and characterized by SEM, XRD and TEM probes. The Compton profile [Formula: see text] of nanoZrO2 is measured by Compton spectrometer 59.54[Formula: see text]KeV Gamma rays (Americium-241) source. The study finds out that EMD in nanoZrO2 is narrower comparing in case bulk ZrO2. This study adopts the ionic-model-based free atom [Formula: see text] calculation for many configurations (Zr)[Formula: see text](O[Formula: see text])2 ([Formula: see text]) to measure the charge transfer (CT) on the compound formation. According to this study’s findings, CT values in these materials are ranged from 1.5 to 1.0 electrons from Zr to O atom.

Double-layered acrylic resin denture base with nanoparticle additions: An in vitro study

STATEMENT OF PROBLEM

Whether the addition of different antifungal nanoparticles to denture base materials may affect physical or esthetic properties of the resulting nanocomposite is unclear.

PURPOSE

The purpose of this in vitro study was to determine how a new method of adding antifungal nanofiller affects the properties of the processed nanocomposite denture base material.

MATERIAL AND METHODS

Heat-polymerized acrylic resin specimens were prepared according to each test specification. Zirconium dioxide nanoparticles (ZrO₂NPs) and silver nanoparticles (AgNPs) were added in 0.5, 1.0, and 1.5% of acrylic resin powder. The specimens were divided into 2 groups according to the acrylic resin packing method: 1 layer packed conventionally in one step and 2 layers packed in 2 steps, first with unmodified acrylic resin and then by a thin layer of modified acrylic resin before the final closure. The control group was made of unaltered acrylic resin in 1 step. Flexural strength (FS), translucency, and surface roughness (R_a) were measured. A microbial assay was performed by using the direct culture and slide count methods. Three-way ANOVA and Tukey post hoc tests were used to identify statistical differences among groups (α=.05).

RESULTS

The addition of ZrO₂NPs and AgNPs in the 1- or 2-layer specimens reduced Candida albicans adhesion (P<.001). In the 1- and 2-layer specimens, FS significantly increased with ZrO₂NPs. AgNPs decreased FS only in the 1-layer specimen (P<.001). Surface roughness was not changed for the 1- and 2-layer specimens with ZrO₂NPs or the 1-layer specimen with 0.5% AgNPs (P>.05), while other AgNP groups exhibited increased surface roughness (P<.001). AgNPs significantly lowered translucency in the 1- and 2-layer specimens (P<.001), while ZrO₂NPs decreased translucency only in the 1-layer specimen (P<.001).

CONCLUSIONS

The addition of ZrO₂NPs in the double-layer technique decreased Candida adhesion and improved FS without affecting surface roughness, while AgNPs decreased Candida adhesion and FS and increased surface roughness. Both nanofillers decreased the translucency except 0.5% ZrO₂NPs, which did not change translucency when applied in 2 layers.

Prosthodontic Applications of Polymethyl Methacrylate (PMMA): An Update

A wide range of polymers are commonly used for various applications in prosthodontics. Polymethyl methacrylate (PMMA) is commonly used for prosthetic dental applications, including the fabrication of artificial teeth, denture bases, dentures, obturators, orthodontic retainers, temporary or provisional crowns, and for the repair of dental prostheses. Additional dental applications of PMMA include occlusal splints, printed or milled casts, dies for treatment planning, and the embedding of tooth specimens for research purposes. The unique properties of PMMA, such as its low density, aesthetics, cost-effectiveness, ease of manipulation, and tailorable physical and mechanical properties, make it a suitable and popular biomaterial for these dental applications. To further improve the properties (thermal properties, water sorption, solubility, impact strength, flexural strength) of PMMA, several chemical modifications and mechanical reinforcement techniques using various types of fibers, nanoparticles, and nanotubes have been reported recently. The present article comprehensively reviews various aspects and properties of PMMA biomaterials, mainly for prosthodontic applications. In addition, recent updates and modifications to enhance the physical and mechanical properties of PMMA are also discussed.

Nanometals in Dentistry: Applications and Toxicological Implications-a Systematic Review

Nanotechnology is a vital part of health care system, including the dentistry. This branch of technology has been incorporated into various fields of dentistry ranging from diagnosis to prevention and treatment. The latter involves application of numerous biomaterials that help in restoration of esthetic and functional dentition. Over the past decade, these materials were modified through the incorporation of metal nanoparticles (NP) like silver (Ag), gold (Au), titanium (Ti), zinc (Zn), copper (Cu), and zirconia (Zr). They enhanced antimicrobial, mechanical, and regenerative properties of these materials. However, lately, the toxicological implications of these nanometal particles have been realized. They were associated with cytotoxicity, genotoxicity altered inflammatory processes, and reticuloendothelial system toxicity. As dental biomaterials containing metal NPs remain functional in oral cavity over prolonged periods, it is important to know their toxicological effects in humans. With this background, the present systematic review is aimed to gain an insight into the plausible applications and toxic implications of nano-metal particles as related to dentistry.

Influence of Addition of Different Nanoparticles on the Surface Properties of Poly(methylmethacrylate) Denture Base Material

PURPOSE

To evaluate and compare the surface properties (roughness and hardness) of poly(methylmethacrylate) denture base material modified with zirconium dioxide (ZNPs), silicon dioxide (SNPs), and diamond (DNPs) nanoparticles.

MATERIALS AND METHODS

Two hundred sixty heat-polymerized acrylic resin disks (15 × 2 mm) were prepared. ZNPs, SNPs, and DNPs were added in concentrations of 0%, 0.5%, 1.0%, 2.5%, and 5.0% by weight of acrylic powder. This yielded a total of 13 groups for each test according to filler type and concentration (n = 10/group). The control group was made of pure acrylic. A mechanical polisher was used to standardize specimens' surfaces before testing. A profilometer and Vickers hardness indenter were used to test the surface roughness and hardness, respectively. ANOVA and Tukey post hoc tests were used for data analysis (α = 0.05).

RESULTS

In comparison to control, results showed a nonsignificant increase in surface roughness (R_a ) of acrylic material after the addition of 0.5% nanoparticles (ZNPs p = 0.168, SNPs p = 0.166, and DNPs p = 0.177), while a significant increase was seen with all other concentrations (p ˂ 0.05). R_a values of ZNP and DNP groups were significantly higher than those of the SNPs group (p < 0.001). The addition of any of the fillers to acrylic denture base materials significantly increased the hardness (p ˂ 0.05), with ZNPs and DNPs having values lower than those of the SNPs group (p < 0.001).

CONCLUSIONS

Although nanofiller addition increased the hardness of denture base material, R_a was adversely affected when the concentration exceeded 0.5%. Therefore, 0.5% is suggested to be the most appropriate ratio to improve hardness with acceptable R_a .

Influence of artificial aging and ZrO2 nanoparticle-reinforced repair resin on the denture repair strength

Background

The purpose of this study was to evaluate the effect of aging process on the tensile strength (TS) of repaired acrylic denture base using ZrO2 nanoparticles (nano-ZrO2)-reinforced autopolymerized resin.

Material and Methods

A total of 240 heat-polymerized acrylic resin specimens (n=10) were prepared and sectioned creating 2 mm-repair-gap. Autopolymerized acrylic resin, pure and modified with 2.5, 5, and 7.5wt% nano-ZrO2 were used for specimens repair. TS of repaired specimens were measured using the universal testing machine after water immersion at 37oC for 2, 7 and 30 days. At each time interval, half the immersed specimens underwent thermo-cycling aging process (5000 cycles at 5/55°C) before TS testing. One-way ANOVA and Tukey-Kramer multiple-comparison tests were used for data analysis at α=0.05.

Results

Aging process for all groups showed significant differences in TS between unreinforced and nano-ZrO2 reinforced groups (p<0.05). Within immersed nano-ZrO2-reinforced specimens, 5% group immersed for 30-days showed the highest significant TS value (p<0.05). With regards to thermocycling, 5% group showed the highest TS values after 2-days and 30-days groups while after 7-days, significant differences were found between 2.5% group and 5% and 7.5% groups (p<0.05). SEM images analysis displayed the ductile fracture type for nano-ZrO2 reinforced groups.

Conclusions

In summary, 5.0%-nano-ZrO2 addition to repair resin showed an improvement in tensile strength of repaired acrylic resin with different aging processes. Key words:Acrylic resins, denture repair, tensile strength, thermocycling, water storage, zirconium oxide nanoparticle.

Influence of silanized silica and silanized feldspar addition on the mechanical behavior of polymethyl methacrylate resin denture teeth

STATEMENT OF PROBLEM

Artificial denture teeth made of polymethyl methacrylate (PMMA) resin have good adhesion to the denture base but are relatively soft and have limited wear resistance during function.

PURPOSE

The purpose of this in vitro study was to evaluate the influence of the addition of 2 inorganic nanofillers on the flexural strength, maximal displacement, elastic modulus, Isolde impact resistance, and Brinell hardness of acrylic resin denture teeth.

MATERIAL AND METHODS

Heat polymerizing polymethyl methacrylate resin was mixed with silanized silica or silanized feldspar in concentrations of 5 wt%, 10 wt%, and 15 wt%. The first test was conducted after 24 hours of storage in laboratory conditions, and the second assessment was conducted after 3 months of storage in distilled water at 37 °C. The Brinell hardness was evaluated, and the elastic modulus and maximal displacement at fracture were calculated. The flexural strength and Isolde impact resistance were measured with a 3-point flexural test. Acrylic resin specimens without filler addition were used as a control group. Statistical analysis included 2-way ANOVA for independent variables (α=.05) and the Student t test for time-dependent changes (α=.05). These were performed with Statistica 12 software.

RESULTS

The acrylic resin specimens modified with the addition of silanized feldspar had significantly higher Brinell hardness, elastic modulus, maximal displacement, and flexural strength and also had no adverse effect on Isolde impact resistance compared with the conventional acrylic resin. Silica filler increased the Brinell hardness and elastic modulus of acrylic resins but significantly reduced the flexural strength and Isolde impact resistance.

Impact of different surface treatments and repair material reinforcement on the flexural strength of repaired PMMA denture base material

This study assessed the impact of surface treatments and repair resin reinforcement with zirconium oxide nano-particles (nano-ZrO₂) on flexural strength (FS) of repaired denture base. A total of 320 heat-polymerized acrylic resin specimens were prepared and sectioned creating 2-mm gap. According to repair surface treatment, specimens were distributed into four groups: I) methyl methacrylate (M); II) alumina-blasted (AB); III) AB+silane coupling agent (SC); and IV) AB+methacrylate based composite bonding agent (MA). Groups were subdivided into 4 (n=20) according to nano-ZrO₂ concentration (0, 2.5, 5, 7.5 wt%). Half the specimens were thermo-cycled before testing. FS was determined by three-point bending test. Statistical analysis was done using ANOVA and Tukey-Kramer multiple comparison tests, with α=0.05. Alumina-blasting+(SC) or (MA) significantly increased FS of repaired specimens compared to control (p<0.05). All surface-treated specimens combined with nano-ZrO₂ reinforced repair resin significantly increased FS.

The Impact of Polymerization Technique and Glass-Fiber Reinforcement on the Flexural Properties of Denture Base Resin Material

OBJECTIVE

 Different polymerization and reinforcement techniques have been tested to enhance the mechanical characteristics of denture base acrylic resins. The goal of the present study was to evaluate the influence of autoclave polymerization techniques with glass fiber reinforcement on the flexural strength and elastic modulus of polymethyl methacrylate denture base resins.

MATERIALS AND METHODS

 Ninety specimens were fabricated from heat-polymerized acrylic resin and randomly distributed depending on the polymerization technique into three groups (n = 30): water bath polymerization, short-cycle autoclave polymerization, and long-cycle autoclave polymerization. Each group was further divided into three subgroups (n = 10) based on the concentration of glass fiber 0, 2.5, and 5wt%. The flexural strength and elastic modulus were investigated using a universal testing machine. One-way ANOVA and Tukey's post hoc test were performed to analyze the results (α = 0.05).

RESULTS

 The flexural strength and elastic modulus values were significantly higher in 5wt% glass fiber reinforced long-cycle autoclave group in comparison with the other test groups (p < 0.05).

CONCLUSIONS

The long-cycle autoclave polymerization technique with the glass fiber reinforcement significantly increased the flexural strength and elastic modulus of the denture base resin material.

Effect of SiO2 Nanoparticles Addition on the Flexural Strength of Repaired Acrylic Denture Base

Objective  The objective of this study was to evaluate the effect of nano-SiO ₂ addition on the flexural strength (FS) of repaired acrylic denture base.

Materials and Methods  Heat-polymerized acrylic resin specimens were fabricated in dimensions of (65 × 10 × 2.5 ± 0.1 mm ³ ) and then sectioned and prepared, creating repair gap with butt (90 degrees) and bevel (45 degrees) repair surface designs forming two main groups according to joint design. Further subdivision was done into four groups ( n = 10) according to nano-SiO ₂ concentration: one unmodified group and three modified groups (0.25, 0.5, and 0.75 wt %) in the autopolymerized repair resin. Each pair of a specimen was assembled in a mold and repaired according to manufacturer’s recommendations.

Statistical Analysis  Three-point bending test was done to measure FS, followed by scanning electron microscope (SEM) examination for fracture surface analysis. Data were analyzed using ANOVA and Tukey’s post hoc test (α = 0.05).

Results  The addition of nano-SiO ₂ significantly improved FS of repaired acrylic resin in comparison to the unmodified group ( p ˂ 0.05). For butt joint, significant differences between nano-SiO ₂ reinforced groups were noticed ( p ˂ 0.05), while reinforced beveled groups did not differ significantly ( p ˃ 0.05). Bevel design remarkably increased FS compared with butt design per respective filler concentration. From the SEM images, improved FS was presented with a homogeneous distribution of nano-SiO ₂ within polymethyl methacrylate.

Conclusion  Nano-SiO ₂ addition to repair resin and 45 degree-beveled repair surface increased FS of repaired acrylic resin.