Recycling of TiO2-containing waste and utilization by photocatalytic degradation of a reactive dye solution

Advanced cellulose-based hydrogel TiO2 catalyst composites for efficient photocatalytic degradation of organic dye methylene blue

Sustainable cellulose-based hydrogels are used in medicine and environmental science. Hydrogels' porosity makes them excellent adsorbents and stable substrates for immobilizing photocatalysts to remove organic dyes. Despite their potential, the implementation of hydrogels for this purpose is still limited due to their high synthesis temperature and low cellulose content. To overcome these challenges, this study develops cellulose-based hydrogels, which have a high cellulose content and can be easily synthesized under ambient conditions. Containing a higher cellulose concentration than previous hydrogels, the synthesized hydrogels are more stable and can be reused numerous times in treatment operations. The hydrogel properties were investigated using Fourier transform infrared spectroscopy, X-ray diffraction and thermal analysis. Scanning electronic microscopy revealed that TiO2 nanoparticles were homogeneously distributed throughout the hydrogel's matrices. In addition, transparent hydrogels allow light to pass through, making them suitable substrates to remove organic dye. The results showed that the hydrogel with TiO2 was able to degrade nearly 90% of organic dye within 180 min. Furthermore, the hydrogel with the embedded catalyst exhibits the potential for reusability with a regeneration efficiency of 80.01% after five runs. These findings suggest that this novel hydrogel is a promising candidate for water pollution remediation.

Environmental Footprint Assessment of Methylene Blue Photodegradation using Graphene-based Titanium Dioxide

To date, photocatalysis has received much attention in terms of the degradation of organic pollutants in wastewater. Various studies have shown that graphene-based photocatalysts are one of the impressive options owing to their intriguing features, including high surface area, good conductivity, low recombination rate of electron-hole pair, and fast charge separation and transfer. However, the environmental impacts of the photocatalysts synthesis and their photodegradation activity remain unclear. Thus, this report aims to identify the environmental impacts associated with the photodegradation of methylene blue (MB) over reduced graphene oxide/titanium oxide photocatalyst (TiO2/rGO) using Life Cycle Assessment (LCA). The life cycle impacts were assessed using ReCiPe 2016 v1.1 midpoint method, Hierachist version in Gabi software. A cradle-to-gate approach and a functional unit of 1 kg TiO2/rGOwere adopted in the study. Several important parameters, such as the solvent type (ultrapure water, ethanol, and isopropanol), with/without silver ion doping, and visible light power consumption (150, 300, and 500 W) were evaluated in this study. In terms of the selection of solvent, ultrapure water is certainly a better choice since it contributed the least negative impact on the environment. Furthermore, it is not advisable to dope the photocatalyst with silver ions since the increment in performance is insufficient to offset the environmental impact that it caused. The results of different power of visible light for MB degradation showed that the minimum power level, 150 W, could give a comparable photodegradation efficiency and better environmental impacts compared to higher power light sources. Copyright © 2023 by Authors, Published by BCREC Group. This is an open access article under the CC BY-SA License (https://creativecommons.org/licenses/by-sa/4.0). 

Preparation of S-Scheme g-C3N4/ZnO Heterojunction Composite for Highly Efficient Photocatalytic Destruction of Refractory Organic Pollutant

In this study, graphitic carbon nitride (g-C3N4)-based ZnO heterostructure was synthesized using a facile calcination method with urea and zinc nitrate hexahydrate as the initiators. According to the scanning electron microscopic (SEM) images, spherical ZnO particles can be seen along the g-C3N4 nanosheets. Additionally, the X-ray diffraction (XRD) analysis reveals the successful synthesis of the g-C3N4/ZnO. The photocatalytic activity of the synthesized catalyst was tested for the decolorization of crystal violet (CV) as an organic refractory contaminant. The impacts of ZnO molar ratio, catalyst amount, CV concentration, and H2O2 concentration on CV degradation efficiency were investigated. The obtained outcomes conveyed that the ZnO molar ratio in the g-C3N4 played a prominent role in the degradation efficiency, in which the degradation efficiency reached 95.9% in the presence of 0.05 mmol of ZnO and 0.10 g/L of the catalyst in 10 mg/L of CV through 120 min under UV irradiation. Bare g-C3N4 was also tested for dye decolorization, and a 76.4% dye removal efficiency was obtained. The g-C3N4/ZnO was also tested for adsorption, and a 32.3% adsorption efficiency was obtained. Photocatalysis, in comparison to adsorption, had a dominant role in the decolorization of CV. Lastly, the results depicted no significant decrement in the CV degradation efficiency in the presence of the g-C3N4/ZnO photocatalyst after five consecutive runs.

Iron-loaded leonardite powder for Fenton oxidation of Reactive Red 180 dye removal

Fenton oxidation is an effective and valuable method for wastewater treatment. To inhibit environmental impacts and increase overall reaction efficiencies, it is important to develop advanced catalysts. This paper illustrates an experimental study on the elimination of RR180 dye from synthetic aqueous solutions with raw leonardite and different iron-loaded leonardite powders, Fe(0)-loaded leonardite, and Fe(II)-loaded leonardite. The effect of solution pH (2.0-6.0), catalyst amount (0.10-1.5 g/L), H₂O₂ concentration (10-50 µL/L), and dye concentration (10-30 ppm) was tested to achieve maximum color removal efficiency using the three catalysts. At pH = 2, color removal efficiencies were higher and more suitable. Initial experiments showed the advantage of using Fe(II)-loaded leonardite on using Fe(0)-loaded leonardite. Fe(II)-loaded leonardite catalyst was the most efficient in RR180 color removal compared to the other tested reagents. Color removal in function of solution pH did not decrease much when Fe(II)-loaded leonardite was used (100 to 96%) when pH was increased from 2.0 to 6.0. In the other hand, dye removal has been significantly affected in the case of using raw leonardite, Fe(0)-loaded leonardite (93 to 0%), and (100 to 13%) in the same pH range, respectively. At optimum experimental conditions, catalyst amount: 0.75 g/L for Fe(II) and Fe(0)-loaded leonardite and 1.5 g/L for raw leonardite; dye concentration: 10 ppm; solution pH: 2.0; H₂O₂ concentration: 50 µL/L; volume: 100 mL and reaction time: 60 min, RR180 dye removal efficiencies were 91%, 100%, and 100% by raw leonardite, Fe(0)-loaded leonardite and Fe(II)-loaded leonardite, respectively. The stability and reusability of the tested catalyst was investigated up to ten cycles. The experimental results revealed that both Fe(0)-loaded leonardite and Fe(II)-loaded leonardite can be used in Fenton reaction up to four cycles without decreasing their efficiency in RR180 color removal. The characterization of the catalysts was established using scanning electron microscope with energy dispersive X-ray spectroscopy (SEM-EDX). The synthesized catalyst can be used at large scale in any textile industry to effectively remove dyes resulting in high elimination rates at the optimal determined and studied conditions.

Photocatalytic activity of calcined chicken eggshells for Safranin and Reactive Red 180 decolorization

One of the most important problems affecting the environment today is the inability to adequately treat wastewater containing dyes. Among of the many treatment processes used in the treatment of dye-containing wastewater, photocatalytic based wastewater treatment processes attract the attention of scientists as a new, economically feasible, and promising approach which has been in practice for a few decades. However, in order to use these processes in wider areas, cheap and effective catalysts are still being developed today. In this study, the photocatalytic activity of eggshell-CaO produced from waste chicken eggshells was investigated for decolorization of Safranin (Basic Red 2) and Reactive Red 180 (RR180) dyes. First, sintering process was applied to the waste chicken eggshells at different temperatures (300, 600, 900 °C) in order to observe CaO formation from the eggshells. Second, the parameters such as photocatalyst amount, pH, concentration of dyes, and reaction time were optimized on dye removal efficiency in photocatalytic experiments. The optimum conditions were performed under visible light and found to be 1 g/L of catalyst amount (sintered at 900 °C), original solution pH (6.80 for Safranin and 6.60 for RR180), and 5 mg/L of dye concentration. The photocatalytic removal efficiencies of Safranin and RR180 dyes were 100% and 97.90%, respectively, under the determined optimum experimental conditions. The adsorption efficiency of the dyes that could be realized during the photocatalytic experiment was measured as 20.99% and 9.99% for Safranin and RR180 dyes, respectively.