Optimization of Mechanical and Setting Properties in Acrylic Bone Cements Added with Graphene Oxide

Modification of polymethylmethacrylate bone cement with halloysite clay nanotubes

BACKGROUND

Polymethylmethacrylate (PMMA) bone cement is used in orthopedics and dentistry to get primary fixation to bone but doesn't provide a mechanically and biologically stable bone interface. Therefore, there was a great demand to improve the properties of the PMMA bone cement to reduce its clinical usage limitations and enhance its success rate. Recent studies demonstrated that the addition of halloysite nanotubes (HNTs) to a polymeric-based material can improve its mechanical and thermal characteristics.

OBJECTIVES

The purpose of the study is to assess the compressive strength, flexural strength, maximum temperature, and setting time of traditional PMMA bone cements that have been manually blended with 7 wt% HNT fillers.

METHODS

PMMA powder and monomer liquid were combined to create the control group, the reinforced group was made by mixing the PMMA powder with 7 wt% HNT fillers before liquid mixing. Chemical characterization of the HNT fillers was employed by X-ray fluorescence (XRF). The morphological examination of the cements was done using a scanning electron microscope (SEM). Analytical measurements were made for the compressive strength, flexural strength, maximum temperature, and setting time. Utilizing independent sample t-tests, the data was statistically assessed to compare mean values (p < 0.05).

RESULTS

The findings demonstrated that the novel reinforced PMMA-based bone cement with 7 wt% HNT fillers showed higher mean compressive strength values (93 MPa) and higher flexural strength (72 MPa). and lower maximum temperature values (34.8 °C) than the conventional PMMA bone cement control group, which was (76 MPa), (51 MPa), and (40 °C), respectively (P < 0.05). While there was no significant difference in the setting time between the control and the modified groups.

CONCLUSION

The novel PMMA-based bone cement with the addition of 7 wt% HNTs can effectively be used in orthopedic and dental applications, as they have the potential to enhance the compressive and flexural strength and reduce the maximum temperatures.

Effect of using nano-particles of magnesium oxide and titanium dioxide to enhance physical and mechanical properties of hip joint bone cement

In this work, the effect of adding Magnesium Oxide (MgO) and Titanium Dioxide (TiO2) nanoparticles to enhance the properties of the bone cement used for hip prosthesis fixation. Related to previous work on enhanced bone cement properties utilizing MgO and TiO2, samples of composite bone cement were made using three different ratios (0.5%:1%, 1.5%:1.5%, and 1%:0.5%) w/w of MgO and TiO2 to determine the optimal enhancement ratio. Hardness, compression, and bending tests were calculated to check the mechanical properties of pure and composite bone cement. The surface structure was studied using Fourier transform infrared spectroscopy (FTIR) and Field emission scanning electron microscopy (FE-SEM). Setting temperature, porosity, and degradation were calculated for each specimen ratio to check values matched with the standard range of bone cement. The results demonstrate a slight decrease in porosity up to 2.2% and degradation up to 0.17% with NP-containing composites, as well as acceptable variations in FTIR and setting temperature. The compression strength increased by 2.8% and hardness strength increased by 1.89% on adding 0.5%w/w of MgO and 1.5%w/w TiO2 NPs. Bending strength increases by 0.35% on adding 1.5% w/w of MgO and 0.5% w/w TiO2 NPs, however, SEM scan shows remarkable improvement for surface structure.

Effect of surface modification of graphene oxide with a reactive silane coupling agent on the mechanical properties and biocompatibility of acrylic bone cements

Carbon allotrope materials (i.e. carbon nanotubes (CNTs), graphene, graphene oxide (GO)), have been used to reinforce acrylic bone cement. Nevertheless, the intrinsic incompatibility among the above materials produces a deficient interphase. Thus, in this work, the effect of the content of functionalized graphene oxide with a reactive silane on the mechanical properties and cell adhesion of acrylic bone cement was studied. GO was obtained by an oxidative process on natural graphite; subsequently, GO was functionalized with 3-methacryloxypropyltrimethoxysilane (MPS) to enhance the interphase between the graphenic material and acrylic polymeric matrix. Pristine GO and functionalized graphene oxide (GO-MPS) were characterized physicochemically (XPS, XRD, FTIR, and Raman) and morphologically (SEM and TEM). Silanized GO was added into the acrylic bone cement at different concentrations; the resulting materials were characterized mechanically, and their biocompatibility was also evaluated. The physicochemical characterization results showed that graphite was successfully oxidized, and the obtained GO was successfully functionalized with the silane coupling agent (MPS). SEM and TEM images showed that the GO is composed of few stacked layers. Compression testing results indicated a tendency of increasing stiffness and toughness of the acrylic bone cements at low concentration of functionalized GO. Additionally, the bending testing results showed a slightly increase in bone cement strain with the incorporation of GO-MPS. Finally, all samples exhibited cell viability higher than 70%, which means that materials are considered non-cytotoxic, according to the ISO 10993-5 standard.

Editorial on Special Issue “Biomaterials, Polymers and Tissue Engineering”

The development of new materials, new manufacturing methods, and new techniques has attracted interest from many researchers in recent decades [...]