Effects of Wollastonite on Fire Properties of Particleboard Made from Wood and Chicken Feather Fibers

Physical and Mechanical Properties of Particleboard Produced with Addition of Walnut (Juglans regia L.) Wood Residues

The depletion of natural resources and increased demand for wood and wood-based materials have directed researchers and the industry towards alternative raw materials for composite manufacturing, such as agricultural waste and wood residues as substitutes of traditional wood. The potential of reusing walnut (Juglans regia L.) wood residues as an alternative raw material in particleboard manufacturing is investigated in this work. Three-layer particleboard was manufactured in the laboratory with a thickness of 16 mm, target density of 650 kg∙m^-3 and three different levels (0%, 25% and 50%) of walnut wood particles, bonded with urea-formaldehyde (UF) resin. The physical properties (thickness swelling after 24 h) and mechanical properties (bending strength, modulus of elasticity and internal bond strength) were evaluated in accordance with the European standards. The effect of UF resin content and nominal applied pressure on the properties of the particleboard was also investigated. Markedly, the laboratory panels, manufactured with 50% walnut wood residues, exhibited flexural properties and internal bond strength, fulfilling the European standard requirements to particleboards used in load-bearing applications. However, none of the boards met the technical standard requirements for thickness swelling (24 h). Conclusively, walnut wood residues as a waste or by-product of the wood-processing industry can be efficiently utilized in the production of particleboard in terms of enhancing its mechanical properties.

Fire Parameters of Spruce (Picea abies Karst. (L.)) Dust Layer from Different Wood Technologies Slovak Case Study

The issue of the formation of wood dust particles in the work environment is still an actual topic in terms of its impact on employee health and the risk of fire or explosion in a woodworking operation. This article deals with the characteristics of spruce dust (Picea abies Karst. (L.)), which was taken from several types of wood technology. Experimental samples of spruce dust were taken from four types of sawing technologies, including grinding, briquetting and from the suction device container. The physical parameters of the samples taken were monitored and the particle size analysis was determined. The granulometric composition of the samples is significantly different. The sample of spruce wood dust from sawing has the most numerous fraction (250 µm), while the sample from grinding has the most numerous fraction 63–250 µm (87%).The aim of the paper was to monitor the minimum ignition temperature of the settled spruce dust layer and to look for a significant dependence of the minimum ignition temperature and ignition time on the type of spruce dust sample. A significant dependence was not confirmed. Significant moisture dependence of the samples was confirmed; the highest humidity was observed in the container, the lowest in sawing.

Structural Application of Lightweight Panels Made of Waste Cardboard and Beech Veneer

In recent years, the furniture design trends include ensuring ergonomic standards, development of new environmentally friendly materials, optimised use of natural resources, and sustainably increased conversion of waste into value-added products. The circular economy principles require the reuse, recycling or upcycling of materials. The potential of reusing waste corrugated cardboard to produce new lightweight boards suitable for furniture and interior applications was investigated in this work. Two types of multi-layered panels were manufactured in the laboratory from corrugated cardboard and beech veneer, bonded with urea-formaldehyde (UF) resin. Seven types of end corner joints of the created lightweight furniture panels and three conventional honeycomb panels were tested. Bending moments and stiffness coefficients in the compression test were evaluated. The bending strength values of the joints made of waste cardboard and beech veneer exhibited the required strength for application in furniture constructions or as interior elements. The joints made of multi-layer panels with a thickness of 51 mm, joined by dowels, demonstrated the highest bending strength and stiffness values (33.22 N∙m). The joints made of 21 mm thick multi-layer panels and connected with Confirmat had satisfactory bending strength values (10.53 N∙m) and Minifix had the lowest strength values (6.15 N∙m). The highest stiffness values (327 N∙m/rad) were determined for the 50 mm thick cardboard honeycomb panels connected by plastic corner connector and special screw Varianta, and the lowest values for the joints made of 21 mm thick multi-layer panels connected by Confirmat (40 N∙m/rad) and Minifix (43 N∙m/rad), respectively. The application of waste corrugated cardboard as a structural material for furniture and interiors can be improved by further investigations.

The Effect of Heat Flux to the Fire-Technical and Chemical Properties of Spruce Wood (Picea abies L.)

The paper assesses the influence of the heat flux on spruce wood (Picea abies L.) behavior. The heat flux was performed at 15, 20, 25, and 30 kW·m⁻². The fire-technical properties, such as the mass burning rate, charring thickness, charring rate, as well as the chemical composition (contents of the extractives, lignin, cellulose, holocellulose), of wood were determined. The highest burning rate of spruce wood of 0.32%·s⁻¹ was reached at the heat flux of 30 kW·m⁻². The charring rate ranged from 1.004 mm·min⁻¹ (15 kW·m⁻²) to 2.016 mm·min⁻¹ (30 kW·m⁻²). The proposed model of the charring process of spruce wood in time and appropriate thickness as a selected parameter is applicable in validation of the results of computer fire models in the design of fire protection of wooden buildings. The decrease in the holocellulose content mostly caused by the degradation of hemicelluloses was observed during thermal loading. The biggest decrease in hemicelluloses (24.94%) was recorded in samples loaded at 30 kW·m⁻². The contents of cellulose increased due to the structural changes (carbonization and crosslinking), the content of lignin increased as well due to its higher thermal stability compared to saccharides, as well as the resulting lignin condensation.

Thermophysical Properties of Larch Bark Composite Panels

The effects of using 100% larch bark (Larix decidua Mill) as a raw material for composite boards on the thermophysical properties of this innovative material were investigated in this study. Panels made of larch bark with 4–11 mm and 10–30 mm particle size, with ground bark oriented parallel and perpendicular to the panel’s plane at densities varying from 350 to 700 kg/m³ and bonded with urea-formaldehyde adhesive were analyzed for thermal conductivity, thermal resistivity and specific heat capacity. It was determined that there was a highly significant influence of bulk density on the thermal conductivity of all the panels. With an increase in the particle size, both parallel and perpendicular to the panel´s plane direction, the thermal conductivity also increased. The decrease of thermal diffusivity was a consequence of the increasing particle size, mostly in the parallel orientation of the bark particles due to the different pore structures. The specific heat capacity is not statistically significantly dependent on the density, particle size, glue amount and particle orientation.