Organic and Inorganic PCL-Based Electrospun Fibers

Hydrolytic Degradation and Bioactivity of Electrospun PCL-Mg-NPs Fibrous Mats

In this work, the in vitro degradation behavior of nanofibers was investigated in phosphate buffer solution (PBS) and simulated body fluid (SBF) to study their degradation behavior, as well as their bioactivity. The degradation was studied at different immersion times in order to evaluate how the presence of Mg-based nanoparticles can affect the degradation in terms of morphology, crystallinity, degradation rate and pH changes, and finally to evaluate the bioactivity of PCL-based electrospun nanofibers. We found that the degradation of the materials takes more than 3 months; however, the presence of nanoparticles seems to have an accelerating effect on the degradation of the electrospun nanofibers based on PCL. In fact, a reduction in diameter of almost 50% was observed with the highest content of both types of nanoparticles and an increase in crystallinity after 296 days of immersion in PBS. Moreover, the carbonyl index was calculated from an FTIR analysis, and a reduction of 20-30% was observed due to the degradation effect. Additionally, the bioactivity of PCL-based electrospun nanofibers was studied and the formation of crystals on the nanofibers surface was detected, except for neat electrospun PCL related to the formation of NaCl and apatites, depending on the amount and type of nanoparticles. The presence of apatites was confirmed by an XRD analysis and FT-IR analysis observing the characteristic peaks; furthermore, the EDX analysis demonstrated the formation of apatites than can be reconducted to the presence of HA when 20 wt% of nanoparticles is added to the PCL electrospun fibers.

Fabrication and characterization of electrospun GelMA/PCL/CS nanofiber composites for wound dressing applications

In the present study, the effect of different ratios of GelMA concentration has been exhibited for wound dressing implementation by the electrospinning method using a new polymer combination of Gelatin methacrylate (GelMA)/Polycaprolactone (PCL)/Chitosan (CS). The nanofiber composites were fabricated due to their biocompatible, biodegradable, improved mechanical strength, low degradation rate, and hydrophilic nature to develop cell-mimicking, cell adhesion, proliferation, and differentiation. Different concentrations of GelMA were added to the PCL/CS solution as 5, 10, and 20 wt%, respectively, in the formic acid/acetic acid (7:3) solution. A photoinitiator was added to the solution for photo-crosslinking of GelMA. The influence of different solution concentrations (5, 10, and 20 wt%) on the structure’s nanofiber production and fiber morphology was examined. SEM micrographs revealed that varied GelMA concentrations resulted in suitable and stable nanofiber composites. The average diameter of nanofiber composites grows as the GelMA concentration rises. FTIR, DSC, tensile test, degradation, and swelling test were evaluated. The results demonstrated that high mechanical strength, hydrophilic properties, and a slow degradation rate were observed with the presence and increment of GelMA concentration within the nanofiber composites. The antibacterial potential of GelMA/PCL/CS nanofiber composites was evaluated against P. aeruginosa and S. aureus using a disc diffusion assay. In vitro cell culture research was conducted by seeding NIH 3T3 fibroblast cells on nanofiber composites, proving these cells’ high cell proliferation rate, viability, and adhesion. 10 wt% GelMA-based nanofiber composites were found to have great potential for wound dressing applications.

Advances in Electrospun Hybrid Nanofibers for Biomedical Applications

Electrospun hybrid nanofibers, based on functional agents immobilized in polymeric matrix, possess a unique combination of collective properties. These are beneficial for a wide range of applications, which include theranostics, filtration, catalysis, and tissue engineering, among others. The combination of functional agents in a nanofiber matrix offer accessibility to multifunctional nanocompartments with significantly improved mechanical, electrical, and chemical properties, along with better biocompatibility and biodegradability. This review summarizes recent work performed for the fabrication, characterization, and optimization of different hybrid nanofibers containing varieties of functional agents, such as laser ablated inorganic nanoparticles (NPs), which include, for instance, gold nanoparticles (Au NPs) and titanium nitride nanoparticles (TiNPs), perovskites, drugs, growth factors, and smart, inorganic polymers. Biocompatible and biodegradable polymers such as chitosan, cellulose, and polycaprolactone are very promising macromolecules as a nanofiber matrix for immobilizing such functional agents. The assimilation of such polymeric matrices with functional agents that possess wide varieties of characteristics require a modified approach towards electrospinning techniques such as coelectrospinning and template spinning. Additional focus within this review is devoted to the state of the art for the implementations of these approaches as viable options for the achievement of multifunctional hybrid nanofibers. Finally, recent advances and challenges, in particular, mass fabrication and prospects of hybrid nanofibers for tissue engineering and biomedical applications have been summarized.

Compositional Influence on the Morphology and Thermal Properties of Woven Non-Woven Mats of PLA/OLA/MgO Electrospun Fibers

In the present work, a statistical study of the morphology and thermal behavior of poly(lactic acid) (PLA)/oligomer(lactic acid) (OLA)/magnesium oxide nanoparticles (MgO), electrospun fibers (efibers) has been carried out. The addition of both, OLA and MgO, is expected to modify the final properties of the electrospun PLA-based nanocomposites for their potential use in biomedical applications. Looking for the compositional optimization of these materials, a Box−Wilson design of experiment was used, taking as dependent variables the average fiber diameter as the representative of the fiber morphologies, as well as the glass transition temperature (Tg) and the degree of crystallinity (Xc) as their thermal response. The results show <r2> values of 73.76% (diameter), 88.59% (Tg) and 75.61% (Xc) for each polynomial fit, indicating a good correlation between both OLA and MgO, along with the morphological as well as the thermal behavior of the PLA-based efibers in the experimental space scanned.

Shape-Memory Materials via Electrospinning: A Review

This review aims to point out the importance of the synergic effects of two relevant and appealing polymeric issues: electrospun fibers and shape-memory properties. The attention is focused specifically on the design and processing of electrospun polymeric fibers with shape-memory capabilities and their potential application fields. It is shown that this field needs to be explored more from both scientific and industrial points of view; however, very promising results have been obtained up to now in the biomedical field and also as sensors and actuators and in electronics.

Nature-Derived and Synthetic Additives to poly(ɛ-Caprolactone) Nanofibrous Systems for Biomedicine; an Updated Overview

As a low cost, biocompatible, and bioresorbable synthetic polymer, poly (ɛ-caprolactone) (PCL) is widely used for different biomedical applications including drug delivery, wound dressing, and tissue engineering. An extensive range of in vitro and in vivo tests has proven the favourable applicability of PCL in biomedicine, bringing about the FDA approval for a plethora of PCL made medical or drug delivery systems. This popular polymer, widely researched since the 1970s, can be readily processed through various techniques such as 3D printing and electrospinning to create biomimetic and customized medical products. However, low mechanical strength, insufficient number of cellular recognition sites, poor bioactivity, and hydrophobicity are main shortcomings of PCL limiting its broader use for biomedical applications. To maintain and benefit from the high potential of PCL, yet addressing its physicochemical and biological challenges, blending with nature-derived (bio)polymers and incorporation of nanofillers have been extensively investigated. Here, we discuss novel additives that have been meant for enhancement of PCL nanofiber properties and thus for further extension of the PCL nanofiber application domain. The most recent researches (since 2017) have been covered and an updated overview about hybrid PCL nanofibers is presented with focus on those including nature-derived additives, e.g., polysaccharides and proteins, and synthetic additives, e.g., inorganic and carbon nanomaterials.

Evaluation of Functional Features of Lignocellulosic Particle Composites Containing Biopolymer Binders

In this research, the assessment of the impact of natural biopolymer binders on selected mechanical and physical properties of lignocellulosic composites manufactured with different resination (12%, 15%, 20%). Different mechanical and physical properties were determined: modulus of rupture, modulus of elasticity, internal bonding strength, thickness swelling, water absorption, contact angle, and density profile. Moreover, thermal properties such as thermogravimetric analysis and differential scanning calorimetry were studied for the polymers. The results showed significant improvement of characterized features of the composites produced using biopolymers. However, the rise of the properties was visible when the binder content raised from 12% to 15%. Further increase of biopolymer binder did not imply a considerable change. The most promising biopolymer within the tested ones seems to be polycaprolactone (PCL).

Effects of Montmorillonite and Gentamicin Addition on the Properties of Electrospun Polycaprolactone Fibers

Electrospinning was used to obtain multifunctional fibrous composite materials with a matrix of poly-ɛ-caprolactone (PCL) and 2 wt.% addition of a nanofiller: montmorillonite (MMT), montmorillonite intercalated with gentamicin sulphate (MMTG) or gentamicin sulphate (G). In the first stage, the aluminosilicate gallery was modified by introducing gentamicin sulfate into it, and the effectiveness of the intercalation process was confirmed on the basis of changes in the clay particle size from 0.5 µm (for MMT) to 0.8 µm (for MMTG), an increase in the interplanar distance d₀₀₁ from 12.3 Å (for MMT) to 13.9 Å (for MMTG) and altered clay grain morphology. In the second part of the experiment, the electrospinning process was carried out in which the polymer nonwovens with and without the modifier were prepared directly from dichloromethane (DCM) and N,N-dimethylformamide (DMF). The nanocomposite fibrous membranes containing montmorillonite were prepared from the same polymer solution but after homogenization with the modifier (13 wt.%). The degree of dispersion of the modifier was evaluated by average microarray analysis from observed area (EDS), which was also used to determine the intercalation of montmorillonite with gentamicin sulfate. An increase in the size of the fibers was found for the materials with the presence of the modifier, with the largest diameters measured for PCL_MMT (625 nm), and the smaller ones for PCL_MMTG (578 nm) and PCL_G (512 nm). The dispersion of MMT and MMTG in the PCL fibers was also confirmed by indirect studies such as change in mechanical properties of the nonwovens membrane, where the neat PCL nonwoven was used as a reference material. The addition of the modifier reduced the contact angle of PCL nonwovens (from 120° for PCL to 96° for PCL_G and 98° for PCL_MMTG). An approximately 10% increase in tensile strength of the nonwoven fabric with the addition of MMT compared to the neat PCL nonwoven fabric was also observed. The results of microbiological tests showed antibacterial activity of all obtained materials; however, the inhibition zones were the highest for the materials containing gentamicin sulphate, and the release time of the active substance was significantly extended for the materials with the addition of montmorillonite containing the antibiotic. The results clearly show that the electrospinning technique can be effectively used to obtain nanobiocomposite fibers with the addition of nonintercalated and intercalated montmorillonite with improved strength and increased stiffness compared to materials made only of the polymer fibers, provided that a high filler dispersion in the spinning solution is obtained.

PLA Electrospun Fibers Reinforced with Organic and Inorganic Nanoparticles: A Comparative Study

In this work, different poly (lactic acid) (PLA)-based nanocomposite electrospun fibers, reinforced with both organic and inorganic nanoparticles, were obtained. As organic fibers, cellulose nanocrystals, CNC, both neat and functionalized by “grafting from” reaction, chitosan and graphene were used; meanwhile, hydroxyapatite and silver nanoparticles were used as inorganic fibers. All of the nanoparticles were added at 1 wt% with respect to the PLA matrix in order to be able to compare their effect. The main aim of this work was to study the morphological, thermal and mechanical properties of the different systems, looking for differences between the effects of the addition of organic or inorganic nanoparticles. No differences were found in either the glass transition temperature or the melting temperature between the different electrospun systems. However, systems reinforced with both neat and functionalized CNC exhibited an enhanced degree of crystallinity of the electrospun fibers, by up to 12.3%. From a mechanical point of view, both organic and inorganic nanoparticles exhibited a decreased elastic modulus and tensile strength in comparison to neat electrospun PLA fibers, improving their elongation at break. Furthermore, all of the organic and inorganic reinforced systems disintegrated under composting conditions after 35 days.

Antimicrobial Active Bioplastics Using Triangular Silver Nanoplate Integrated Polycaprolactone and Polylactic Acid Films

An innovative antimicrobial technology for plastic surfaces is presented. We report the synthesis and scale-up of triangular silver nanoplates (TSNPs) and their integration into polycaprolactone (PCL) and polylactic acid (PLA) polymers through a solvent-casting technique. The TSNPs have a high geometric aspect ratio and strong local surface plasmon resonance (LSPR) response, which provides an effective tool for monitoring their integrity during processing and integration with the biodegradable plastics. An aqueous-based seed-mediated chemical method was used to synthesize the TSNPs, and characterisation was carried out using TEM and UV (Ultraviolet)-VIS (Visible) spectroscopy to measure LSPR profiles. The UV-VIS spectra of silver seeds and TSNPs exhibited characteristic peaks at 395 and 600 nm respectively. Synthesized TSNPs were coated with thiol-terminated polyethylene glycol (SH-PEG) and transferred into chloroform in order to effect compatibility with PCL and PLA. TSNP/PCL and TSNP/PLA composite films were prepared by solvent casting. The morphological structure, thermal, mechanical, and antimicrobial properties of the TSNP-incorporated composite films were evaluated. Results showed the TSNP-treated films had a rougher surface than the bare films. Insignificant changes in the thermal properties of TSNP-treated films compared to bare ones were also observed, which indicated the thermal stability of the composite films. The tensile strength and antimicrobial properties of the composite films were increased after TSNP incorporation. TSNP/PCL and TSNP/PLA films exhibited improved antimicrobial activity against Escherichia coli and Staphylococcus aureus with antimicrobial effect (AE) values ranging between 0.10 and 0.35. The obtained results and demonstrated TSNP production scalability validate the TSNP treated PCL and PLA films as a composite material with desirable antimicrobial effect for wide-ranging surface applications.

In Vitro Degradation of Plasticized PLA Electrospun Fiber Mats: Morphological, Thermal and Crystalline Evolution

In the present work, fiber mats of poly(lactic acid), PLA, plasticized by different amounts of oligomer lactic acid, OLA, were obtained by electrospinning in order to investigate their long term hydrolytic degradation. This was performed in a simulated body fluid for up to 352 days, until the complete degradation of the samples is reached. The evolution of the plasticized electrospun mats was followed in terms of morphological, thermal, chemical and crystalline changes. Mass variation and water uptake of PLA-based electrospun mats, together with pH stability of the immersion media, were also studied during the in vitro test. The results showed that the addition of OLA increases the hydrolytic degradation rate of PLA electrospun fiber mats. Moreover, by adding different amounts of OLA, the time of degradation of the electrospun fiber mats can be modulated over the course of a year. Effectively, by increasing the amount of OLA, the diameter of the electrospun fibers decreases more rapidly during degradation. On the other hand, the degree of crystallinity and the dimension of the α crystals of the electrospun fiber mats are highly affected not only by the presence but also by the amount of OLA during the whole process.

Electrospinning of PCL-Based Blends: Processing Optimization for Their Scalable Production

In this work poly(ε-caprolactone) (PCL) based electrospun mats were prepared by blending PCL with microcrystalline cellulose (MCC) and poly(3-hydroxybutyrate) (PHB). The electrospinning processing parameters were firstly optimized with the aim to obtain scalable PCL-based electrospun mats to be used in the industrial sector. Neat PCL as well as PCL-MCC and PCL-PHB based mats in different proportions (99:1; 95:5; 90:10) were prepared. A complete morphological, thermal and mechanical characterization of the developed materials was carried out. Scanning electron microscopy (SEM) observations showed that the addition of PHB to the PCL matrix considerably reduced the formation of beads. Both the addition of MCC and PHB reduced the thermal stability of PCL, but obtained materials with enough thermal stability for the intended use. The electrospun PCL fibers show greatly reduced flexibility with respect to the PCL bulk material, however when PCL is blended with PHB their stretchability is increased, changing their elongation at break from 35% to 70% when 10 wt% of PHB is blended with PCL. However, the mechanical response of the different blends increases with respect to the neat electrospun PCL, offering the possibility to modulate their properties according to the required industrial applications.

Potential Applications of Magnesium-Based Polymeric Nanocomposites Obtained by Electrospinning Technique

In the last few decades, the development of new electrospun materials with different morphologies and advanced multifunctional properties are strongly consolidated. There are several reviews that describe the processing, use and characterization of electrospun nanocomposites, however, based on our knowledge, no review on electrospun nanocomposites reinforced with nanoparticles (NPs) based on magnesium, Mg-based NPs, are reported. Therefore, in the present review, we focus attention on the fabrication of these promising electrospun materials and their potential applications. Firstly, the electrospinning technique and its main processing window-parameters are described, as well as some post-processing methods used to obtain Mg-based materials. Then, the applications of Mg-based electrospun nanocomposites in different fields are pointed out, thus taking into account the current trend in developing inorganic-organic nanocomposites to gradually satisfy the challenges that the industry generates. Mg-based electrospun nanocomposites are becoming an attractive field of research for environmental remediation (waste-water cleaning and air filtration) as well as for novel technical textiles. However, the mayor application of Mg-based electrospun materials is in the biomedical field, as pointed out. Therefore, this review aims to clarify the tendency in using electrospinning technique and Mg-based nanoparticles to huge development at industrial level in the near future.