Characterization of Polyamide 6/Multilayer Graphene Nanoplatelet Composite Textile Filaments Obtained Via In Situ Polymerization and Melt Spinning

Microfiber Fabricated via Microfluidic Spinning toward Tissue Engineering Applications

Microfibers, a type of long, thin, and flexible material, can be assembled into functional 3D structures by folding, binding, and weaving. As a novel spinning method, combining microfluidic technology and wet spinning, microfluidic spinning technology can precisely control the size, morphology, structure, and composition of the microfibers. Particularly, the process is mild and rapid, which is suitable for preparing microfibers using biocompatible materials and without affecting the viability of cells encapsulated. Furthermore, owing to the controllability of microfluidic spinning, microfibers with well-defined structures (such as hollow structures) will contribute to the exchange of nutrients or guide cell orientation. Thus, this method is often used to fabricate microfibers as cell scaffolds for cell encapsulation or adhesion and can be further applied to biomimetic fibrous tissues. In this review, the focus is on different fiber structures prepared by microfluidic spinning technology, including solid, hollow, and heterogeneous structures, generated from three essential elements: spinning platform, fiber composition, and solidification methods. Furthermore, the application of microfibers is described with different structures in tissue engineering, such as blood vessels, skeletal muscle, bone, nerves, and lung bronchi. Finally, the challenges and future development prospects of microfluidic spinning technology in tissue engineering applications are discussed.

Assessment of new composites containing polyamide-6 and lead monoxide as shields against ionizing photonic radiation based on computational and experimental methods

This study aimed to introduce new composites, containing polyamide-6 (PA6) and lead monoxide (PbO), to protect against ionizing photon sources used for diagnostic and therapeutic purposes. Five composites, containing various weight percentages of PbO filler (0, 5, 10, 20, and 50%), were developed in this study. Initially, the numerical attenuation value was estimated using the XMuDat program by calculating the mass attenuation coefficients at different energy levels. Next, the samples were synthesized based on the melt-mixing method in a laboratory mixing extruder. Their characteristics were also determined by scanning electron microscopy (SEM), energy dispersive X-ray (EDX) analysis, X-ray diffraction (XRD), and thermogravimetric analysis (TGA). Finally, experimental radiation attenuation tests were carried out. Based on the SEM results, the acceptable filler weight percentage was up to 20%. However, substantial aggregates were formed at the highest weight percentage. The results of XRD analysis showed a higher tendency for crystallization by decreasing the amorphous area while increasing the filler weight percentage. Moreover, the mass loss rate was monitored at different temperatures, revealing that the filler incorporation improved the thermal durability of the samples. The radiation results showed a good agreement between the experimental and computational data, except when aggregates formation was substantial. The experimental data revealed that when the lead weight percentage increased from 0% (crude PA6) to 50%, the half-value layer decreased from 3.13 to 0.17 cm at an energy level of 59 keV and from 7.28 to 4.97 cm at an energy level of 662 keV. Following the studied mechanism, the superiority of lead/polyamide composites can be found in the high adsorption of photon radiation at low energies (E < 0.20 MeV) and significant attenuation at medium and higher energies. Considering these promising results, the shielding properties of these composites can be further analyzed via more practical investigations.

Assessment of new composites containing polyamide-6 and lead monoxide as shields against ionizing photonic radiation based on computational and experimental methods

This study aimed to introduce new composites, containing polyamide-6 (PA6) and lead monoxide (PbO), to protect against ionizing photon sources used for diagnostic and therapeutic purposes. Five composites, containing various weight percentages of PbO filler (0, 5, 10, 20, and 50%), were developed in this study. Initially, the numerical attenuation value was estimated using the XMuDat program by calculating the mass attenuation coefficients at different energy levels. Next, the samples were synthesized based on the melt-mixing method in a laboratory mixing extruder. Their characteristics were also determined by scanning electron microscopy (SEM), energy dispersive X-ray (EDX) analysis, X-ray diffraction (XRD), and thermogravimetric analysis (TGA). Finally, experimental radiation attenuation tests were carried out. Based on the SEM results, the acceptable filler weight percentage was up to 20%. However, substantial aggregates were formed at the highest weight percentage. The results of XRD analysis showed a higher tendency for crystallization by decreasing the amorphous area while increasing the filler weight percentage. Moreover, the mass loss rate was monitored at different temperatures, revealing that the filler incorporation improved the thermal durability of the samples. The radiation results showed a good agreement between the experimental and computational data, except when aggregates formation was substantial. The experimental data revealed that when the lead weight percentage increased from 0% (crude PA6) to 50%, the half-value layer decreased from 3.13 to 0.17 cm at an energy level of 59 keV and from 7.28 to 4.97 cm at an energy level of 662 keV. Following the studied mechanism, the superiority of lead/polyamide composites can be found in the high adsorption of photon radiation at low energies (E < 0.20 MeV) and significant attenuation at medium and higher energies. Considering these promising results, the shielding properties of these composites can be further analyzed via more practical investigations.

Thermal and Quasi-Static Mechanical Characterization of Polyamide 6-Graphene Nanoplatelets Composites

The growing demand for lightweight and multifunctional products in numerous industrial fields has recently fuelled a growing interest in the development of materials based on polymer matrices including graphene-like particles, intrinsically characterized by outstanding mechanical, thermal, and electrical properties. Specifically, with regard to one of the main mass sectors, which is the automotive, there has been a significant increase in the use of reinforced polyamides for underhood applications and fuel systems thanks to their thermal and chemical resistance. In this frame, polyamide 6 (PA6) composites filled with graphene nanoplatelets (GNPs) were obtained by melt-compounding and compared in terms of thermal and mechanical properties with the neat matrix processed under the same condition. The results of the experimental tests have shown that the formulations studied so far offer slight improvements in terms of thermal stability but much more appreciable benefits regarding both tensile and flexural parameters with respect to the reference material. Among these effects, the influence of the filler content on the strength parameter is noteworthy. However, the predictable worsening of the graphene sheet dispersion for GNPs contents greater than 3%, as witnessed by scanning electron images of the tensile fractured sections of specimens, affected the ultimate performance of the more concentrated formulation.

Supramolecular exfoliation of layer silicate clay by novel cationic pillar[5]arene intercalants

Clays are multi-layered inorganic materials that can be used to prepare nanocomposite fillers. Because the multi-layered structure is thermodynamically stable, it is difficult to change a multi-layered material into single layers to improve its dispersity. Previously, clays were modified with dodecylammonium cations to promote complexation with nylon 6, nylon 66, polypropylene, polyethylene, polystyrene, and polycaprolactone to increase the mechanical strength (and/or thermal stability) of the composite material; however, complete exfoliation could not be achieved in these composites. In this study, pillar[5]arenes are synthesized and functionalized with ten cationic substituents as novel intercalants for modifying bentonite clay, which is a multi-layered metal-cation-containing silicate. The pillar[5]arenes exfoliate the clay by forming polyrotaxanes with poly(ethylene glycol) through host–guest interactions.