Study on the Effect of Zinc on the Rheological, Mechanical and Thermal Properties and Fire Hazard of Unfilled and Filled CR/BR Vulcanizates

Cross-Linking Characteristics, Morphology, Dynamics, and Mechanical and Thermal Properties of Polychloroprene/Polybutadiene/Nano-Zinc (CR/BR/nZn) Compositions with Reduced Fire Hazard

The properties of unconventional blends of crystallizable and thermo-cross-linkable polychloroprene (CR) with polybutadiene (BR) were investigated in this study. The compositions were prepared using the method of reactive processing and cross-linking in the presence of nano-sized zinc (nZn). The purpose of the research was to assess the efficacy of nano-zinc as a curing agent of polychloroprene and polybutadiene (CR/BR) composites and to obtain rubber goods characterized by increased flame resistance. The blends were filled with nano-silica (aerosil) and fillers of natural origin (chalcedonite or silitin). The cross-linking process was characterized by determining the kinetics curves, the equilibrium swelling, and the Mooney-Rivlin elasticity constants. The morphology of the vulcanizate surface was specified by scanning electron microscopy (SEM). The dynamic and mechanical properties, flammability, and toxicity of gaseous substances involved in thermal decomposition were determined. Mass changes and thermal effects were studied using simultaneous thermal analysis (STA). It was confirmed that nano-zinc is an efficient curing agent for the polychloroprene and polybutadiene compositions, with a satisfactory degree of cross-linking (αc = 0.10, CRI = 4.11 min-1), good mechanical strength (TSb = 5 MPa), satisfactory tear resistance (Ts = 2.9 N/mm), and very high flame resistance (OI = 30%, HRRmax = 283 kW/m2). Filled products could be used as non-combustible materials, confirming the low fire hazard (1/tflashover = 3.5-6.4 kW/m2∙s). The most effective filler of the tested composites was nano-sized silica.

The Use of Copper Oxides as Cross-Linking Substances for Chloroprene Rubber and Study of the Vulcanizates Properties. Part I

The purpose of this work was to verify the ability to cross-link the chloroprene rubber (CR) by using copper oxides: copper(I) oxide or copper(II) oxide. The use of copper oxides arises from the need to limit the application of ZnO as a cross-linking agent of CR. The obtained results indicate that CR compositions cross-linked with copper oxides are characterized by good mechanical properties and a high cross-linking degree. The results show that the type and the amount of copper oxides influence the cross-linking of the CR and the properties of the vulcanizates. For compositions containing copper(II) oxide, the properties are linearly dependent on the amount of CuO. Such a relationship is difficult to notice in the case of the use of copper(I) oxide—when analyzing individual parameters, the best results are obtained for different samples. Infrared spectroscopy (IR) studies confirmed the possibility of cross-linking of chloroprene rubber with copper oxides. This is evidenced by the characteristic changes in the intensity of the bands. Structural changes in the material during heating were determined by the thermal analysis—differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Regardless of the type and amount of copper oxide, all compositions exhibit similar characteristics, and there are no significant changes in the glass transition temperature of the material.