Alumina Femoral Head Fracture: An in Vitro Study

A fracture of a ceramic femoral head is reported in this study. Fractures of ceramic femoral heads are uncommon and reports on this complication are rare. After 3 million cycles, on a twelve station hip simulator that tested alumina femoral head against polyethylene acetabular cup, fracture of the ceramic ball was observed. The retrieved specimen consisted of three large ceramic fragments from the same ceramic femoral head, a polyethylene acetabular cup and a stainless steel jig. Careful and detailed examination of the removed components was made. The fracture of the ceramic ball resulted in damage to the metal taper of the jig component which was fixed into the simulator.

Neurodevelopmental risk factors in schizophrenia

The authors review environmental and neurodevelopmental risk factors for schizophrenic disorders, with emphasis on minor physical anomalies, particularly craniofacial anomalies and dermatoglyphic variations. The high prevalence of these anomalies among schizophrenic subjects supports the neurodevelopmental theory of the etiology of schizophrenia, since they suggest either genetically or epigenetically controlled faulty embryonic development of structures of ectodermal origin like brain and skin. This may disturb neurodevelopment that in turn may cause these subjects to be at increased risk for the development of schizophrenia and related disorders. The precise confirmation of this theory, at least in some cases, will provide further understanding of these illnesses, allowing easy and inexpensive identification of subjects at risk and providing guidelines for the development of new pharmacological interventions for early treatment and even for primary prevention of the illness.

Alumina femoral head fracture: an in vitro study

A fracture of a ceramic femoral head is reported in this study. Fractures of ceramic femoral heads are uncommon and reports on this complication are rare. After 3 million cycles, on a twelve station hip simulator that tested alumina femoral head against polyethylene acetabular cup, fracture of the ceramic ball was observed. The retrieved specimen consisted of three large ceramic fragments from the same ceramic femoral head, a polyethylene acetabular cup and a stainless steel jig. Careful and detailed examination of the removed components was made. The fracture of the ceramic ball resulted in damage to the metal taper of the jig component which was fixed into the simulator.