The Effect of Polyacrylate Emulsion Coating with Unmodified and Modified Nano-TiO2 on Weathering Resistance of Untreated and Heat-Treated Wood

In this research, the influence of titanium dioxide (TiO2) nanoparticles and their modifications on the weathering resistance of untreated and heat-treated wood was studied. The wood samples were coated with polyacrylate waterborne emulsion coatings that contain nano-TiO2 in the amount of 0.75 wt.%. Two types of modifiers were used to modify the nano-TiO2 surface: 2,2'-azobis(2-methylpropionamide) dihydrochloride (AIBA) and 3-aminopropyltrimethoxy silane (AMPTS). Coated and uncoated wood samples were exposed to accelerated weathering by application of sunlight, water and moisture for 360 h. During the research, the dry film thickness, color, gloss and hardness of the surface of the samples were measured. The obtained results showed that the effect of the addition and surface modification of nano-TiO2 on the color and gloss stability was different on untreated and heat-treated ash wood, and that accelerated weathering causes an increase in surface hardness and a decrease in thickness of the dry coating.

Analysis of Bonding Mechanisms of Various Implants and Adhesives in Laminated Oak-Wood Elements

This study analysed the bonding mechanisms and strength between wood and non-wood implants in producing laminated oak-wood beams. The suitability of different types of adhesives, namely for load-bearing and general purpose, was also analysed. Three different types of non-wood implants-carbon fibres, glass fibres, and aluminium were glued with epoxy resin (ER), thermoplastic 1-k polyurethane adhesives (PUR), structural polyurethane adhesives (PUR 2 and PUR 3), and polyvinyl acetate (PVAc) adhesives and bonds were tested for shear strength (SS) according to ISO 6238:2018. Results of the bond quality expressed as the ultimate load to failure and displacement were recorded using the universal mechanical testing machine in combination with the digital image correlation (DIC) method. Before the shear test, all the samples were conditioned in dry and wet climatic conditions. Test results indicated that the application of PUR adhesives for bonding carbon and glass fibres with oak wood could sufficiently replace two-component ER, which is generally recommended for such purposes but is very challenging to utilise in industrial conditions. PVAc adhesives proved efficient only for combination with AL implants and in dry conditions. Aluminium sheets were shown to require surface pre-treatment, such as sanding and degreasing or a different type of adhesive to achieve sufficient adhesion.