The Effect of the Microstructure and Viscosity of Modified Bitumen on the Strength of Asphalt Concrete

The purpose of these studies was to establish the influence of the microstructural and rheological characteristics of modified bitumen compositions on the strength indicators of asphalt concrete. The effect of additives concentration on the rheological characteristics and microstructure of binary "bitumen-surfactant", "bitumen-AG-4I", and ternary "bitumen-AG-4I-AG-4I" systems has been studied. To assess the effect of bitumen dispersion on the physical and mechanical characteristics of modified asphalt concrete samples, the compressive strength value was determined. The following chemicals have been used as additives: the original product AS-1, industrial additive AMDOR-10, and used sealant AG-4I, a product based on polyisobutylene and petroleum oils. At an increased content of AG-4I (C ≥ 1.0 g/dm3) in ternary systems, the contribution of the emerging intermolecular polyisobutylene network to the development of structuring processes increases while the viscous effect of the surfactant AS-1 decreases. It has been established that the minimum size of bee-like bitumen structures (1.66 µm) is recorded with the joint presence of additives in the bitumen, AS-1 at a level of 1.0 g/dm3 and AG-4I at a level of 1.0 g/dm3. Under the same concentration regimes of the ternary bitumen composition, the maximum increase in compressive strength RD was achieved with the smallest size of bee-like structures of modified bitumen.

Increasing the Adhesion of Bitumen to the Surface of Mineral Fillers through Modification with a Recycled Polymer and Surfactant Obtained from Oil Refining Waste

The purpose of this study was to optimize the processes of wetting fillers by varying the content of such additives as a surfactant and polymer in bitumen-mineral compositions in order to achieve optimal performance. The cosine of the contact angle was used as a criterion for assessing the adhesion of the bitumen binder to the surface of crushed stone. The effect of the additives' concentration on surface tension and adhesive efficiency in binary and ternary bitumen compositions was studied. The following chemicals were used as additives: the original product AS-1, industrial additive AMDOR-10, and used sealant AG-4I, a product based on polyisobutylene and petroleum oils. AS-1 was obtained from the oil refining waste in the laboratory of M. Kozybayev North Kazakhstan University. The ternary "bitumen-AG-4I-AS-1" composition provided a maximum decrease in the contact angle by 15.96° (gray crushed stone) and by 14.06° (red crushed stone) relative to original bitumen, providing better wettability of the mineral filler particles with the bitumen, and as a result, maximum adhesion between the bitumen and crushed stone. The optimal performance of the bitumen-mineral composition was recorded with the joint presence of additives in the bitumen: AS-1 at a level of 1.0 g/dm3 and AG-4I at a level of 1.0 g/dm3.

Evaluation of Bitumen Modification Using a Fast-Reacting SBS Polymer at a Low Modifier Percentage

The study presented in this paper investigates the application of asphalt bitumen modification using a fast-reacting SBS polymer at a low modifier percentage. The hypothesis is that a fast-reacting styrene-butadiene-styrene (SBS) polymer that composes only 2% to 3% of the weight of the bitumen modification could extend the life of the pavement surfacing and pavement performance at relatively low input costs, increasing the net present value produced by the pavement during its life cycle. To confirm or refute this hypothesis, two types of road bitumens CA 35/50 and 50/70 were modified with low amounts of fast-reacting SBS polymer with the expectation of attaining properties similar to a 10/40-65 modified bitumen. For each type of unmodified bitumen, bitumen modification and comparative 10/40-65 modified bitumen, the following tests were conducted: needle penetration, softening point-ring and ball test method, and ductility test. The second part of the article focuses on a comparison of asphalt mixtures with different compositions of coarse-grain curves. For each mixture, complex modulus with varying temperatures and fatigue resistances are represented by the Wöhler diagram and compared. Based on in labo testing, the impact of the modification on pavement performance is evaluated. Life cycle changes for each type of modified and unmodified mixtures are quantified as road user costs, and attained benefits are compared with increased construction costs.

A Temperature-Independent Methodology for Polymer Bitumen Modification Evaluation Based on DSR Measurement

Owing to the continuous increase of traffic loads, bitumen modification has been manifested as an efficient methodology to enhance asphaltic pavement performance. Currently, the modification index, defined as the ratio of mechanical properties (e.g., complex modulus) before and after bitumen modification, is extensively adopted to evaluate the modification degree. However, bituminous materials behave as temperature-dependent, which indicates that the mechanical property varies with measured temperatures. As a result, the calculated modification index also shows temperature-dependent property, which inhibits the use of modification index. For this reason, this study introduced a method to eliminate the temperature-dependency of the modification index. In specific, a mathematical model considering the properties of modifiers was firstly established to predict the modification index-temperature curve (MI-T curve). In what follows, the temperature-dependency of modification index was analyzed to verify the proposed model on three types of modifiers, which were graphene, Styrene-Butadiene-Styrene (SBS), and Ethyl-Vinyl-Acetate (EVA), respectively. The results indicated that the developed model could efficiently predict the MI-T curves. Besides, the effective modification area (EMA) and optimal modification index (OMI) were two reasonable indicators that evaluate the bitumen modification without considering the temperature-dependency.