Cotton-based health care textile: a mini review

Bioactive and biodegradable cotton fabrics produced via synergic effect of plant extracts and essential oils in chitosan coating system

Functional antibacterial textile materials are in great demand in the medical sector. In this paper, we propose a facile, eco-friendly approach to the design of antibacterial biodegradable cotton fabrics. Cotton fiber fabrics were enhanced with a chitosan coating loaded with plant extracts and essential oils. We employed Fourier-transform infrared (FTIR) and X-ray photoelectron spectroscopy (XPS), UV-Vis spectrophotometry, optical microscopy, scanning electron microscopy (SEM), and thermogravimetric analysis (TGA) to characterize the color, structure, and thermal properties of the modified fabrics. The fabrics were found to effectively induce growth inhibition of Gram-positive and Gram-negative bacteria, especially when a synergic system of aloe vera extract and cinnamon essential oil was applied in the coating formulation. Additionally, we observed significant color and weight changes after 5, 10, and 20 days in soil biodegradability tests. Given the straightforward modification process and the use of non-toxic natural materials, these innovative bio-based and biodegradable cotton fabrics show great promise as protective antimicrobial textiles for healthcare applications.

Blood Coagulation Activities of Cotton-Alginate-Copper Composites

Alginate-based materials have gained significant attention in the medical industry due to their biochemical properties. In this article, we aimed to synthesize Cotton-Alginate-Copper Composite Materials (COT-Alg(-)Cu(2+)). The main purpose of this study was to assess the biochemical properties of new composites in the area of blood plasma coagulation processes, including activated partial thromboplastin time (aPTT), prothrombin time (PT), and thrombin time (TT). This study also involved in vitro antimicrobial activity evaluation of materials against representative colonies of Gram-positive and Gram-negative bacteria and antifungal susceptibility tests. The materials were prepared by immersing cotton fibers in an aqueous solution of sodium alginate, followed by ionic cross-linking of alginate chains within the fibers with Cu(II) ions to yield antimicrobial activity. The results showed that the obtained cotton-alginate-copper composites were promising materials to be used in biomedical applications, e.g., wound dressing.

Nonleaching Antimicrobial Cotton Fabrics Finished with Hyperbranched Polylysine

The choice of the antimicrobial agent and finishing process is very important for the activity, durability, and safety of antimicrobial fabrics. Here, a novel antimicrobial cotton fabric (HPL-CF) was constructed by covalently bonding an antimicrobial agent, hyperbranched polylysine (HPL), onto the surface of a cotton fabric (CF) pretreated with a silane coupling agent, 3-chloropropyltrimethoxysilane (CPTMS). The multiple amino groups contained in the periphery of HPL make it possible to react with the CF to form multiple bonds, which is beneficial to improve the durability and safety of HPL-CFs. The obtained HPL-CFs exhibited excellent antimicrobial activities against Escherichia coli (E. coli, Gram-negative bacteria), Staphylococcus aureus (S. aureus, Gram-positive bacteria), and Candida albicans (C. albicans, fungi) even when the CF was treated with HPL solution at the concentration of 0.5 wt %. HPL2.0-CFs maintained 98, >99, and >99% of antimicrobial ratios for E. coli, S. aureus, and C. albicans, respectively, after 50 equiv of domestic laundering cycles, surpassing the requirements of the AAA class. The halo method, cell compatibility, and skin irritation assays all prove the fine safety of HPL-CFs. This work demonstrates the great advantages of applying HPL in the antimicrobial finishing of fabrics.

Physical and Mechanical Characterization of a Functionalized Cotton Fabric with Nanocomposite Based on Silver Nanoparticles and Carboxymethyl Chitosan Using Green Chemistry

Cotton is the most widely used natural fiber for textiles but its innate capacity to absorb moisture, retain oxygen, and high specific surface area make it more prone to microbial contamination, becoming an appropriate medium for the growth of bacteria and fungi. In recent years, the incorporation of silver nanoparticles in textile products has been widely used due to their broad-spectrum antibacterial activity and low toxicity towards mammalian cells. The aim of the current study is to synthesize and characterize a nanocomposite based on silver nanoparticles and carboxymethyl chitosan (AgNPs-CMC), which was utilized to provide a functional finish to cotton fabric. The scanning electron microscope (SEM) to produce a scanning transmission electron microscope (STEM) image showed that the nanocomposite presents AgNPs with a 5–20 nm size. The X-ray diffraction (XRD) analysis confirmed the presence of silver nanoparticles. The concentration of silver in the functionalized fabric was evaluated by inductively coupled plasma optical emission spectrometry (ICP-OES), which reported an average concentration of 13.5 mg of silver per kg of functionalized fabric. SEM showed that silver nanoparticles present a uniform distribution on the surface of the functionalized cotton fabric fibers. On the other hand, by infrared spectroscopy, it was observed that the functionalized fabric variation (compared to control) had a displaced peak of intensity at 1594.32 cm−1, corresponding to carboxylate anions. Similarly, Raman spectroscopy showed an intense peak at 1592.84 cm−1, which corresponds to the primary amino group of carboxymethyl chitosan, and a peak at 1371.5 cm−1 corresponding to the carboxylic anions. Finally, the physical and mechanical tests of tensile strength and color index of the functional fabric reported that it was no different (p ˃ 0.05) than the control fabric. Our results demonstrate that we have obtained an improved functionalized cotton fabric using green chemistry that does not alter intrinsic properties of the fabric and has the potential to be utilized in the manufacturing of hospital garments.