The influence of scaffold material on chondrocytes under inflammatory conditions

Irrigating degradation properties of silk fibroin-collagen type II composite cartilage scaffold in vitro and in vivo

Silk fibroin-collagen type II scaffolds are promising in cartilage tissue engineering due to their suitable biological functionality to promote proliferation of chondrocytes in vitro. However, their degradation properties, which are of crucial importance as scaffold degradation should consistent with the new tissue formation process, are still unknown. In this study, degradability of silk fibroin-collagen type II cartilage scaffolds was probed both in vitro and in vivo. In vitro degradation experiments show that the scaffolds decreased 32.25 % ± 0.62 %, 34.27 % ± 0.96 %, 36.27 % ± 2.39 % in weight after 8 weeks of degradation at the irrigation velocity of 0 mL/min, 7.89 mL/min and 15.79 mL/min. The degradation ratio, which increases with time and increasing irrigation velocity, is described by combining the built mathematic model and finite element modeling method. The scaffolds after 8 weeks of degradation in vitro keep their mechanical structural integrity to support new tissues. In vivo degradation experiments conducted in rabbits further show that the scaffolds degrade gradually, be absorbed with time and finally collapse in structure. The degradation process is accompanied by the growth of fibrous tissues and the scaffold is filled by fibrous tissues after 12 weeks of implantation. Immunohistology analysis shows that the inflammation caused by scaffolds is controllable and gradually alleviates with time. To sum up, silk fibroin-collagen type II cartilage scaffolds, which show suitable mechanical properties and biocompatibility during degradation in vitro and in vivo, have great potential in cartilage repair. The novelty of the study is that it not only introduces a mathematical model to predict the irrigation degradation ratio, but also provides experimental degradation data support for clinical application of silk fibroin-collagen type II cartilage scaffolds.

Fish cartilage: A promising source of biomaterial for biological scaffold fabrication in cartilage tissue engineering

Here, engineered cartilage-like scaffold using an extracellular matrix (ECM) from sturgeon fish cartilage provided a chondroinductive environment to stimulate cartilaginous matrix synthesis in human adipose stem cells (hASCs). Three dimensional porous and degradable fish cartilage ECM-derived scaffold (FCS) was produced using a protocol containing chemical decellularization, enzymatic solubilization, freeze-drying and EDC-crosslinking treatments and the effect of different ECM concentrations (10, 20, 30, and 40 mg/ml) on prepared scaffolds was investigated through physical, mechanical and biological analysis. The histological and scanning electron microscopy analysis revealed the elimination of the cell fragments and a 3-D interconnected porous structure, respectively. Cell viability assay displayed no cytotoxic effects. The prepared porous constructs of fish cartilage ECM were seeded with hASCs for 21 days and compared to collagen (Col) and collagen-10% hyaluronic acid (Col-HA) scaffolds. Cell culture results evidenced that the fabricated scaffolds could provide a proper 3-D structure to support the adhesion, proliferation and chondrogenic differentiation of hASCs considering the synthesis of specific proteins of cartilage, collagen type II (Col II) and aggrecan (ACAN). Based on the results of the present study, it can be concluded that the porous scaffold derived from fish cartilage ECM possesses an excellent potential for cartilage tissue engineering.

Trends in Bone Metastasis Modeling

Bone is one of the most common sites for cancer metastasis. Bone tissue is composed by different kinds of cells that coexist in a coordinated balance. Due to the complexity of bone, it is impossible to capture the intricate interactions between cells under either physiological or pathological conditions. Hence, a variety of in vivo and in vitro approaches have been developed. Various models of tumor-bone diseases are routinely used to provide valuable information on the relationship between metastatic cancer cells and the bone tissue. Ideally, when modeling the metastasis of human cancers to bone, models would replicate the intra-tumor heterogeneity, as well as the genetic and phenotypic changes that occur with human cancers; such models would be scalable and reproducible to allow high-throughput investigation. Despite the continuous progress, there is still a lack of solid, amenable, and affordable models that are able to fully recapitulate the biological processes happening in vivo, permitting a correct interpretation of results. In the last decades, researchers have demonstrated that three-dimensional (3D) methods could be an innovative approach that lies between bi-dimensional (2D) models and animal models. Scientific evidence supports that the tumor microenvironment can be better reproduced in a 3D system than a 2D cell culture, and the 3D systems can be scaled up for drug screening in the same way as the 2D systems thanks to the current technologies developed. However, 3D models cannot completely recapitulate the inter- and intra-tumor heterogeneity found in patients. In contrast, ex vivo cultures of fragments of bone preserve key cell-cell and cell-matrix interactions and allow the study of bone cells in their natural 3D environment. Moreover, ex vivo bone organ cultures could be a better model to resemble the human pathogenic metastasis condition and useful tools to predict in vivo response to therapies. The aim of our review is to provide an overview of the current trends in bone metastasis modeling. By showing the existing in vitro and ex vivo systems, we aspire to contribute to broaden the knowledge on bone metastasis models and make these tools more appealing for further translational studies.

Integrational Technologies for the Development of Three-Dimensional Scaffolds as Platforms in Cartilage Tissue Engineering

The prevalence of osteoarthritis is on the rise, and an effective treatment for cartilage defects is still being sought. Cartilage tissue in vivo encompasses complex structures and composition, both of which influence cells and many properties of the native cartilage. The extracellular matrix structure and components provides both morphological cues and the necessary signals to promote cell functions including metabolism, proliferation, and differentiation. In the present study, cryo-printing and electrospinning were combined to produce multizone scaffolds that consist of three distinctive zones. These scaffolds successfully mimic the collagen fiber orientation of the native cartilage. Moreover, in vitro analysis of chondrocyte-seeded scaffolds demonstrated the ability of multizone scaffolds to support long-term chondrocyte attachment and survival over a 5 week culture period. Moreover, multizone scaffolds were found to regulate the expression of key genes in comparison to the controls and allowed the detection of sulfated glycosaminoglycan. Evaluation of the compressive properties revealed that the multizone scaffolds possess more suitable mechanical properties, for the native cartilage, in comparison to the electrospun and phase-separated controls. Multizone scaffolds provide viable initial platforms that capture the complex structure and compressive properties of the native cartilage. They also maintain chondrocyte phenotype and function, highlighting their potential in cartilage tissue engineering applications.

Noncovalent Sericin-Chitosan Scaffold: Physical Properties and Low Cytotoxicity Effect

This research aims to utilize sericin, which is the waste from boiling silk cocoon, for the supramolecular scaffold preparation with chitosan. A suitable method for the self-assembled scaffold formation of sericin and chitosan at 1:1 stoichiometry is presented and the morphological and physical properties of the scaffold are studied. The effect of an alcohol/NaOH solution on the secondary structure of sericin protein within the sericin-chitosan scaffold, with adjusted pH, was investigated. Additionally, the scaffold was tested in a native phosphate buffer solution (PBS). The results show that sericin increases the porosity of scaffold while chitosan increases the rigidity. The self-assembled sericin and chitosan material is nontoxic to human cells and which can adhere and spread well on such support. For the effect of the molecular weight of chitosan (15,000 and 100,000 g/mol), the scaffold made from lower molecular weight (MW) chitosan provides a somewhat smaller porosity, but a similar swelling ratio and water uptake. On the basis of this research, sericin, which is a silk waste from the textile industry, can be utilized to produce a self-assembled scaffold with chitosan in order to increase the porosity of the scaffold. This type of scaffold is not toxic and can be used for the adhesion of fibroblast cells.

Enhanced chondrogenic differentiation of equine bone marrow-derived mesenchymal stem cells in zirconia microwell substrata

In human cartilage tissue engineering, three-dimensional zirconia substrata have the potential advantage of producing many uniform cell clusters of controlled size without xenobiotic material, allowing easy clinical application. The objective of this study was to evaluate the possibility of using zirconia porous three-dimensional microwell substrata for chondrogenic differentiation of equine bone marrow-derived mesenchymal stem cells (BMMSCs) in vitro. In regular medium, 8 × 10⁵, 2 × 10⁶, and 5 × 10⁶ equine BMMSCs from five thoroughbred horses were cultured on zirconia microwell substrata for 4 days to allow formation of clusters. The medium was replaced by chondrogenic culture medium. After chondrogenic culture for 7, 14 and 21 days, analysis of collagen type II alpha 1 gene (COL2A1) gene expression and observation of chondrogenic aggregates by scanning electron microscopy (SEM) were performed. SEM showed size-controlled cell clusters and increasing extracellular matrix over time when using 5 × 10⁶ cells. The expression of COL2A1 on day 7 and 14 with 5 × 10⁶ cells was significantly higher than that of conventional pellet culture with 2 × 10⁶ cells. Histological evaluation by immunohistochemical staining for type II collagen (ColII) was performed after chondrogenic culture for 7 days. The clusters showed wide distribution of ColII. The results suggest that the zirconia substrata have the potential to enhance the chondrogenic differentiation of equine BMMSCs, allowing effective equine cartilage tissue engineering without xenobiotic materials.

Silk fibroin-poly(lactic acid) biocomposites: Effect of protein-synthetic polymer interactions and miscibility on material properties and biological responses

A protein-polymer blend system based on silkworm silk fibroin (SF) and polylactic acid (PLA) was systematically investigated to understand the interaction and miscibility of proteins and synthetic biocompatible polymers in the macro- and micro-meter scales, which can dramatically control the cell responses and enzyme biodegradation on the biomaterial interface. Silk fibroin, a semicrystalline protein with beta-sheet crystals, provides controllable crystal content and biodegradability; while noncrystallizable PDLLA provides hydrophobicity and thermal stability in the system. Differential scanning calorimetry (DSC) combined with scanning electron microscope (SEM) showed that the morphology of the blend films was uniform on a macroscopic scale, yet with tunable micro-phase patterns at different mixing ratios. Fourier transform infrared analysis (FTIR) revealed that structures of the blend system, such as beta-sheet crystal content, gradually changed with the mixing ratios. All blended samples have better stability than pure SF and PLA samples as evidenced by thermogravimetric analysis. Protease XIV enzymatic study showed that the biodegradability of the blend samples varied with their blending ratios and microscale morphologies. Significantly, the topology of the micro-phase patterns on the blends can promote cell attachment and manipulate the cell growth and proliferation. This study provided a useful platform for understanding the fabrication strategies of protein-synthetic polymer composites that have direct biomedical and green chemistry applications.

Integration of C-type natriuretic peptide gene-modified bone marrow mesenchymal stem cells with chitosan/silk fibroin scaffolds as a promising strategy for articular cartilage regeneration

The treatment of articular cartilage defects has become a major clinical concern. Currently, additional efforts are necessary to develop effective methods to cure this disease. In this work, we combined gene therapy with tissue engineering methods to test their effect on cartilage repair. In in vitro experiments, we obtained C-type natriuretic peptide (CNP) gene-modified bone marrow-derived mesenchymal stem cells (BMSCs) by transfection with recombinant adenovirus containing the CNP gene and revealed that CNP gene-modified BMSCs had good chondrogenic differentiation ability. By the freeze-drying method, we successfully synthesized a chitosan/silk fibroin (CS/SF) porous scaffold, which had a suitable aperture size for chondrogenesis. Then, we loaded CNP gene-modified BMSCs onto CS/SF scaffolds and tested their effect on repairing full-thickness cartilage defects in rat joints. The gross morphology and histology examination results showed that the composite of the CNP gene-modified BMSCs and CS/SF scaffolds had better repair effects than those of the other three groups at each time point. Additionally, compared to the group with BMSCs and scaffolds, we found that there was more cartilage matrix in the CNP gene-modified BMSCs and CS/SF scaffolds group. Data obtained in the present study suggest that the composite of CNP gene-modified BMSCs and CS/SF scaffolds represent promising strategies for repairing focal cartilage lesions.

3D Scaffolds Based on Conductive Polymers for Biomedical Applications

3D scaffolds appear to be a cost-effective ultimate answer for biomedical applications, facilitating rapid results while providing an environment similar to in vivo tissue. These biomaterials offer large surface areas for cell or biomaterial attachment, proliferation, biosensing and drug delivery applications. Among 3D scaffolds, the ones based on conjugated polymers (CPs) and natural nonconductive polymers arranged in a 3D architecture provide tridimensionality to cellular culture along with a high surface area for cell adherence and proliferation as well electrical conductivity for stimulation or sensing. However, the scaffolds must also obey other characteristics: homogeneous porosity, with pore sizes large enough to allow cell penetration and nutrient flow; elasticity and wettability similar to the tissue of implantation; and a suitable composition to enhance cell-matrix interactions. In this Review, we summarize the fabrication methods, characterization techniques and main applications of conductive 3D scaffolds based on conductive polymers. The main barrier in the development of these platforms has been the fabrication and subsequent maintenance of the third dimension due to challenges in the manipulation of conductive polymers. In the last decades, different approaches to overcome these barriers have been developed for the production of conductive 3D scaffolds, demonstrating a huge potential for biomedical purposes. Finally, we present an overview of the emerging strategies developed to manufacture 3D conductive scaffolds, the techniques used to fully characterize them, and the biomedical fields where they have been applied.

Bombyx mori derived scaffolds and their use in cartilage regeneration: a systematic review

For the last two decades, silk has been extensively used as scaffolds in tissue engineering because of its remarkable properties. Unfortunately, the aneural property of cartilage limits its regenerative potential which can be achieved using tissue engineering approach. A lot of research has been published searching for the optimization of silk fibroin (SF) and its blends in order to get the best cartilage mimicking properties. However, according to our best knowledge, there is no systematic review available regarding the use of Bombyx mori derived biomaterials limited to cartilage related studies. This systematic review highlights the in vitro and in vivo work done for the past 7 years on structural and functional properties of B. mori derived biomaterials together with different parameters for cartilage regeneration. PubMed database was searched focusing on in vitro and in vivo studies using the search thread "silk fibroin" and "cartilage". A total of 40 articles met the inclusion criteria. All the articles were deeply studied for cell types, scaffold types and animal models used along with study design and results. Five types of cells were used for in vitro while seven types of cells were used for in vivo studies. Three types of animal models were used for scaffold implantation purpose. Moreover, different types of scaffolds either seeded with cells or supplemented with various factors were explored and discussed in detail. Results suggest the suitability of silk as a better biomaterial because of its cartilage mimicking properties.

Chondrocyte and mesenchymal stem cell derived engineered cartilage exhibits differential sensitivity to pro-inflammatory cytokines

Tissue engineering is a promising approach for the repair of articular cartilage defects, with engineered constructs emerging that match native tissue properties. However, the inflammatory environment of the damaged joint might compromise outcomes, and this may be impacted by the choice of cell source in terms of their ability to operate anabolically in an inflamed environment. Here, we compared the response of engineered cartilage derived from native chondrocytes and mesenchymal stem cells (MSCs) to challenge by TNFα and IL-1β in order to determine if either cell type possessed an inherent advantage. Compositional (extracellular matrix) and functional (mechanical) characteristics, as well as the release of catabolic mediators (matrix metalloproteinases [MMPs], nitric oxide [NO]) were assessed to determine cell- and tissue-level changes following exposure to IL-1β or TNF-α. Results demonstrated that MSC-derived constructs were more sensitive to inflammatory mediators than chondrocyte-derived constructs, exhibiting a greater loss of proteoglycans and functional properties at lower cytokine concentrations. While MSCs and chondrocytes both have the capacity to form functional engineered cartilage in vitro, this study suggests that the presence of an inflammatory environment is more likely to impair the in vivo success of MSC-derived cartilage repair. © 2018 Orthopaedic Research Society. Published by Wiley Periodicals, Inc. J Orthop Res 36:2901-2910, 2018.

Genipin-Enhanced Fibrin Hydrogel and Novel Silk for Intervertebral Disc Repair in a Loaded Bovine Organ Culture Model

(1) Background: Intervertebral disc (IVD) repair represents a major challenge. Using functionalised biomaterials such as silk combined with enforced hydrogels might be a promising approach for disc repair. We aimed to test an IVD repair approach by combining a genipin-enhanced fibrin hydrogel with an engineered silk scaffold under complex load, after inducing an injury in a bovine whole organ IVD culture; (2) Methods: Bovine coccygeal IVDs were isolated from ~1-year-old animals within four hours post-mortem. Then, an injury in the annulus fibrosus was induced by a 2 mm biopsy punch. The repair approach consisted of genipin-enhanced fibrin hydrogel that was used to fill up the cavity. To seal the injury, a Good Manufacturing Practise (GMP)-compliant engineered silk fleece-membrane composite was applied and secured by the cross-linked hydrogel. Then, IVDs were exposed to one of three loading conditions: no load, static load and complex load in a two-degree-of-freedom bioreactor for 14 days. Followed by assessing DNA and matrix content, qPCR and histology, the injured discs were compared to an uninjured control IVD that underwent the same loading profiles. In addition, the genipin-enhanced fibrin hydrogel was further investigated with respect to cytotoxicity on human stem cells, annulus fibrosus, and nucleus pulposus cells; (3) Results: The repair was successful as no herniation could be detected for any of the three loading conditions. Disc height was not recovered by the repair DNA and matrix contents were comparable to a healthy, untreated control disc. Genipin resulted being cytotoxic in the in vitro test but did not show adverse effects when used for the organ culture model; (4) Conclusions: The current study indicated that the combination of the two biomaterials, i.e., genipin-enhanced fibrin hydrogel and an engineered silk scaffold, was a promising approach for IVD repair. Furthermore, genipin-enhanced fibrin hydrogel was not suitable for cell cultures; however, it was highly applicable as a filler material.

Development and biological validation of a cyclic stretch culture system for the ex vivo engineering of tendons

INTRODUCTION

An innovative approach to the treatment of tendon injury or degeneration is given by engineered grafts, made available through the development of bioreactors that generate tendon tissue in vitro, by replicating in vivo conditions. This work aims at the design of a bioreactor capable of applying a stimulation of cyclic strain on cell constructs to promote the production of bioartificial tissue with mechanical and biochemical properties resembling those of the native tissue.

METHODS

The system was actuated by an electromagnet and design specifications were imposed as follows. The stimulation protocol provides to scaffolds a 3% preload, a 10% deformation, and a stimulation frequency rate set at 0.5, 1, and 2 Hz, which alternates stimulation/resting phases. Porcine tenocytes were seeded on collagen scaffolds and cultured in static or dynamic conditions for 7 and 14 days.

RESULTS

The culture medium temperature did not exceed 37°C during prolonged culture experiments. The applied force oscillates between 1.5 and 4.5 N. The cyclic stimulation of the engineered constructs let both the cells and the scaffold fibers align along the strain direction in response to the mechanical stimulus.

CONCLUSION

We designed a pulsatile strain bioreactor for tendon tissue engineering. The in vitro characterization shows a preferential cell alignment at short time points. Prolonged culture time, however, seems to influence negatively on the survival of the cells indicating the need of further optimization concerning the culture conditions and the mechanical stimulation.

Development of bioabsorbable polylactide membrane with controllable hydrophilicity for adjustment of cell behaviours

Cell functions can be mediated through their interactions with the microenvironments, which highly depend on the surface state of the substrate. However, how to finely adjust the surface of biomaterials is still very challenging. In this study, poly(d,l-lactide) (PDLLA) with high molecular weight was synthesized via ring opening polymerization, which was hot-pressed into PDLLA membrane. In order to modify the hydrophobicity of the membrane (a limiting factor for its biomedical application), an amphiphilic monomethoxyl poly(ethylene glycol)-b-poly(d,l-lactide) (PEG-PDLLA) was selected to improve its surface hydrophilicity through a simple self-assembly approach. It was found that the contact angles of the modified membrane can be well controlled by variation of PEG-PDLLA concentrations. In vitro cell biological study indicates that optimized cell adhesion can be achieved on the modified membrane with a contact angle of around 50° via its self-assembly with an ethanol/water solution of PEG-PDLA (35 mg ml-1). The surface modification of the membrane also changed its biodegradation property in the process of its incubation period up to 240 days. The surface modification method may afford an effective way for adjustment of the surface (interface) of membrane (scaffolds) of different biomaterials, beyond polylactide.

Hydrogels for Cartilage Regeneration, from Polysaccharides to Hybrids

The aims of this paper are: (1) to review the current state of the art in the field of cartilage substitution and regeneration; (2) to examine the patented biomaterials being used in preclinical and clinical stages; (3) to explore the potential of polymeric hydrogels for these applications and the reasons that hinder their clinical success. The studies about hydrogels used as potential biomaterials selected for this review are divided into the two major trends in tissue engineering: (1) the use of cell-free biomaterials; and (2) the use of cell seeded biomaterials. Preparation techniques and resulting hydrogel properties are also reviewed. More recent proposals, based on the combination of different polymers and the hybridization process to improve the properties of these materials, are also reviewed. The combination of elements such as scaffolds (cellular solids), matrices (hydrogel-based), growth factors and mechanical stimuli is needed to optimize properties of the required materials in order to facilitate tissue formation, cartilage regeneration and final clinical application. Polymer combinations and hybrids are the most promising materials for this application. Hybrid scaffolds may maximize cell growth and local tissue integration by forming cartilage-like tissue with biomimetic features.

Safety of Intra-Articular Implantation of Oligo[Poly(ethylene glycol) Fumarate] Scaffolds into the Rabbit Knee

Implantable biomaterials supporting extended release of pharmacologic agents may permit localized intra-articular delivery of drugs that modulate the fibrotic response to injuries and surgery. Oligo[poly (ethylene glycol)] fumarate (OPF) is an attractive organic carrier, but its safety profile within synovial joints remains unclear. Here, we assessed the safety of OPF sponges using a validated in vivo model of knee arthrofibrosis. A cohort of 102 rabbits was divided into five groups: arthrotomy only (24), arthrotomy with OPF scaffold placement (24), surgically induced contracture (24), surgically induced contracture with OPF scaffold placement (24), and control without any surgical intervention (6). Six rabbits per surgical group were sacrificed at 72 h, 2, 8, and 24 weeks. Outcomes included biomechanical testing of range of motion, histologic analysis of synovial and cartilage tissues, and scaffold degradation. Cartilage histology and biomechanical measurements were comparable between groups with and without OPF. Synovial inflammation scores were similar among most groups with a minimally elevated score in the rabbits with arthrotomy and OPF versus those with arthrotomy alone. Scores for synovial tissues in rabbits with contracture and OPF were clinically equivalent to those with contractures alone. Most animals (92%) retained scaffold fragments at 24 weeks. Thus, OPF scaffolds implanted into native or arthrofibrotic rabbit knees neither induce nor aggravate cartilage damage, synovial inflammation, or contractures. The apparent safety of OPF scaffolds suggests that they are suitable carriers for the controlled delivery of reagents into the intra-articular joint space to treat arthrofibrosis.

Intra-articular implantation of collagen scaffold carriers is safe in both native and arthrofibrotic rabbit knee joints

Objectives

Sustained intra-articular delivery of pharmacological agents is an attractive modality but requires use of a safe carrier that would not induce cartilage damage or fibrosis. Collagen scaffolds are widely available and could be used intra-articularly, but no investigation has looked at the safety of collagen scaffolds within synovial joints. The aim of this study was to determine the safety of collagen scaffold implantation in a validated in vivo animal model of knee arthrofibrosis.

Materials and Methods

A total of 96 rabbits were randomly and equally assigned to four different groups: arthrotomy alone; arthrotomy and collagen scaffold placement; contracture surgery; and contracture surgery and collagen scaffold placement. Animals were killed in equal numbers at 72 hours, two weeks, eight weeks, and 24 weeks. Joint contracture was measured, and cartilage and synovial samples underwent histological analysis.

Results

Animals that underwent arthrotomy had equivalent joint contractures regardless of scaffold implantation (-13.9° versus -10.9°, equivalence limit 15°). Animals that underwent surgery to induce contracture did not demonstrate equivalent joint contractures with (41.8°) or without (53.9°) collagen scaffold implantation. Chondral damage occurred in similar rates with (11 of 48) and without (nine of 48) scaffold implantation. No significant difference in synovitis was noted between groups. Absorption of the collagen scaffold occurred within eight weeks in all animals

Conclusion

Our data suggest that intra-articular implantation of a collagen sponge does not induce synovitis or cartilage damage. Implantation in a native joint does not seem to induce contracture. Implantation of the collagen sponge in a rabbit knee model of contracture may decrease the severity of the contracture.

Cite this article: J. A. Walker, T. J. Ewald, E. Lewallen, A. Van Wijnen, A. D. Hanssen, B. F. Morrey, M. E. Morrey, M. P. Abdel, J. Sanchez-Sotelo. Intra-articular implantation of collagen scaffold carriers is safe in both native and arthrofibrotic rabbit knee joints. Bone Joint Res 2016;6:162–171. DOI: 10.1302/2046-3758.63.BJR-2016-0193.

Potential of Agarose/Silk Fibroin Blended Hydrogel for in Vitro Cartilage Tissue Engineering

An osteoarthritis pandemic has accelerated exploration of various biomaterials for cartilage reconstruction with a special emphasis on silk fibroin from mulberry (Bombyx mori) and non-mulberry (Antheraea assamensis) silk worms. Retention of positive attributes of the agarose standard and nullification of its negatives are central to the current agarose/silk fibroin hydrogel design. In this study, hydrogels of mulberry and non-mulberry silk fibroin blended with agarose were fabricated and evaluated in vitro for two weeks for cartilaginous tissue formation. The fabricated hydrogels were physicochemically characterized and analyzed for cell viability, proliferation, and extra cellular matrix deposition. The amalgamation of silk fibroin with agarose impacted the pore size, as illustrated by field emission scanning electron microscopy studies, swelling behavior, and in vitro degradation of the hydrogels. Fourier transform infrared spectroscopy results indicated the blend formation and confirmed the presence of both components in the fabricated hydrogels. Rheological studies demonstrated enhanced elasticity of blended hydrogels with G' > G″. Biochemical analysis revealed significantly higher levels of sulfated glycosaminoglycans (sGAGs) and collagen (p ≤ 0.01) in blended hydrogels. More specifically, the non-mulberry silk fibroin blend showed sGAG and collagen content (∼1.5-fold) higher than that of the mulberry blend (p ≤ 0.05). Histological and immunohistochemical analyses further validated the enhanced deposition of sGAG and collagen, indicating maintenance of chondrogenic phenotype within constructs after two weeks of culture. Real-time PCR analysis further confirmed up-regulation of cartilage-specific aggrecan, sox-9 (∼1.5-fold) and collagen type II (∼2-fold) marker genes (p ≤ 0.01) in blended hydrogels. The hydrogels demonstrated immunocompatibility, which was evidenced by minimal in vitro secretion of tumor necrosis factor-α (TNF-α) by murine macrophages. Taken together, the results suggest promising attributes of blended hydrogels and particularly the non-mulberry silk fibroin/agarose blends as alternative biomaterial for cartilage tissue engineering.

Engineering DN hydrogels from regenerated silk fibroin and poly(N-vinylcaprolactam)

The development of novel hydrogels that possess adequate elasticity and toughness to withstand mechanically active environments, along with being biocompatible, remains a significant challenge in the design of materials for tissue engineering applications. In this study, a family of regenerated silk fibroin (RSF) based double network (DN) hydrogels were fabricated for the first time using a rapid one-pot method. The DN hydrogels combine the rigid covalently crosslinked RSF with the softer poly(N-vinylcaprolactam) (PVCL) through strong physical interactions. The formation of these DN hydrogels resulted in an improvement of the water uptake capacity, elasticity and toughness compared to the individual RSF hydrogel. The elasticity of the RSF/PVCL DN hydrogels was closer to that of native cartilage, which makes them promising materials for cartilage regeneration applications. An in vitro study on adhesion, proliferation and differentiation of a mouse pre-chondrocyte cell line (ATDC5) conducted using microscopic analysis, a cell proliferation assay and RT-PCR confirmed the cells cultured on the less stiff hydrogels demonstrated the most favourable chondrogenic response. Thus, this study demonstrates the potential of RSF-based hybrid hydrogels for cartilage tissue engineering applications.

Design and characterization of microcapsules-integrated collagen matrixes as multifunctional three-dimensional scaffolds for soft tissue engineering

Three-dimensional (3D) porous scaffolds based on collagen are promising candidates for soft tissue engineering applications. The addition of stimuli-responsive carriers (nano- and microparticles) in the current approaches to tissue reconstruction and repair brings about novel challenges in the design and conception of carrier-integrated polymer scaffolds. In this study, a facile method was developed to functionalize 3D collagen porous scaffolds with biodegradable multilayer microcapsules. The effects of the capsule charge as well as the influence of the functionalization methods on the binding efficiency to the scaffolds were studied. It was found that the binding of cationic microcapsules was higher than that of anionic ones, and application of vacuum during scaffolds functionalization significantly hindered the attachment of the microcapsules to the collagen matrix. The physical properties of microcapsules-integrated scaffolds were compared to pristine scaffolds. The modified scaffolds showed swelling ratios, weight losses and mechanical properties similar to those of unmodified scaffolds. Finally, in vitro diffusional tests proved that the collagen scaffolds could stably retain the microcapsules over long incubation time in Tris-HCl buffer at 37°C without undergoing morphological changes, thus confirming their suitability for tissue engineering applications. The obtained results indicate that by tuning the charge of the microcapsules and by varying the fabrication conditions, collagen scaffolds patterned with high or low number of microcapsules can be obtained, and that the microcapsules-integrated scaffolds fully retain their original physical properties.

Silk scaffolds for musculoskeletal tissue engineering

The musculoskeletal system, which includes bone, cartilage, tendon/ligament, and skeletal muscle, is becoming the targets for tissue engineering because of the high need for their repair and regeneration. Numerous factors would affect the use of musculoskeletal tissue engineering for tissue regeneration ranging from cells used for scaffold seeding to the manufacture and structures of materials. The essential function of the scaffolds is to convey growth factors as well as cells to the target site to aid the regeneration of the injury. Among the variety of biomaterials used in scaffold engineering, silk fibroin is recognized as an ideal material for its impressive cytocompatibility, slow biodegradability, and excellent mechanical properties. The current review describes the advances made in the fabrication of silk fibroin scaffolds with different forms such as films, particles, electrospun fibers, hydrogels, three-dimensional porous scaffolds, and their applications in the regeneration of musculoskeletal tissues.

Active Nanofibrous Membrane Effects on Gingival Cell Inflammatory Response

Alpha-melanocyte stimulating hormone (α-MSH) is involved in normal skin wound healing and also has anti-inflammatory properties. The association of α-MSH to polyelectrolyte layers with various supports has been shown to improve these anti-inflammatory properties. This study aimed to evaluate the effects of nanofibrous membrane functionalized with α-MSH linked to polyelectrolyte layers on gingival cell inflammatory response. Human oral epithelial cells (EC) and fibroblasts (FB) were cultured on plastic or electrospun Poly-#-caprolactone (PCL) membranes with α-MSH covalently coupled to Poly-L-glutamic acid (PGA-α-MSH), for 6 to 24 h. Cells were incubated with or without Porphyromonas gingivalis lipopolysaccharide (Pg-LPS). Cell proliferation and migration were determined using AlamarBlue test and scratch assay. Expression of interleukin-6 (IL-6), tumor necrosis factor (TNF-α), and transforming growth factor-beta (TGF-β) was evaluated using RT-qPCR method. Cell cultures on plastic showed that PGA-α-MSH reduced EC and FB migration and decreased IL-6 and TGF-β expression in Pg-LPS stimulated EC. PGA-α-MSH functionalized PCL membranes reduced proliferation of Pg-LPS stimulated EC and FB. A significant decrease of IL-6, TNF-α, and TGF-β expression was also observed in Pg-LPS stimulated EC and FB. This study showed that the functionalization of nanofibrous PCL membranes efficiently amplified the anti-inflammatory effect of PGA-α-MSH on gingival cells.

3D-Printed ABS and PLA Scaffolds for Cartilage and Nucleus Pulposus Tissue Regeneration

Painful degeneration of soft tissues accounts for high socioeconomic costs. Tissue engineering aims to provide biomimetics recapitulating native tissues. Biocompatible thermoplastics for 3D printing can generate high-resolution structures resembling tissue extracellular matrix. Large-pore 3D-printed acrylonitrile butadiene styrene (ABS) and polylactic acid (PLA) scaffolds were compared for cell ingrowth, viability, and tissue generation. Primary articular chondrocytes and nucleus pulposus (NP) cells were cultured on ABS and PLA scaffolds for three weeks. Both cell types proliferated well, showed high viability, and produced ample amounts of proteoglycan and collagen type II on both scaffolds. NP generated more matrix than chondrocytes; however, no difference was observed between scaffold types. Mechanical testing revealed sustained scaffold stability. This study demonstrates that chondrocytes and NP cells can proliferate on both ABS and PLA scaffolds printed with a simplistic, inexpensive desktop 3D printer. Moreover, NP cells produced more proteoglycan than chondrocytes, irrespective of thermoplastic type, indicating that cells maintain individual phenotype over the three-week culture period. Future scaffold designs covering larger pore sizes and better mimicking native tissue structure combined with more flexible or resorbable materials may provide implantable constructs with the proper structure, function, and cellularity necessary for potential cartilage and disc tissue repair in vivo.

Clinical applications of naturally derived biopolymer-based scaffolds for regenerative medicine

Naturally derived polymeric biomaterials, such as collagens, silks, elastins, alginates, and fibrins are utilized in tissue engineering due to their biocompatibility, bioactivity, and tunable mechanical and degradation kinetics. The use of these natural biopolymers in biomedical applications is advantageous because they do not release cytotoxic degradation products, are often processed using environmentally-friendly aqueous-based methods, and their degradation rates within biological systems can be manipulated by modifying the starting formulation or processing conditions. For these reasons, many recent in vivo investigations and FDA-approval of new biomaterials for clinical use have utilized natural biopolymers as matrices for cell delivery and as scaffolds for cell-free support of native tissues. This review highlights biopolymer-based scaffolds used in clinical applications for the regeneration and repair of native tissues, with a focus on bone, skeletal muscle, peripheral nerve, cardiac muscle, and cornea substitutes.

Chondrocytes behaviors within type I collagen microspheres and bulk hydrogels: an in vitro study

Cell niche, which is considered to be critical to the proliferation and differentiation of cells, is one of the most important aspects for the design and development of ideal scaffolds in tissue engineering.

Anti-inflammatory strategies in cartilage repair

Cartilage defects are normally concomitant with posttraumatic inflammation and pose a major challenge in cartilage repair. Due to the avascular nature of cartilage and its inability to surmount an inflammatory response, the cartilage is easily attacked by proinflammatory factors and oxidative stress; if left untreated, osteoarthritis may develop. Suppression of inflammation has always been a crux for cartilage repair. Pharmacological drugs have been successfully applied in cartilage repair; however, they cannot optimally work alone. This review article will summarize current pharmacological drugs and their application in cartilage repair. The development of extracellular matrix-based scaffolds and preconditioned tissue-specific stem cells will be emphasized because both of these tissue engineering components could contribute to an enhanced ability not only for cartilage regeneration but also for anti-inflammation. These strategies could be combined to boost cartilage repair under inflammatory conditions.

Scaffold structure and fabrication method affect proinflammatory milieu in three-dimensional-cultured chondrocytes

Cartilage tissue engineering has emerged as an attractive therapeutic option for repairing damaged cartilage tissue in the arthritic joint. High levels of proinflammatory cytokines present at arthritic joints can cause cartilage destruction and instability of the engineered cartilage tissue, and thus it is critical to engineer strong and stable cartilage that is resistant to the inflammatory environment. In this study, we demonstrate that scaffolding materials with different pore sizes and fabrication methods influence the microenvironment of chondrocytes and the response of these cells to proinflammatory cytokines, interleukin-1beta, and tumor necrosis factor alpha. Silk scaffolds prepared using the organic solvent hexafluoroisopropanol as compared to an aqueous-based method, as well as those with larger pore sizes, supported the deposition of higher cartilage matrix levels and lower expression of cartilage matrix degradation-related genes, as well as lower expression of endogenous proinflammatory cytokines IL-1β in articular chondrocytes. These biochemical properties could be related to the physical properties of the scaffolds such as the water uptake and the tendency to leach or adsorb proinflammatory cytokines. Thus, scaffold structure may influence the behavior of chondrocytes by influencing the microenvironment under inflammatory conditions, and should be considered as an important component for bioengineering stable cartilage tissues.

Liquid perfluorochemical-supported hybrid cell culture system for proliferation of chondrocytes on fibrous polylactide scaffolds

CP5 bovine chondrocytes were cultured on biodegradable electrospun fibrous polylactide (PLA) scaffolds placed on a flexible interface formed between two immiscible liquid phases: (1) hydrophobic perfluorochemical (PFC) and (2) aqueous culture medium, as a new way of cartilage implant development. Robust and intensive growth of CP5 cells was achieved in our hybrid liquid-solid-liquid culture system consisting of the fibrous PLA scaffolds in contrast to limited growth of the CP5 cells in traditional culture system with PLA scaffold placed on solid surface. The multicellular aggregates of CP5 cells covered the surface of PLA scaffolds and the chondrocytes migrated through and overgrew internal fibers of the scaffolds. Our hybrid culture system simultaneously allows the adhesion of adherent CP5 cells to fibers of PLA scaffolds as well as, due to use of phase of PFC, enhances the mass transfer in the case of supplying/removing of respiratory gases, i.e., O2 and CO2. Our flexible (independent of vessel shape) system is simple, ready-to-use and may utilize a variety of polymer-based scaffolds traditionally proposed for implant development.