Electrochemical oxidation of gaseous benzene on a Sb-SnO2/foam Ti nano-coating electrode in all-solid cell

Electrocatalytic oxidation of gaseous toluene in an all-solid cell using a foam Ti/Sb-SnO2/β-PbO2 anode

Mineralization of benzene, toluene, and xylene (BTX) with high efficiency at room temperature is still a challenge for the purification of indoor air. In this work, a foam Ti/Sb-SnO2/β-PbO2 anode catalyst was prepared for electrocatalytically oxidizing gaseous toluene in an all-solid cell at ambient temperature. The complex Ti/Sb-SnO2/β-PbO2 anode, which was prepared by sequentially deposing Sb-SnO2 and β-PbO2 on a foam Ti substrate, shows high electrocatalytic oxidation efficiency of toluene (80%) at 7 hr of reaction and high CO2 selectivity (94.9%) under an optimized condition, i.e., a cell voltage of 2.0 V, relative humidity of 60% and a flow rate of 100 mL/min. The better catalytic performance can be ascribed to the high production rate of ⋅OH radicals from discharging adsorbed water and the inhibition of oxygen evolution on the surface of foam Ti/Sb-SnO2/β-PbO2 anode when compared with the foam Ti/Sb-SnO2 anode. Our results demonstrate that prepared complex electrodes can be potentially used for electrocatalytic removal of gaseous toluene at room temperature with a good performance.

Electrochemical removal of gaseous benzene using a flow-through reactor with efficient and ultra-stable titanium suboxide/titanium-foam anode at ambient temperature

Catalytic oxidation technology is currently considered as a feasible approach to degrade and mineralize volatile organic compounds (VOCs). However, it is still challenging to realize efficient removal of VOCs through catalytic oxidation at room temperature. In our study, a novel flow-through electrocatalytic reactor was designed, composed of porous solid-electrolyte, gas-permeable titanium sub-oxides/titanium-foam (TiSO/Ti-foam) as anode and platinum coated titanium foam (Pt/Ti-foam) as cathode. This device could oxidize nearly 100% of benzene (10 ppm) to carbon dioxide at a current density of 1.2 mA/cm² under room temperature. More importantly, the device maintained excellent stability over 1000 h. Mechanism of benzene mineralization was discussed. Hydroxyl radicals generated on the TiSO/Ti-foam anode played a crucial role in the oxidation of benzene. This study provides a promising prototype of the electrochemical air purifier, and may find its application in domestic and industrial air pollution control.

Cytotoxic aquatic pollutants and their removal by nanocomposite-based sorbents

Water is an extremely essential compound for human life and, hence, accessing drinking water is very important all over the world. Nowadays, due to the urbanization and industrialization, several noxious pollutants are discharged into water. Water pollution by various cytotoxic contaminants, e.g. heavy metal ions, drugs, pesticides, dyes, residues a drastic public health issue for human beings; hence, this topic has been receiving much attention for the specific approaches and technologies to remove hazardous contaminants from water and wastewater. In the current review, the cytotoxicity of different sorts of aquatic pollutants for mammalian is presented. In addition, we will overview the recent advances in various nanocomposite-based adsorbents and different approaches of pollutants removal from water/wastewater with several examples to provide a backdrop for future research.

Facile sealing treatment with stannous citrate complex to enhance performance of electrodeposited Ti/SnO2-Sb electrode

Ti/SnO₂-Sb is a promising anode for electrochemical advanced oxidation process with advantages of low cost and no secondary pollution, while suffers from low work economy due to the short service life. In this study, a facile strategy was proposed to fabricate Ti/SnO₂-Sb electrode with high oxidation ability and long service life based on novelly sealing electrodeposited Sn-Sb coating with stannous citrate complex. The treated Ti/SnO₂-Sb electrode exhibited an accelerated service life of 41.5 h (100 mA cm^-2; 0.5 M H₂SO₄) and a degradation rate constant for methylene blue dye of 1.02 h^-1 which were respectively 11.9 and 2.5 times as that of the untreated electrode. It was found out that the complex could well repair the coating defects inside or outside and form a covering film to tighten the coating, and was then mineralized during the following calcination process to achieve a uniform, rough and highly active SnO₂-Sb catalytic layer. The distinctive structure was confirmed by XRD, SEM, XPS and FT-IR. The sealing treatment could be achieved by in situ electrodepositing Sn-Sb coating from or ex situ dipping Sn-Sb coating in solution containing stannous citrate complex followed by drying in air. This study provided a novel, facile and effective strategy to enhance performance of Ti/SnO₂-Sb electrode that could be easily achieved in both laboratory and industrial scales and combined with other strategies.

Degradation of aqueous cefotaxime in electro-oxidation - electro-Fenton -persulfate system with Ti/CNT/SnO2-Sb-Er anode and Ni@NCNT cathode

Due to the potential threatening of antibiotics in aqueous environment, a novel electro-oxidation (EO) - electro-Fenton (EF) -persulfate (PS) system with the addition of peroxydisulfate and Fe²⁺ was installed for the degradation of cefotaxime. Ti/CNT/SnO₂-Sb-Er with an ultra-high oxygen evolution potential (2.15 V) and enhanced electrocatalytic surface area was adopted as anode. The OH production and electrode stability test demonstrated great improvement in the electrochemical performances. Ni@NCNT cathode was tested with higher H₂O₂ generation by the presence of nitrogen functionalities due to the acceleration of electron transfer of O₂ reduction. Experiment results indicated CNT and ErO₂ modification increased the molecular and TOC removal of cefotaxime. Coupling processes of EO-EF and EO-PS both resulted in shorter electrolysis time for complete cefotaxime removal, however, the mineralization ability of EO-PS process was lower than EO-EF, which might result from the immediate vanishing of PS. Thus, a further improved treatment EO-EF-PS system achieved an 81.6% TOC removal towards 50 mg L^-1 cefotaxime after 4 h electrolysis, under the optimal working condition Fe²⁺ = PS = 1 mM. The influence of current density and initial concentration on the performance of all processes was assessed. Methanol and tert-butanol were added in the system as OH and SO₄^- scavengers, which illustrating the mechanism of EO-EF-PS oxidizing process was the result of the two free radicals. Major intermediates were deduced and the degradation pathway of cefotaxime was analyzed. This research provides a potential coupling process with high antibiotic removal efficiency and effective materials for practical uses.