Adhesive class I restorations in sound molar teeth incorporating combined resin-composite and glass ionomer materials: CAD-FE modeling and analysis

Optimizing restorative procedure and material selection for pulpotomized primary molars: Mechanical characterization by 3D finite element analysis

Purpose

This study aimed to assess the stress distribution in pulpotomized primary molars with different types of restorative materials using 3D-finite element analysis (FEA), and provide valuable insights into the selection and application of restorative materials, with the ultimate goal of reducing the risk of pulpotomy failure and protecting residual dental tissue.

Methods

Four 3D models of pulpotomized primary molars with different restorative materials according to the material and its elastic modulus were analysed: resin composite, stainless steel crowns (SSCs), prefabricated zirconia crowns and endocrowns. The food layer was also designed before vertical and bucco-lingual forces were applied to simulate physiological masticatory conditions. The results were obtained by colorimetric graphs of the von Mises stresses (VMS) in the restoration and tooth remnant. The maximum shear stress on the bonding interfaces and pressure stress on the Mineral trioxide aggregate (MTA)-pulp interfaces were recorded.

Results

The results of the 3D-FEA showed that all restorative materials generated stresses and strains on the tooth structure after pulpotomy. In the resin composite group, the marginal enamel exhibited the highest stress peaks. In the zirconia crown and SSC groups, there was a concentration of stress at the dentin-restoration margin. The shear stress concentrations were mainly at the adhesive margins, with lower levels around endocrowns compared to other groups. MTA in the resin composite group experienced more VMS than in the other group. The resin composite group also generated relatively higher pressure stress values at the MTA-pulp interface compared to the other groups.

Significance

In the model of primary teeth following pulpotomy, the three types of restorations covering the occlusal surface can effectively reduce the stress on pulp capping materials under occlusal loads, thereby potentially decreasing the risk of pulpotomy failure. In addition, the group of endocrowns demonstrated reduced stress at the bonding interface and in the stress concentration zone near the dentist-restoration edge, making them more effective at protecting residual dental tissue.

Biomechanical reinforcement by CAD-CAM materials affects stress distributions of posterior composite bridges: 3D finite element analysis

OBJECTIVES

This 3D finite element analysis study aimed to investigate the effect of reinforcing CAD-CAM bars on stress distribution in various components of a posterior composite bridge.

METHODS

A virtual model mimicking the absence of an upper second premolar was created, featuring class II cavity preparations on the proximal surfaces of the adjacent abutment teeth surrounding the edentulous space. Five distinct finite element analysis (FEA) models were generated, each representing a CAD-CAM reinforcing bar material: 3-YTZP (IPS. emax ZirCAD MO; Zr), lithium disilicate (IPS e.max CAD; EX), nano-hybrid resin composite (Grandio Blocs; GB), Fibre-reinforced composite (Trilor; Tri), and polyetheretherketone (PEEK). A veneering resin composite was employed to simulate the replacement of the missing premolar (pontic). In the FEA, an axial force of 600 N and a transverse load of 20 N were applied at the center of the pontic. Subsequently, maximum von Mises (mvM) and maximum principal stresses (σmax) were computed across various components of the generated models. Additionally, shear stresses at the interface between the CAD-CAM bars and the veneering resin composite were determined.

RESULTS

CAD-CAM materials with high modulus of elasticity, such as Zr and EX, exhibited the highest mvM stresses and shear stresses while transferring the lowest stress to the veneering resin composite in comparison to other materials. Conversely, PEEK demonstrated the lowest mvM stresses but produced the highest stresses within the veneering resin composite. There was a uniform distribution of mvM stresses in the remaining tooth structure among all groups, except for a noticeable elevation in the molar region of Zr and EX groups.

SIGNIFICANCE

Reinforcing CAD-CAM bar materials with a high modulus of elasticity, such as Zr and EX, may result in debonding failures at the connector sites of posterior composite bridges. Conversely, GB, PEEK, and Tri have the potential to cause fracture failures at the connectors rather than debonding.

Comparison of the stress distribution in base materials and thicknesses in composite resin restorations

Resin-based composite materials are commonly used for restorations, but their dimensional changes during the polymerization could cause various clinical problems. This study evaluated the influence of a base of different materials and thicknesses on the stress magnitude and distribution in a second maxillary premolar with an MOD resin composite restoration using three-dimensional finite element analysis. A sound tooth without cavity was considered as the control group (ST), and another group was restored with composite resin without applying a base material in a MOD cavity (CR). The other three groups were restored with composite resin along with the following base materials: glass ionomer cement, low-viscosity resin, and tricalcium silicate, respectively (CR-GIC, CR-LR, and CR-TS). These three groups were further divided into two subgroups according to the thickness of the base layer: thin (0.5 mm) and thick (1.0 mm). The stress distribution was compared using the maximum principal stress after polymerization shrinkage and vertical loading with 600 N on the occlusal surface. Group ST showed the lowest stress value, and its stress propagation was confined to outer enamel surfaces only. Group CR demonstrated the highest stress distribution in the tooth-restoration interface with increased failure risk on marginal areas. The thin and thick subgroups of the three groups with a base layer had lower stress levels than Group CR. The base materials reduced the marginal stress caused by polymerization shrinkage of composite resin in MOD cavities. Different base materials and thicknesses did not affect the stress distribution.

Biomechanical behavior and Weibull survival of CAD-CAM endocrowns with different marginal designs: A 3D finite element analysis

OBJECTIVES

To evaluate and compare the effect of tooth preparation designs and different CADCAM. materials on stress distribution and Weibull survival probability of endocrowns. applied to root canal-treated lower first permanent molar using the 3D finite element. analysis method.

METHODS

A root canal-treated lower first permanent molar was prepared for endocrowns with a. butt joint or with a ferrule design by placing, circumferentially, a 1-mm wide shoulder. finish line. The prepared molar was scanned for the two designs and modeled on a 3D. Finite element model. Monolithic zirconia (IPS e.max ZirCAD MT, FCZ), lithium. disilicate (IPS e.max CAD, EX), and nano-ceramic resin composite (Lava Ultimate, LU). CAD-CAM materials were used for each preparation to design the virtual endocrown. A. total of six models were built according to the different tooth preparation designs and. endocrown materials. An occlusal load of 600 N and a transverse load of 20 N in. magnitude that simulates the average occlusal load was directed toward the occlusal. surfaces. von Mises and maximum principle values were evaluated Weibull risk-ofrupture. analysis was used to analyze the survival probability of the restorations and. tooth in the different models.

RESULTS

The highest von Mises were found in the butt joint design for FCZ, EX, and LU (45.3. MPa, 35.2 MPa, and 24.2 MPa, respectively) compared to the ferrule design for the. same materials (42.6 MPa, 31.2 MPa, and 23.6 MPa, respectively). For von Mises. stress distribution in the remaining part of tooth structure (dentin), the highest stresses. were found in LUFerrule which was closely similar to LUButt joint (135.4 MPa and. 134.7 MPa, respectively), followed by EXFerrule and FCZFerrule (132.2 MPa and. 131.7 MPa, respectively), while the lowest stresses were found in EXButt joint and. FCZButt joint (129.0 MPa and 128.4 MPa, respectively). Shear stresses within the. resin cement were the highest in FCZ and EX compared to LU. EX was found to be the. most reliable material with the highest survival probability, while FCZ showed the. lowest survival probability according to the Weibull risk-of-fracture results.

SIGNIFICANCE

Materials with high elastic modulus transfer more stresses to the endocrown and less. to the remaining tooth structure. Endocrown tooth preparation with ferrule design has. better stress distribution and magnitude compared to the butt joint design.

Multi-response optimisation analysis of material properties in dental restorative composites under the influence of thermal and thermomechanical stimuli - A 3D finite element study

OBJECTIVES

Restored teeth undergo more damage than intact teeth. Therefore, the scientific investigation of their mechanical and physical behaviour under varying oral conditions is vital. The current study is to numerically investigate the stresses on a class-II mesio-occluso-distal (MOD) restored molar due to thermal and thermomechanical stimuli with varying input properties such as coefficient of thermal expansion and elastic properties. This is performed to optimise the dental restoration material, thereby reducing the stresses and failure of the restoration.

METHODS

An upper molar was scanned using μ-CT for segmenting and modelling the enamel and dentine. A class-II MOD cavity was then prepared on the model, after which non-manifold meshing was generated. The coefficient of thermal expansion (CTE) and elastic modulus (E) properties of the restoration were varied from 20 × 10-6 °C-1 to 55 × 10-6 °C-1 and 5 GPa-20 GPa, respectively. After the material properties and boundary conditions were set for the finite element (FE) analysis, the thermal and thermomechanical loading analyses were performed to demonstrate the influence of input parameters on the stress. The maximum values of principal stresses on the restoration-enamel junction and the restoration were evaluated. The results were statistically processed using analysis of variance, response surface methodology (RSM) and optimisation analysis to estimate the most optimum inputs for minimising principal stresses.

RESULTS

The study reveals that the location of principal stress occurs at the restoration-enamel junction (REJ) and the restoration changes based on the composite material value of E and CTE due to thermal and thermomechanical stimuli. The REJ showed higher principal stress than restoration during the application of both thermal and thermomechanical stimuli, making it more vulnerable to fracture and failure. Moreover, the study showed non-linear variations in the values and locations of principal stresses due to thermal and thermomechanical stimuli with the change in the property of the restoration composite used. Finally, this study derived an optimised restorative value for CTE and E due to the application of thermal and simultaneous thermal and mechanical stimuli.

CONCLUSION

This study highlights the importance of choosing the suitable material properties of the restoration composite by dental clinicians to repair a large class MOD cavity. The findings from this study also suggest that the difference in the values of E and CTE in a dental restoration composite when compared with the enamel causes a lack of uniformity in mechanical and thermal properties, thereby forming stress concentrations at the interfaces. The study establishes two optimised CTE and E values for the MOD restoration composite as 25 × 10-6 °C-1 and 20 GPa and 37 × 10-6 °C-1 and 5 GPa, respectively.

Effect of different endodontic access preparations on the biomechanical behavior of lithium disilicate and resin nanoceramic onlay restorations: An in vitro and 3D finite element analysis study

STATEMENT OF PROBLEM

The effect of different sizes of endodontic access preparations on the performance of lithium disilicate glass-ceramic and resin nanoceramic onlay restorations is unclear.

PURPOSE

The purpose of this in vitro and 3D finite element analysis study was to assess the effect of a conservative endodontic access cavity and a traditional endodontic access cavity on the fracture resistance and stress distribution of lithium disilicate glass-ceramic and resin nanoceramic onlays.

MATERIAL AND METHODS

Sixty caries-free human mandibular molars were anatomically prepared for onlays and divided into 6 groups. After restoration with a lithium disilicate glass-ceramic (N=30) or resin nanoceramic (N=30), each material was further divided into traditional or conservative endodontic access cavity or intact tooth groups. After endodontic therapy and thermocycling, all specimens were submitted to a cycle fatigue test and then loaded until fracture. Failure type and location after debonding or fracture were classified and recorded. Furthermore, stress distribution in the 6 models was analyzed by using a finite element analysis software program. The data were compared by using a 2-way ANOVA test and the Tukey post hoc test (α=.05). The Weibull modulus and Weibull failure probabilities were also estimated for each group.

RESULTS

The lithium disilicate glass-ceramic onlays had lower fracture resistance values than the resin nanoceramic onlays in both the traditional and conservative endodontic access cavity groups (P<.05). The fracture resistance of the 2 materials for onlays with endodontic access was significantly lower than that for the intact restorations (P<.05). No significant difference was found between the fracture resistance of Lava Ultimate restorations with traditional endodontic access and conservative endodontic access, while the fracture resistance of EMAX restorations with traditional endodontic access was significantly lower than that of restorations with conservative endodontic access (P<.05). A higher percentage of irreparable fractures was found in the 3 resin nanoceramic restoration groups. The von Mises stresses were higher in the lithium disilicate glass-ceramic restorations than in the resin nanoceramic restorations with the same access cavities. The von Mises stresses in the tooth structure were higher with the resin nanoceramic restorations than with the lithium disilicate glass-ceramic restorations with the same access cavities.

CONCLUSIONS

An endodontic access cavity had more influence on the lithium disilicate glass-ceramic onlays than on the resin nanoceramic onlays, and a traditional endodontic access cavity significantly decreased the fracture resistance of lithium disilicate glass-ceramic onlays.

Enhancing the mechanical stability of restored teeth with interfacial cracks: Finite element analysis

OBJECTIVES

This study aims to enhance the mechanical stability of restored molar teeth with class II occlusal-distal (OD) cavities. We seek to achieve this goal through a comprehensive investigation of three primary factors: (1) the choice of restoration material properties, (2) internal cavity geometries, and (3) the impact of double-layered restoration configurations.

METHODS

To achieve our objectives, we initiated by creating two-dimensional (2D) models of restored teeth featuring class II OD cavities, utilizing scanned and segmented images of maxillary molar teeth. We drew 2D profiles of dentine and enamel, which were then imported into finite element analysis (FEA) software. To explore various cavity geometries, we implemented a total of thirteen different designs, encompassing straight, oblique, grooved, curved, and double-layered configurations. We utilized a semi-circular stone to simulate the application of contact load on the restored tooth. We applied identical boundary conditions and contact loading across all models. To assign material properties, we developed a Python code, enabling the automatic assignment of seven elastic moduli ranging from 2 GPa to 26 GPa to the restoration materials. Meanwhile, constant material properties were assigned to the enamel and dentine. In total, we conducted 133 FEA simulations to comprehensively analyse the effects of the aforementioned factors on the strength and performance of restored molar teeth.

RESULTS

Our analysis revealed two key factors significantly influencing the mechanical resistance of treated teeth, particularly in the presence of a crack or debonding: (1) the marginal geometry of the OD cavity and (2) the elastic modulus of the restorative material. However, altering the internal cavity angle and implementing a double-layered restoration did not significantly influence the restored tooth's overall strength and performance in the face of crack or debonding situations.

SIGNIFICANCE

The findings of this study have substantial implications for designing and restoring class II OD cavities to enhance resistance to cracks or debonding. The use of curved marginal geometries in restoration design can significantly improve fracture resistance, with double-curved geometries reducing stress concentrations by approximately 43% compared to straight cavities. These results offer valuable guidance for strengthening the structural integrity of restored teeth, calling for further experimental investigations to explore practical applications and benefits.

Effects of different treatment modalities on biomechanical behavior of maxillary incisors with external invasive cervical resorption at different progression levels

BACKGROUND/AIM

This study aimed to evaluate the biomechanical behavior of maxillary incisors with external invasive cervical resorption (EICR) at different progression levels after receiving different modes of treatment under occlusal forces using finite element analysis (FEA).

MATERIALS AND METHODS

Three-dimensional (3D) models of intact maxillary central incisors were constructed and modified to include EICR cavities with different progression levels in the buccal cervical areas. The EICR cavities confined to dentin were repaired using Biodentine™ (Septodont Ltd., Saint Maur des Fausse ́s, France), resin composite, or glass ionomer cement (GIC) . Additionally, EICR cavities with pulp invasion requiring direct pulp capping were simulated as repaired using Biodentine only or 1 mm thick Biodentine and either resin composite or GIC for the rest of the cavity. Moreover, models with root canal treatment and EICR defects repaired using Biodentine, resin composites, or GIC were also generated. A force of 240 N was applied to the incisal edge. The principal stresses in the dentin were evaluated.

RESULTS

GIC showed more favorable results than the other materials in EICR cavities confined to the dentin. However, Biodentine alone resulted in more favorable minimum principal stresses (Pmin ) compared to other materials in EICR cavities with close pulp proximity. Exceptionally, the models localized in the coronal third of the root with a circumferential extension of the cavity >90° showed more favorable results for GIC. The presence of root canal treatment had no significant effect on stress values.

CONCLUSIONS

Based on this FEA study the use of GIC in EICR lesions confined to the dentin is recommended. However, Biodentine may be a better option for restoring EICR lesions close to the pulp with or without root canal treatment. Except when the circumferential extension of the cavity is >90°, the use of GIC may be more advantageous.

Fracture Resistance of Class II MOD Cavities Restored by Direct and Indirect Techniques and Different Materials Combination

This study aimed to evaluate the fracture resistance of class II MOD cavities restored using different techniques and materials. Sixty extracted maxillary molars were selected and standardized class II MOD cavities were prepared using a custom-made paralleling device. The specimens were divided into four groups based on the restoration technique used: Group 1 (direct resin composite), Group 2 (short-fiber-reinforced composite resin), Group 3 (composite polyethylene fiber reinforcement), and Group 4 (CAD/CAM resin inlays). Fracture resistance was assessed for each group after thermocycling aging for 10,000 cycles. The mode of fracture was assigned to five types using Burke's classification. To compare the fracture force among the tested materials, a paired sample t-test was performed. The significance level for each test was set at p < 0.05. Significant differences in fracture resistance were observed among the different restoration techniques. CAD/CAM inlays (2166 ± 615 N), short-fiber-reinforced composite resin (2471 ± 761 N), and composite polyethylene fiber reinforcement (1923 ± 492 N) showed superior fracture resistance compared to the group restored with direct resin composite (1242 ± 436 N). The conventional resin composite group exhibited the lowest mean fracture resistance. The choice of restoration material plays a critical role in the clinical survival of large MOD cavities. CAD/CAM inlays and fiber-reinforced composites offer improved fracture resistance, which is essential for long-term success in extensive restorations.

Study on the Restoration of Class II Carious Cavities by Virtual Methods: Simulation of Mechanical Behavior

The restoration of class II cavities is predominantly carried out with composite materials. Due to the high failure rate in restoring this type of cavity, composite materials with much-improved properties and new application techniques have been promoted. The study aimed to analyze the mechanical behavior of several topical composite materials (nanocomposites, nanohybrids and ormocer) using different application techniques. In a lower second molar, a class II occlusal cavity was prepared. As filling materials, we used the following combinations: Admira Fusion and Admira Fusion Flow, Grandio and Grandio Flow, Filtek Supreme XT and Filtek Supreme Flow. These were applied using a snow plow, injection molded and Bichacho techniques. Three-dimensional scanning of the molar with the prepared cavity was performed, and then scanning of each layer of added composite material was performed, obtaining three-dimensional models. The virtual molar models were analyzed with software specific to the finite element analysis method, where their physical-mechanical properties were entered and assigned to the components of the virtual molar. Simulations at high forces specific to bruxism were then carried out and analyzed, and compared. The values of displacements and strain, for all six analyzed situations, are relatively small (range from 5.25 × 10^-6-3.21 × 10^-5 for displacement, 6.22 × 10^-3-4.34 × 10^-3 for strain), which validates all three methods and the materials used. As far as the stress values are concerned, they are similar for all methods (250-300 MPa), except for the snow plow and injection-molded techniques using Grandio and Grandio Flow composites, where the maximum von Mises stress value was more than double (approximately 700 MPa). When using the combination of Grandio and Grandio Flow materials, the 1 mm thickness of the fluid composite layer was found to have a major influence on occlusal forces damping as opposed to 0.5 mm. Therefore, the Bichacho technique is indicated at the expense of the snow plow and injection-molded techniques. The composite materials used by us in this study are state-of-the-art, with clear indications for restoring cavities resulting from the treatment of carious lesions. However, their association and application technique in the case of Class II cavities is of clinical importance for resistance to masticatory forces.

Simulating the shrinkage-induced interfacial damage around Class I composite resin restorations with damage mechanics

OBJECTIVES

To investigate the shrinkage-induced damage at the composite-tooth interface by finite element analysis (FEA) using the cohesive zone model (CZM).

METHODS

Axisymmetric models of Class I restorations were created to illustrate the interfacial damage around composite resin restorations of different dimensions, with polymerization shrinkage modeled analogously to thermal shrinkage. The damage to the adhesive interface was determined using a CZM based on the fracture strength and fracture energy. To show the effects of damage, conventional models with perfectly bonded composite resin restorations were created as controls.

RESULTS

The results indicated interfacial damage at the butt-joint cavosurface margin, dentinoenamel junction, and internal line angle. The percentage of damaged interfacial area was found to increase with decreasing diameter for restorations of the same height. For a given diameter, the damage was more severe for restorations of greater depth. The effects of the damage were further illustrated in the model with a restoration of 2-mm diameter and height. The interfacial damage occurred primarily at the internal line angle (83.3 % of all the damaged interfacial area), leading to local stress relief (from 18.3 MPa to 12.8 MPa), but also higher stress at the damage fronts. Greater local shrinkage was found in composites adjacent to the damage.

SIGNIFICANCE

The damage mechanics-based CZM is an essential refinement of the FEA to predict interfacial damage and its implications. The extent of damage was found to be greater around restorations with smaller diameters and greater depths. The entire simulation is available via an open-source platform to facilitate further applications in adhesive dentistry.

Stress distribution in resin-based CAD-CAM implant-supported crowns

OBJECTIVE

This study aimed to evaluate the influence of new resin-based CAD-CAM implant-supported materials on posterior crown restoration stress and strain concentrations.

METHODS

A previous 3D implant model was edited to receive a cement-retained posterior crown manufactured with different CAD/CAM materials (Estelite P Block, Estelite Block II or Estelite Layered Block). Each solid model was exported to the computer-aided engineering software and submitted to the finite element analysis of stress and strain. Material properties were assigned to each solid with isotropic and homogeneous behavior according to the manufacturer information. A vertical load of 600 N was applied in the occlusal region of the crown, via a simulated food bolus, and stress was calculated in Von Misses (σVM) for the implant, abutment and screw, Maximum (σMAX) Principal Stresses for the crown and microstrain for the bone.

RESULTS

All simulated materials showed acceptable stresses levels with a similar stress pattern among the models. At the crown intaglio region and cement layer, however, differences were observed: Estelite P Block showed a lower tensile and shear stresses magnitude when compared to other resin-based materials with lower elastic modulus.

SIGNIFICANCE

The stress effect of different resin-based CAD-CAM implant-supported crowns is predominant in the crown and cement layer, with Estelite P Block showing 7.4 % versus 9.3 % and 9.2 % for Estelite Block II and Estelite Layered Block of crown failure risk.

Effect of crown stiffness and prosthetic screw absence on the stress distribution in implant-supported restoration: A 3D finite element analysis

This in-silico investigation evaluated the mechanical impact of Morse tape implant-abutment interface and retention system (with and without screw) and restorative materials (composite block and monolithic zirconia) by means of a three-dimensional finite element analysis (3D-FEA). Four 3D models were designed for the lower first molar. A dental implant (4.5 × 10 mm B&B Dental Implant Company) was digitized (micro CT) and exported to computer-aided design (CAD) software. Non-uniform rational B-spline surfaces were reconstructed, generating a 3D volumetric model. Four different models were generated with the same Morse-type connection, but with a different locking system (with and without active screw) and a different crown material made of composite block and zirconia. The D2 bone type, which contains cortical and trabecular tissues, was designed using data from the database. The implants were juxtaposed inside the model after Boolean subtraction. Implant placement depth was simulated for the implant model precisely at crestal bone level. Each acquired model was then imported into the finite element analysis (FEA) software as STEP files. The Von Mises equivalent strains were calculated for the peri-implant bone and the Von Mises stress for the prosthetic structures. The highest strain values in bone tissue occurred in the peri-implant bone interface and were comparable in the four implant models (8.2918e-004-8.6622e-004 mm/mm). The stress peak in the zirconia crown (64.4 MPa) was higher than in the composite crown (52.2 MPa) regardless of the presence of the prosthetic screw. The abutment showed the lowest stress peaks (99.71-92.28 MPa) when the screw was present (126.63-114.25 MPa). Based on this linear analysis, it is suggested that the absence of prosthetic screw increases the stress inside the abutment and implant, without effect on the crown and around the bone tissue. Stiffer crowns concentrate more stress on its structure, reducing the amount of stress on the abutment.

Fracture resistance of Ceramic-Polymer hybrid materials using microscopic finite element analysis and experimental validation

The objective of this paper is to elucidate the response to contact stresses of Polymer Infiltrated Ceramic Network (PICN) using the microscopic viscoplastic finite elements, validated by clinically relevant in vitro tests. A feldspathic ceramic material, namely Vita Mark II, is an interconnected structure infiltrated with the polymer (PMMA). Axisymmetric finite element microstructure models are reconstructed from two-dimensional images of a PICN microstructure. Viscoplastic finite element analysis (FEA) with various degrees of microscopic damages occurring over contact is performed. The force-displacement responses obtained from FEA are validated with Hertzian contact tests. Finite element results for force-displacement, stresses and strains in each phase are discussed. We hypothesize that the resistance to fracture of PICN can be further improved by microstructural tailoring. The experimental evidence suggests that a composite material is both more resistant to displacement under load and more resistant to crack initiation and propagation, as hypothesized. Further parametric study on the effects of various volume fractions of two phases in PICN is done to provide some insight on increased contact damage resistance of PICN as well as potential optimization of microstructures.

Evaluation of the Mechanical Properties of Three Resin-Modified Glass-Ionomer Materials

This study is aimed at evaluating the flexural strength (FS), fracture toughness (FT), and diametral tensile strength (DTS) of three resin-modified glass-ionomer cements (RMGICs): Ketac Nano, Riva Light Cure, and Fuji II LC. One hundred twenty specimens were prepared from the RMGIC materials ( $n=10$ ). The cements were mixed and inserted into different mould sizes according to the test performed: FS: rectangular Teflon mould ( $32\text{mm}\times 3.15\text{mm}\times 2\text{mm}$ ); FT: notchless triangular prism (NTP) Teflon mould ( $6\text{mm}\times 6\text{mm}\times 6\text{mm}\times 12\text{mm}$ ); and DTS: ring road stainless steel mould ( $6\text{mm}\times 3\text{mm}$ ). Specimens were light cured for 20 seconds on each surface and stored in distilled water at ${37}^{°}\text{C}\pm 2^{°}\text{C}$ for seven days prior to tests. To evaluate the influence of storage in the mechanical properties of the RMGIs, specimens tested for DTS were stored in distilled water at ${37}^{°}\text{C}\pm 2^{°}\text{C}$ for 32 days prior to test. Data were analyzed by ANOVA and Tukey’s test ( $\alpha =0.05$ ). Fuji II LC presented significantly higher values for all tests employed when compared to Ketac Nano and Riva LC RMGIs. There was no significant difference on DTS before and after the 32-day storage for each material. Fuji II LC presented superior mechanical properties when compared to Ketac Nano, and Riva LC storage showed no influence on the mechanical properties of the RMGI materials tested.

Numerical and Experimental Investigations of Humeral Greater Tuberosity Fractures with Plate Fixation under Different Shoulder Rehabilitation Activities

The incidence of humerus greater tuberosity (GT) fractures is about 20% in patients with proximal humerus fractures. This study aimed to investigate the biomechanical performances of the humerus GT fracture stabilized by a locking plate with rotator cuff function for shoulder rehabilitation activities. A three-dimensional finite element model of the GT-fracture-treated humerus with a single traction force condition was analyzed for abduction, flexion, and horizontal flexion activities and validated by the biomechanical tests. The results showed that the stiffness calculated by the numerical models was closely related to that obtained by the mechanical tests with a correlation coefficient of 0.88. Under realistic rotator cuff muscle loading, the shoulder joint had a larger displacement at the fracture site (1.163 mm), as well as higher bone stress (60.6 MPa), higher plate stress (29.1 MPa), and higher mean screw stress (37.3 MPa) in horizontal flexion rehabilitation activity when compared to that abduction and flexion activities. The horizontal flexion may not be suggested in the early stage of shoulder joint rehabilitation activities. Numerical simulation techniques and experimental designs mimicked clinical treatment plans. These methodologies could be used to evaluate new implant designs and fixation strategies for the shoulder joint.

The synergetic effect of pulp chamber extension depth and occlusal thickness on stress distribution of molar endocrowns: a 3-dimensional finite element analysis

The aim of this study was to evaluate the effects of butt margin, occlusal thickness and pulp chamber extension depth on stress distributions on mandibular molar endodontically treated teeth (ETT) with EMAX endocrown restoration using 3-dimensional finite element analysis (FEA). The FEA models of endocrown with flat surface or curve surface of butt margin were firstly evaluated stress distributions, and then 9 FEA models of endocrown with 1-, 2- or 3-mm pulp chamber extension depth and 1-, 2- or 3-mm occlusal thickness were generated using curve surface of butt margin. In all of FEA models, a 200 N of vertical load or horizontal load was applied, and the von Mises stress (VMS) were evaluated. The results showed that curve surface of butt margin offered more adhesive area of enamel, though VMS on the prepared teeth was similar in flat surface and curve surface models. In 9 endocrown models, 2-mm occlusal thickness showed the lowest VMS on restorations, teeth tissue and root furcations, and 2-mm extension depth displayed the lowest VMS on root furcations under vertical load. Also, 2-mm extension depth exhibited the lowest VMS on restorations and teeth tissue under horizontal load. Within the limitations of this FEA study, the results of this study could be used as an aid for dentists to better devise endocrown restorations. Graphical abstract.

Final Colour of Ultratranslucent Multilayered Zirconia Veneers, Effect of Thickness, and Resin Cement Shade

Background

Aesthetic restorations should be able to mimic the natural colour depth of teeth, affected by several factors including material properties. There is a lack of information regarding the effect of cement shade and material thickness on the final colour of ultratranslucent multilayered zirconia veneers.

Objectives

This study evaluated the effect of ceramic thickness and resin cement shade on the final colour of different layers of ultratranslucent multilayered (UTML) zirconia veneers.

Methods

This in vitro study produced 90 rectangular-shaped specimens with nonsintered Katana UTML monolithic zirconia (Kuraray Noritake Dental, Tokyo, Japan), shade A1 blocks. Ceramic samples were prepared in two groups of 0.7 mm and 0.5 mm thicknesses, 45 of each (a: 8 × 11 × 0.5 mm; b: 8 × 11 × 0.7 mm). Specimens of each thickness were further divided into 5 groups: universal, clear, brown, white, and opaque (n = 9). Each adhesive resin cement (Panavia V5) was applied between the ceramic samples and composite substrate. The colour values were measured using a spectrophotometer in baseline and after resin cement application according to the CIELab system. For all samples, ΔE00 values were obtained. Data were evaluated with SPSS 25 using the three-way ANOVA test (p < 0.05).

Results

The factors of cement shade, ceramic thickness, and ceramic layers have statistically significant effect on ΔE00 values (p < 0.001). The results showed lower ΔE00 values with thicker ceramic veneers. Tukey test results showed that the opaque and brown shade had a significantly greater ΔE00 values comparing to universal (p = 0.004), clear, and white shades (p < 0.001).

Conclusion

The colour change was greater in lower ceramic thickness. Different shades of resin cement and layers of UTML zirconia differently affected the final colour.

Effect of erosive media on microhardness and fracture toughness of CAD-CAM dental materials

Background

Erosive acids might create surface flaws and deteriorate the mechanical properties of CAD-CAM materials. This invitro study aimed to investigate the effect of simulated gastric HCl and extrinsic erosive acids on surface microhardness and fracture toughness of CAD-CAM materials.

Methods

400 bar-shaped specimens (17×4×2 mm³) were prepared from 4 different CAD-CAM dental materials (n = 100/group); monolithic zirconia (Ceramill Zolid HT+, Amanngirbach, Austria), lithium disilicate ceramic (IPS e.max CAD, Ivoclar Vivadent, Liechtenstein), nanohybrid resin composite (Grandio Blocs, VOCO) and polymer-infiltrated glass network (Vita Enamic, VITA Zahnfabrik). Specimens from each material type were further subdivided into 5 groups (n = 20) according to the erosive media applied (simulated gastric HCl, white wine, Coca-Cola®, orange juice, and artificial saliva that served as a control). Specimens were immersed for 24 h in an incubator at 37 ℃, then ultrasonically cleaned in distilled water and air-dried. Half of the specimens were tested for Vickers microhardness (VHN) at parameters of 500 gf for 10 s, while the rest of the specimens underwent 3-point flexure till fracture. Fractured surfaces were examined under a scanning electron microscope (SEM) for fracture toughness (K_IC) calculation using the quantitative fractographic analysis method. Data collected were statistically analyzed using two-way analysis of variance (α = 0.05) after verification of data normality and homogeneity of variances.

Results

Erosive media created surface flaws that lowered the surface microhardness of the material and initiated the fracture pattern under different loads according to material type. The material type was a more predominant factor than erosive media that affected either the microhardness or the fracture toughness of CAD-CAM dental materials. The highest VHN and K_IC values were found among Ceramill Zolid HT+ groups followed by IPS e.max CAD and Grandio Blocs regardless of the erosive media employed. Erosive media significantly reduced the VHN and K_IC in Vita Enamic specimens compared to the rest of the material types.

Conclusion

All CAD-CAM materials used, except Vita Enamic, showed high resistance against the erosive acids indicating higher longevity of the material in patients frequently exposed to either extrinsic or intrinsic acid.

A Dual Discriminator Adversarial Learning Approach for Dental Occlusal Surface Reconstruction

Objective. Restoring the correct masticatory function of partially edentulous patient is a challenging task primarily due to the complex tooth morphology between individuals. Although some deep learning-based approaches have been proposed for dental restorations, most of them do not consider the influence of dental biological characteristics for the occlusal surface reconstruction. Description. In this article, we propose a novel dual discriminator adversarial learning network to address these challenges. In particular, this network architecture integrates two models: a dilated convolutional-based generative model and a dual global-local discriminative model. While the generative model adopts dilated convolution layers to generate a feature representation that preserves clear tissue structure, the dual discriminative model makes use of two discriminators to jointly distinguish whether the input is real or fake. While the global discriminator focuses on the missing teeth and adjacent teeth to assess whether it is coherent as a whole, the local discriminator aims only at the defective teeth to ensure the local consistency of the generated dental crown. Results. Experiments on 1000 real-world patient dental samples demonstrate the effectiveness of our method. For quantitative comparison, the image quality metrics are used to measure the similarity of the generated occlusal surface, and the root mean square between the generated result and the target crown calculated by our method is 0.114 mm. In qualitative analysis, the proposed approach can generate more reasonable dental biological morphology. Conclusion. The results demonstrate that our method significantly outperforms the state-of-the-art methods in occlusal surface reconstruction. Importantly, the designed occlusal surface has enough anatomical morphology of natural teeth and superior clinical application value.

Mechanical Behavior of Alkasite Posterior Restorations in Comparison to Polymeric Materials: A 3D-FEA Study

The present investigation evaluated the effect of the combination of different dental filling materials in Class I cavities under occlusal loading using three-dimensional finite elements analysis (FEA). Six computer-generated and restored models of a lower molar were created in the CAD software and compared according to the biomechanical response during chewing load condition. Two adhesively bonded bulk restorative materials [bulk-fill resin composite (BF) or Alkasite (Alk)] were evaluated with or without the presence of a base material below (flowable resin composite or glass ionomer cement). A food bolus was placed on the occlusal surface mimicking the compressive occlusal load (600 N) during the static linear analysis. The maximum principal stress (tensile) was calculated as stress criteria in enamel, dentin and restoration. All models showed high stresses along the enamel/restoration margin with a similar stress trend for models restored with the same upper-layer material. Stress values up to 12.04 MPa (Alk) or up to 11.12 MPa (BF) were recorded at the enamel margins. The use of flexible polymeric or ionic base material in combination with bulk-fill resin composite or Alk did not reduce the stress magnitude in dentine and enamel. Class I cavities adhesively restored with bulk-fill resin composite showed lighter stress concentration as well as Alk. Therefore, adhesively bonded Alk restoration showed a promising mechanical behavior when used with different base materials or as a bulk restoration for posterior Class I cavity.

A Preliminary In Vitro Study of 3D Full-Field Strain Distribution in Human Whole Premolars Using Digital Image Correlation

Full-field measurements can provide a more complete description of the behavior of human whole tooth under load. To that end, in vitro experiments were carried out to measure the full-field buccal surface strains of human premolars free of caries and abrasion using digital image correlation (DIC). Experimental results show that both the value field and the orientation field of strains can be observed exactly, both of which contain a wealth of information. Furthermore, the strain distributions between the crown and the root of specimens were significantly different (p < 0.001). An interesting observation was a watershed at the cementoenamel junction (CEJ) which separates the orientation field of strains into two distinct parts; the watershed was also observed in the value field of strains in some specimens whose geometries changed obviously at the CEJ. Another interesting observation was that the minor strains increased linearly from cervical to apical regions in the root cementum. Experimental results also support the viewpoint that mechanisms of non-carious cervical lesions (NCCLs) may in part be due to the changing orientation of tensile strains, as well as their magnitude, and they also support the hypothesis that occlusal force can contribute to root fractures.

Influence of margin design and restorative material on the stress distribution of endocrowns: a 3D finite element analysis

Background

This study aimed to evaluate the stress distributions in endocrown restorations as applied to endodontically treated teeth (ETT), according to the factors of “margin design” (four levels) and “restorative material” (six levels).

Methods

Four 3D-finite elements models were constructed for endocrown restored molars considering different margin designs. Model A was prepared with a flat butt joint margin and received an endocrown with a 2.0-mm occlusal thickness. Model B was prepared with a 20° bevel margin and received an endocrown with a 2.0-mm occlusal thickness. Model C was prepared with an axial reduction and 1-mm shoulder margin and received an endocrown with a 2.0-mm occlusal thickness. Model D was prepared with an anatomic margin and received an endocrown with a 2.0-mm occlusal thickness. The following endocrown materials were used: In-Ceram Zirconia (Zr), Vita Suprinity (VS), IPS Empress (IE), Grandio blocs (GR), VisCalor bulk (VS), and CopraPeek Light (CP). The Load application (600 N) was performed at the food bolus and tooth surface during the closing phase of the chewing cycle. The results for the endocrown and tooth remnants were determined according to the von Mises stress. The failure risk of the cement layer was also calculated based on the normal stress criterion.

Results

Model D (with an anatomic margin) showed the greatest stress concentrations, especially in the irregular and sharp angles of the restoration and tooth remnants. The stress concentrated on the dentin was significantly lower in Model B with a 20° bevel margin (20.86 MPa), i.e., 1.3 times lower than the other three margin designs (27.80 MPa). Restorative materials with higher elastic moduli present higher stress concentrations inside the endocrown and transmit less stress to the cement layer, resulting in lower bonding failure risks. In contrast, materials with an elastic modulus similar to that of dentin presented with a more homogeneous stress distribution on the whole structure.

Conclusions

An endocrown with a 20° bevel margin design could be a favorable preparation option for ETT. Composite resins (GR and VC) exhibit a more even stress distribution, and seem to be more promising materials for endocrown molars.

Finite element analysis and nanomechanical properties of composite and ceramic dental onlays

The aim is to evaluate the mechanical properties of the composite and ceramic based indirect restorative materials used in dental treatments with scanning nanoindentation test (NT). Finite element analysis (FEA) was applied to investigate the stress distribution. Four hybrid composite materials; Indirect resin composite (IRC), Resin nanoceramic (RNC), Polymer infiltrated ceramic (PIC) and Zirconia-reinforced lithium-di-silicate (ZRC) were divided into two subgroups for NT (n = 20) and fracture test (n = 40). Statistical analyses were performed with independent t-test, ANOVA and post-hoc Tukey tests (p ≤ 0.05). The highest hardness, elasticity and fracture toughness were observed in ZRC (p = 0.001). Frequency of vertical root fractures in RNC and IRC were statistically lower than ZRC (p = 0.032). Reinforced CAD-CAM ceramics revealed higher mechanical properties compared with IRC materials. The FEA model for fracture mechanism of RNC demonstrated lowest stress values and uniform stress distribution amongst all groups, while ZRC and PIC presented the highest fracture toughness.

Influence of Framework Material and Posterior Implant Angulation in Full-Arch All-on-4 Implant-Supported Prosthesis Stress Concentration

This study evaluated the influence of distal implants angulation and framework material in the stress concentration of an All-on-4 full-arch prosthesis. A full-arch implant-supported prosthesis 3D model was created with different distal implant angulations and cantilever arms (30° with 10-mm cantilever; 45° with 10-mm cantilever and 45° with 6-mm cantilever) and framework materials (Cobalt–chrome [CoCr alloy], Yttria-stabilized tetragonal zirconia polycrystal [Y-TZP] and polyetheretherketone [PEEK]). Each solid was imported to computer-aided engineering software, and tetrahedral elements formed the mesh. Material properties were assigned to each solid with isotropic and homogeneous behavior. The contacts were considered bonded. A vertical load of 200 N was applied in the distal region of the cantilever arm, and stress was evaluated in Von Misses (σVM) for prosthesis components and the Maximum (σMAX) and Minimum (σMIN) Principal Stresses for the bone. Distal implants angled in 45° with a 10-mm cantilever arm showed the highest stress concentration for all structures with higher stress magnitudes when the PEEK framework was considered. However, distal implants angled in 45° with a 6-mm cantilever arm showed promising mechanical responses with the lowest stress peaks. For the All-on-4 concept, a 45° distal implants angulation is only beneficial if it is possible to reduce the cantilever’s length; otherwise, the use of 30° should be considered. Comparing with PEEK, the YTZP and CoCr concentrated stress in the framework structure, reducing the stress in the prosthetic screw.

Influence of fiber insertion and different material type on stress distribution in endocrown restorations: a 3D-FEA study

The study aimed to evaluate the effects of fibers insertion and restorative material type on the stress distribution in endocrowns with finite element analysis. Five 3D models of first mandibular molars were created and restored as follows: (1) IN: intact tooth, (2) IPS-E: tooth restored with lithium disilicat ceramic endocrowns, (3) C-E: tooth restored with composite endocrowns, (4) IPS-E + F: lithium disilicate ceramic endocrowns + fiber, (5) C-E + F: composite endocrowns + fiber. Vertical masticatory load was imitated with finite element analysis. The equivalent stress of von Mises failure criterion (mvM) was calculated. The maximum mvM stress, enamel/crown, dentin and cement were compared among models and strength of the materials. Endocrowns presented a lower mvM stress level than intact tooth. In IPS-E, the mvM stress values in the crown and dentin were higher than C-E, while the mvM stress values in cement were higher in C-E group. Fibers insertion did not affect the stress level of IPS-E and C-E groups. In IPS model, fiber showed more stress absorption than C-E. The restorative material type changed the stress distribution of endocrown restorations. The fiber application did not affect the stress distribution in either endocrown group. But, more stress absorption was observed in fiber under IPS-E than C-E.

Functional or Nonfunctional Cusps Preservation for Molars Restored with Indirect Composite or Glass-Ceramic Onlays: 3D FEA Study

Evidence regarding the effect of the onlay preparation design for different CAD/CAM restorative materials considering the preservation of cusps is lacking. Molars were 3D-modeled in four preparation designs for onlay restoration: traditional design with functional cusp coverage (TFC), non-retentive design with functional cusp coverage (NFC), traditional design with non-functional cusp coverage (TNFC) and non-retentive design with non-functional cusp coverage (NNFC). The restorations were simulated with two CAD/CAM restorative materials: LD—lithium disilicate (IPS e.max CAD) and RC—resin composite (GrandioBloc). A 100 N axial load was applied to the occlusal surface, simulating the centric contact point. Von Mises (VM) and maximum principal (Pmax) stress were evaluated for restorations, cement layer and dental substrate. The non-retentive preparation design reduced the stress concentration in the tooth structure in comparison to the conventional retentive design. For LD onlays, the stress distribution on the restoration intaglio surface showed that the preparation design, as well as the prepared cusp, influenced the stress magnitude. The non-retentive preparation design provided better load distribution in both restorative materials and more advantageous for molar structure. The resin composite restoration on thenon-functional cusp is recommended when the functional cusp is preserved in order to associate conservative dentistry and low-stress magnitude.

The effect of dental restoration geometry and material properties on biomechanical behaviour of a treated molar tooth: A 3D finite element analysis

OBJECTIVES

To test the hypothesis that restoration of class II mesio-occlusal-distal (MOD) cavities can be strengthened through judicious choice of restoration geometry and material properties.

METHODS

An intact extracted human maxillary molar tooth was digitized, segmented, reconstructed, and four 3D restored tooth models were developed with four different restoration geometries: one straight, one single-curved, and two double-curved. Stress analysis was conducted for representative loading using finite element analysis, and maximum principal stresses were determined at the dentine-enamel and restoration-enamel junctions. A range of restorative material elastic moduli (5-80 GPa) and Poisson's ratios (0.25-0.35) were studied. Vertical loads of 400 N were applied on occlusal points, while the roots of the molar teeth, below the crevices, were supported in all directions. All the materials were modelled as homogeneous, isotropic, and elastic.

RESULTS

The maximum principal stresses at the restoration-enamel junctions were strongly dependent on the MOD restoration geometries. Peak stresses occurred along the palatal surface of the restoration rather than the opposite buccal surface. Double-curved restorations showed the lowest peak stress at restoration-enamel junctions. Choice of the mechanical properties of restorative material in the range of 5-35 GPa further reduced stress concentrations on the enamel.

SIGNIFICANCE

Class II MOD restorations may be stronger if designed with double-curved marginal geometries that can reduce stress concentrations. Designs with convex and concave geometries were particularly effective because they reduced stress concentrations dramatically. Results suggest that relatively minor changes to the geometry of a restoration can have a substantial effect on stress at the restoration-enamel junction and motivate future experimental analysis.

Effect of Biologically Oriented Preparation Technique on the Stress Concentration of Endodontically Treated Upper Central Incisor Restored with Zirconia Crown: 3D-FEA

The aim of this study was to evaluate the effect of biologically oriented preparation technique on the stress concentration of endodontically treated upper central incisors restored with zirconia crown (yttria-stabilized zirconia polycrystalline ceramic) through finite element analysis (FEA). Four models of maxillary central incisors containing enamel, dentin, periodontal ligament, cortical and medullary bone were created in CAD. Each model received a polymeric core-build up with nanofilled dental resin composite. The evaluated models were SM-preparation in shoulder 90°; CM-chamfer preparation; BOPT-biologically oriented preparation technique and BOPTB-BOPT preparation 1 mm below the cement-enamel junction. All models received zirconia crowns (5Y-TZP), fiberglass post and 1 mm ferrule. The models were imported into the analysis software with parameters for mechanical structural testing using the maximum principal stress and the tensile strength as the analysis criteria. Then, load of 150 N was applied at the cingulum with 45° slope to the long axis of the tooth, with the fixed base for each model. The type of marginal preparation affected the stresses concentration in endodontically treated teeth and in the zirconia crown margin. Considering the stress magnitude only, BOPT is a viable option for anterior monolithic zirconia crowns; however, with the highest stress magnitude at the restoration margin.

Influence of restorative material and cement on the stress distribution of endocrowns: 3D finite element analysis

Purpose

This study aimed to evaluate the influence of different types of restorative materials and resin cements on the stress distribution in the regions of the restoration, cement layer and dental remnant in endodontically treated posterior endocrowns.

Methods

A 3D finite element analysis (FEA) model of the first mandibular molar that was restored with an endocrown designed by computer-aided design (CAD) software was generated. Three kinds of restorative materials (Vita Enamic (VE), IPS e.max CAD (EMX) and Grandio blocs (GR)) and two types of cementing materials (NX3 and Maxcem Elite Chroma (MX)) were analysed with such a model. The food layer was also designed before vertical (600 N) forces were applied to simulate physiological masticatory conditions. Thermal expansion was used to simulate the polymerization shrinkage effects of cement layers. The results were obtained by colorimetric graphs of the maximum principal stress in the restoration and tooth remnant. The failure risk of the cement layer was also calculated based on the normal stress.

Results

The elastic modulus was positively correlated with the tensile stress peak values in the restoration, mainly at the intaglio surface. However, in the cervical enamel and cement layer, restorative material with a higher elastic modulus generated lower peak stress values. The cement with a higher elastic modulus resulted in higher stress peak values inside the cement layer. The combination of EMX (restorative material) and NX3 (cement material) in the cement layer resulted in the lowest failure risk.

Significance

The ceramic material EMX with a higher elastic modulus appeared to be more effective at protecting the cement layer and residual enamel tissue. Based on the analysis of the failure risk of the cement layer, the combination of EMX and NX3 was recommended as an optional material for endocrowns for endodontically treated posterior teeth.

The role of cortical zone level and prosthetic platform angle in dental implant mechanical response: A 3D finite element analysis

OBJECTIVE

The aim of this study was to evaluate the influence of three different dental implant neck geometries, under a combined compressive/shear load using finite element analysis (FEA). The implant neck was positioned in D2 quality bone at the crestal level or 2 mm below.

METHODS

One dental implant (4.2 × 9 mm) was digitized by reverse engineering techniques using micro CT and imported into Computer Aided Design (CAD) software. Non-uniform rational B-spline surfaces were reconstructed, generating a 3D volumetric model similar to the digitized implant. Three different models were generated with different implant neck configurations, namely 0°, 10° and 20°. D2 quality bone, composed of cortical and trabecular structure, was modeled using data from CT scans. The implants were included in the bone model using a Boolean operation. Two different fixture insertion depths were simulated for each implant: 2 mm below the crestal bone and exactly at the level of the crestal bone. The obtained models were imported to FEA software in STEP format. Von Mises equivalent strains were analyzed for the peri-implant D2 bone type, considering the magnitude and volume of the affected surrounding cortical and trabecular bone. The highest strain values in both cortical and trabecular tissue at the peri-implant bone interface were extracted and compared.

RESULTS

All implant models were able to distribute the load at the bone-implant contact (BIC) with a similar strain pattern between the models. At the cervical region, however, differences were observed: the models with 10° and 20° implant neck configurations (Model B and C), showed a lower strain magnitude when compared to the straight neck (Model A). These values were significantly lower when the implants were situated at crestal bone levels. In the apical area, no differences in strain values were observed.

SIGNIFICANCE

The implant neck configuration influenced the strain distribution and magnitude in the cortical bone and cancellous bone tissues. To reduce the strain values and improve the load dissipation in the bone tissue, implants with 10° and 20 neck configuration should be preferred instead of straight implant platforms.

Effect of Direct and Indirect Materials on Stress Distribution in Class II MOD Restorations: A 3D-Finite Element Analysis Study

The aim of this study is to investigate the stress distributions of different restoration options for class II mesio-occluso-distal (MOD) cavities. A class II MOD cavity with proximal box gingival floor 1 mm below cementoenamel junction was designed in a mandibular first molar tooth model. 3D finite-element analysis (FEA) and 3D-CAD modelling were used to examine the occlusal stresses distributed to the remaining buccal enamel (RBE), remaining lingual enamel (RLE), adhesive surfaces, and restorative materials by direct and indirect materials resulting from a 600 N of static occlusal load stimulating foodstuff. von Mises (VM) and maximum principal (Pmax) stresses were evaluated for two CAD/CAM materials and three direct materials. CAD/CAM materials exerted less stress than the direct restorative materials. Significant von Mises and Pmax stress value differences were seen among all restoration models on RBE. Reducing RLE and including it into the cavity would be a more effective option for this model in this scenario. As VM and Pmax stresses of PIHC CAD/CAM material for RBE and dentin were significantly lower than other tested materials, it may be the choice of material for indirect MOD restorations.

Finite Element Modelling and Experimental Validation of the Enamel Demineralisation Process at the Rod Level

In the past years, a significant amount of effort has been directed at the observation and characterisation of caries using experimental techniques. Nevertheless, relatively little progress has been made in numerical modelling of the underlying demineralisation process.

The present study is the first attempt to provide a simplified calculation framework for the numerical simulation of the demineralisation process at the length scale of enamel rods and its validation by comparing the data with statistical analysis of experimental results.

FEM model was employed to simulate a time-dependent reaction-diffusion equation process in which H ions diffuse and cause demineralisation of the enamel. The local orientation of the hydroxyapatite crystals was taken into account. Experimental analysis of the demineralising front was performed using advanced high-resolution synchrotron X-ray micro-Computed Tomography. Further experimental investigations were conducted by means of SEM and STEM imaging techniques.

Besides establishing and validating the new modelling framework, insights into the role of the etchant solution pH level were obtained. Additionally, some light was shed on the origin of different types of etching patterns by simulating the demineralisation process at different etching angles of attack.

The implications of this study pave the way for simulations of enamel demineralisation within different complex scenarios and across the range of length scales. Indeed, the framework proposed can incorporate the presence of chemical species other than H ions and their diffusion and reaction leading to dissolution and re-precipitation of hydroxyapatite. It is the authors’ hope and aspiration that ultimately this work will help identify new ways of controlling and preventing caries.

3D Finite Element Analysis of Rotary Instruments in Root Canal Dentine with Different Elastic Moduli

The aim of the present investigation was to calculate the stress distribution generated in the root dentine canal during mechanical rotation of five different NiTi endodontic instruments by means of a finite element analysis (FEA). Two conventional alloy NiTi instruments F360 25/04 and F6 Skytaper 25/06, in comparison to three heat treated alloys NiTI Hyflex CM 25/04, Protaper Next 25/06 and One Curve 25/06 were considered and analyzed. The instruments’ flexibility (reaction force) and geometrical features (cross section, conicity) were previously investigated. For each instrument, dentine root canals with two different elastic moduli(18 and 42 GPa) were simulated with defined apical ratios. Ten different CAD instrument models were created and their mechanical behaviors were analyzed by a 3D-FEA. Static structural analyses were performed with a non-failure condition, since a linear elastic behavior was assumed for all components. All the instruments generated a stress area concentration in correspondence to the root canal curvature at approx. 7 mm from the apex. The maximum values were found when instruments were analyzed in the highest elastic modulus dentine canal. Strain and von Mises stress patterns showed a higher concentration in the first part of curved radius of all the instruments. Conventional Ni-Ti endodontic instruments demonstrated higher stress magnitudes, regardless of the conicity of 4% and 6%, and they showed the highest von Mises stress values in sound, as well as in mineralized dentine canals. Heat-treated endodontic instruments with higher flexibility values showed a reduced stress concentration map. Hyflex CM 25/04 displayed the lowest von Mises stress values of, respectively, 35.73 and 44.30 GPa for sound and mineralized dentine. The mechanical behavior of all rotary endodontic instruments was influenced by the different elastic moduli and by the dentine canal rigidity.

Effect of Shrinking and No Shrinking Dentine and Enamel Replacing Materials in Posterior Restoration: A 3D-FEA Study

The aim of the present study was to investigate the effect of shrinking and no shrinking dental filling materials combination in posterior restorations under the combined effects of polymerization shrinkage and occlusal load by means of 3D Finite Elements Analysis. Six computer-generated and restored class I or class II cavities models of a lower molar were designed in the CAD software and evaluated according to the cavity and restorative procedure. Different shrinking and no shrinking adhesive materials combination with diverse Young’s modulus were considered. A food bolus was modeled on the occlusal surface replicating the chewing load using static linear analyses Polymerization shrinkage was simulated for the shrinking different restorative materials. The maximum principal stress was selected as analysis criteria. All models exhibited higher stresses along the dentine restoration interfaces with different magnitude and a similar stress trend along enamel restoration interface. Stress values up to 22 MPa and 19 MPa were recorded in the enamel and restoration, respectively. The use of elastic not shrinking material layer in combination with bulk fill composite reduced the stress magnitude in dentine and enamel to replace dental tissues. Class I and class II posterior cavities adhesively restored with shrinking filling material’s combination showed the most unfavorable stress concentrations and the multilayer technique is a promising restorative alternative in posterior adhesive restorations when deep dentin and enamel volumes are missing.

Evaluation of the Flexural Strength, Water Sorption, and Solubility of a Glass Ionomer Dental Cement Modified Using Phytomedicine

Objectives: Various medicinal plant parts and extracts have been proven to be sources of biologically active compounds, many of which have been incorporated in the production of new pharmaceutical compounds. Thus, the aim of this study was to increase the antimicrobial properties of a glass ionomer cement (GIC) through its modification with a mixture of plant extracts, which were evaluated along with a 0.5% chlorohexidine-modified GIC (CHX-GIC) with regard to the water sorption, solubility, and flexural strength. Methods: Salvadora persica, Olea europaea, and Ficus carcia leaves were prepared for extraction with ethyll alcohol using a Soxhlet extractor for 12 h. The plant extract mixture (PE) was added in three different concentrations to the water used for preparation of a conventional freeze-dried GIC (groups 1:1, 2:1, and 1:2). Specimens were then mixed according to the manufacturer’s instructions and tested against the unmodified GIC (control) and a GIC modified with 0.5% chlorhexidine. Water sorption and solubility were evaluated after 7 days of immersion in distilled water. Flexural strength was evaluated in a three-point bending test after 24 h using a universal material testing machine at a crosshead speed of 1 mm/min. One-way analysis of variance (ANOVA) was used for comparison between the groups. Tukey’s post hoc test was used for pairwise comparison when the ANOVA test was significant. Results: There were no statistically significant differences between the control (M = 20.5%), CHX-GIC (M = 19.6%), 1:1 (M = 20.0%), 1:2 (M = 19.5%), and 2:1 (19.7%) groups with regard to the percentage of water sorption, while for water solubility the 2:1 (M = −0.39%) plant-modified group was significantly different from all of the other groups. Flexural strength test results showed that the 2:1 group (M = 26.1 MPa) recorded significantly higher mean values compared to all other tested groups. Conclusion and clinical relevance: The plant extracts did not negatively affect the water sorption and solubility of the GIC, while the flexural strength was improved by the addition of the plant extract at higher concentrations.

Effects of fiber reinforcement on adaptation and bond strength of a bulk-fill composite in deep preparations

OBJECTIVE

This study investigated the effect of plasma-treated leno weaved ultra-high-molecular-weight polyethylene fiber placement on gap formation and microtensile bond strength (MTBS) of a bulk-fill composite in deep cavity.

METHODS

Resin composite molds (3 mm width, 4 mm depth) were treated with Clearfil SE Bond 2 and restored with 3 techniques : (1) Surefil SDR flow (SDR) placed in bulk (BLK), (2) SDR placed in two unequal increments (INC) and (3) SDR placed after an increment of SDR placed with wetted polyethylene fiber (Ribbond Ultra) at the cavity floor (FRC). As a control, the cavities were bulk-filled with SDR and no bonding agent (n = 12). All the specimens were subjected to real-time and 3D imaging by SS-OCT (1330 nm) to calculate the total volume of gap formed (mm³) at the cavity floor and between the composite increments. For MTBS, the occlusal cavities of the similar dimensions (3 × 3 × 4 mm³) were prepared on extracted molars with similar composite placement techniques (BLK, INC and FRC). After 24 h 37 °C water storage, the specimens were sectioned using a diamond saw to create 0.7 × 0.7 mm² beams for MTBS, and subjected to bond testing at a crosshead speed of 1 mm/min. Data for both tests was analyzed by one-way ANOVA and multiple-comparisons with Bonferroni correction (α = 0.05).

RESULTS

The gap volumes were different among the groups (p < 0.05). The largest cavity floor gaps (mm³) were observed in the control group (2.00 ± 0.08); followed by BLK (0.74 ± 0.20) and INC (0.02 ± 0.01). In FRC, the cavity floor was gap-free in all specimens but some separation was observed between the two increments. MTBS values (MPa) were 13.8 ± 7.6, 31.7 ± 12.5 and 28.3 ± 8.5 for BLK, INC and FRC groups. There was no significant difference between FRC and INC and both were different from BLK (p < 0.05).

SIGNIFICANCE

Gap formation of the bulk-fill composite at cavity floor was significantly reduced with the placement of a fiber-reinforced increment at the base of the deep preparation. The fiber-reinforced increment acts as a shrinkage stress breaker and protects the bonded interface at deep dentin.