Facile self-assembly N-doped graphene quantum dots/graphene for oxygen reduction reaction

Transient N-GQDs/PVA nanocomposite thin film for memristor application

In recent years quantum dot (QDs) based resistive switching devices(memristors) have gained a lot of attention. Here we report the resistive switching behavior of nitrogen-doped graphene quantum dots/Polyvinyl alcohol (N-GQDs/PVA) degradable nanocomposite thin film with different weight percentages (wt.%) of N-GQDs. The memristor device was fabricated by a simple spin coating technique. It was found that 1 wt% N-GQDs/PVA device shows a prominent resistive switching phenomenon with good cyclic stability, high on/off ratio of ~102and retention time of ∼104s. From a detailed experimental study of band structure, we conclude that memristive behavior originates from the space charge controlled conduction (SCLC) mechanism. Further transient property of built memristive device was studied. Within three minutes of being submerged in distilled water, the fabricated memory device was destroyed. This phenomenon facilitates the usage of fabricated memristor devices to develop memory devices for military and security purposes.

Metal-organic framework derived transition metal sulfides grown on carbon nanofibers as self-supported catalysts for hydrogen evolution reaction

Metal-organic framework (MOF) derived transition metal-based electrocatalysts have received great attention as substitutes for noble metal-based hydrogen evolution catalysts. However, the low conductivity and easy detachments from electrodes of raw MOF have seriously hindered their applications in hydrogen evolution reaction. Herein, we report the facile preparation of Co-NSC@CBC84, a porous carbon-based and self-supported catalyst containing Co9S8 active species, by pyrolysis and sulfidation of in-situ grown ZIF-67 on polydopamine-modified biomass bacterial cellulose (PDA/BC). As a binder-free and self-supported electrocatalyst, Co-NSC@CBC84 exhibits superior electrocatalytic properties to other reported cobalt-based sulfide catalytic materials and has good stability in 0.5 M H2SO4 electrolyte. At the current density of 10 mA cm-2, only an overpotential of 138 mV was required, corresponding to a Tafel slope of 123 mV dec-1, owing to the strong synergy effect between Co-NSC nanoparticles and CBC substrate. This work therefore provides a feasible approach to prepare self-supported transition metal sulfides as HER catalysts, which is helpful for the development of noble metal-free catalysts and biomass carbon materials.

From Pristine to Heteroatom-Doped Graphene Quantum Dots: An Essential Review and Prospects for Future Research

Graphene quantum dots (GQDs) are carbon-based zero-dimensional materials that have received considerable scientific interest due to their exceptional optical, electrical, and optoelectrical properties. Their unique electronic band structures, influenced by quantum confinement and edge effects, differentiate the physical and optical characteristics of GQDs from other carbon nanostructures. Additionally, GQDs can be synthesized using various top-down and bottom-up approaches, distinguishing them from other carbon nanomaterials. This review discusses recent advancements in GQD research, focusing on their synthesis and functionalization for potential applications. Particularly, various methods for synthesizing functionalized GQDs using different doping routes are comprehensively reviewed. Based on previous reports, current challenges and future directions for GQDs research are discussed in detail herein.

Interfacial engineering of a vertically stacked graphene/h-BN heterostructure as an efficient electrocatalyst for hydrogen peroxide synthesis

Recently, it was reported that an in-plane graphene (G)/hexagonal boron nitride (h-BN) (G/h-BN) heterostructure provided the catalytic activity for H2O2 synthesis by the 2 e- oxygen reduction reaction (ORR). However, there are few reports on the vertically stacked G/h-BN heterostructure, which refers to the stacking of graphene domains on the surface of h-BN. Herein, a simulated chemical vapor deposition method is proposed for fabricating a heterostructure of abundant vertically stacked G/h-BN by in situ growing graphene quantum dots (GQDs) on porous h-BN sheets. The performance of our vertically stacked heterostructure catalyst is superior to that of reported carbon-based electrocatalysts under an alkaline environment, with an H2O2 selectivity of 90-99% in a wide potential range (0.35 V-0.7 V vs. RHE), over 90% faradaic efficiency, and high mass activity of 1167 mmol gcatalyst-1 h-1. The experimental results and density functional theory (DFT) simulation verified that the vertically stacked heterostructure exhibits an excellent catalytic performance for the 2 e- ORR, and the edge B atoms in the B-centered AB stacking model are the most active catalytic sites. This research adequately demonstrates the promising catalytic activity of the vertically stacked G/h-BN heterostructure and provides a facile route for fabricating other vertically stacked heterostructures.

Chitosan-Based Electrochemical Sensors for Pharmaceuticals and Clinical Applications

Chitosan (CTS), a biocompatible and multifunctional material derived from chitin, has caught researchers' attention in electrochemical detection due to its unique properties. This review paper provides a comprehensive overview of the recent progress and applications of CTS-based electrochemical sensors in the analysis of pharmaceutical products and other types of samples, with a particular focus on the detection of medicinal substances. The review covers studies and developments from 2003 to 2023, highlighting the remarkable properties of CTS, such as biocompatibility, chemical versatility, and large surface area, that make it an excellent candidate for sensor modification. Combining CTS with various nanomaterials significantly enhances the detection capabilities of electrochemical sensors. Various types of CTS-based sensors are analyzed, including those utilizing carbon nanomaterials, metallic nanoparticles, conducting polymers, and molecularly imprinted CTS. These sensors exhibit excellent sensitivity, selectivity, and stability, enabling the precise and reliable detection of medications. The manufacturing strategies used for the preparation of CTS-based sensors are described, the underlying detection mechanisms are elucidated, and the integration of CTS sensors with transducer systems is highlighted. The prospects of CTS-based electrochemical sensors are promising, with opportunities for miniaturization, simultaneous detection, and real-time monitoring applications.

Emerging Trends of Carbon-Based Quantum Dots: Nanoarchitectonics and Applications

Carbon-based quantum dots (QDs) have emerged as a fascinating class of advanced materials with a unique combination of optoelectronic, biocompatible, and catalytic characteristics, apt for a plethora of applications ranging from electronic to photoelectrochemical devices. Recent research works have established carbon-based QDs for those frontline applications through improvements in materials design, processing, and device stability. This review broadly presents the recent progress in the synthesis of carbon-based QDs, including carbon QDs, graphene QDs, graphitic carbon nitride QDs and their heterostructures, as well as their salient applications. The synthesis methods of carbon-based QDs are first introduced, followed by an extensive discussion of the dependence of the device performance on the intrinsic properties and nanostructures of carbon-based QDs, aiming to present the general strategies for device designing with optimal performance. Furthermore, diverse applications of carbon-based QDs are presented, with an emphasis on the relationship between band alignment, charge transfer, and performance improvement. Among the applications discussed in this review, much focus is given to photo and electrocatalytic, energy storage and conversion, and bioapplications, which pose a grand challenge for rational materials and device designs. Finally, a summary is presented, and existing challenges and future directions are elaborated.

NBOH Site-Activated Graphene Quantum Dots for Boosting Electrochemical Hydrogen Peroxide Production

Carbon materials are considered promising 2/4 e^- oxygen reduction reaction (ORR) electrocatalysts for synthesizing H₂ O₂ /H₂ O via regulating heteroatom dopants and functionalization. Here, various doped and functionalized graphene quantum dots (GQDs) are designed to reveal the crucial active sites of carbon materials for ORR to produce H₂ O₂ . Density functional theory (DFT) calculations predict that the edge structure involving edge N, B dopant pairs and further OH functionalization to the B (NBOH) is an active center for 2e^- ORR. To verify the above predication, GQDs with an enriched density of NBOH (NBO-GQDs) are designed and synthesized by the hydrothermal reaction of NH₂ edge-functionalized GQDs with H₃ BO₃ forming six-member heterocycle containing the NBOH structure. When dispersed on conductive carbon substrates, the NBO-GQDs show H₂ O₂ selectivity of over 90% at 0.7 -0.8 V versus reversible hydrogen electrode in the alkaline solution in a rotating ring-disk electrode setup. The selectivity retains 90% of the initial value after 12 h stability test. In a flow cell setup, the H₂ O₂ production rate is up to 709 mmol g_catalyst ^-1  h^-1 , superior to most reported carbon- and metal-based electrocatalysts. This work provides molecular insight into the design and formulation of highly efficient carbon-based catalysts for sustainable H₂ O₂ production.

Platinum-Functionalized Graphene Oxide: One-Pot Synthesis and Application as an Electrocatalyst

This paper presents the preparation of platinum on a reduced graphene oxide matrix (PtrGO) using the microwave-assisted method with three different pH solutions. The platinum concentration determined by energy-dispersive X-ray analysis (EDX) was 4.32 (weight%), 2.16 (weight %) and 5.70 (weight%), corresponding to pH 3.3, 11.7 and 7.2, respectively. Pt functionalization of reduced graphene oxide (rGO) decreased the rGO specific surface, as shown by Brunauer, Emmett and Teller (BET) analysis. An XRD spectrum of platinum-decorated reduced graphene oxide (rGO) showed the presence of the associated phases of rGO and centered cubic platinum peaks. An oxygen reduction reaction (ORR) electrochemical characterization performed using the rotating disk electrode (RDE) method showed that in PtGO1 synthetized in an acidic environment, with 4.32 Pt (weight%) determined by EDX, platinum is much more dispersed, which explains its better electrochemical oxygen reduction reaction performance. Koutecky-Levich (K-L) plots calculated at different potentials prove a good linear relationship. Electron transfer numbers (n) determined from the K-L plots are between 3.1 and 3.8, which confirms that the ORR for all the samples can be regarded as first-order reaction kinetics of O₂ concentration formed on the Pt surface during ORR.

Coupling Fe3 C Nanoparticles and N-Doping on Wood-Derived Carbon to Construct Reversible Cathode for Zn-Air Batteries

Electrochemical reduction of oxygen plays a critical role in emerging electrochemical energy technologies. Multiple electron transfer processes, involving adsorption and activation of O₂ and generation of protons from water molecules, cause the sluggish kinetics of the oxygen reduction reaction (ORR). Herein, a double-active-site catalyst of Fe₃ C nanoparticles coupled to paulownia wood-derived N-doped carbon (Fe₃ C@NPW) is fabricated via an active-site-uniting strategy. One site on Fe₃ C nanoparticles contributes to activating water molecules, while another site on N-doped carbon is responsible for activating oxygen molecules. Benefiting from the synergistic effect of double active sites, Fe₃ C@NPW delivers a remarkable catalytic activity for ORR with a half-wave potential of 0.87 V (vs. RHE) in alkaline electrolyte, outperforming commercial Pt/C catalyst. Moreover, zinc-air batteries (ZABs) assembled with Fe₃ C@NPW as a catalyst on cathode achieve a large specific capacity of 804.4 mA h g_Zn^-1 and a long-term stability of 780 cycles. The model solid-state ZABs also display satisfactory performances with an open-circuit voltage of 1.39 V and a high peak power density of 78 mW cm^-2 . These outstanding performances reach the level of first-rank among the non-noble metal electrode materials. This work offers a promising approach to creating double-active-site catalysts by the active-site-uniting strategy for energy conversion fields.

A Facile "Double-Catalysts" Approach to Directionally Fabricate Pyridinic NB-Pair-Doped Crystal Graphene Nanoribbons/Amorphous Carbon Hybrid Electrocatalysts for Efficient Oxygen Reduction Reaction

Carbon material is a promising electrocatalyst for the oxygen reduction reaction (ORR). Doping of heteroatoms, the most widely used modulating strategy, has attracted many efforts in the past decade. Despite all this, the catalytic activity of heteroatoms-modulated carbon is hard to compare to that of metal-based electrocatalysts. Here, a "double-catalysts" (Fe salt, H₃ BO₃ ) strategy is presented to directionally fabricate porous structure of crystal graphene nanoribbons (GNs)/amorphous carbon doped by pyridinic NB pairs. The porous structure and GNs accelerate ion/mass and electron transport, respectively. The N percentage in pyridinic NB pairs accounts for ≈80% of all N species. The pyridinic NB pair drives the ORR via an almost 4e^- transfer pathway with a half-wave potential (0.812 V vs reversible hydrogen electrode (RHE)) and onset potential (0.876 V vs RHE) in the alkaline solution. The ORR catalytic performance of the as-prepared carbon catalysts approximates commercial Pt/C and outperforms most prior carbon-based catalysts. The assembled Zn-air battery exhibits a high peak power density of 94 mW cm^-2 . Density functional theory simulation reveals that the pyridinic NB pair possesses the highest catalytic activity among all the potential configurations, due to the highest charge density at C active sites neighboring B, which enhances the interaction strength with the intermediates in the p-band center.

Photo-induced green synthesis of bimetallic Ag/Pd nanoparticles decorated reduced graphene oxide/nitrogen-doped graphene quantum dots nanocomposite as an amperometric sensor for nitrite detection

The present study introduces a novel nanocomposite based on reduced graphene oxide, nitrogen-doped graphene quantum dots, and palladium and silver nanoparticles (rGO/NGQD/AgPd) as an electrocatalyst toward nitrite oxidation reaction. Metal nanoparticles were prepared via a green one-pot photochemical reduction procedure utilizing UV light and NGQD simultaneously as a reducing and directing agent. Formation of the nanocomposite was thoroughly demonstrated by the FT-IR, XRD, Raman, XPS, FE-SEM, and TEM characterization tests. Various electrochemical tests evaluated the efficiency of the prepared sensing platform on the surface of a gold working electrode. Sensitivity and limit of detection (LOD) were calculated to be 0.854 μA.μM^-1.cm^-2 and 0.052 μM, respectively, from the chronoamperometry data. Finally, the proposed sensor was successfully applied for the determination of nitrite ions in river and mineral water samples as natural water sources.

N, P-Codoped Graphene Dots Supported on N-Doped 3D Graphene as Metal-Free Catalysts for Oxygen Reduction

Nitrogen and phosphorus-codoped graphene dots supported on nitrogen-doped three-dimensional graphene (N, P-GDs/N-3DG) have been synthesized by a facile freeze-annealing process. On the surface of the 3D interconnected porous structure, the N, P-GDs are uniformly dispersed. The as-prepared N, P-GDs/N-3DG material served as a metal-free catalyst for oxygen reduction reaction (ORR) in an alkaline medium and evaluated by a rotating ring-disk electrode. The N, P-GDs/N-3DG catalyst exhibits excellent ORR activity, which is comparable to that of the commercial Pt/C catalyst. Furthermore, it exhibits a higher tolerance to methanol and better stability than the Pt/C. This enhanced electrochemical catalytic performance can be ascribed to the presence of abundant functional groups and edge defects. This study indicates that P-N bonded structures play a vital role as the active sites in ORR.

Carbon Dots-Decorated Carbon-Based Metal-Free Catalysts for Electrochemical Energy Storage

In the past ten years, carbon dots-decorated, carbon-based, metal-free catalysts (CDs-C-MFCs) have become the fastest-growing branch in the metal-free materials for energy storage field. However, the further development of CDs-C-MFCs needs to clear up the electronic transmission mechanism rather than primarily relying on trial-and-error approaches. This review presents systematically and comprehensively for the first time the latest advances of CDs-C-MFCs in supercapacitors and metal-air batteries. The structure-performance relationship of these materials is carefully discussed. It is indicated that carbon dots (CDs) can act as the electron-rich regions in CDs-C-MFCs owing to their unique properties, such as quantum confinement effects, abundant defects, countless functional groups, etc. More importantly, specific doping can effectively modify the charge/spin distribution and then facilitate electron transfer. In addition, present challenges and future prospects of the CDs-C-MFCs are also given.

Nitrogen and phosphorous doped graphene quantum dots: Excellent flame retardants and smoke suppressants for polyacrylonitrile nanocomposites

Nitrogen (N-GQD) as well as nitrogen and phosphorous co-doped (NP-GQD) graphene quantum dots were demonstrated as novel, low cost, green and highly effective flame retardants and smoke suppressants for polyacrylonitrile (PAN) nanocomposites. The N-GQD and NP-GQD samples were synthesized by hydrothermal method with citric acid as the main reactant. For the first time, the flame retardant and smoke suppressant properties of the NP-GQD were studied. The GQDs were introduced into PAN by solvent blending route. Subsequently, thermal stability, flame retardancy, fire behavior, fire hazard and structure of the residual char were investigated by thermogravimetric analysis (TGA), UL-94 vertical burning test, cone calorimetry, FE-SEM, and Raman spectroscopy. Results showed that both PAN/N-GQD and PAN/NP-GQD nanocomposites had higher flame retardancy and smoke suppressant behavior in addition to lower fire hazard properties than neat PAN. Furthermore, the residual chars for the nanocomposite samples were increased in comparison to the neat PAN. The improvements were even more significant in case of the PAN/NP-GQD due to the synergistic effect of nitrogen and phosphorous. The improvements were mainly ascribed to the ability of the N-GQD and NP-GQD to provide stronger and larger protective char barrier layers, which was even more pronounced in case of the NP-GQD.

Glassy carbon electrodes modified with reduced graphene oxide-MoS2-poly (3, 4-ethylene dioxythiophene) nanocomposites for the non-enzymatic detection of nitrite in water and milk

The detrimental effect of (NO₂^-) on environment, a sensitive and selective detection of nitrite (NO₂^-) ions with point-to-care device is need to be fabricated. Herein, we report the non-enzymatic nitrite sensor using a novel reduced graphene oxide/molybdenum disulfide/poly (3, 4-ethylene dioxythiophene) (rGO/MoS₂/PEDOT) nanocomposite electrode. The rGO/MoS₂/PEDOT nanocomposite was synthesized using facile and cost-effective hydrothermal and polymerization approaches. The characteristics of rGO-MoS₂-PEDOT nanocomposite was investigated by X-ray diffraction (XRD), Fourier transform infrared (FT-IR), Raman, transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS) and Brunauer-Emmett-Teller (BET) analyses. The rGO-MoS₂-PEDOT nanocomposite modified glassy carbon electrode (GCE) was directly used for electrocatalytic detection of nitrite ions present in the solution. TEM images show the PEDOT nanoparticles with an average size of 100-120 nm are uniformly covered on the outer face of rGO-MoS₂ nanosheets. The interaction between the PEDOT and rGO-MoS₂ is evidenced in the FTIR, XRD and XPS studies, and they produced synergistic effect, resulting enhanced electrocatalytic performance activity towards oxidation of nitrite. Under optimized conditions, the fabricated electrode exhibited remarkably good sensitivity (874.19 μA μM^-1 cm^-2), low detection limit (LOD) (0.059 μM, S/N = 3), wide linear range (0.001-1 mM) of nitrite with desirable selectivity, long-term stability and reproducibility. Furthermore, the practical feasibility of the fabricated sensor is validated by the successful detection of nitrite ion in some water and milk samples with excellent correlation. Thus, feasible easier synthesis method was adopted first time to fabricate rGO-MoS₂-PEDOT nanocomposite nitrite sensor in the milk and water samples with enhanced selectivity, sensitivity and LOD.

Porous Carbon Networks Derived From Graphitic Carbon Nitride for Efficient Oxygen Reduction Reaction

Great efforts have been dedicated to finding economic and efficient oxygen reduction reaction (ORR) for fuel cell technology. Among various catalysts, N-doped carbon-based nanomaterials have attracted much attention due to low-cost, noble metal free, and good durability. Herein, we developed a facile and economic strategy to prepare nitrogen-doped carbon networks for efficient ORR application. The g-C₃N₄ is used as the template and N source, and dopamine is used as the carbon source. By simple hydrothermal treatment and sintering, N-doped carbon network structures with high specific surface area, effective ORR activity, and superior durability could be acquired. The present strategy is free of involving generally multistep, poisonous reagents, and complication of removing template for fabrication of 3D carbon structures.

Recent Advances on Graphene Quantum Dots: From Chemistry and Physics to Applications

Graphene quantum dots (GQDs) that are flat 0D nanomaterials have attracted increasing interest because of their exceptional chemicophysical properties and novel applications in energy conversion and storage, electro/photo/chemical catalysis, flexible devices, sensing, display, imaging, and theranostics. The significant advances in the recent years are summarized with comparative and balanced discussion. The differences between GQDs and other nanomaterials, including their nanocarbon cousins, are emphasized, and the unique advantages of GQDs for specific applications are highlighted. The current challenges and outlook of this growing field are also discussed.

Boosting the electrochemical oxygen reduction activity of hemoglobin on fructose@graphene-oxide nanoplatforms

A metal-free oxygen reduction reaction (ORR) electrocatalyst with outstanding performance was obtained through an easy and one-pot synthesis of hemoglobin functionalized fructose@graphene-oxide (GO) nanocomposites.

Vertically Aligned N-Doped Diamond/Graphite Hybrid Nanosheets Epitaxially Grown on B-Doped Diamond Films as Electrocatalysts for Oxygen Reduction Reaction in an Alkaline Medium

Diamond/graphite hybrid nanosheets (DGNSs) have been epitaxially grown on boron-doped diamond (BDD) films from CH₄/H₂ mixture gas by microwave plasma chemical vapor deposition. The DGNSs are vertically aligned on the crystal facets of the BDD films uniformly, densely, and orderly. The DGNSs are composed of the core diamond sheets and the surface graphitic overlayers, which possess an open edge structure. By posttreatment in NH₃ atmosphere in a microwave plasma or a tube furnace, the N-doped DGNSs (NDGNSs) were obtained. The electrocatalytic performance toward oxygen reduction reaction (ORR) for the DGNSs was greatly enhanced after doping with N, and the doped pyridinic N contributes more to the ORR. The electrocatalytic activity for ORR of the NDGNSs doped at 650 °C in NH₃ in a tube furnace is the highest in all of the samples, which is comparable to the commercial Pt/C. The present work provides a novel electrocatalyst for the ORR with high performance.

Nitrogen-doped graphene and graphene quantum dots: A review onsynthesis and applications in energy, sensors and environment

Doping of nitrogen is a promising strategy to modulate chemical, electronic, and structural functionalities of graphene (G)and graphene quantum dots (GQDs) for their outstanding properties in energy and environmental applications.This paper reviews various synthesis approaches of nitrogen-doped graphene (N-G) and nitrogen-doped graphene quantum dots (N-GQDs).;Thermal, ultrasonic, solvothermal, hydrothermal, and electron-beam methods have been applied to synthesize N-G and N-GQDs.These nitrogen-doped carbon materials are characterized to obtain their structural configurations in order to achieve better performance in their applications compared to only either graphene or graphene quantum dots.Both N-G and N-GQDs may be converted into functional materials by integrating with other compounds such as metal oxides/nitrides, polymers, and semiconductors.These functional materials demonstrate superior performance over N-G and N-GQDs materials.Examples of applications of N-G and N-GQDs include supercapacitors, batteries, sensors, fuel cells, solar cells, and photocatalyst.

A comparison of nitrogen-doped sonoelectrochemical and chemical graphene nanosheets as hydrogen peroxide sensors

Nitrogen-doped graphene nanosheet (N-SEGN) with pyrrolic nitrogen and 5-9 vacancy defects has been successfully prepared from a hydrothermal reaction of tetra-2-pyridinylpyrazine and sonoelectrochemistry-exfoliated graphene nanosheet, with point defects. Additionally, based on the same reaction using chemically reduced graphene oxide, nitrogen-doped chemically reduced graphene oxide (N-rGO) with graphitic nitrogen was prepared. The N-SEGN and N-rGO were used as a non-enzymatic H₂O₂ sensors. The sensitivity of the N-SEGN was 231.3 μA·mM^-1·cm^-2, much greater than 57.3 μA·mM^-1·cm^-2 of N-rGO. The N-SEGN showed their potential for being a H₂O₂ sensor.

Folic acid-functionalized graphene quantum dots with tunable fluorescence emission for cancer cell imaging and optical detection of Hg2+

Functional groups may alter the optical and electrical characteristics of graphene quantum dots and lead to unusual properties and related applications.

Role of Pyridinic-N for Nitrogen-doped graphene quantum dots in oxygen reaction reduction

Nitrogen-doped graphene quantum dots (N-GQDs) exhibit exciting properties in the oxygen reduction reaction (ORR) for ample electrocatalytic edging and N-doped active sites. However, low yield and high dispersity of N-GQDs prohibit their direct application as the electrocatalyst. In this paper, two facile hydrothermal progress were developed to synthesize the high-yield N-GQDs with the diameter of ca. 2-6nm and the hybrid of N-GQDs/Reduced Graphene Oxide (N-GQDs/r-GO). The results demonstrated that the N-GQDs/r-GO display remarkable electrocatalytic activity. Moreover, it can be found that the pyridinic-N plays a major role in ORR. Both the average electron transfer number and the onset potential depend on the content of pyridinic-N. The proposed synthesis strategy is facile and low-cost, serving as a feasible method for the development of highly efficient electrocatalysts.

Recent progress in the preparation and application of quantum dots/graphene composite materials

Quantum dots/graphene (QDs/GR) composite materials show a distinct synergistic effect between the QDs and graphene, which has aroused vast attention toward their unique characteristics in the last few decades.

Synergistically Enhanced Electrocatalytic Performance of an N-Doped Graphene Quantum Dot-Decorated 3D MoS2-Graphene Nanohybrid for Oxygen Reduction Reaction

Nitrogen-doped graphene quantum dots (N-GQDs) were decorated on a three-dimensional (3D) MoS2-reduced graphene oxide (rGO) framework via a facile hydrothermal method. The distribution of N-GQDs on the 3D MoS2-rGO framework was confirmed using X-ray photoelectron spectroscopy, energy dispersive X-ray elemental mapping, and high-resolution transmission electron microscopy techniques. The resultant 3D nanohybrid was successfully demonstrated as an efficient electrocatalyst toward the oxygen reduction reaction (ORR) under alkaline conditions. The chemical interaction between the electroactive N-GQDs and MoS2-rGO and the increased surface area and pore size of the N-GQDs/MoS2-rGO nanohybrid synergistically improved the ORR onset potential to +0.81 V vs reversible hydrogen electrode (RHE). Moreover, the N-GQDs/MoS2-rGO nanohybrid showed better ORR stability for up to 3000 cycles with negligible deviation in the half-wave potential (E 1/2). Most importantly, the N-GQDs/MoS2-rGO nanohybrid exhibited a superior methanol tolerance ability even under a high concentration of methanol (3.0 M) in alkaline medium. Hence, the development of a low-cost metal-free graphene quantum dot-based 3D nanohybrid with high methanol tolerance may open up a novel strategy to design selective cathode electrocatalysts for direct methanol fuel cell applications.