Transmission Electron Microscopy Reveals Deposition of Metal Oxide Coatings onto Metal–Organic Frameworks

Zirconium-based metal-organic frameworks and their roles in electrocatalysis

Due to their exceptional chemical stability in water and high structural tunability, zirconium(IV)-based MOFs (Zr-MOFs) have been considered attractive materials in the broad fields of electrocatalysis. Numerous studies published since 2015 have attempted to utilise Zr-MOFs in electrocatalysis, with the porous framework serving as either the active electrocatalyst or the scaffold or surface coating to further enhance the performance of the actual electrocatalyst. Herein, the roles of Zr-MOFs in electrocatalytic processes are discussed, and some selected examples reporting the applications of Zr-MOFs in various electrocatalytic reactions, including several studies from our group, are overviewed. Challenges, limitations and opportunities in using Zr-MOFs in electrocatalysis in future studies are discussed.

A MOF@Metal Oxide Heterostructure Induced by Post-Synthetic Gamma-Ray Irradiation for Catalytic Reduction

Metal-organic framework (MOF) based heterostructures, which exhibit enhanced or unexpected functionality and properties due to synergistic effects, are typically synthesized using post-synthetic strategies. However, several reported post-synthetic strategies remain unsatisfactory, considering issues such as damage to the crystallinity of MOFs, presence of impure phases, and high time and energy consumption. In this work, we demonstrate for the first time a novel route for constructing MOF based heterostructures using radiation-induced post-synthesis, highlighting the merits of convenience, ambient conditions, large-scale production, and notable time and energy saving. Specifically, a new HKUST-1@Cu2O heterostructure was successfully synthesized by simply irradiating a methanol solution dispersed of HKUST-1 with gamma ray under ambient conditions. The copper source of Cu2O was directly derived from in situ radiation etching and reduction of the parent HKUST-1, without the use of any additional copper reagents. Significantly, the resulting HKUST-1@Cu2O heterostructure exhibits remarkable catalytic performance, with a catalytic rate constant nearly two orders of magnitude higher than that of the parent HKUST-1.

Recent Advances of Bimetallic-Metal Organic Frameworks: Preparation, Properties, and Fluorescence-Based Biochemical Sensing Applications

Bimetallic-metal organic frameworks (BiM-MOFs) or bimetallic organic frameworks represent an innovative and promising class of porous materials, distinguished from traditional monometallic MOFs by their incorporation of two metal ions alongside organic linkers. BiM-MOFs, with their unique crystal structure, physicochemical properties, and composition, demonstrate distinct advantages in the realm of biochemical sensing applications, displaying improvements in optical properties, stability, selectivity, and sensitivity. This comprehensive review explores into recent advancements in leveraging BiM-MOFs for fluorescence-based biochemical sensing, providing insights into their design, synthesis, and practical applications in both chemical and biological sensing. Emphasizing fluorescence emission as a transduction mechanism, the review aims to guide researchers in maximizing the potential of BiM-MOFs across a broader spectrum of investigations. Furthermore, it explores prospective research directions and addresses challenges, offering valuable perspectives on the evolving landscape of fluorescence-based probes rooted in BiM-MOFs.

Defect-enabling zirconium-based metal-organic frameworks for energy and environmental remediation applications

This comprehensive review explores the diverse applications of defective zirconium-based metal-organic frameworks (Zr-MOFs) in energy and environmental remediation. Zr-MOFs have gained significant attention due to their unique properties, and deliberate introduction of defects further enhances their functionality. The review encompasses several areas where defective Zr-MOFs exhibit promise, including environmental remediation, detoxification of chemical warfare agents, photocatalytic energy conversions, and electrochemical applications. Defects play a pivotal role by creating open sites within the framework, facilitating effective adsorption and remediation of pollutants. They also contribute to the catalytic activity of Zr-MOFs, enabling efficient energy conversion processes such as hydrogen production and CO2 reduction. The review underscores the importance of defect manipulation, including control over their distribution and type, to optimize the performance of Zr-MOFs. Through tailored defect engineering and precise selection of functional groups, researchers can enhance the selectivity and efficiency of Zr-MOFs for specific applications. Additionally, pore size manipulation influences the adsorption capacity and transport properties of Zr-MOFs, further expanding their potential in environmental remediation and energy conversion. Defective Zr-MOFs exhibit remarkable stability and synthetic versatility, making them suitable for diverse environmental conditions and allowing for the introduction of missing linkers, cluster defects, or post-synthetic modifications to precisely tailor their properties. Overall, this review highlights the promising prospects of defective Zr-MOFs in addressing energy and environmental challenges, positioning them as versatile tools for sustainable solutions and paving the way for advancements in various sectors toward a cleaner and more sustainable future.

Chemical complexity for targeted function in heterometallic titanium-organic frameworks

Research on metal-organic frameworks is shifting from the principles that control the assembly, structure, and porosity of these reticular solids, already established, into more sophisticated concepts that embrace chemical complexity as a tool for encoding their function or accessing new properties by exploiting the combination of different components (organic and inorganic) into these networks. The possibility of combining multiple linkers into a given network for multivariate solids with tunable properties dictated by the nature and distribution of the organic connectors across the solid has been well demonstrated. However, the combination of different metals remains still comparatively underexplored due to the difficulties in controlling the nucleation of heterometallic metal-oxo clusters during the assembly of the framework or the post-synthetic incorporation of metals with distinct chemistry. This possibility is even more challenging for titanium-organic frameworks due to the additional difficulties intrinsic to controlling the chemistry of titanium in solution. In this perspective article we provide an overview of the synthesis and advanced characterization of mixed-metal frameworks and emphasize the particularities of those based in titanium with particular focus on the use of additional metals to modify their function by controlling their reactivity in the solid state, tailoring their electronic structure and photocatalytic activity, enabling synergistic catalysis, directing the grafting of small molecules or even unlocking the formation of mixed oxides with stoichiometries not accessible to conventional routes.

Research Progress on Metal-Organic Frameworks by Advanced Transmission Electron Microscopy

Metal-organic frameworks (MOFs), composed of metal nodes and inorganic linkers, are promising for a wide range of applications due to their unique periodic frameworks. Understanding structure-activity relationships can facilitate the development of new MOFs. Transmission electron microscopy (TEM) is a powerful technique to characterize the microstructures of MOFs at the atomic scale. In addition, it is possible to directly visualize the microstructural evolution of MOFs in real time under working conditions via in situ TEM setups. Although MOFs are sensitive to high-energy electron beams, much progress has been made due to the development of advanced TEM. In this review, we first introduce the main damage mechanisms for MOFs under electron-beam irradiation and two strategies to minimize these damages: low-dose TEM and cryo-TEM. Then we discuss three typical techniques to analyze the microstructure of MOFs, including three-dimensional electron diffraction, imaging using direct-detection electron-counting cameras, and iDPC-STEM. Groundbreaking milestones and research advances of MOFs structures obtained with these techniques are highlighted. In situ TEM studies are reviewed to provide insights into the dynamics of MOFs induced by various stimuli. Additionally, perspectives are analyzed for promising TEM techniques in the research of MOFs' structures.

MOFs-based Fe@YAU-101/GCE electrochemical sensor platform for highly selective detecting trace multiplex heavy metal ions

The construction of sensors with specific recognition functions can easily, sensitively and efficiently detect heavy metal ions, which is a demand in the field of electrochemical sensing and an important topic in the detection of environmental pollutants. An electrochemical sensor based on MOFs composites was developed for sensing of multiplex metal ions. The large surface area, adjustable porosities and channels in MOFs facilitate successful loading of sufficient quantities highly active units. The active units and pore structures of MOFs are regulated and synergetic with each other to enhance the electrochemical activity of MOFs composites. Thus, the selectivity, sensitivity and reproducibility of MOFs composites have been improved. Fortunately, after characterization, Fe@YAU-101/GCE sensor with strong signal was successfully constructed. In the presence of target metal ions in solution, the Fe@YAU-101/GCE can efficiently and synchronously identify Hg²⁺, Pb²⁺, and Cd²⁺. The detection limits (LOD) are 6.67 × 10^-10 M(Cd²⁺), 3.33 × 10^-10 M(Pb²⁺) and 1.33 × 10^-8 M (Hg²⁺), and are superior to the permissible limits set by the National Environmental Protection Agency. The electrochemical sensor is simple without sophisticated instrumentation and testing processes, hence promising for practical applications.

Zr- and Ti-based metal-organic frameworks: synthesis, structures and catalytic applications

Recently, Zr- and Ti-based metal-organic frameworks (MOFs) have gathered increasing interest in the field of chemistry and materials science, not only for their ordered porous structure, large surface area, and high thermal and chemical stability, but also for their various potential applications. Particularly, the unique features of Zr- and Ti-based MOFs enable them to be a highly versatile platform for catalysis. Although much effort has been devoted to developing Zr- and Ti-based MOF materials, they still suffer from difficulties in targeted synthesis, especially for Ti-based MOFs. In this Feature Article, we discuss the evolution of Zr- and Ti-based MOFs, giving a brief overview of their synthesis and structures. Furthermore, the catalytic uses of Zr- and Ti-based MOF materials in the previous 3-5 years have been highlighted. Finally, perspectives on the Zr- and Ti-based MOF materials are also proposed. This work provides in-depth insight into the advances in Zr- and Ti-based MOFs and boosts their catalytic applications.

Highlighting the Importance of Characterization Techniques Employed in Adsorption Using Metal-Organic Frameworks for Water Treatment

The accumulation of toxic heavy metal ions continues to be a global concern due to their adverse effects on the health of human beings and animals. Adsorption technology has always been a preferred method for the removal of these pollutants from wastewater due to its cost-effectiveness and simplicity. Hence, the development of highly efficient adsorbents as a result of the advent of novel materials with interesting structural properties remains to be the ultimate objective to improve the adsorption efficiencies of this method. As such, advanced materials such as metal-organic frameworks (MOFs) that are highly porous crystalline materials have been explored as potential adsorbents for capturing metal ions. However, due to their diverse structures and tuneable surface functionalities, there is a need to find efficient characterization techniques to study their atomic arrangements for a better understanding of their adsorption capabilities on heavy metal ions. Moreover, the existence of various species of heavy metal ions and their ability to form complexes have triggered the need to qualitatively and quantitatively determine their concentrations in the environment. Hence, it is crucial to employ techniques that can provide insight into the structural arrangements in MOF composites as well as their possible interactions with heavy metal ions, to achieve high removal efficiency and adsorption capacities. Thus, this work provides an extensive review and discussion of various techniques such as X-ray diffraction, Brunauer-Emmett-Teller theory, scanning electron microscopy and transmission electron microscopy coupled with energy dispersive spectroscopy, and X-ray photoelectron spectroscopy employed for the characterization of MOF composites before and after their interaction with toxic metal ions. The review further looks into the analytical methods (i.e., inductively coupled plasma mass spectroscopy, ultraviolet-visible spectroscopy, and atomic absorption spectroscopy) used for the quantification of heavy metal ions present in wastewater treatment.

Metal-hydrogen-pi-bonded organic frameworks

We report the synthesis and characterization of a new series of permanently porous, three-dimensional metal-organic frameworks (MOFs), M-HAF-2 (M = Fe, Ga, or In), constructed from tetratopic, hydroxamate-based, chelating linkers. The structure of M-HAF-2 was determined by three-dimensional electron diffraction (3D ED), revealing a unique interpenetrated hcb-a net topology. This unusual topology is enabled by the presence of free hydroxamic acid groups, which lead to the formation of a diverse network of cooperative interactions comprising metal-hydroxamate coordination interactions at single metal nodes, staggered π-π interactions between linkers, and H-bonding interactions between metal-coordinated and free hydroxamate groups. Such extensive, multimodal interconnectivity is reminiscent of the complex, noncovalent interaction networks of proteins and endows M-HAF-2 frameworks with high thermal and chemical stability and allows them to readily undergo postsynthetic metal ion exchange (PSE) between trivalent metal ions. We demonstrate that M-HAF-2 can serve as versatile porous materials for ionic separations, aided by one-dimensional channels lined by continuously π-stacked aromatic groups and H-bonding hydroxamate functionalities. As an addition to the small group of hydroxamic acid-based MOFs, M-HAF-2 represents a structural merger between MOFs and hydrogen-bonded organic frameworks (HOFs) and illustrates the utility of non-canonical metal-coordinating functionalities in the discovery of new bonding and topological patterns in reticular materials.

MOF-enabled confinement and related effects for chemical catalyst presentation and utilization

A defining characteristic of nearly all catalytically functional MOFs is uniform, molecular-scale porosity. MOF pores, linkers and nodes that define them, help regulate reactant and product transport, catalyst siting, catalyst accessibility, catalyst stability, catalyst activity, co-catalyst proximity, composition of the chemical environment at and beyond the catalytic active site, chemical intermediate and transition-state conformations, thermodynamic affinity of molecular guests for MOF interior sites, framework charge and density of charge-compensating ions, pore hydrophobicity/hydrophilicity, pore and channel rigidity vs. flexibility, and other features and properties. Collectively and individually, these properties help define overall catalyst functional behaviour. This review focuses on how porous, catalyst-containing MOFs capitalize on molecular-scale confinement, containment, isolation, environment modulation, energy delivery, and mobility to accomplish desired chemical transformations with potentially superior selectivity or other efficacy, especially in comparison to catalysts in homogeneous solution environments.

Construction of bimetallic FeCo–SA/DABCO nanosheets by modulating the electronic structure for improved electrocatalytic oxygen evolution

For energy conversion and storage, the electrochemical oxygen evolution process (OER) is the crucial half-reaction process.

Lattice-Guided Construction and Harvest of a Naturally Nonpreferred Metal-Organic Framework

Constructing metal-organic frameworks (MOFs) to have a desired structure from the given components is critical to achieve ideal MOFs with optimal properties. However, thermodynamics and/or kinetics typically impose a restriction on MOF structures. Here, we report the MOF farming concept to produce a naturally nonpreferred structure from the given components. The HKUST-1 template offers ideal places for the efficient seeding and epitaxial growth of Ga-MIL-88B that is a naturally nonpreferred structure however intentionally produced instead of the preferred Ga-MIL-68. The MOF growth on the differently shaped HKUST-1 templates (octahedral, cuboctahedral, and cubic), containing different exposed lattices, proves that a hexagonal lattice with an exposed {111} plane of HKUST-1 selectively directs the perpendicular growth of Ga-MIL-88B, owing to the lattice matching with the {001} plane of Ga-MIL-88B. The grown Ga-MIL-88B is isolated in a pure form, and the refreshed template is reused to grow additional Ga-MIL-88B.

Hierarchically porous metal hydroxide/metal-organic framework composite nanoarchitectures as broad-spectrum adsorbents for toxic chemical filtration

We demonstrate that the hierarchically porous metal hydroxide/metal-organic framework composite nanoarchitectures exhibit broad-spectrum removal activity for three chemically distinct toxic gases, viz. acid gases, base gases, and nitrogen oxides. A facile and general in-situ hydrolysis strategy combined with gentle ambient pressure drying (APD) was utilized to integrate both Zr(OH)₄ and Ti(OH)₄ with the amino-functionalized MOF-808 xerogel (G808-NH₂). The M(OH)₄/G808-NH₂ xerogel composites manifested 3D crystalline porous networks and substantially hierarchical porosity, with controllable amounts of amorphous M(OH)₄ nanoparticles residing at the edge of xerogel particles. Microbreakthrough tests were performed under both dry and moist conditions to evaluate the filtration capabilities of the composites against three representative compounds: SO₂, NH₃, and NO₂. Compared with the pristine G808-NH₂ xerogel, the incorporation of M(OH)₄ effectively enhanced the broad-spectrum toxic chemical mitigation ability of the material, with the highest SO₂, NH₃, and NO₂ breakthrough uptake reaching 74.5, 55.3, and 394.0 mg/g, respectively. Post-breakthrough characterization confirmed the abundant M-OH groups with diverse binding configurations, alongside the unsaturated M (IV) centers on the surface of M(OH)₄ provided extra adsorption sites for irreversible toxic chemical capture besides Van der Waals driven physisorption. The ability to achieve high-capacity adsorption and strong retention for multiple contaminants is of great significance for real-world filtration applications.

A Close Look at Molecular Self-Assembly with the Transmission Electron Microscope

Molecular self-assembly is pervasive in the formation of living and synthetic materials. Knowledge gained from research into the principles of molecular self-assembly drives innovation in the biological, chemical, and materials sciences. Self-assembly processes span a wide range of temporal and spatial domains and are often unintuitive and complex. Studying such complex processes requires an arsenal of analytical and computational tools. Within this arsenal, the transmission electron microscope stands out for its unique ability to visualize and quantify self-assembly structures and processes. This review describes the contribution that the transmission electron microscope has made to the field of molecular self-assembly. An emphasis is placed on which TEM methods are applicable to different structures and processes and how TEM can be used in combination with other experimental or computational methods. Finally, we provide an outlook on the current challenges to, and opportunities for, increasing the impact that the transmission electron microscope can have on molecular self-assembly.

Metal–Organic Frameworks as Versatile Platforms for Organometallic Chemistry

Metal–organic frameworks (MOFs) are emerging porous materials with highly tunable structures developed in the 1990s, while organometallic chemistry is of fundamental importance for catalytic transformation in the academic and industrial world for many decades. Through the years, organometallic chemistry has been incorporated into functional MOF construction for diverse applications. Here, we will focus on how organometallic chemistry is applied in MOF design and modifications from linker-centric and metal-cluster-centric perspectives, respectively. Through structural design, MOFs can function as a tailorable platform for traditional organometallic transformations, including reaction of alkenes, cross-coupling reactions, and C–H activations. Besides, an overview will be made on other application categories of organometallic MOFs, such as gas adsorption, magnetism, quantum computing, and therapeutics.

Differentiating Zr/HfIV Aqueous Polyoxocation Chemistry with Peroxide Ligation

This work complements our recent discovery of new phases derived from zirconium perchlorate by addition of hydrogen peroxide. Here, we investigate analogous reactions with hafnium perchlorate, which is found to have modifications of the Clearfield-Vaughan tetramer (CVT). For hafnium perchlorate derivatives, we find distorted versions of CVT by X-ray diffraction and study the reaction solutions by SAXS, Raman spectroscopy, and ESI-MS. Furthermore, we investigate mixed Hf-Zr solution and solid phases and find the latter resemble the zirconium family at low Hf concentrations and the hafnium family at higher hafnium contents.

Destruction of Metal-Organic Frameworks: Positive and Negative Aspects of Stability and Lability

Metal-organic frameworks (MOFs), constructed from organic linkers and inorganic building blocks, are well-known for their high crystallinity, high surface areas, and high component tunability. The stability of MOFs is a key prerequisite for their potential practical applications in areas including storage, separation, catalysis, and biomedicine since it is essential to guarantee the framework integrity during utilization. However, MOFs are prone to destruction under external stimuli, considerably hampering their commercialization. In this Review, we provide an overview of the situations where MOFs undergo destruction due to external stimuli such as chemical, thermal, photolytic, radiolytic, electronic, and mechanical factors and offer guidelines to avoid unwanted degradation happened to the framework. Furthermore, we discuss possible destruction mechanisms and their varying derived products. In particular, we highlight cases that utilize MOF instability to fabricate varying materials including hierarchically porous MOFs, monolayer MOF nanosheets, amorphous MOF liquids and glasses, polymers, metal nanoparticles, metal carbide nanoparticles, and carbon materials. Finally, we provide a perspective on the utilization of MOF destruction to develop advanced materials with a superior hierarchy for various applications.

Bimetallic metal-organic frameworks and their derivatives

Bimetallic metal-organic frameworks (MOFs) have two different metal ions in the inorganic nodes. According to the metal distribution, the architecture of bimetallic MOFs can be classified into two main categories namely solid solution and core-shell structures. Various strategies have been developed to prepare bimetallic MOFs with controlled compositions and structures. Bimetallic MOFs show a synergistic effect and enhanced properties compared to their monometallic counterparts and have found many applications in the fields of gas adsorption, catalysis, energy storage and conversion, and luminescence sensing. Moreover, bimetallic MOFs can serve as excellent precursors/templates for the synthesis of functional nanomaterials with controlled sizes, compositions, and structures. Bimetallic MOF derivatives show exposed active sites, good stability and conductivity, enabling them to extend their applications to the catalysis of more challenging reactions and electrochemical energy storage and conversion. This review provides an overview of the significant advances in the development of bimetallic MOFs and their derivatives with special emphases on their preparation and applications.

Pine cone mold: a toolbox for fabricating unique metal/carbon nanohybrid electrocatalysts

Nature presents delicate and complex materials systems beyond those fathomable by humans, and therefore, extensive effort has been made to utilize or mimic bio-materials and bio-systems in various fields. Biomass, an inexhaustible natural materials source, can also present good opportunities for the development of unprecedented, advanced materials and processing systems. Herein, we demonstrate the use of pine cones as a biomass mold for creating new and useful metal/carbon nanohybrids (MCNHs). The inherent water-induced folding actuation of the cone scales allows the casting of an aqueous solution of a single metal precursor or a binary metal mixture into the cone mold by simply immersing the cone in the solution. The cone actively absorbs aqueous-phase metal precursors through the bract scales and the precursor ions introduced into the cone are anchored to the functional groups of the interior tissues of the cone. Subsequent heat treatment successfully led to the formation of unique MCNHs. Iron, manganese, and cobalt were employed as model metals, binary mixtures of which were also cast into the cone mold to create further versatile MCNHs. Nanoparticulate metals were formed on the carbon supports, where the size, size distribution, and crystallinity of the nanoparticles were highly dependent on the identity of the single-component precursor and the combination of precursors. Consequently, the electrochemical activity of the MCNHs also depended on which metal precursors were cast into the cone mold. The MCNH prepared from the mixture of iron and manganese precursors (M_FeMnCNH) showed the best electrochemical activity. As model applications, M_FeMnCNH was applied to electrode materials for electrochemical charge storage and the oxygen evolution reaction. An electrochemical capacitor cell based on the M_FeMnCNH electrodes showed excellent performance with energy densities of 38.7-54.2 W h kg^-1 at power densities of 16 000-160 kW kg^-1. In addition, M_FeMnCNH demonstrated a low overpotential of 464 mV and fast kinetics with a Tafel slope of 64.6 mV dec^-1 as an electrocatalyst for the oxygen evolution reaction in 1.0 M KOH. These results substantiate that pine cones as a biomass mold show great promise for creating versatile MCNHs through further combination of various precursors.

A Facile Method for Preparing UiO-66 Encapsulated Ru Catalyst and its Application in Plasma-Assisted CO2 Methanation

With increasing applications of metal-organic frameworks (MOFs) in the field of gas separation and catalysis, the preparation and performance research of encapsulating metal nanoparticles (NPs) into MOFs (M@MOF) have attracted extensive attention recently. Herein, an Ru@UiO-66 catalyst is prepared by a one-step method. Ru NPs are encapsulated in situ in the UiO-66 skeleton structure during the synthesis of UiO-66 metal-organic framework via a solvothermal method, and its catalytic activity for CO₂ methanation with the synergy of cold plasma is studied. The crystallinity and structural integrity of UiO-66 is maintained after encapsulating Ru NPs according to the X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). As illustrated by X-ray photoelectron spectroscopy (XPS), high resolution transmission electron microscopy (HRTEM), and mapping analysis, the Ru species of the hydration ruthenium trichloride precursor are reduced to metallic Ru NPs without additional reducing processes during the synthesis of Ru@UiO-66, and the Ru NPs are uniformly distributed inside the Ru@UiO-66. Thermogravimetric analysis (TGA) and N₂ sorption analysis show that the specific surface area and thermal stability of Ru@UiO-66 decrease slightly compared with that of UiO-66 and was ascribed to the encapsulation of Ru NPs in the UiO-66 skeleton. The results of plasma-assisted catalytic CO₂ methanation indicate that Ru@UiO-66 exhibits excellent catalytic activity. CO₂ conversion and CH₄ selectivity over Ru@UiO-66 reached 72.2% and 95.4% under 13.0 W of discharge power and a 30 mL·min^-1 gas flow rate ( V H 2 : V C O 2 = 4 : 1 ), respectively. Both values are significantly higher than pure UiO-66 with plasma and Ru/Al₂O₃ with plasma. The enhanced performance of Ru@UiO-66 is attributed to its unique framework structure and excellent dispersion of Ru NPs.

Quo vadis niobium? Divergent coordination behavior of early-transition metals towards MOF-5

Treatment of MOF-5 with NbCl4(THF)2 in acetonitrile leads to incorporation of Nb(iv) centers in a fashion that diverges from the established cation metathesis reactivity of this iconic material. A combination of X-ray absorption spectroscopy analysis and reactivity studies altogether supported by density functional theory computational studies document an unprecedented binding mode for the Zn4O(O2C-)6 secondary building units (SBUs), which in Nb(iv)-MOF-5 function as κ 2-chelating ligands for NbCl4 moieties, with no exchange of Zn2+ observed. This unusual reactivity expands the portfolio of post-synthetic modification techniques available for MOFs, exemplified here by MOF-5, and underscores the diverse coordination environments offered by this and potentially other MOFs towards heterometal species.

De novo synthesis of mesoporous photoactive titanium(iv)-organic frameworks with MIL-100 topology

Most developments in the chemistry and applications of metal-organic frameworks (MOFs) have been made possible thanks to the value of reticular chemistry in guiding the unlimited combination of organic connectors and secondary building units (SBUs) into targeted architectures. However, the development of new titanium-frameworks still remains limited by the difficulties in controlling the formation of persistent Ti-SBUs with predetermined directionality amenable to the isoreticular approach. Here we report the synthesis of a mesoporous Ti-MOF displaying a MIL-100 topology. MIL-100(Ti) combines excellent chemical stability and mesoporosity, intrinsic to this archetypical family of porous materials, with photoactive Ti3(μ3-O) metal-oxo clusters. By using high-throughput synthetic methodologies, we have confirmed that the formation of this SBU is thermodynamically favored as it is not strictly dependent on the metal precursor of choice and can be regarded as an adequate building block to control the design of new Ti-MOF architectures. We are confident that the addition of a mesoporous solid to the small number of crystalline, porous titanium-frameworks available will be a valuable asset to accelerate the development of new porous photocatalysts without the pore size limitations currently imposed by the microporous materials available.

Recent Advances in Amphiphilic Polymer-Oligonucleotide Nanomaterials via Living/Controlled Polymerization Technologies

Over the past decade, the field of polymer-oligonucleotide nanomaterials has flourished because of the development of synthetic techniques, particularly living polymerization technologies, which provide access to polymers with well-defined architectures, precise molecular weights, and terminal or side-chain functionalities. Various "living" polymerization methods have empowered chemists with the ability to prepare functional polymer-oligonucleotide conjugates yielding a library of architectures, including linear diblock, comb, star, hyperbranched star, and gel morphologies. Since oligonucleotides are hydrophilic and synthetic polymers can be tailored with hydrophobicity, these amphiphilic polymer-oligonucleotide conjugates are capable of self-assembling into nanostructures with different shapes, leading to many high-value-added biomedical applications, such as drug delivery systems, gene regulation, and 3D-bioprinting. This review aims to highlight the main living polymerization approaches to polymer-oligonucleotide conjugates, including ring-opening metathesis polymerization, atom transfer radical polymerization (ATRP), reversible addition-fragmentation transfer polymerization (RAFT), and ring-opening polymerization of cyclic esters and N-carboxyanhydride. The self-assembly properties and resulting applications of polymer-DNA hybrid materials are highlighted as well.

Postsynthetic Metal Exchange in a Metal-Organic Framework Assembled from Co(III) Diphosphine Pincer Complexes

A Zr metal-organic framework (MOF) 1-CoCl₃ has been synthesized by solvothermal reaction of ZrCl₄ with a carboxylic acid-functionalized Co^III-P^NN^NP pincer complex H₄(L-CoCl₃) ([L-CoCl₃]^4- = [(2,6-(NHPAr₂)₂C₆H₃)CoCl₃]^4-, Ar = p-C₆H₄CO₂^-). The structure of 1-CoCl₃ has been determined by X-ray powder diffraction and exhibits a csq topology that differs from previously reported ftw-net Zr MOFs assembled from related Pd^II- and Pt^II-P^NN^NP pincer complexes. The Co-P^NN^NP pincer species readily demetallate upon reduction of Co^III to Co^II, allowing for transmetalation with late second and third row transition metals in both the homogeneous complex and 1-CoCl₃. Reaction of 1-CoCl₃ with [Rh(nbd)Cl]₂ (nbd = 2,5-nobornadiene) results in complete Rh/Co metal exchange at the supported diphosphine pincer complexes to generate 1-RhCl, which has been inaccessible by direct solvothermal synthesis. Treating 1-CoCl₃ with PtCl₂(SMe₂)₂ in the presence of the mild reductant NEt₃ resulted in nearly complete Co substitution by Pt. In addition, a mixed metal pincer MOF, 1-PtRh, was generated by sequential substitution of Co with Pt followed by Rh.

The chemistry of multi-component and hierarchical framework compounds

This review is expected to provide a library of multi-component hierarchically porous compounds, which shall guide the state-of-the-art design of future porous materials with unprecedented tunability, synergism and precision.

Secondary building units as the turning point in the development of the reticular chemistry of MOFs

The secondary building unit (SBU) approach was a turning point in the discovery of permanently porous metal-organic frameworks (MOFs) and in launching the field of reticular chemistry. In contrast to the single-metal nodes known in coordination networks, the polynuclear nature of SBUs allows these structures to serve as rigid, directional, and stable building units in the design of robust crystalline materials with predetermined structures and properties. This concept has also enabled the development of MOFs with ultra-high porosity and structural complexity. The architectural, mechanical, and chemical stability of MOFs imparted by their SBUs also gives rise to unique framework chemistry. All of this chemistry -including ligand, linker, metal exchange, and metallation reactions, as well as precisely controlled formation of ordered vacancies- is carried out with full retention of the MOF structure, crystallinity, and porosity. The unique chemical nature of SBUs makes MOFs useful in many applications including gas and vapor adsorption, separation processes, and SBU-mediated catalysis. In essence, the SBU approach realizes a long-standing dream of scientists by bringing molecular chemistry (both organic and inorganic) to extended solid-state structures. This contribution highlights the importance of the SBUs in the development of MOFs and points to the tremendous potential still to be harnessed.