Zhang W, Li L, Huang C, Ngai T, Hu L. Effect of Sintering Temperature and Solution Treatment on Phase Changes and Mechanical Properties of High-Nitrogen Stainless Steel Prepared by MIM. MATERIALS (BASEL, SWITZERLAND) 2023; 16:2135. [PMID: 36984015 PMCID: PMC10053328 DOI: 10.3390/ma16062135] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Subscribe] [Scholar Register] [Received: 01/05/2023] [Revised: 02/24/2023] [Accepted: 03/05/2023] [Indexed: 06/18/2023]
Abstract
High-nitrogen stainless steel (HNSS) has been widely concerned and studied owing to its excellent mechanical, corrosion resistance, and biocompatibility properties. A series of HNSS was prepared by metal injection molding (MIM) using gas atomized Fe-Cr-Mn-Mo-0.3 N duplex stainless steel powders. Both sintering and solution treatments were carried out in an N2 atmosphere. The effects of nitrogen distribution and phase transformation on the mechanical properties of MIM HNSS during sintering and solution were studied. The results show that as the sintering temperature increased, the sample density increased, but the total nitrogen content decreased. Nitrogen and Cr2N concentration gradients along the cross-section of as-sintered samples were formed after cooling. The high nitrogen content promotes the decomposition of γ: γsaturated translated to γ and Cr2N. Meanwhile, the low Mn content in austenite also decomposes γ: γ translated to α and Cr2N. After solution treatment, a single γ phase was obtained for samples sintered at 1200 to 1320 °C. For solution treatment samples sintered at 1320 and 1350 °C, their tensile strength was 988.76 and 1036.12 MPa; yield strength was 615.61 and 636.14 MPa, and elongation was 42.58 and 40.08%, respectively. These values vastly exceeded the published MIM HNSS values.
Collapse
|
2
|
Sotoudeh Bagha P, Paternoster C, Khakbiz M, Sheibani S, Gholami N, Mantovani D. Surface Modification of an Absorbable Bimodal Fe-Mn-Ag Alloy by Nitrogen Plasma Immersion Ion Implantation. MATERIALS (BASEL, SWITZERLAND) 2023; 16:1048. [PMID: 36770055 PMCID: PMC9919902 DOI: 10.3390/ma16031048] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Figures] [Subscribe] [Scholar Register] [Received: 12/06/2022] [Revised: 01/11/2023] [Accepted: 01/16/2023] [Indexed: 06/18/2023]
Abstract
Recently, Fe-Mn-based alloys have been increasingly catching the attention of the scientific community, because of their tunable and outstanding mechanical properties, and suitable degradation behavior for biomedical applications. In spite of these assets, their corrosion rate (CR) is, in general, too low to satisfy the requirements that need to be met for cardiovascular device applications, such as stents. In fact, the CR is not always the same for all of the degradation stages of the material, and in addition, a finely tuned release rate, especially during the first steps of the corrosion pattern, is often demanded. In this work, a resorbable bimodal multi-phase alloy Fe-3Mn-1Ag was designed by mechanical alloying and spark plasma sintering (SPS) to accelerate the corrosion rate. The presence of several phases, for example α-Fe, α-Mn, γ-FeMn and Ag, provided the material with excellent mechanical properties (tensile strength UTS = 722 MPa, tensile strain A = 38%) and a higher corrosion rate (CR = 3.2 ± 0.2 mm/year). However, higher corrosion rates, associated with an increased release of degradation elements, could also raise toxicity concerns, especially at the beginning of the corrosion pattern. In this study, The focus of the present work was the control of the CR by surface modification, with nitrogen plasma immersion ion implantation (N-PIII) treatment that was applied to mechanically polished (MP) samples. This plasma treatment (PT) improved the corrosion resistance of the material, assessed by static degradation immersion tests (SDITs), especially during the first degradation stages. Twenty-eight days later, the degradation rate reached the same value of the MP condition. Nitrogen compounds on the surface of the substrate played an important role in the corrosion mechanism and corrosion product formation. The degradation analysis was carried out also by potentiodynamic tests in modified Hanks' balanced salt solution (MHBSS), and Dulbecco's phosphate buffered saline solution (DPBSS). The corrosion rate was higher in MHBSS for both conditions. However, there was no significant difference between the corrosion rate of the PT in DPBSS (CR = 1.9 ± 0.6 mm/year) and in MHBSS (CR = 2 ± 1.4 mm/year). The cell viability was assessed with human vein endothelial cells (HUVECs) via an indirect metabolic activity test (MTT assay). Due to the lower ion release of the PT condition, the cell viability increased significantly. Thus, nitrogen implantation can control the in vitro corrosion rate starting from the very first stage of the implantation, improving cell viability.
Collapse
Affiliation(s)
- Pedram Sotoudeh Bagha
- BiionixTM (Bionic Materials, Implants & Interfaces) Cluster, Department of Medicine, University of Central Florida College of Medicine, Orlando, FL 32827, USA
| | - Carlo Paternoster
- Lab Biomaterials and Bioengineering, CRC-I, Department of Mining, Metallurgical and Materials Engineering & CHU de Quebec Research Center, Regenerative Medicine, Laval University, Quebec City, QC G1V 0A6, Canada
| | - Mehrdad Khakbiz
- Department of Chemical and Biochemical Engineering, Rutgers, The State University of New Jersey, Piscataway, NJ 088854, USA
- Division of Biomedical Engineering, Faculty of New Sciences and Technologies, University of Tehran, Tehran 14395-1561, Iran
| | - Saeed Sheibani
- School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran 11155-4563, Iran
| | - Navid Gholami
- Department of Tissue Engineering and Applied Cell Sciences, School of Advanced Technologies in Medicine, Tehran University of Medical Sciences, Tehran 14177-55469, Iran
| | - Diego Mantovani
- Lab Biomaterials and Bioengineering, CRC-I, Department of Mining, Metallurgical and Materials Engineering & CHU de Quebec Research Center, Regenerative Medicine, Laval University, Quebec City, QC G1V 0A6, Canada
| |
Collapse
|
3
|
Microstructure and Mechanical Properties of Modified 316L Stainless Steel Alloy for Biomedical Applications Using Powder Metallurgy. MATERIALS 2022; 15:ma15082822. [PMID: 35454514 PMCID: PMC9027153 DOI: 10.3390/ma15082822] [Citation(s) in RCA: 3] [Impact Index Per Article: 1.5] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 12/22/2021] [Revised: 03/26/2022] [Accepted: 03/28/2022] [Indexed: 02/05/2023]
Abstract
AISI 316L stainless steel (SS) is one of the extensively used biomaterials to produce implants and medical devices. It provides a low-cost solution with ample mechanical properties, corrosion resistance, and biocompatibility compared to its counterpart materials. However, the implants made of this material are subjected to a short life span in human physiological conditions leading to the leaching of metal ions, thus limiting its use as a biomaterial. In this research, the addition of boron, titanium, and niobium with varying concentrations in the SS matrix has been explored. This paper explores the impact of material composition on modified SS alloy’s physical and mechanical properties. The study’s outcomes specify that the microhardness increases for all the alloy compositions, with a maximum increase of 64.68% for the 2 wt.% niobium added SS alloy. On the other hand, the tensile strength decreased to 297.40 MPa for the alloy containing 0.25 wt.% boron and 2 wt.% titanium additions compared to a tensile strength of 572.50 MPa for pure SS. The compression strength increased from 776 MPa for pure SS to 1408 MPa for the alloy containing niobium and titanium additions in equal concentrations.
Collapse
|
4
|
Ali S, Irfan M, Muhammad Niazi U, Rani AMA, Shah I, Legutko S, Rahman S, Jalalah M, Alsaiari MA, Glowacz A, AlKahtani FS. Synthesis, Surface Nitriding and Characterization of Ti-Nb Modified 316L Stainless Steel Alloy Using Powder Metallurgy. MATERIALS 2021; 14:ma14123270. [PMID: 34199244 PMCID: PMC8231788 DOI: 10.3390/ma14123270] [Citation(s) in RCA: 2] [Impact Index Per Article: 0.7] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 04/14/2021] [Revised: 06/07/2021] [Accepted: 06/09/2021] [Indexed: 11/16/2022]
Abstract
The powder metallurgy (PM) technique has been widely used for producing different alloy compositions by the addition of suitable reinforcements. PM is also capable of producing desireable mechanical and physical properties of the material by varying process parameters. This research investigates the addition of titanium and niobium in a 316L stainless steel matrix for potential use in the biomedical field. The increase of sintering dwell time resulted in simultaneous sintering and surface nitriding of compositions, using nitrogen as the sintering atmosphere. The developed alloy compositions were characterized using OM, FESEM, XRD and XPS techniques for quantification of the surface nitride layer and the nitrogen absorbed during sintering. The corrosion resistance and cytotoxicity assessments of the developed compositions were carried out in artificial saliva solution and human oral fibroblast cell culture, respectively. The results indicated that the nitride layer produced during sintering increased the corrosion resistance of the alloy and the developed compositions are non-cytotoxic. This newly developed alloy composition and processing technique is expected to provide a low-cost solution to implant manufacturing.
Collapse
Affiliation(s)
- Sadaqat Ali
- School of Mechanical & Manufacturing Engineering, National University of Sciences and Technology (NUST), H-12, Islamabad 44000, Pakistan
- Correspondence: (S.A.); (U.M.N.); (S.L.)
| | - Muhammad Irfan
- Electrical Engineering Department, College of Engineering, Najran University Saudi Arabia, Najran 61441, Saudi Arabia; (M.I.); (S.R.); (F.S.A.)
| | - Usama Muhammad Niazi
- Mechanical Engineering Department, National University of Technology, Islamabad 44000, Pakistan;
- Mechanical Engineering Department, National Skills University, Islamabad 44000, Pakistan
- Correspondence: (S.A.); (U.M.N.); (S.L.)
| | - Ahmad Majdi Abdul Rani
- Mechanical Engineering Department, Universiti Teknologi PETRONAS (UTP), Bandar Seri Iskandar 32610, Perak Darul Ridzuan, Malaysia;
| | - Imran Shah
- Mechanical Engineering Department, National University of Technology, Islamabad 44000, Pakistan;
| | - Stanislaw Legutko
- Faculty of Mechanical Engineering, Poznan University of Technology, 3 Piotrowo str., 60-965 Poznan, Poland
- Correspondence: (S.A.); (U.M.N.); (S.L.)
| | - Saifur Rahman
- Electrical Engineering Department, College of Engineering, Najran University Saudi Arabia, Najran 61441, Saudi Arabia; (M.I.); (S.R.); (F.S.A.)
| | - Mohammed Jalalah
- Promising Centre for Sensors and Electronic Devices (PCSED), Najran University Saudi Arabia, Najran 61441, Saudi Arabia;
| | - Mabkhoot A. Alsaiari
- Empty qaurter research unit, Chemistry department, college of Science and art at Sharurah, Najran University Saudi Arabia, Najran 61441, Saudi Arabia;
| | - Adam Glowacz
- Department of Automatic Control and Robotics, Faculty of Electrical Engineering, Automatics, Computer Science and Biomedical Engineering, AGH University of Science and Technology, al. A. Mickiewicza 30, 30-059 Kraków, Poland;
| | - Fahad Salem AlKahtani
- Electrical Engineering Department, College of Engineering, Najran University Saudi Arabia, Najran 61441, Saudi Arabia; (M.I.); (S.R.); (F.S.A.)
| |
Collapse
|
5
|
Abstract
Additive manufacturing (AM) processes have undergone significant progress in recent years, having been implemented in sectors as diverse as automotive, aerospace, electrical component manufacturing, etc. In the medical sector, different devices are printed, such as implants, surgical guides, scaffolds, tissue engineering, etc. Although nowadays some implants are made of plastics or ceramics, metals have been traditionally employed in their manufacture. However, metallic implants obtained by traditional methods such as machining have the drawbacks that they are manufactured in standard sizes, and that it is difficult to obtain porous structures that favor fixation of the prostheses by means of osseointegration. The present paper presents an overview of the use of AM technologies to manufacture metallic implants. First, the different technologies used for metals are presented, focusing on the main advantages and drawbacks of each one of them. Considered technologies are binder jetting (BJ), selective laser melting (SLM), electron beam melting (EBM), direct energy deposition (DED), and material extrusion by fused filament fabrication (FFF) with metal filled polymers. Then, different metals used in the medical sector are listed, and their properties are summarized, with the focus on Ti and CoCr alloys. They are divided into two groups, namely ferrous and non-ferrous alloys. Finally, the state-of-art about the manufacture of metallic implants with AM technologies is summarized. The present paper will help to explain the latest progress in the application of AM processes to the manufacture of implants.
Collapse
|
6
|
Optimization of Sintering Parameters of 316L Stainless Steel for In-Situ Nitrogen Absorption and Surface Nitriding Using Response Surface Methodology. Processes (Basel) 2020. [DOI: 10.3390/pr8030297] [Citation(s) in RCA: 6] [Impact Index Per Article: 1.5] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 02/03/2023] Open
Abstract
This research investigates the simultaneous sintering and surface nitriding of 316L stainless steel alloy using powder metallurgy method. The influence of sintering temperature and dwell time are investigated for maximum nitrogen absorption, densification and increased microhardness using response surface methodology (RSM). In this study, 316L stainless steel powder was compacted at 800 MPa and sintered at two different temperatures of 1150 and 1200 °C with varying dwell times of 1, 3, 5 and 8 h in nitrogen atmosphere. The sintered compacts were then characterized for their microstructure, densification, microhardness and nitrogen absorption. The results revealed that increased dwell time assisted nitrogen to diffuse into stainless steel matrix along with the creation of nitride layer onto the sample surface. The microhardness and density also increased with increasing dwell time. A densification of 7.575 g/cm3 and microhardness of 235 HV were obtained for the samples sintered at 1200 °C temperature with 8 h dwell time. The simultaneous sintering and surface nitriding technique developed in this research work can help in improving corrosion resistance of this material and controlling leaching of metal ions for its potential use in biomedical applications.
Collapse
|
7
|
Abstract
The developments in the field of rehabilitation are proceeding hand in hand with those of cybernetics, with the result of obtaining increasingly performing prostheses and rehabilitations for patients. The purpose of this work is to make a brief exposition of new technologies regarding composites materials that are used in the prosthetic and rehabilitative fields. Data collection took place on scientific databases, limited to a collection of data for the last five years, in order to present news on the innovative and actual materials. The results show that some of the most commonly used last materials are glass fibers and carbon fibers. Even in the robotics field, materials of this type are beginning to be used, thanks above all to the mechanical performances they offer. Surely these new materials, which offer characteristics similar to those in humans, could favor both the rehabilitation times of our patients, and also a better quality of life.
Collapse
|
8
|
The Influence of Nitrogen Absorption on Microstructure, Properties and Cytotoxicity Assessment of 316L Stainless Steel Alloy Reinforced with Boron and Niobium. Processes (Basel) 2019. [DOI: 10.3390/pr7080506] [Citation(s) in RCA: 11] [Impact Index Per Article: 2.2] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 01/09/2023] Open
Abstract
In the past, 316L stainless steel (SS) has been the material of choice for implant manufacturing. However, the leaching of nickel ions from the SS matrix limits its usefulness as an implant material. In this study, an efficient approach for controlling the leaching of ions and improving its properties is presented. The composition of SS was modified with the addition of boron and niobium, which was followed by sintering in nitrogen atmosphere for 8 h. The X-ray diffraction (XRD) results showed the formation of strong nitrides, indicating the diffusion of nitrogen into the SS matrix. The X-ray photoelectron spectroscopy (XPS) analysis revealed that a nitride layer was deposited on the sample surface, thereby helping to control the leaching of metal ions. The corrosion resistance of the alloy systems in artificial saliva solution indicated minimal weight loss, indicating improved corrosion resistance. The cytotoxicity assessment of the alloy system showed that the developed modified stainless steel alloys are compatible with living cells and can be used as implant materials.
Collapse
|