Biomaterial characterization of off-the-shelf decellularized porcine pericardial tissue for use in prosthetic valvular applications

Impact of the Different Chemical-Based Decellularization Protocols on the Properties of the Caprine Pericardium

PURPOSE

This study aims to decellularized caprine pericardium tissue with varied non-ionic surfactant and anionic detergent concentrations.

METHODS

Protocol A consists of 1%, 0.5%, and 0.25% (w/v) sodium dodecyl sulphate (SDS). Protocol B uses 1%, 0.5%, and 0.25% (w/v) Triton X-100. Protocol C comprised 0.5% SDS + 0.5% Triton X-100, 0.5% + 0.25%, and 0.25% SDS + 0.5% Triton X-100.

RESULTS

Protocol B left a few countable cells in the pericardium tissue, but treatments A and C removed all cells. DNA quantification also demonstrated that protocol B had the most leftover DNA after decellularization. The pericardium tissue treated with an equal combination of anionic detergent and non-ionic surfactant preserves the matrix. However, changing the anionic detergent-non-ionic surfactant ratio disrupted the microstructure. Protocol A decreased pericardium tissue secant modulus (p < 0.05). Protocol B-treated pericardium tissue matched native tissue secant modulus and ultimate tensile stress. Protocol C strengthened pericardium tissue.

CONCLUSION

The intact extracellular matrix and biomechanical properties like native tissues require optimal chemical doses and combinations.

Decellularization and characterization of camel pericardium as a new scaffold for tissue engineering and regenerative medicine

BACKGROUND

Valvular heart diseases (VHDs) have become prevalent in populations due to aging. Application of different biomaterials for cardiac valve regeneration and repair holds a great promise for treatment of VHD. Aortic valve replacement using tissue-engineered xenografts is a considered approach, and the pericardium of different species such as porcine and bovine has been studied over the last few years. It has been suggested that the animal origin can affect the outcomes of replacement.

METHODS

So, herein, we at first decellularized and characterized the camel pericardium (dCP), then characterized dCP with H&E staining, in vitro and in vivo biocompatibility and mechanical tests and compared it with decellularized bovine pericardium (dBP), to describe the potency of dCP as a new xenograft and bio scaffold.

RESULTS

The histological assays indicated less decluttering and extracellular matrix damage in dCP after decellularization compared to the dBP also dCP had higher Young Modulus (105.11), and yield stress (1.57  ±  0.45). We observed more blood vessels and also less inflammatory cells in the dCP sections after implantation.

CONCLUSIONS

In conclusion, the results of this study showed that the dCP has good capabilities not only for use in VHD treatment but also for other applications in tissue engineering and regenerative medicine.

Double crosslinking decellularized bovine pericardium of dialdehyde chondroitin sulfate and zwitterionic copolymer for bioprosthetic heart valves with enhanced antithrombogenic, anti-inflammatory and anti-calcification properties

Due to the increasing aging population and the advancements in transcatheter aortic valve replacement (TAVR), the use of bioprosthetic heart valves (BHVs) in patients diagnosed with valvular disease has increased substantially. Commercially available glutaraldehyde (GA) cross-linked biological valves suffer from reduced durability due to a combination of factors, including the high cell toxicity of GA, subacute thrombus, inflammation and calcification. In this study, oxidized chondroitin sulfate (OCS), a natural polysaccharide derivative, was used to replace GA to cross-link decellularized bovine pericardium (DBP), carrying out the first crosslinking of DBP to obtain OCS-BP. Subsequently, the zwitterion radical copolymerization system was introduced in situ to perform double cross-linking to obtain double crosslinked BHVs with biomimetic modification (P(APM/MPC)-OCS-BP). P(APM/MPC)-OCS-BP presented enhanced mechanical properties, collagen stability and enzymatic degradation resistance due to double crosslinking. The ex vivo AV-shunt assay and coagulation factors test suggested that P(APM/MPC)-OCS-BP exhibited excellent anticoagulant and antithrombotic properties due to the introduction of P(APM/MPC). P(APM/MPC)-OCS-BP also showed good HUVEC-cytocompatibility due to the substantial reduction of its residual aldehyde group. The subcutaneous implantation also demonstrated that P(APM/MPC)-OCS-BP showed a weak inflammatory response due to the anti-inflammatory effect of OCS. Finally, in vivo and in vitro results revealed that P(APM/MPC)-OCS-BP exhibited an excellent anti-calcification property. In a word, this simple cooperative crosslinking strategy provides a novel solution to obtain BHVs with good mechanical properties, and HUVEC-cytocompatibility, anti-coagulation, anti-inflammatory and anti-calcification properties. It might be a promising alternative to GA-fixed BP and exhibited good prospects in clinical applications.

Hydrogel-polyurethane fiber composites with enhanced microarchitectural control for heart valve replacement

Polymeric heart valves offer the potential to overcome the limited durability of tissue based bioprosthetic valves and the need for anticoagulant therapy of mechanical valve replacement options. However, developing a single-phase material with requisite biological properties and target mechanical properties remains a challenge. In this study, a composite heart valve material was developed where an electrospun mesh provides tunable mechanical properties and a hydrogel coating confers an antifouling surface for thromboresistance. Key biological responses were evaluated in comparison to glutaraldehyde-fixed pericardium. Platelet and bacterial attachment were reduced by 38% and 98%, respectively, as compared to pericardium that demonstrated the antifouling nature of the hydrogel coating. There was also a notable reduction (59%) in the calcification of the composite material as compared to pericardium. A custom 3D-printed hydrogel coating setup was developed to make valve composites for device-level hemodynamic testing. Regurgitation fraction (9.6 ± 1.8%) and effective orifice area (1.52 ± 0.34 cm2 ) met ISO 5840-2:2021 requirements. Additionally, the mean pressure gradient was comparable to current clinical bioprosthetic heart valves demonstrating preliminary efficacy. Although the hemodynamic properties are promising, it is anticipated that the random microarchitecture will result in suboptimal strain fields and peak stresses that may accelerate leaflet fatigue and degeneration. Previous computational work has demonstrated that bioinspired fiber microarchitectures can improve strain homogeneity of valve materials toward improving durability. To this end, we developed advanced electrospinning methodologies to achieve polyurethane fiber microarchitectures that mimic or exceed the physiological ranges of alignment, tortuosity, and curvilinearity present in the native valve. Control of fiber alignment from a random fiber orientation at a normalized orientation index (NOI) 14.2 ± 6.9% to highly aligned fibers at a NOI of 85.1 ± 1.4%. was achieved through increasing mandrel rotational velocity. Fiber tortuosity and curvilinearity in the range of native valve features were introduced through a post-spinning annealing process and fiber collection on a conical mandrel geometry, respectively. Overall, these studies demonstrate the potential of hydrogel-polyurethane fiber composite as a heart valve material. Future studies will utilize the developed advanced electrospinning methodologies in combination with model-directed fabrication toward optimizing durability as a function of fiber microarchitecture.

Comparison of Bovine- and Porcine-Derived Decellularized Biomaterials: Promising Platforms for Tissue Engineering Applications

Animal-derived xenogeneic biomaterials utilized in different surgeries are promising for various applications in tissue engineering. However, tissue decellularization is necessary to attain a bioactive extracellular matrix (ECM) that can be safely transplanted. The main objective of the present study is to assess the structural integrity, biocompatibility, and potential use of various acellular biomaterials for tissue engineering applications. Hence, a bovine pericardium (BP), porcine pericardium (PP), and porcine tunica vaginalis (PTV) were decellularized using a Trypsin, Triton X (TX), and sodium dodecyl sulfate (SDS) (Trypsin + TX + SDS) protocol. The results reveal effective elimination of the cellular antigens with preservation of the ECM integrity confirmed via staining and electron microscopy. The elasticity of the decellularized PP (DPP) was markedly (p < 0.0001) increased. The tensile strength of DBP, and DPP was not affected after decellularization. All decellularized tissues were biocompatible with persistent growth of the adipose stem cells over 30 days. The staining confirmed cell adherence either to the peripheries of the materials or within their matrices. Moreover, the in vivo investigation confirmed the biocompatibility and degradability of the decellularized scaffolds. Conclusively, Trypsin + TX + SDS is a successful new protocol for tissue decellularization. Moreover, decellularized pericardia and tunica vaginalis are promising scaffolds for the engineering of different tissues with higher potential for the use of DPP in cardiovascular applications and DBP and DPTV in the reconstruction of higher-stress-bearing abdominal walls.

Preparation of extracellular matrix of fish swim bladders by decellularization with supercritical carbon dioxide

Fish swim bladders used to be considered as byproducts or waste in fishery; however, they are potential materials for biological medicine with abundant collagen. In this work, an efficient noncytotoxic decellularization process using sodium dodecyl sulfate (SDS) ternary system assisted with supercritical carbon dioxide (scCO2) as the green extraction fluid and ethanol (ET) as the cosolvent has been developed to harvest acellular fish swim bladders (AFSBs). The experimental results show that the tissue treated by SDS assisted with scCO2 and ethanol at 37 °C and 25 MPa can be decellularized thoroughly and maintains intact fibers and uniform pore distribution, which resulting in a tensile strength of 5.61 MPa and satisfactory biocompatibility. Meanwhile, the residual SDS content in scCO2/SDS/ET ternary system is 0.0122% which is significantly lower than it in scCO2/SDS system due to the enhanced mass transfer rate of SDS in tissues by scCO2 with ethanol. The synergy between SDS and ethanol can enhance the diffusion coefficient and the solubility of SDS in scCO2, which reduced the contact time between SDS and tissues. Meaningfully, the results obtained in this work can not only provide a novel strategy to produce acellular matrix with superior properties, but also offer a further understanding of the decellularization through scCO2 extraction processing with the synergy of suitable detergent/cosolvent.

Biological Scaffolds for Congenital Heart Disease

Congenital heart disease (CHD) is the most predominant birth defect and can require several invasive surgeries throughout childhood. The absence of materials with growth and remodelling potential is a limitation of currently used prosthetics in cardiovascular surgery, as well as their susceptibility to calcification. The field of tissue engineering has emerged as a regenerative medicine approach aiming to develop durable scaffolds possessing the ability to grow and remodel upon implantation into the defective hearts of babies and children with CHD. Though tissue engineering has produced several synthetic scaffolds, most of them failed to be successfully translated in this life-endangering clinical scenario, and currently, biological scaffolds are the most extensively used. This review aims to thoroughly summarise the existing biological scaffolds for the treatment of paediatric CHD, categorised as homografts and xenografts, and present the preclinical and clinical studies. Fixation as well as techniques of decellularisation will be reported, highlighting the importance of these approaches for the successful implantation of biological scaffolds that avoid prosthetic rejection. Additionally, cardiac scaffolds for paediatric CHD can be implanted as acellular prostheses, or recellularised before implantation, and cellularisation techniques will be extensively discussed.

In vitro evaluation of crosslinked bovine pericardium as potential scaffold for the oral cavity

BACKGROUND

Bovine pericardium (BP) is a scaffold widely used in soft tissues regeneration; however, its calcification in contact with glutaraldehyde, represent an opportunity for its application in hard tissues, such as bone in the oral cavity.

OBJECTIVE

To develop and to characterize decellularized and glutaraldehyde-crosslinked bovine pericardium (GC-BP) as a potential scaffold for guided bone regeneration GBR.

METHODS

BP samples from healthy animals of the bovine zebu breed were decellularized and crosslinked by digestion with detergents and glutaraldehyde respectively. The resulting cell-free scaffold was physical, chemical, mechanical, and biologically characterized thought hematoxylin and eosin staining, DNA quantification, scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), uniaxial tensile test, cell viability and live and dead assay in cultures of dental pulp stem cells (DPSCs).

RESULTS

The decellularization and crosslinking of BP appeared to induce conformational changes of the CLG molecules, which led to lower mechanical properties at the GC-BP scaffold, at the same time that promoted cell adhesion and viability of DPSCs.

CONCLUSION

This study suggests that the decellularized and GC-BP is a scaffold with the potential to be used promoting DPSCs recruitment, which has a great impact on the dental area.

Small intestinal submucosa-derived extracellular matrix as a heterotopic scaffold for cardiovascular applications

Structural cardiac lesions are often surgically repaired using prosthetic patches, which can be biological or synthetic. In the current clinical scenario, biological patches derived from the decellularization of a xenogeneic scaffold are gaining more interest as they maintain the natural architecture of the extracellular matrix (ECM) after the removal of the native cells and remnants. Once implanted in the host, these patches can induce tissue regeneration and repair, encouraging angiogenesis, migration, proliferation, and host cell differentiation. Lastly, decellularized xenogeneic patches undergo cell repopulation, thus reducing host immuno-mediated response against the graft and preventing device failure. Porcine small intestinal submucosa (pSIS) showed such properties in alternative clinical scenarios. Specifically, the US FDA approved its use in humans for urogenital procedures such as hernia repair, cystoplasties, ureteral reconstructions, stress incontinence, Peyronie's disease, penile chordee, and even urethral reconstruction for hypospadias and strictures. In addition, it has also been successfully used for skeletal muscle tissue reconstruction in young patients. However, for cardiovascular applications, the results are controversial. In this study, we aimed to validate our decellularization protocol for SIS, which is based on the use of Tergitol 15 S 9, by comparing it to our previous and efficient method (Triton X 100), which is not more available in the market. For both treatments, we evaluated the preservation of the ECM ultrastructure, biomechanical features, biocompatibility, and final bioinductive capabilities. The overall analysis shows that the SIS tissue is macroscopically distinguishable into two regions, one smooth and one wrinkle, equivalent to the ultrastructure and biochemical and proteomic profile. Furthermore, Tergitol 15 S 9 treatment does not modify tissue biomechanics, resulting in comparable to the native one and confirming the superior preservation of the collagen fibers. In summary, the present study showed that the SIS decellularized with Tergitol 15 S 9 guarantees higher performances, compared to the Triton X 100 method, in all the explored fields and for both SIS regions: smooth and wrinkle.

Dual-crosslinked bioprosthetic heart valves prepared by glutaraldehyde crosslinked pericardium and poly-2-hydroxyethyl methacrylate exhibited improved antithrombogenicity and anticalcification properties

Bioprosthetic heart valves (BHVs) have been widely used due to the revolutionary transcatheter aortic valve replacement (TAVR) techniques but suffer from a limited lifespan. Previous modification methods of BHVs mainly rely on glutaraldehyde precrosslinking and subsequent modification. In this study, we have engineered a Poly-2-Hydroxyethyl methacrylate (pHEMA) coated BHV based on co-crosslinking and co-polymerization strategies. Our BHV overcomes previous limitations of glutaraldehyde prefixation by introducing free molecules before crosslinking to achieve the crosslinking and allyl moiety immobilization simultaneously. Decellularized porcine pericardium and 2-Amino-4-pentenoic acid (APA) are firstly co-crosslinked by glutaraldehyde to obtain alkenylated porcine pericardium (APA-PP), then APA-PP is copolymerized with hydrophilic monomer 2-Hydroxyethyl methacrylate (HEMA) to prepare pHEMA grafted porcine pericardium (HEMA-PP). Compared with traditional glutaraldehyde crosslinked pericardium (GA), HEMA-PP exhibits decreased cytotoxicity and significantly increased endothelialial cells proliferation (7-folds higher than GA after 3-day incubation). In vitro and ex vivo hemocompatibility studies demonstrate the superiority of HEMA-PP in anti-thrombogenicity, where the platelet adhesion decreased by levels of approximately 89% compared to GA. Moreover, HEMA-PP maintains structurally stable with a low level of calcification in the subcutaneous model. The hydrodynamic performance and durability are proven to meet the requirements of ISO 5840-3. Altogether, HEMA-PP may have the potential for future clinical application. STATEMENT OF SIGNIFICANCE: Currently, bioprosthetic heart valves (BHVs) have drawbacks including cytotoxicity, calcification and thrombosis, which would accelerate structural valvular degeneration and limit the service life of BHVs. We developed a new modification strategy that could simultaneously improve the biocompatibility, anti-calcification and anti-thrombotic properties of BHVs. Moreover, the appropriate durability and hydrodynamic property demonstrated the potential of our strategy for clinical application. This work will potentially prolong the service life of BHVs and provide new insight for the modification of BHVs.

Decellularized Extracellular Matrix Scaffolds for Cardiovascular Tissue Engineering: Current Techniques and Challenges

Cardiovascular diseases are the leading cause of global mortality. Over the past two decades, researchers have tried to provide novel solutions for end-stage heart failure to address cardiac transplantation hurdles such as donor organ shortage, chronic rejection, and life-long immunosuppression. Cardiac decellularized extracellular matrix (dECM) has been widely explored as a promising approach in tissue-regenerative medicine because of its remarkable similarity to the original tissue. Optimized decellularization protocols combining physical, chemical, and enzymatic agents have been developed to obtain the perfect balance between cell removal, ECM composition, and function maintenance. However, proper assessment of decellularized tissue composition is still needed before clinical translation. Recellularizing the acellular scaffold with organ-specific cells and evaluating the extent of cardiomyocyte repopulation is also challenging. This review aims to discuss the existing literature on decellularized cardiac scaffolds, especially on the advantages and methods of preparation, pointing out areas for improvement. Finally, an overview of the state of research regarding the application of cardiac dECM and future challenges in bioengineering a human heart suitable for transplantation is provided.

Development of Antithrombogenic ECM-Based Nanocomposite Heart Valve Leaflets

Thrombogenicity, which is commonly encountered in artificial heart valves after replacement surgeries, causes valvular failure. Even life-long anticoagulant drug use may not be sufficient to prevent thrombogenicity. In this study, it was aimed to develop a heart valve construct with antithrombogenic properties and suitable mechanical strength by combining multiwalled carbon nanotubes within a decellularized bovine pericardium. In this context, the decellularization process was performed by using the combination of freeze–thawing and sodium dodecyl sulfate (SDS). Evaluation of decellularization efficiency was determined by histology (Hematoxylin and Eosin, DAPI and Masson’s Trichrome) and biochemical (DNA, sGAG and collagen) analyses. After the decellularization process of the bovine pericardium, composite pericardial tissues were prepared by incorporating −COOH-modified multiwalled carbon nanotubes (MWCNTs). Characterization of MWCNT incorporation was performed by ATR-FTIR, TGA, and mechanical analysis, while SEM and AFM were used for morphological evaluations. Thrombogenicity assessments were studied by platelet adhesion test, Calcein-AM staining, kinetic blood clotting, hemolysis, and cytotoxicity analyses. As a result of this study, the composite pericardial material revealed improved mechanical and thermal stability and hemocompatibility in comparison to decellularized pericardium, without toxicity. Approximately 100% success is achieved in preventing platelet adhesion. In addition, kinetic blood-coagulation analysis demonstrated a low rate and slow coagulation kinetics, while the hemolysis index was below the permissible limit for biomaterials.

Tissue-engineered composite tracheal grafts create mechanically stable and biocompatible airway replacements

We tested composite tracheal grafts (CTG) composed of a partially decellularized tracheal graft (PDTG) combined with a 3-dimensional (3D)-printed airway splint for use in long-segment airway reconstruction. CTG is designed to recapitulate the 3D extracellular matrix of the trachea with stable mechanical properties imparted from the extraluminal airway splint. We performed segmental orthotopic tracheal replacement in a mouse microsurgical model. MicroCT was used to measure graft patency. Tracheal neotissue formation was quantified histologically. Airflow dynamic properties were analyzed using computational fluid dynamics. We found that CTG are easily implanted and did not result in vascular erosion, tracheal injury, or inflammation. Graft epithelialization and endothelialization were comparable with CTG to control. Tracheal collapse was absent with CTG. Composite tracheal scaffolds combine biocompatible synthetic support with PDTG, supporting the regeneration of host epithelium while maintaining graft structure.

A Biohybrid Material With Extracellular Matrix Core and Polymeric Coating as a Cell Honing Cardiovascular Tissue Substitute

Objective

To investigate the feasibility of a hybrid material in which decellularized pericardial extracellular matrix is functionalized with polymeric nanofibers, for use as a cardiovascular tissue substitute.

Background

A cardiovascular tissue substitute, which is gradually resorbed and is replaced by host's native tissue, has several advantages. Especially in children and young adults, a resorbable material can be useful in accommodating growth, but also enable rapid endothelialization that is necessary to avoid thrombotic complications. In this study, we report a hybrid material, wherein decellularized pericardial matrix is functionalized with a layer of polymeric nanofibers, to achieve the mechanical strength for implantation in the cardiovascular system, but also have enhanced cell honing capacity.

Methods

Pericardial sacs were decellularized with sodium deoxycholate, and polycaprolactone-chitosan fibers were electrospun onto the matrix. Tissue-polymer interaction was evaluated using spectroscopic methods, and the mechanical properties of the individual components and the hybrid material were quantified. In-vitro blood flow loop studies were conducted to assess hemocompatibility and cell culture methods were used to assess biocompatibility.

Results

Encapsulation of the decellularized matrix with 70 μm thick matrix of polycaprolactone-chitosan nanofibers, was feasible and reproducible. Spectroscopy of the cross-section depicted new amide bond formation and C–O–C stretch at the interface. An average peel strength of 56.13 ± 11.87 mN/mm2 was measured, that is sufficient to withstand a high shear of 15 dynes/cm2 without delamination. Mechanical strength and extensibility ratio of the decellularized matrix alone were 18,000 ± 4,200 KPa and 0.18 ± 0.03% whereas that of the hybrid was higher at 20,000 ± 6,600 KPa and 0.35 ± 0.20%. Anisotropy index and stiffness of the biohybrid were increased as well. Neither thrombus formation, nor platelet adhesion or hemolysis was measured in the in-vitro blood flow loop studies. Cellular adhesion and survival were adequate in the material.

Conclusion

Encapsulating a decellularized matrix with a polymeric nanofiber coating, has favorable attributes for use as a cardiovascular tissue substitute.

Evaluation of Pericardial Tissues from Assorted Species as a Tissue-Engineered Heart Valve Material

Decellularized pericardial tissue is a strong candidate for a TEHV material as ECM is present to guide cellular infiltration and fixed porcine and bovine pericardial tissue have existing use in bioprosthetic heart valves. In this work, we compare the mechanical and microstructural properties of decellularized-sterilized (DS) porcine, bovine, and bison pericardial tissues with respect to use as a TEHV. H&E staining was used to verify removal of cellular content post-decellularization and to evaluate collagen fiber structure. Additionally, uniaxial and biaxial tension testing were used to compare mechanical performance and, for the latter, acquire constitutive model parameters for subsequent finite element (FE) modeling. H&E staining revealed complete removal of cellular content and good collagen fiber structure. Tensile testing showed comparable mechanical strength between the three DS pericardial tissues and considerably stronger mechanical properties compared to native tissues. Bovine and bison DS pericardial tissues showed the strongest mechanical performance in the FE models with bison demonstrating the overall best mechanical characteristics. The increased thickness of bovine and bison tissues coupled with the strong mechanical behavior and ECM structure indicates that these materials will be resistant to damage until sufficient cellular infiltration has occurred such that damaged tissue can be repaired.

Characterization of Composite Nano-Bioscaffolds Based on Collagen and Supercritical Fluids-Assisted Decellularized Fibrous Extracellular Matrix

Nano-bioscaffolds obtained from decellularized tissues have been employed in several medical applications. Nano-bioscaffolds could provide structural support for cell attachment and a suitable environment with sufficient porosity for cell growth and proliferation. In this study, a new combined method constitutes a decellularization protocol to remove the tissue and cellular molecules from porcine dermis for preparation of nano-bioscaffolds with fibrous extracellular matrix via pre- and post-treatment of supercritical fluids. The supercritical fluids-assisted nano-bioscaffolds were characterized by peptide identification, infrared spectrum of absorption, morphology, histological observations, DNA quantification, and hemocompatibility. Further, the resulting nano-bioscaffolds could be employed to obtain new cross-linked composite nano-bioscaffold containing collagen and acellular matrix.

In Vitro Evaluation of Acellular Collagen Matrices Derived from Porcine Pericardium: Influence of the Sterilization Method on Its Biological Properties

The aim of this study were characterize acellular collagen matrices derived from porcine pericardium (PP) and to evaluate their properties after sterilization by ethylene oxide and gamma ray. PP matrices were subjected to alkaline hydrolysis (AH), and samples were characterized for biological stability, membrane thickness measurements, differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). Subsequently, the matrices were frozen, lyophilized and sterilized by ethylene oxide or gamma radiation. For in vitro assays, CHO-K1 cell culture was used and evaluated for cytotoxicity, clonogenic survival assay, genotoxicity and mutagenicity. Analysis of variance (ANOVA) was used, followed by Dunnett's post-test, with a significance level of 5%. After AH, there was no significant change in matrix thickness. The relative biodegradability of the material after implantation was observed. Morphology and dimensions had small changes after AH. As for cell viability, none of the tested matrices showed a statistically significant difference (p > 0.05; Dunnett) regardless of the sterilization method. Furthermore, it was found that PP matrices did not interfere with the proliferation capacity of CHO-K1 cells (p > 0.05; Dunnett). As for genotoxicity, when sterilized with ethylene oxide (NP, P12 and P24), it showed genotoxic potential, but it was not genotoxic when sterilized by gamma radiation. No mutagenic effects were observed in either group. PP-derived collagen matrices hydrolyzed at different times were not cytotoxic. It is concluded that the best method of sterilization is through gamma radiation, since no significant changes were observed in the properties of the PP matrices.

Generation of glycans depleted decellularized porcine pericardium, using digestive enzymatic supplements and enzymatic mixtures for food industry

BACKGROUND

Xenogeneic pericardium has been used largely for various applications in cardiovascular surgery. Nevertheless, xenogeneic pericardial patches fail mainly due to their antigenic components. The xenoantigens identified as playing a major role in recipient immune response are the Galα1-3Gal (α-Gal) epitope, the non-human sialic acid N-glycolylneuraminic acid (Neu5Gc), and the porcine SDa antigen, associated with both proteins and lipids. The reduction in glycans from porcine pericardium might hinder or reduce the immunogenicity of xenogeneic scaffolds.

METHODS

Decellularized porcine pericardia were further treated at different time points and dilutions with digestive enzymatic supplements and enzymatic mixtures applied for food industry, for the removal of potentially immunogenic carbohydrates. Carbohydrates removal was investigated using up to 8 different lectin stains for the identification of N- and O-glycosylations, as well as glycolipids. Histoarchitectural changes in the ECM were assessed using Elastica van Gieson stain, whereas changes in mechanical properties were investigated via uniaxial tensile test and burst pressure test.

RESULTS

Tissues after enzymatic treatments showed a dramatic decrease in lectin stainings in comparison to tissues which were only decellularized. Histological assessment revealed cell-nuclei removal after decellularization. Some of the enzymatic treatments induced elastic lamellae disruption. Tissue strength decreased after enzymatic treatment; however, treated tissues showed values of burst pressure higher than physiological transvalvular pressures.

CONCLUSIONS

The application of these enzymatic treatments for tissue deglycosylation is totally novel, low cost, and appears to be very efficient for glycan removal. The immunogenic potential of treated tissues will be further investigated in subsequent studies, in vitro and in vivo.

Customized 3D printed bioreactors for decellularization-High efficiency and quality on a budget

Decellularization (DC) of biomaterials with bioreactors is widely used to produce scaffolds for tissue engineering. This study uses 3D printing to develop efficient but low-cost DC bioreactors. Two bioreactors were developed to decellularize pericardial patches and vascular grafts. Flow profiles and pressure distribution inside the bioreactors were optimized by steady-state computational fluid dynamics (CFD) analysis. Printing materials were evaluated by cytotoxicity assessment. Following evaluation, all parts of the bioreactors were 3D printed in a commercial fused deposition modeling printer. Samples of bovine pericardia and porcine aortae were decellularized using established protocols. An immersion and agitation setup was used as a control. With histological assessment, DNA quantification and biomechanical testing treatment effects were evaluated. CFD analysis of the pericardial bioreactor revealed even flow and pressure distribution in between all pericardia. The CFD analysis of the vessel bioreactor showed increased intraluminal flow rate and pressure compared to the vessel's outside. Cytotoxicity assessment of the used printing material revealed no adverse effect on the tissue. Complete DC was achieved for all samples using the 3D printed bioreactors while DAPI staining revealed residual cells in aortic vessels of the control group. Histological analysis showed no structural changes in the decellularized samples. Additionally, biomechanical properties exhibited no significant change compared to native samples. This study presents a novel approach to manufacturing highly efficient and low budget 3D printed bioreactors for the DC of biomaterials. When compared to standard protocols, the bioreactors offer a cost effective, fast, and reproducible approach, which vastly improves the DC results.

Crosslinking porcine aortic valve by radical polymerization for the preparation of BHVs with improved cytocompatibility, mild immune response, and reduced calcification

Over one million artificial heart valve transplantations are performed each year due to valvular stenosis or regurgitation. Among them, bioprosthetic heart valves (BHVs) are increasingly being used because of the absence of the need for lifelong anticoagulation. Almost all of the commercial BHVs are treated with Glutaraldehyde (GLUT). As GLUT-treated BHVs are prone to calcification and structural degradation, their durability is greatly reduced with a service life of only 12-15 years. The physiological structure and mechanical properties of the porcine aortic valve (PAV) are closer to that of a human heart valve, so in this study, PAV is used as the model to explore the comprehensive properties of the prepared BHVs by radical polymerization crosslinking method. We found that PAV treated by radical polymerization crosslinking method showed similar ECM stability and biaxial mechanical properties with GLUT-treated PAV. However, radical polymerization crosslinked PAV exhibited better cytocompatibility and endothelialization potential in vitro cell experiment as better anticalcification potential and reduced immune response than GLUT-treated PAV through subcutaneous animal experiments in rats. To conclude, a novel crosslinking method of non-glutaraldehyde fixation of xenogeneic tissues for the preparation of BHVs is expected.

Sterilization and disinfection methods for decellularized matrix materials: Review, consideration and proposal

Sterilization is the process of killing all microorganisms, while disinfection is the process of killing or removing all kinds of pathogenic microorganisms except bacterial spores. Biomaterials involved in cell experiments, animal experiments, and clinical applications need to be in the aseptic state, but their physical and chemical properties as well as biological activities can be affected by sterilization or disinfection. Decellularized matrix (dECM) is the low immunogenicity material obtained by removing cells from tissues, which retains many inherent components in tissues such as proteins and proteoglycans. But there are few studies concerning the effects of sterilization or disinfection on dECM, and the systematic introduction of sterilization or disinfection for dECM is even less. Therefore, this review systematically introduces and analyzes the mechanism, advantages, disadvantages, and applications of various sterilization and disinfection methods, discusses the factors influencing the selection of sterilization and disinfection methods, summarizes the sterilization and disinfection methods for various common dECM, and finally proposes a graphical route for selecting an appropriate sterilization or disinfection method for dECM and a technical route for validating the selected method, so as to provide the reference and basis for choosing more appropriate sterilization or disinfection methods of various dECM.

•

Asepsis is the prerequisite for the experiment and application of biomaterials.

•

Sterilization or disinfection affects physic-chemical properties of biomaterials.

•

Mechanism, advantages and disadvantages of sterilization or disinfection methods.

•

Factors influencing the selection of sterilization or disinfection methods.

•

Selection of sterilization or disinfection methods for decellularized matrix.

Bioengineered percutaneous heart valves for transcatheter aortic valve replacement: a comparative evaluation of decellularised bovine and porcine pericardia

Glutaraldehyde-treated, surgical bioprosthetic heart valves undergo structural degeneration within 10-15 years of implantation. Analogous preliminary results were disclosed for percutaneous heart valves (PHVs) realized with similarly-treated tissues. To improve long-term performance, decellularised scaffolds can be proposed as alternative fabricating biomaterials. The aim of this study was to evaluate whether bovine and porcine decellularised pericardia could be utilised to manufacture bioengineered percutaneous heart valves (bioPHVs) with adequate hydrodynamic performance and leaflet resistance to crimping damage. BioPHVs were fabricated by mounting acellular pericardia onto commercial stents. Independently from the pericardial species used for valve fabrication, bioPHVs satisfied the minimum hydrodynamic performance criteria set by ISO 5840-3 standards and were able to withstand a large spectrum of cardiac output conditions, also during extreme backpressure, without severe regurgitation, especially in the case of the porcine group. No macroscopic or microscopic leaflet damage was detected following bioPHV crimping. Bovine and porcine decellularized pericardia are both suitable alternatives to glutaraldehyde-treated tissues. Between the two types of pericardial species tested, the porcine tissue scaffold might be preferable to fabricate advanced PHV replacements for long-term performance. CONDENSED ABSTRACT: Current percutaneous heart valve replacements are formulated with glutaraldehyde-treated animal tissues, prone to structural degeneration. In order to improve long-term performance, bovine and porcine decellularised pericardia were utilised to manufacture bioengineered replacements, which demonstrated adequate hydrodynamic behaviour and resistance to crimping without leaflet architectural alteration.

FRESH 3D Bioprinting a Full-Size Model of the Human Heart

Recent advances in embedded three-dimensional (3D) bioprinting have expanded the design space for fabricating geometrically complex tissue scaffolds using hydrogels with mechanical properties comparable to native tissues and organs in the human body. The advantage of approaches such as Freeform Reversible Embedding of Suspended Hydrogels (FRESH) printing is the ability to embed soft biomaterials in a thermoreversible support bath at sizes ranging from a few millimeters to centimeters. In this study, we were able to expand this printable size range by FRESH bioprinting a full-size model of an adult human heart from patient-derived magnetic resonance imaging (MRI) data sets. We used alginate as the printing biomaterial to mimic the elastic modulus of cardiac tissue. In addition to achieving high print fidelity on a low-cost printer platform, FRESH-printed alginate proved to create mechanically tunable and suturable models. This demonstrates that large-scale 3D bioprinting of soft hydrogels is possible using FRESH and that cardiac tissue constructs can be produced with potential future applications in surgical training and planning.

Bovine Pericardium of High Fibre Dispersion Has High Fatigue Life and Increased Collagen Content; Potentially an Untapped Source of Heart Valve Leaflet Tissue

Bioprosthetic heart valves (BHVs) are implanted in aortic valve stenosis patients to replace the native, dysfunctional valve. Yet, the long-term performance of the glutaraldehyde-fixed bovine pericardium (GLBP) leaflets is known to reduce device durability. The aim of this study was to investigate a type of commercial-grade GLBP which has been over-looked in the literature to date; that of high collagen fibre dispersion (HD). Under uniaxial cyclic loading conditions, it was observed that the fatigue behaviour of HD GLBP was substantially equivalent to GLBP in which the fibres are highly aligned along the loading direction. It was also found that HD GLBP had a statistically significant 9.5% higher collagen content when compared to GLBP with highly aligned collagen fibres. The variability in diseased BHV delivery sites results in unpredictable and complex loading patterns across leaflets in vivo. This study presents the possibility of a shift from the traditional choice of circumferentially aligned GLBP leaflets, to that of high fibre dispersion arrangements. Characterised by its high fatigue life and increased collagen content, in addition to multiple fibre orientations, GLBP of high fibre dispersion may provide better patient outcomes under the multi-directional loading to which BHV leaflets are subjected in vivo.

Characterization of biomaterials intended for use in the nucleus pulposus of degenerated intervertebral discs

Biomaterials for regeneration of the intervertebral disc must meet complex requirements conforming to biological, mechanical and clinical demands. Currently no consensus on their characterization exists. It is crucial to identify parameters and their method of characterization for accurate assessment of their potential efficacy, keeping in mind the translation towards clinical application. This review systematically analyses the characterization techniques of biomaterial systems that have been used for nucleus pulposus (NP) restoration and regeneration. Substantial differences in the approach towards assessment became evident, hindering comparisons between different materials with respect to their suitability for NP restoration and regeneration. We have analysed the current approaches and identified parameters necessary for adequate biomaterial characterization, with the clinical goal of functional restoration and biological regeneration of the NP in mind. Further, we provide guidelines and goals for their measurement. STATEMENT OF SIGNIFICANCE: Biomaterials intended for restoration of regeneration of the nucleus pulposus within the intervertebral disc must meet biological, biomechanical and clinical demands. Many materials have been investigated, but a lack of consensus on which parameters to evaluate leads to difficulties in comparing materials as well as mostly partial characterization of the materials in question. A gap between current methodology and clinically relevant and meaningful characterization is prevalent. In this article, we identify necessary methods and their implementation for complete biomaterial characterization in the context of clinical applicability. This will allow for a more unified approach to NP-biomaterials research within the field as a whole and enable comparative analysis of novel materials yet to be developed.

A preliminary study on the development of a novel biomatrix by decellularization of bovine spinal meninges for tissue engineering applications

Here, we aim at developing a novel biomatrix from decellularized bovine spinal meninges for tissue engineering and regenerative medicine applications. Within this concept, the bovine spinal meninges were decellularized using 1% Triton X-100 for 48 h, and residual nuclear content was determined with double-strand DNA content analysis and agarose gel electrophoresis. The major matrix components such as sulfated GAGs and collagen before and after the decellularization process were analyzed with DMMB, hydroxyproline assay and SDS-PAGE. Subsequently, the native bovine spinal meninges (nBSM) and decellularized BSM (dBSM) were physiochemically characterized via ATR-FTIR spectroscopy, TGA, DMA and tensile strength test. The dsDNA content in the nBSM was 153.39 ± 53.93 ng/mg dry weight, versus in the dBSM was 39.47 ± 4.93 ng/mg (n = 3) dry weight and DNA fragments of more than 200 bp in length were not detected in the dBSM by agarose gel electrophoresis. The sulfated GAGs contents for nBSM and dBSM were observed to be 10.87 ± 1.2 and 11.42 ± 2.01 μg/mg dry weight, respectively. The maximum strength of dBSM in dry and wet conditions was found to be 19.67 ± 0.21 MPa and 13.97 ± 0.17 MPa, while nBSM (dry) was found to be 26.26 ± 0.28 MPa. MTT, SEM, and histology results exhibited that the cells attached to the surface of dBSM, and proliferated on the dBSM. In conclusion, the in vitro preliminary study has demonstrated that the dBSM might be a proper and new bioscaffold for tissue engineering and regenerative medicine applications.

FLIm and Raman Spectroscopy for Investigating Biochemical Changes of Bovine Pericardium upon Genipin Cross-Linking

Biomaterials used in tissue engineering and regenerative medicine applications benefit from longitudinal monitoring in a non-destructive manner. Label-free imaging based on fluorescence lifetime imaging (FLIm) and Raman spectroscopy were used to monitor the degree of genipin (GE) cross-linking of antigen-removed bovine pericardium (ARBP) at three incubation time points (0.5, 1.0, and 2.5 h). Fluorescence lifetime decreased and the emission spectrum redshifted compared to that of uncross-linked ARBP. The Raman signature of GE-ARBP was resonance-enhanced due to the GE cross-linker that generated new Raman bands at 1165, 1326, 1350, 1380, 1402, 1470, 1506, 1535, 1574, 1630, 1728, and 1741 cm-1. These were validated through density functional theory calculations as cross-linker-specific bands. A multivariate multiple regression model was developed to enhance the biochemical specificity of FLIm parameters fluorescence intensity ratio (R2 = 0.92) and lifetime (R2 = 0.94)) with Raman spectral results. FLIm and Raman spectroscopy detected biochemical changes occurring in the collagenous tissue during the cross-linking process that were characterized by the formation of a blue pigment which affected the tissue fluorescence and scattering properties. In conclusion, FLIm parameters and Raman spectroscopy were used to monitor the degree of cross-linking non-destructively.

Curcumin-crosslinked acellular bovine pericardium for the application of calcification inhibition heart valves

Glutaraldehyde (GA) crosslinked bovine or porcine pericardium tissues exhibit high cell toxicity and calcification in the construction of bioprosthetic valves, which accelerate the failure of valve leaflets and motivate the exploration for alternatives. Polyphenols, including curcumin, procyanidin and quercetin, etc, have showed great calcification inhibition potential in crosslinking collagen and elastin scaffolds. Herein, we developed an innovative phenolic fixing technique by using curcumin as the crosslinking reagent for valvular materials. X-ray photoelectron spectroscopy and Fourier transform infrared spectrometry assessments confirmed the hydrogen bond between curcumin and acellular bovine pericardium. Importantly, the calcification inhibition capability of the curcumin-crosslinked bovine pericardium was proved by the dramatically reduced Ca²⁺ content in the curcumin-fixed group in in vitro assay, a juvenile rat subcutaneous implants model, as well as an osteogenic differentiation model. In addition, the results showed that the curcumin-fixed bovine pericardium exhibited better performance in the areas of mechanical performance, hemocompatibility and cytocompatibility, in comparison with the GA group and the commercialized product. In summary, we demonstrated that curcumin was a feasible crosslinking reagent to fix acellular bovine pericardium, which showed great potential for biomedical applications, particularly in cardiovascular biomaterials with calcification inhibition capacity.

Sterilization and Cross-Linking Combined with Ultraviolet Irradiation and Low-Energy Electron Irradiation Procedure: New Perspectives for Bovine Pericardial Implants in Cardiac Surgery

BACKGROUND

 Bovine pericardium is the major natural source of patches and aortic valve substitutes in cardiac repair procedures. However, long-term tissue durability and biocompatibility issues lead to degeneration (e.g., calcification) that requires reoperation. Tissue preparation strategies, including glutaraldehyde fixation, are reasons for the deterioration of pericardial tissues. We describe a pretreatment procedure involving sterilization and cross-linking combined with ultraviolet (UV) irradiation and low-energy electron irradiation (SULEEI). This innovative, glutaraldehyde-free protocol improves the mechanical aspects and biocompatibility of porcine pericardium patches.

METHODS

 We adopted the SULEEI protocol, which combines decellularization, sterilization, and cross-linking, along with UV irradiation and low-energy electron irradiation, to pretreat bovine pericardium. Biomechanics, such as ultimate tensile strength and elasticity, were investigated by comparing SULEEI-treated tissue with glutaraldehyde-fixed analogues, clinical patch materials, and an aortic valve substitute. Histomorphological and cellular aspects were investigated by histology, DNA content analysis, and degradability.

RESULTS

 Mechanical parameters, including ultimate tensile strength, elasticity (Young's modulus), and suture retention strength, were similar for SULEEI-treated and clinically applied bovine pericardium. The SULEEI-treated tissues showed well-preserved histoarchitecture that resembled all pericardial tissues investigated. Fiber density did not differ significantly. DNA content after the SULEEI procedure was reduced to less than 10% of the original tissue material, and more than 50% of the SULEEI-treated pericardium was digested by collagenase.

CONCLUSION

 The SULEEI procedure represents a new treatment protocol for the preparation of patches and aortic valve prostheses from bovine pericardial tissue. The avoidance of glutaraldehyde fixation may lessen the tissue degeneration processes in cardiac repair patches and valve prostheses.

A Comprehensive Comparison of Bovine and Porcine Decellularized Pericardia: New Insights for Surgical Applications

Xenogeneic pericardium-based substitutes are employed for several surgical indications after chemical shielding, limiting their biocompatibility and therapeutic durability. Adverse responses to these replacements might be prevented by tissue decellularization, ideally removing cells and preserving the original extracellular matrix (ECM). The aim of this study was to compare the mostly applied pericardia in clinics, i.e. bovine and porcine tissues, after their decellularization, and obtain new insights for their possible surgical use. Bovine and porcine pericardia were submitted to TRICOL decellularization, based on osmotic shock, detergents and nuclease treatment. TRICOL procedure resulted in being effective in cell removal and preservation of ECM architecture of both species' scaffolds. Collagen and elastin were retained but glycosaminoglycans were reduced, significantly for bovine scaffolds. Tissue hydration was varied by decellularization, with a rise for bovine pericardia and a decrease for porcine ones. TRICOL significantly increased porcine pericardial thickness, while a non-significant reduction was observed for the bovine counterpart. The protein secondary structure and thermal denaturation profile of both species' scaffolds were unaltered. Both pericardial tissues showed augmented biomechanical compliance after decellularization. The ECM bioactivity of bovine and porcine pericardia was unaffected by decellularization, sustaining viability and proliferation of human mesenchymal stem cells and endothelial cells. In conclusion, decellularized bovine and porcine pericardia demonstrate possessing the characteristics that are suitable for the creation of novel scaffolds for reconstruction or replacement: differences in water content, thickness and glycosaminoglycans might influence some of their biomechanical properties and, hence, their indication for surgical use.

Swim Bladder as a Novel Biomaterial for Cardiovascular Materials with Anti-Calcification Properties

Calcification is a major cause of cardiovascular materials failure and deterioration, which leads to the restriction of their wide application. To develop new materials with anti-calcification capability is an urgent clinical requirement. Herein, a natural material derived from swim bladders as one promising candidate is introduced, which is prepared by decellularization and glutaraldehyde (GA) crosslinking. Data show that the swim bladder is mainly composed of collagen I, glycosaminoglycan (GAG), and elastin, especially rich in elastin, in accordance with higher elastic modulus in comparison to bovine pericardium. Moreover, the calcification of this material is proved dramatically lower than that of bovine pericardium by in vitro calcification assessments and in vivo assay using a rat subcutaneous implantation model. Meanwhile, good cytocompatibility, hemocompatibility, and enzymatic stability are demonstrated by in vitro assays. Further, a small diameter vascular graft using this material is successfully developed by rolling method and in situ implantation assay using a rat abdominal artery replacement model shows great performances in the aspect of higher patency and lower calcification. Taken together, these superior properties of swim bladder-derived material in anti-calcification, proper mechanical strength and stability, and excellent hemocompatibility and cytocompatibility endow it a great candidate as cardiovascular biomaterials.

Sterilization of epidermal growth factor with supercritical carbon dioxide and peracetic acid; analysis of changes at the amino acid and protein level

Aseptic processing and terminal sterilization become increasingly challenging as medical devices become more complex and include active biologics. Terminal sterilization is preferred for patient safety and production costs. We aimed to determine how sterilization using supercritical CO₂ (scCO₂) with low levels of peracetic acid (PAA) affects amino acids and human epidermal growth factor (EGF) as a model protein. In a benchtop reactivity test, the amino acids methionine, tryptophan, arginine and lysine reacted with low levels of PAA in solution. At PAA levels used for scCO₂ sterilization, however, mass spectrometry only identified oxidative adducts on methionine and tryptophan. Mass spectrometry analysis of EGF exposed to scCO₂/PAA identified oxidative adducts on residues Met₂₁, Trp₄₉ and Trp₅₀, as well as a low level of truncations after residues Trp₄₉ and Trp₅₀. Importantly, processing of EGF in solution with scCO₂ did not affect its native conformation, and sterilized EGF maintained its activity in cell proliferation assays. When processing samples in lyophilized form with scCO₂/PAA, amino acids did not react with PAA and the presence of adducts was strongly reduced on methionine and tryptophan, both as single amino acids and in EGF. Truncation after tryptophan residues did not occur. EGF sterilized in the lyophilized form retained its activity when processing occurred with added moisture. These results have significant implications for the maintenance of biological function in sterilized decellularized scaffolds and the ability to manufacture terminally sterilized combination devices containing therapeutic peptides or proteins.

Mechanical and finite element evaluation of a bioprinted scaffold following recellularization in a rat subcutaneous model

Tissue engineered heart valves (TEHV) provide several advantages over currently available aortic heart valve replacements. Bioprinting provides a patient-specific means of developing a TEHV scaffold from imaging data, and the capability to embed the patient's own cells within the scaffold. In this work we investigated the remodeling capacity of a collagen-based bio-ink by implanting bioprinted disks in a rat subcutaneous model for 2, 4 and 12 weeks and evaluating the mechanical response using biaxial testing and subsequent finite element (FE) modeling. Samples explanted after 2 and 4 weeks showed inferior mechanical properties compared to native tissues while 12 week explants showed a mechanical response of similar magnitude but did not demonstrate the anisotropy present in native tissues. In the FE analysis, the model utilizing mechanical properties from samples explanted after 12 weeks showed the closest mechanical behavior to the native tissues. However, in diastole native tissues showed higher stress in the leaflet belly and lower strain at the commissures compared to 12 week explants, likely due to the anisotropy present in the native tissues. Thus, either further remodeling is required in situ in the aortic valve position or by in vitro preconditioning in an environment such as a bioreactor. Regardless, these results demonstrate the utility of FE analysis to optimize bioprinting process parameters for the most favorable in vivo mechanical performance.

In Silico Performance of a Recellularized Tissue Engineered Transcatheter Aortic Valve

Commercially available heart valves have many limitations, such as a lack of re-modeling, risk of calcification and thromboembolic problems. Many state-of-the-art tissue engineered heart valves rely on recellularization. Current in vitro testing is insufficient in characterizing a soon to be living valve. It is imperative to understand the performance of an in situ valve, but due to the complex in vivo environment this is difficult to accomplish. Finite element analysis has become a standard tool for modeling mechanical behavior of heart valves; yet, research to date has mostly focused on commercial valves. The purpose of this study has been to develop finite element models of a decellularized and recellularized tissue engineered heart valve. Mechanical properties from porcine aortic valves were utilized to develop finite element models, which were run through a full physiological cardiac cycle. Maximum principal stresses and strains from the leaflets and commissures were analyzed. The results of this study demonstrate that the explanted tissues had reduced mechanical strength compared to the implants but were similar to the native tissues. For the finite element models the explanted recellularized leaflets showed lower stress but increased compliance in the leaflet belly compared to native tissues and higher compliance than implant tissues. Histology demonstrated recellularization and remodeling although remodeled collagen had no clear directionality. In conclusion, we observed successful recellularization and remodeling of the tissue, however, the mechanical response indicates the further remodeling is required following implantation in the aortic/pulmonary position.

In Vivo Response of Acellular Porcine Pericardial for Tissue Engineered Transcatheter Aortic Valves

Current heart valve prostheses have limitations that include durability, inability to grow in pediatric patients, and lifelong anticoagulation. Transcatheter aortic valve replacements are minimally invasive procedures, and therefore have emerged as an alternative to traditional valve prostheses. In this experiment, the regenerative capacity of potential tissue engineered transcatheter valve scaffolds (1) acellular porcine pericardium and (2) mesenchymal stem cell-seeded acellular porcine pericardium were compared to native porcine aortic valve cusps in a rat subcutaneous model for up to 8 weeks. Immunohistochemistry, extracellular matrix evaluation, and tissue biomechanics were evaluated on the explanted tissue. Acellular valve scaffolds expressed CD163, CD31, alpha smooth muscle actin, and vimentin at each time point indicating host cell recellularization; however, MSC-seeded tissue showed greater recellularization. Inflammatory cells were observed with CD3 biomarker in native porcine pericardial tissue throughout the study. No inflammation was observed in either acellular or MSC-seeded scaffolds. There was no mechanical advantage observed in MSC-seeded tissue; however after the first week post-explant, there was a decrease in mechanical properties in all groups (p < 0.05). MSC-seeded and acellular porcine pericardium expressed decreased inflammatory response and better host-cell recellularization compared to the native porcine aortic valve cusps.

Preservation strategies for decellularized pericardial scaffolds for off-the-shelf availability

Decellularized biological scaffolds hold great promise in cardiovascular surgery. In order to ensure off-the-shelf availability, routine use of decellularized scaffolds requires tissue banking. In this study, the suitability of cryopreservation, vitrification and freeze-drying for the preservation of decellularized bovine pericardial (DBP) scaffolds was evaluated. Cryopreservation was conducted using 10% DMSO and slow-rate freezing. Vitrification was performed using vitrification solution (VS83) and rapid cooling. Freeze-drying was done using a programmable freeze-dryer and sucrose as lyoprotectant. The impact of the preservation methods on the DBP extracellular matrix structure, integrity and composition was assessed using histology, biomechanical testing, spectroscopic and thermal analysis, and biochemistry. In addition, the cytocompatibility of the preserved scaffolds was also assessed. All preservation methods were found to be suitable to preserve the extracellular matrix structure and its components, with no apparent signs of collagen deterioration or denaturation, or loss of elastin and glycosaminoglycans. Biomechanical testing, however, showed that the cryopreserved DBP displayed a loss of extensibility compared to vitrified or freeze-dried scaffolds, which both displayed similar biomechanical behavior compared to non-preserved control scaffolds. In conclusion, cryopreservation altered the biomechanical behavior of the DBP scaffolds, which might lead to graft dysfunction in vivo. In contrast to cryopreservation and vitrification, freeze-drying is performed with non-toxic protective agents and does not require storage at ultra-low temperatures, thus allowing for a cost-effective and easy storage and transport. Due to these advantages, freeze-drying is a preferable method for the preservation of decellularized pericardium. STATEMENT OF SIGNIFICANCE: Clinical use of DBP scaffolds for surgical reconstructions or substitutions requires development of a preservation technology that does not alter scaffold properties during long-term storage. Conclusive investigation on adverse impacts of the preservation methods on DBP matrix integrity is still missing. This work is aiming to close this gap by studying three potential preservation technologies, cryopreservation, vitrification and freeze-drying, in order to achieve the off-the-shelf availability of DBP patches for clinical application. Furthermore, it provides novel insights for dry-preservation of decellularized xenogeneic scaffolds that can be used in the routine clinical cardiovascular practice, allowing the surgeon the opportunity to choose an ideal implant matching with the needs of each patient.

Biomaterial characterization of off-the-shelf decellularized porcine pericardial tissue for use in prosthetic valvular applications

Fixed pericardial tissue is commonly used for commercially available xenograft valve implants, and has proven durability, but lacks the capability to remodel and grow. Decellularized porcine pericardial tissue has the promise to outperform fixed tissue and remodel, but the decellularization process has been shown to damage the collagen structure and reduce mechanical integrity of the tissue. Therefore, a comparison of uniaxial tensile properties was performed on decellularized, decellularized-sterilized, fixed, and native porcine pericardial tissue versus native valve leaflet cusps. The results of non-parametric analysis showed statistically significant differences (p < .05) between the stiffness of decellularized versus native pericardium and native cusps as well as fixed tissue, respectively; however, decellularized tissue showed large increases in elastic properties. Porosity testing of the tissues showed no statistical difference between decellularized and decell-sterilized tissue compared with native cusps (p > .05). Scanning electron microscopy confirmed that valvular endothelial and interstitial cells colonized the decellularized pericardial surface when seeded and grown for 30 days in static culture. Collagen assays and transmission electron microscopy analysis showed limited reductions in collagen with processing; yet glycosaminoglycan assays showed great reductions in the processed pericardium relative to native cusps. Decellularized pericardium had comparatively low mechanical properties among the groups studied; yet the stiffness was comparatively similar to the native cusps and demonstrated a lack of cytotoxicity. Suture retention, accelerated wear, and hydrodynamic testing of prototype decellularized and decell-sterilized valves showed positive functionality. Sterilized tissue could mimic valvular mechanical environment in vitro, therefore making it a viable potential candidate for off-the-shelf tissue-engineered valvular applications.