Fabrication and characterization of conductive chitosan/gelatin-based scaffolds for nerve tissue engineering

Conductive Biocomposite Made by Two-Photon Polymerization of Hydrogels Based on BSA and Carbon Nanotubes with Eosin-Y

Currently, tissue engineering technologies are promising for the restoration of damaged organs and tissues. For regeneration of electrically conductive tissues or neural interfaces, it is necessary to provide electrical conductivity for the transmission of electrophysiological signals. The developed biocomposite structures presented in this article possess such properties. Their composition includes bovine serum albumin (BSA), gelatin, eosin-Y and single-walled carbon nanotubes (SWCNTs). For the first time, a biocomposite structure was formed from the proposed hydrogel using a nanosecond laser, and a two-photon absorption cross section value of 580 GM was achieved. Increased viscosity over 3 mPa∙s and self-focusing with a nonlinear refractive index of 42 × 10-12 cm2/W make it possible to create a biocomposite structure over the entire specified area. The obtained electrical conductivity value was 19 mS∙cm-1, due to the formation of effective electrically conductive networks. For a biocomposite with a concentration of gelatin 3 wt. %, formed by low-energy near-IR pulses, the survival of Neuro 2A nerve tissue cells was confirmed. The obtained results are important for the creation of new tissue engineering structures and neural interfaces from a biopolymer hydrogel based on the organic dye eosin-Y and carbon nanotubes by two-photon polymerization.

3D-printed cellulose nanocrystals and gelatin scaffolds with bioactive cues for regenerative medicine: Advancing biomedical applications

3D printed scaffolds have revolutionized the field of regenerative medicine by overcoming the lacunas such as precision, customization, and reproducibility observed through traditional methods of scaffold preparation such as freeze-drying, electrospinning, etc. Combining the advantages of 3D printed scaffolds along with bioactive cues such as signaling molecules can be an effective treatment approach. In the present study, cellulose nanocrystals (CNCs) along with gelatin, in different ratios, were used for scaffold preparation through the direct ink writing technique and thoroughly characterized. The scaffolds showed porous microstructure, high swelling ratio (∼390 to 590), degradability and porosity (∼65 %). In vitro biocompatibility assays showed high biocompatibility and no toxicity through live-dead, proliferation and hemolysis assay. Further, the optimum formulation was functionalized with nitric oxide (NO)-releasing modified gelatin to enhance the scaffold's biomedical applicability. Functionality assays with this formulation, scratch, and neurite outgrowth showed positive effects of NO on cell migration and neurite length. The study presents the fabrication, modification, and biomedical applicability of the aforementioned inks, which paves new pathways in the field of 3D printing of scaffolds with significant potential for biomedical applications, soft tissue engineering, and wound dressing, for example.

Development and characterization of Polycaprolactone/chitosan-based scaffolds for tissue engineering of various organs: A review

Research in creating 3D structures mirroring the extracellular matrix (ECM) with accurate environmental cues holds paramount significance in biological applications.Biomaterials that replicate ECM properties-mechanical, physicochemical, and biological-emerge as pivotal tools in mimicking ECM behavior.Incorporating synthetic and natural biomaterials is widely used to produce scaffolds suitable for the intended organs.Polycaprolactone (PCL), a synthetic biomaterial, boasts commendable mechanical properties, albeit with relatively modest biological attributes due to its hydrophobic nature.Chitosan (CTS) exhibits strong biological traits but lacks mechanical resilience for complex tissue regeneration.Notably, both PCL and CTS have demonstrated their application in tissue engineering for diverse types of tissues.Their combination across varying PCL:CTS ratios has increased the likelihood of fabricating scaffolds to address defects in sturdy and pliable tissues.This comprehensive analysis aspires to accentuate their distinct attributes within tissue engineering across different organs.The central focus resides in the role of PCL:CTS-based scaffolds, elucidating their contribution to the evolution of advanced functional 3D frameworks tailored for tissue engineering across diverse organs.Moreover, this discourse delves into the considerations pertinent to each organ.

Innovations in hydrogel-based manufacturing: A comprehensive review of direct ink writing technique for biomedical applications

Direct ink writing (DIW) stands as a pioneering additive manufacturing technique that holds transformative potential in the field of hydrogel fabrication. This innovative approach allows for the precise deposition of hydrogel inks layer by layer, creating complex three-dimensional structures with tailored shapes, sizes, and functionalities. By harnessing the versatility of hydrogels, DIW opens up possibilities for applications spanning from tissue engineering to soft robotics and wearable devices. This comprehensive review investigates DIW as applied to hydrogels and its multifaceted applications. The paper introduces a diverse range of printing techniques while providing a thorough exploration of DIW for hydrogel-based printing. The investigation aims to explain the progress made, challenges faced, and potential trajectories that lie ahead for DIW in hydrogel-based manufacturing. The fundamental principles underlying DIW are carefully examined, specifically focusing on rheological attributes and printing parameters, prompting a comprehensive survey of the wide variety of hydrogel materials. These encompass both natural and synthetic variations, all of which can be effectively harnessed for this purpose. Furthermore, the review explores the latest applications of DIW for hydrogels in biomedical areas, with a primary focus on tissue engineering, wound dressing, and drug delivery systems. The document not only consolidates the existing state of DIW within the context of hydrogel-based manufacturing but also charts potential avenues for further research and innovative breakthroughs.

Chitosan scaffolds: Expanding horizons in biomedical applications

Chitosan, a natural polysaccharide from chitin, shows promise as a biomaterial for various biomedical applications due to its biocompatibility, biodegradability, antibacterial activity, and ease of modification. This review overviews "chitosan scaffolds" use in diverse biomedical applications. It emphasizes chitosan's structural and biological properties and explores fabrication methods like gelation, electrospinning, and 3D printing, which influence scaffold architecture and mechanical properties. The review focuses on chitosan scaffolds in tissue engineering and regenerative medicine, highlighting their role in bone, cartilage, skin, nerve, and vascular tissue regeneration, supporting cell adhesion, proliferation, and differentiation. Investigations into incorporating bioactive compounds, growth factors, and nanoparticles for improved therapeutic effects are discussed. The review also examines chitosan scaffolds in drug delivery systems, leveraging their prolonged release capabilities and ability to encapsulate medicines for targeted and controlled drug delivery. Moreover, it explores chitosan's antibacterial activity and potential for wound healing and infection management in biomedical contexts. Lastly, the review discusses challenges and future objectives, emphasizing the need for improved scaffold design, mechanical qualities, and understanding of interactions with host tissues. In summary, chitosan scaffolds hold significant potential in various biological applications, and this review underscores their promising role in advancing biomedical science.

Fabrication and characterization of porous, degradable, biocompatible poly(vinyl alcohol)/tannic acid/gelatin/hyaluronic acid hydrogels with good mechanical properties for cartilage tissue engineering

At present, articular cartilage repair and regeneration remain still one of the most concerned problems due to its poor self-healing capacity. Among the tissue engineering materials, hydrogel is considered an ideal candidate due to its similarity to extracellular matrices. Despite the good biocompatibility of gelatin and hyaluronic acid hydrogels, they are still limited to serve as tissue engineering materials by fast degradation rate and poor mechanical performances. In order to solve these problems, novel polyvinyl alcohol/tannic acid/gelatin/hyaluronic acid (PTGH) hydrogels are prepared by a facile physical crosslinked method. The PTGH hydrogels exhibit a high moisture content (85%) and porosity (87%). Meanwhile, the porous microstructures and mechanical properties (compressive strength: 0.85-2.59 MPa; compressive modulus: 57.88-124.27 kPa) can be controlled by adjusting the mass ratio of PT/GH. In vitro degradation analysis shows that the PTGH hydrogels can be degraded gradually in PBS solution with the presence of lysozyme. For this gel system, based on the hydrogen bonds among molecules, it improved the mechanical properties of gelatin and hyaluronic acid hydrogels. With the degradation of PTGH hydrogels, the release of gelatin and hyaluronic acid can have a continuous effort for the cartilage tissue regeneration and repair. In addition, in vitro cell culture results show that the PTGH hydrogels have no negative effects on chondrocytes growth and proliferation. In all, the PTGH hydrogels exhibit potential applications for articular cartilage tissue repair and regeneration.

Nanomaterials-incorporated hydrogels for 3D bioprinting technology

In the field of tissue engineering and regenerative medicine, various hydrogels derived from the extracellular matrix have been utilized for creating engineered tissues and implantable scaffolds. While these hydrogels hold immense promise in the healthcare landscape, conventional bioinks based on ECM hydrogels face several challenges, particularly in terms of lacking the necessary mechanical properties required for 3D bioprinting process. To address these limitations, researchers are actively exploring novel nanomaterial-reinforced ECM hydrogels for both mechanical and functional aspects. In this review, we focused on discussing recent advancements in the fabrication of engineered tissues and monitoring systems using nanobioinks and nanomaterials via 3D bioprinting technology. We highlighted the synergistic benefits of combining numerous nanomaterials into ECM hydrogels and imposing geometrical effects by 3D bioprinting technology. Furthermore, we also elaborated on critical issues remaining at the moment, such as the inhomogeneous dispersion of nanomaterials and consequent technical and practical issues, in the fabrication of complex 3D structures with nanobioinks and nanomaterials. Finally, we elaborated on plausible outlooks for facilitating the use of nanomaterials in biofabrication and advancing the function of engineered tissues.

The effect of conductive aligned fibers in an injectable hydrogel on nerve tissue regeneration

Injectable hydrogels are a promising treatment option for nervous system injuries due to the difficulty to replace lost cells and nervous factors but research on injectable conductive hydrogels is limited and these scaffolds have poor electromechanical properties. This study developed a chitosan/beta-glycerophosphate/salt hydrogel and added conductive aligned nanofibers (polycaprolactone/gelatin/single-wall carbon nanotube (SWCNT)) for the first time and inspired by natural nerve tissue to improve their biochemical and biophysical properties. The results showed that the degradation rate of hydrogels is proportional to the regrowth of axons and these hydrogels' mechanical (hydrogels without nanofibers or SWCNTs and hydrogels containing these additions have the same Young's modulus as the brain and spinal cord or peripheral nerves, respectively) and electrical properties, and the interconnective structure of the scaffolds have the ability to support cells.

Dual-Pulsed Laser Ablation of Oyster Shell Producing Novel Thin Layers Deposed to Saccharomyces cerevisiae

Dual-pulsed (DPL) laser deposition using oyster shells as targets was studied in order to find out if this method can replace the use of high-power pulsed lasers. Aspects related to changes in the morphological structure of the thin layer but also to the chemical composition of the obtained thin layer were analyzed and compared with the target as well as with the thin layers obtained with a higher power pulsed laser in a single-pulsed (SPL) regime. Orthorhombic structures were noticed with Scanning Electron Microscopy for the thin film obtained in DPL mode compared to the irregular particles obtained in SPL mode. The deacetylation process during ablation was evidenced by Fourier Transform Infrared spectroscopy, resulting in chitosan-based thin films. The effect of the obtained thin films of chitosan on the cells of baker's yeast (Saccharomyces cerevisiae) was studied. Restoration of the yeast paste into initial yeast was noticed mainly when the hemp fabric was used as support for the coating with yeas which was after that coated with chitosan thin film produced by DPL method.

Magnetic Nanofibrous Hydrogels for Dynamic Control of Stem Cell Differentiation

The extracellular matrix in tissue consists of complex heterogeneous soft materials with hierarchical structure and dynamic mechanical properties dictating cell and tissue level function. In many natural matrices, there are nanofibrous structures that serve to guide cell activity and dictate the form and function of tissue. Synthetic hydrogels with integrated nanofibers can mimic the structural properties of native tissue; however, model systems with dynamic mechanical properties remain elusive. Here we demonstrate modular nanofibrous hydrogels that can be reversibly stiffened in response to applied magnetic fields. Iron oxide nanoparticles were incorporated into gelatin nanofibers through electrospinning, followed by chemical stabilization and fragmentation. These magnetoactive nanofibers can be mixed with virtually any hydrogel material and reversibly stiffen the matrix at a low fiber content (≤3%). In contrast to previous work, where a large quantity of magnetic material disallowed cell encapsulation, the low nanofiber content allows matrix stiffening with cells in 3D. Using adipose derived stem cells, we show how nanofibrous matrices are beneficial for both osteogenesis and adipogenesis, where stiffening the hydrogel with applied magnetic fields enhances osteogenesis while discouraging adipogenesis. Skeletal myoblast progenitors were used as a model of tissue morphogenesis with matrix stiffening augmenting myogenesis and multinucleated myotube formation. The ability to reversibly stiffen fibrous hydrogels through magnetic stimulation provides a useful tool for studying nanotopography and dynamic mechanics in cell culture, with a scope for stimuli responsive materials for tissue engineering.

Advances in Organic-Inorganic Hybrid Latex Particles via In Situ Emulsion Polymerization

Hybrid latex particles combine the unique properties of inorganic nano/micro particles with the inherent properties of polymers, exhibiting tremendous potential for a variety of applications. Recent years have witnessed an increased interest in the design and preparation of hybrid latex particles with well-defined size, structure and morphology. Due to its simplicity, versatility and environmental friendliness, the in situ (Pickering) emulsion polymerization has been demonstrated to be a powerful approach for the large-scale preparation of hybrid latex particles. In this review, the strategies and applications of in situ (Pickering) emulsion polymerization for the preparation of hybrid latex particles are systematically summarized. A particular focus is placed on the strategies for the preparation of hybrid latex particles with enhanced properties and well-defined core-shell, yolk-shell, multinuclear, raspberry-like, dumbbell-shaped, multipod-like or armored morphologies. We hope that the considerable advances, examples and principles presented in this review can motivate future contributions to provide a deeper understanding of current preparation technologies, develop new processes, and enable further exploitation of hybrid latex particles with outstanding characteristics and properties.

Graphene Oxide-Carbamoylated Chitosan Hydrogels with Tunable Mechanical Properties for Biological Applications

Chitosan (CH)-based hydrogels have been extensively researched in numerous biological applications, including drug delivery, biosensing, wound healing, and tissue engineering, to name a few. Previously, modified CH hydrogels by carbamoylation, using potassium cyanate (KCNO) as the cross-linker, have shown improvement in viscoelastic properties and biocompatibility. In this study, graphene oxide (GO) nanofillers are added to carbamoylated CH to form a nanocomposite hydrogel and study the influence of CH molecular weight (M_w) and GO loading concentrations on hydrogel properties. The physical properties (swelling, degradation, and porous structure) of the hydrogels can be tuned as required for cell attachment and spreading by varying both the GO concentration and the M_w of CH. Rheological characterization showed an improvement in the mechanical properties (storage modulus, yield stress, and viscosity) of the synthesized CH-GO hydrogels with an increase in the M_w of CH and the GO concentration. Human retinal pigmented epithelial-1 (RPE-1) cells seeded onto the prepared hydrogel scaffolds showed good cell viability, adhesion, and cell spreading, confirming their cytocompatibility, with dependence on both M_w of CH and GO loading.

Fabrication and detection of a novel hybrid conductive scaffold based on alginate/gelatin/carboxylated carbon nanotubes (Alg/Gel/mMWCNTs) for neural tissue engineering

Carbon nanotubes (CNTs), as kinds of conductive carbon nanomaterials, were widely applied in neural tissue engineering due to their excellent electrical conductivity and good biocompatibility. In this study, the carboxyl-modified multi-walled carbon nanotubes (mMWCNTs) were introduced into sodium alginate/gelatin (Alg/Gel) scaffolds to optimize the function of the hybrid scaffolds. The Alg/Gel/mMWCNTs conductive scaffolds with mMWCNTs content of 1%, 3%, and 5% were prepared by freeze-drying, respectively. Following this, the physicochemical properties and biocompatibility of the hybrid scaffolds at different magnetic field intensities were evaluated. The conductive scaffolds were characterized by Scanning electron microscopy (SEM) and Fourier transform infrared spectroscopy (FTIR). In general, the mMWCNTs addition improved the hydrophilic, electrical conductivity and mechanical properties of the composite scaffold, and PC12 cells showed a trend of gradual increase over culture time. Particularly, the Alg/Gel-1%C scaffold exhibited the best cell proliferation behavior. Briefly, the surface contact angle decreased from 74 ± 1° to 60 ± 3°, the electrical conductivity and compressive modulus increased to 1.32 × 10^-3 ± 2.1 × 10^-4 S/cm and 1.40 ± 0.076 Mpa, the G1 phase from 55.67 ± 1.86% to 59.77 ± 0.94% and the G2 phase from 10.32 ± 0.35% to 13.93 ± 1.26%，respectively. In the SEM images, PC12 cells were well-shaped and densely distributed. Therefore, the Alg/Gel/mMWCNTs conductive scaffold has potential as a tissue engineering scaffold in nerve regeneration.

Biomineralization of bone-like hydroxyapatite to upgrade the mechanical and osteoblastic performances of poly(lactic acid) scaffolds

Biomimetic mineralization of high-strength apatite structure essentially relies on mimicking the inorganic building blocks of naturally occurring bones. However, conventional routes still have substantial function gaps in providing precision control over the geometrical dimensions and crystalline morphology of biomineralized apatite. Herein, we conceived the concept of microwave-assisted biomineralization (MAB) to customize 1D hydroxyapatite nanowhiskers (HANWs) at graphene templates, rendering the formation of graphene-hydroxyapatite (Gr-HA) nanohybrids. The HANWs essentially resembled bone apatite in elemental composition (Ca/P = 1.74), diameter (~20 nm), crystallinity (63 %), and rodlike geometry (aspect ratio of ~6). The Gr-HA nanohybrids were uniformly incorporated into poly(lactic acid) (PLA) microfibers (~1 μm) by electrospinning, engendering fibrous membranes with a set of Gr-HA loadings (10, 20 and 30 wt%). Intimate interactions were generated between Gr-HA and PLA matrix, contributing to significant promotion of the mechanical properties for PLA composite membranes. For example, the yield strength and elastic modulus of the PLA composite membranes loaded with 30 wt% Gr-HA achieved 5.4 and 66.4 MPa, increasing nearly 182 % and over 94 % compared to those of pure PLA, respectively. Moreover, the bone-like HANWs endowed PLA membranes with excellent cytocompatibility and good bioactivity, as demonstrated by over 38 % increase in cell viability and rapid apatite formation in mineral solution. The impressive combination of mechanical properties and biological characteristics make the PLA/Gr-HA scaffolds promising for guided tissue/bone regeneration therapy.

Polysaccharide-based nanocomposites for biomedical applications: a critical review

Polysaccharides (PSA) have taken specific position among biomaterials for advanced applications in medicine. Nevertheless, poor mechanical properties are known as the main drawback of PSA, which highlights the need for PSA modification. Nanocomposites PSA (NPSA) are a class of biomaterials widely used as biomedical platforms, but despite their importance and worldwide use, they have not been reviewed. Herein, we critically reviewed the application of NPSA by categorizing them into generic and advanced application realms. First, the application of NPSA as drug and gene delivery systems, along with their role in the field as an antibacterial platform and hemostasis agent is discussed. Then, applications of NPSA for skin, bone, nerve, and cartilage tissue engineering are highlighted, followed by cell encapsulation and more critically cancer diagnosis and treatment potentials. In particular, three features of investigations are devoted to cancer therapy, i.e., radiotherapy, immunotherapy, and photothermal therapy, are comprehensively reviewed and discussed. Since this field is at an early stage of maturity, some other aspects such as bioimaging and biosensing are reviewed in order to give an idea of potential applications of NPSA for future developments, providing support for clinical applications. It is well-documented that using nanoparticles/nanomaterials above a critical concentration brings about concerns of toxicity; thus, their effect on cellular interactions would become critical. We compared nanoparticles used in the fabrication of NPSA in terms of toxicity mechanism to shed more light on future challenging aspects of NPSA development. Indeed, the neutralization mechanisms underlying the cytotoxicity of nanomaterials, which are expected to be induced by PSA introduction, should be taken into account for future investigations.

High-resolution 3D printing of xanthan gum/nanocellulose bio-inks

The current study provides a comprehensive rheology study and a survey on direct ink writing of xanthan gum/cellulose nanocrystal (XG/CNC) bio-inks for developing 3D geometries that mimic soft tissue engineering scaffolds' physical and mechanical properties. The presence of CNC was found to be a critical prerequisite for the printability of XG bio-inks; accordingly, the hybrid XG/CNC bio-inks revealed the excellent viscoelastic properties that enabled precise control of hydrogel shaping and printing of lattice structures composed of up to eleven layers with high fidelity and fair resolution without any deformation after printing. The lyophilized 3D scaffolds presented a porous structure with open and interconnected pores and a porosity higher than 70%, vital features for tissue engineering scaffolds. Moreover, they showed a relatively high swelling of approximately 11 g/g, facilitating oxygen and nutrient exchange. Furthermore, the elastic and compressive moduli of the scaffolds that enhanced significantly upon increasing CNC content were in the range of a few kPa, similar to soft tissues. Finally, no significant cell cytotoxicity was observed against human liver cancer cells (HepG2), highlighting the potential of these developed 3D printed scaffolds for soft tissue engineering applications.

Conductive Bioimprint Using Soft Lithography Technique Based on PEDOT:PSS for Biosensing

Culture platform surface topography plays an important role in the regulation of biological cell behaviour. Understanding the mechanisms behind the roles of surface topography in cell response are central to many developments in a Lab on a Chip, medical implants and biosensors. In this work, we report on a novel development of a biocompatible conductive hydrogel (CH) made of poly (3,4-ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS) and gelatin with bioimprinted surface features. The bioimprinted CH offers high conductivity, biocompatibility and high replication fidelity suitable for cell culture applications. The bioimprinted conductive hydrogel is developed to investigate biological cells’ response to their morphological footprint and study their growth, adhesion, cell–cell interactions and proliferation as a function of conductivity. Moreover, optimization of the conductive hydrogel mixture plays an important role in achieving high imprinting resolution and conductivity. The reason behind choosing a conducive hydrogel with high resolution surface bioimprints is to improve cell monitoring while mimicking cells’ natural physical environment. Bioimprints which are a 3D replication of cellular morphology have previously been shown to promote cell attachment, proliferation, differentiation and even cell response to drugs. The conductive substrate, on the other hand, enables cell impedance to be measured and monitored, which is indicative of cell viability and spread. Two dimensional profiles of the cross section of a single cell taken via Atomic Force Microscopy (AFM) from the fixed cell on glass, and its replicas on polydimethylsiloxane (PDMS) and conductive hydrogel (CH) show unprecedented replication of cellular features with an average replication fidelity of more than 90%. Furthermore, crosslinking CH films demonstrated a significant increase in electrical conductivity from 10⁻⁶ S/cm to 1 S/cm. Conductive bioimprints can provide a suitable platform for biosensing applications and potentially for monitoring implant-tissue reactions in medical devices.

3D printing and properties of cellulose nanofibrils-reinforced quince seed mucilage bio-inks

Plant-based hydrogels have attracted great attention in biomedical fields since they are biocompatible and based on natural, sustainable, cost-effective, and widely accessible sources. Here, we introduced new viscoelastic bio-inks composed of quince seed mucilage and cellulose nanofibrils (QSM/CNF) easily extruded into 3D lattice structures through direct ink writing in ambient conditions. The QSM/CNF inks enabled precise control on printing fidelity where CNF endowed objects with shape stability after freeze-drying and with suitable porosity, water uptake capacity, and mechanical strength. The compressive and elastic moduli of samples produced at the highest CNF content were both increased by ~100% (from 5.1 ± 0.2 kPa and 32 ± 1 kPa to 10.7 ± 0.5 and 64 ± 2 kPa, respectively). These values ideally matched those reported for soft tissues; accordingly, the cell compatibility of the printed samples was evaluated against HepG2 cells (human liver cancer). The results confirmed the 3D hydrogels as being non-cytotoxic and suitable to support attachment, survival, and proliferation of the cells. All in all, the newly developed inks allowed sustainable 3D bio-hydrogels fitting the requirements as scaffolds for soft tissue engineering.

Conductive conduit based on electrospun poly (l-lactide-co-D, l-lactide) nanofibers containing 4-aminopyridine-loaded molecularly imprinted poly (methacrylic acid) nanoparticles used for peripheral nerve regeneration

Using biocompatible polymer nanofibrous conduits with a controlled drug delivery have attracted much attention for peripheral nerve regeneration. This work was aimed at preparing electrospun poly (l-lactide-co-D, l-lactide) (PLDLLA) containing multi-walled carbon nanotubes (MWCNTs) and 4-aminopyridine (4-AP)-loaded molecularly imprinted nanoparticles (MIP_4-AP) as well as evaluating their performance in in vitro and in vivo assessments. After synthesis of MIP_4-AP based on poly (methacrylic acid) with imprinting factor of 1.78, it was incorporated into the PLDLLA/MWCNTs nanofibers to optimize. By adjusting the process variables, the average diameter and electrical conductivity of the nanofibrous sample were 92 nm and 2870 × 10^-7 S cm^-1, respectively. Afterward, 4-AP release of the optimum sample showed the presence of MIP_4-AP leading to initial burst release decrease and plateau level postpone up to 96 h. Moreover, the culture results of PC12 as neuroblastoma cell line on optimal PLDLLA/MWCNTs/MIP_4-AP nanofibrous sample revealed the highest cell proliferation without cytotoxicity compared to neat nanofibers. Eventually, the animal model experiment exhibited that the conductive conduit based on the optimum sample was able to repair the rat's sciatic nerve after four weeks in accordance with sciatic function index and histological studies.

Ascorbic acid-loaded polyvinyl alcohol/cellulose nanofibril hydrogels as precursors for 3D printed materials

We proposed a simple method to process hydrogels containing polyvinyl alcohol and cellulose nanofibrils (PVA/CNF) to prepare volumetric architectures by direct ink writing (DIW). The presence of CNF in the aqueous PVA suspensions conferred rheology profiles that were suitable for extrusion and solidification in pre-designed shapes. The viscoelastic behavior of the hybrid inks enabled precise control on processability and shape retention, for instance, as demonstrated in multilayered lattice structures of high fidelity. After lyophilization, the obtained 3D-printed hydrogels presented a very high porosity, with open and interconnected pores, allowing a high-water uptake capacity (up to 1600%). The mechanical strength of the composite 3D-printed materials matched those of soft tissues, opening opportunities for skin applications. As such, drug-loaded samples revealed a controlled and efficient delivery of an antioxidant (ascorbic acid) in PBS buffer media at 23 °C (~80% for 8 h). Altogether, PVA/CNF hydrogels were introduced as suitable precursors of 3D-lattice geometries with excellent physical and mechanical characteristics.

Preparation and characterization of conductive nerve guide conduit filled with dual drug-loaded nanofibers

Peripheral nerve injury (PNI) has become one of the common clinical diseases. How to promote the regeneration and function recovery of the damaged peripheral nerve has been the focus of attention in the medical field. Evidence suggests that the longitudinal filling of oriented fibers in nerve guide conduit (NGC) is especially beneficial to the repair of long gap PNI. In this study, polypyrrole (PPy) nanospheres (PNSs) were prepared by the soft-templating method, and mixed with poly (lactic acid) (PLA) to prepare conductive PNSs/PLA NGC, and the optimal ratio of PNSs was 4.5%. PLA and vascular endothelial growth factor (VEGF) as shell, chitosan (CS) and paeoniflorin (PF) as core, oriented coaxial nanofibers were obtained and then filled into PNSs/PLA NGC. The composite NGC has excellent mechanical properties, electrical conductivity, hydrophilic properties, and degradation properties. Besides, the successive release of VEGF and PF can play a synergistic role in promoting nerve regeneration. In vitro experiments showed that the composite NGC was nontoxic and suitable for the adhesion and proliferation of nerve cells. In addition, PNSs combined with electrical stimulation (ES) can significantly promote the differentiation and proliferation of nerve cells, which is conducive to nerve regeneration. These positive results indicate that the composite NGC is a promising candidate in the repair of long gap PNI.

In Vitro Evaluation of a Composite Gelatin-Hyaluronic Acid-Alginate Porous Scaffold with Different Pore Distributions for Cartilage Regeneration

Although considerable achievements have been made in the field of regenerative medicine, since self-repair is not an advanced ability of articular cartilage, the regeneration of osteochondral defects is still a challenging problem in musculoskeletal diseases. Cartilage regeneration aims to design a scaffold with appropriate pore structure and biological and mechanical properties for the growth of chondrocytes. In this study, porous scaffolds made of gelatin, hyaluronic acid, alginate, and sucrose in different proportions of 2 g (S_L2) and 4 g (S_L4) were used as porogens in a leaching process. Sucrose with particle size ranges of 88–177 μm (Hμ) and 44–74 μm (SHμ) was added to the colloid, and the individually cross-linked hydrogel scaffolds with controllable pore size for chondrocyte culture were named Hμ-S_L2, Hμ-S_L4, SHμ-S_L2 and SHμ-S_L4. The perforation, porosity, mechanical strength, biocompatibility, and proliferation characteristics of the hydrogel scaffold and its influence on chondrocyte differentiation are discussed. Results show that the addition of porogen increases the porosity of the hydrogel scaffold. Conversely, when porogens with the same particle size are added, the pore size decreases as the amount of porogen increases. The perforation effect of the hydrogel scaffolds formed by the porogen is better at 88–177 μm compared with that at 44–74 μm. Cytotoxicity analysis showed that all the prepared hydrogel scaffolds were non-cytotoxic, indicating that no cross-linking agent residues that could cause cytotoxicity were found. In the proliferation and differentiation of the chondrocytes, the SHμ-S_L4 hydrogel scaffold with the highest porosity and strength did not achieve the best performance. However, due to the compromise between perforation pores, pore sizes, and strength, as well as considering cell proliferation and differentiation, Hμ-SL4 scaffold provided a more suitable environment for the chondrocytes than other groups; therefore, it can provide the best chondrocyte growth environment for this study. The development of hydrogels with customized pore properties for defective cartilage is expected to meet the requirements of the ultimate clinical application.

Polymeric Nanocomposite Structures Based on Functionalized Graphene with Tunable Properties for Nervous Tissue Replacement

Electroconductive scaffolds can be a promising approach to repair conductive tissues when natural healing fails. Recently, nerve tissue engineering constructs have been widely investigated due to the challenges in creating a structure with optimized physiochemical and mechanical properties close to the native tissue. The goal of the current study was to fabricate graphene-containing polycaprolactone/gelatin/polypyrrole (PCL/gelatin/PPy) and polycaprolactone/polyglycerol-sebacate/polypyrrole (PCL/PGS/PPy) with intrinsic electrical properties through an electrospinning process. The effect of graphene on the properties of PCL/gelatin/PPy and PCL/PGS/PPy were investigated. Results demonstrated that graphene incorporation remarkably modulated the physical and mechanical properties of the scaffolds such that the electrical conductivity increased from 0.1 to 3.9 ± 0.3 S m^-1 (from 0 to 3 wt % graphene) and toughness was found to be 76 MPa (PCL/gelatin/PPy 3 wt % graphene) and 143.4 MPa (PCL/PGS/PPy 3 wt % graphene). Also, the elastic moduli of the scaffolds with 0, 1, and 2 wt % graphene were reported as 210, 300, and 340 kPa in the PCL/gelatin/PPy system and 72, 85, and 92 kPa for the PCL/PGS/PPy system. A cell viability study demonstrated the noncytotoxic nature of the resultant scaffolds. The sum of the results presented in this study suggests that both PCL/gelatin/PPy/graphene and PCL/PGS/PPy/graphene compositions could be promising biomaterials for a range of conductive tissue replacement or regeneration applications.

Fabrication and characterisation of a wound dressing composed of polyvinyl alcohol and quince seed mucilage

OBJECTIVE

Providing a suitable environment to improve the healing process is the main target of wound dressing that also protects the wound from additional harms. In the present study, fabrication and characterisation of a new kind of electrospun wound dressing composed of polyvinyl alcohol (PVA) and quince seed mucilage (QSM) is reported.

METHOD

QSM was extracted from quince seeds, purified, freeze-dried and used to produce aqueous solutions containing different amounts of PVA and QSM. The wound dressings were fabricated via the electrospinning method and their characteristics were investigated with scanning electron microscope (SEM) images, Fourier transform infrared (FTIR) spectra, tensile and swelling test, and 3-(4,5-dimethylthiazol-2-yl)-2,5-diphenyl-2H-tetrazolium bromide (MTT) cytotoxicity assay against fibroblast cells.

RESULTS

SEM images confirmed that proper, uniform, non-oriented nanofibres with an average diameter in the range of 60-240nm, depending on the QSM content had been fabricated. The tensile test showed that with increasing QSM content, the tensile strength of fibre increased while elongation at break was decreased, which was consistent with SEM images where the diameter of samples decreased by increasing QSM content. MTT assay showed significant biocompatibility against fibroblast cells; however, it was increased by increased QSM proportion. In addition, SEM images supported the proper adhesion of fibroblast cells on the sample one day after culturing.

CONCLUSION

Overall, the findings of the current study support the potential of PVA/QSM nanofibres as a proper candidate for biomedical applications, especially as a wound dressing.

[In vivo degradation and histocompatibility of modified chitosan based on conductive composite nerve conduit]

Objective

To investigate the in vivo degradation and histocompatibility of modified chitosan based on conductive composite nerve conduit, so as to provide a new scaffold material for the construction of tissue engineered nerve.

Methods

The nano polypyrrole (PPy) was synthesized by microemulsion polymerization, blended with chitosan, and then formed conduit by injecting the mixed solution into a customized conduit formation model. After freeze-drying and deacidification, the nano PPy/chitosan composite conduit (CP conduit) was prepared. Then the CP conduits with different acetyl degree were resulted undergoing varying acetylation for 30, 60, and 90 minutes (CAP1, CAP2, CAP3 conduits). Fourier infrared absorption spectrum and scanning electron microscopy (SEM) were used to identify the conduits. And the conductivity was measured by four-probe conductometer. The above conduits were implanted after the subcutaneous fascial tunnels were made symmetrically on both sides of the back of 30 female Sprague Dawley rats. At 2, 4, 6, 8, 10, and 12 weeks after operation, the morphology, the microstructure, and the degradation rate were observed and measured to assess the in vivo degradation of conduits. HE staining and anti-macrophage immunofluorescence staining were performed to observe the histocompatibility in vivo.

Results

The characteristic peaks of the amide Ⅱ band around 1 562 cm ^-1 appeared after being acetylated, indicating that the acetylation modification of chitosan was successful. There was no significant difference in conductivity between conduits ( P>0.05). SEM observation showed that the surfaces of the conduits in all groups were similar with relatively smooth surface and compact structure. After the conduits were implanted into the rats, with the extension of time, all conduits were collapsed, especially on the CAP3 conduit. All conduits had different degrees of mass loss, and the higher the degree of acetylation, the greater the mass change ( P<0.05). SEM observation showed that there were more pores at 12 weeks after implantation, and the pores showed an increasing trend as the degree of acetylation increased. Histological observation showed that there were more macrophages and lymphocytes infiltration in each group at the early stage. With the extension of implantation time, lymphocytes decreased, fibroblasts increased, and collagen fibers proliferated significantly.

Conclusion

The modified chitosan basedon conductive composite nerve conduit made of nano-PPy/chitosan composite with different acetylation degrees has good biocompatibility, conductivity, and biodegradability correlated with acetylation degree in vivo, which provide a new scaffold material for the construction of tissue engineered nerve.

Alginate/cartilage extracellular matrix-based injectable interpenetrating polymer network hydrogel for cartilage tissue engineering

In the present study, alginate/cartilage extracellular matrix (ECM)-based injectable hydrogel was developed incorporated with silk fibroin nanofibers (SFN) for cartilage tissue engineering. The in situ forming hydrogels were composed of different ionic crosslinked alginate concentrations with 1% w/v enzymatically crosslinked phenolized cartilage ECM, resulting in an interpenetrating polymer network (IPN). The response surface methodology (RSM) approach was applied to optimize IPN hydrogel's mechanical properties by varying alginate and SFN concentrations. The results demonstrated that upon increasing the alginate concentration, the compression modulus improved. The SFN concentration was optimized to reach a desired mechanical stiffness. Accordingly, the concentrations of alginate and SFN to have an optimum compression modulus in the hydrogel were found to be 1.685 and 1.724% w/v, respectively. The gelation time was found to be about 10 s for all the samples. Scanning electron microscope (SEM) images showed homogeneous dispersion of the SFN in the hydrogel, mimicking the natural cartilage environment. Furthermore, water uptake capacity, degradation rate, cell cytotoxicity, and glycosaminoglycan and collagen II secretions were determined for the optimum hydrogel to support its potential as an injectable scaffold for articular cartilage defects.

Conductive chitosan/polyaniline hydrogel with cell-imprinted topography as a potential substrate for neural priming of adipose derived stem cells

Biophysical characteristics of engineered scaffolds such as topography and electroconductivity have shown potentially beneficial effects on stem cell morphology, proliferation, and differentiation toward neural cells. In this study, we fabricated a conductive hydrogel made from chitosan (CS) and polyaniline (PANI) with induced PC12 cell surface topography using a cell imprinting technique to provide both topographical properties and conductivity in a platform. The engineered hydrogel's potential for neural priming of rat adipose-derived stem cells (rADSCs) was determined in vitro. The biomechanical analysis revealed that the electrical conductivity, stiffness, and hydrophobicity of flat (F) and cell-imprinted (CI) substrates increased with increased PANI content in the CS/PANI scaffold. The conductive substrates exhibited a lower degradation rate compared to non-conductive substrates. According to data obtained from F-actin staining and AFM micrographs, both CI(CS) and CI(CS-PANI) substrates induced the morphology of rADSCs from their irregular shape (on flat substrates) into the elongated and bipolar shape of the neuronal-like PC12 cells. Immunostaining analysis revealed that both CI(CS) and CI (CS-PANI) significantly upregulated the expression of GFAP and MAP2, two neural precursor-specific genes, in rADSCs compared with flat substrates. Although the results reveal that both cell-imprinted topography and electrical conductivity affect the neural lineage differentiation, some data demonstrate that the topography effects of the cell-imprinted surface have a more critical role than electrical conductivity on neural priming of ADSCs. The current study provides new insight into the engineering of scaffolds for nerve tissue engineering.

Direct ink writing of aloe vera/cellulose nanofibrils bio-hydrogels

Direct-ink-writing (DIW) of hydrogels has become an attractive research area due to its capability to fabricate intricate, complex, and highly customizable structures at ambient conditions for various applications, including biomedical purposes. In the current study, cellulose nanofibrils reinforced aloe vera bio-hydrogels were utilized to develop 3D geometries through the DIW technique. The hydrogels revealed excellent viscoelastic properties enabled extruding thin filaments through a nozzle with a diameter of 630 μm. Accordingly, the lattice structures were printed precisely with a suitable resolution. The 3D-printed structures demonstrated significant wet stability due to the high aspect ratio of the nano- and microfibrils cellulose, reinforced the hydrogels, and protected the shape from extensive shrinkage upon drying. Furthermore, all printed samples had a porosity higher than 80% and a high-water uptake capacity of up to 46 g/g. Altogether, these fully bio-based, porous, and wet stable 3D structures might have an opportunity in biomedical fields.

Fabrication and evaluation of porous and conductive nanofibrous scaffolds for nerve tissue engineering

Peripheral nerve repair is still one of the major clinical challenges which has received a great deal of attention. Nerve tissue engineering is a novel treatment approach that provides a permissive environment for neural cells to overcome the constraints of repair. Conductivity and interconnected porosity are two required characteristics for a scaffold to be effective in nerve regeneration. In this study, we aimed to fabricate a conductive scaffold with controlled porosity using polycaprolactone (PCL) and chitosan (Chit), FDA approved materials for the use in implantable medical devices. A novel method of using tetrakis (hydroxymethyl) phosphonium chloride (THPC) and formaldehyde was applied for in situ synthesis of gold nanoparticles (AuNPs) on the scaffolds. In order to achieve desirable porosity, different percentage of polyethylene oxide (PEO) was used as sacrificial fiber. Fourier transform infrared spectroscopy (FTIR) and field emission scanning electron microscopy (FE-SEM) results demonstrated the complete removing of PEO from the scaffolds after washing and construction of interconnected porosities, respectively. Elemental and electrical analysis revealed the successful synthesis of AuNPs with uniform distribution and small average diameter on the PCL/Chit scaffold. Contact angle measurements showed the effect of porosity on hydrophilic properties of the scaffolds, where the porosity of 75-80% remarkably improved surface hydrophilicity. Finally, the effect of conductive nanofibrous scaffold on Schwann cells morphology and vaibility was investigated using FE-SEM and MTT assay, respectively. The results showed that these conductive scaffolds had no cytotoxic effect and support the spindle-shaped morphology of cells with elongated process which are typical of Schwann cell cultures.

Valproic Acid Labeled Chitosan Nanoparticles Promote the Proliferation and Differentiation of Neural Stem Cells After Spinal Cord Injury

Chitosan nanoparticles and valproic acid are demonstrated as the protective agents in the treatment of spinal cord injury (SCI). However, the effects of valproic acid-labeled chitosan nanoparticles (VA-CN) on endogenous spinal cord neural stem cells (NSCs) following SCI and the underlying mechanisms involved remain to be elucidated. In this study, the VA-CN was constructed and the effects of VA-CN on NSCs were assessed in a rat model of SCI. We found VA-CN treatment promoted recovery of the tissue and locomotive function following SCI. Moreover, administration of VA-CN significantly enhanced neural stem cell proliferation and the expression levels of neurotrophic factors following SCI. Furthermore, administration of VA-CN led to a decrease in the number of microglia following SCI. In addition, VA-CN treatment significantly increased the Tuj 1- positive cells in the spinal cord of the SCI rats, suggesting that VA-CN could enhance the differentiation of NSCs following SCI. In conclusion, these results demonstrated that VA-CN could improve the functional and histological recovery through promoting the proliferation and differentiation of NSCs following SCI, which would provide a newly potential therapeutic manner for the treatment of SCI.

A Comparative Review of Natural and Synthetic Biopolymer Composite Scaffolds

Tissue engineering (TE) and regenerative medicine integrate information and technology from various fields to restore/replace tissues and damaged organs for medical treatments. To achieve this, scaffolds act as delivery vectors or as cellular systems for drugs and cells; thereby, cellular material is able to colonize host cells sufficiently to meet up the requirements of regeneration and repair. This process is multi-stage and requires the development of various components to create the desired neo-tissue or organ. In several current TE strategies, biomaterials are essential components. While several polymers are established for their use as biomaterials, careful consideration of the cellular environment and interactions needed is required in selecting a polymer for a given application. Depending on this, scaffold materials can be of natural or synthetic origin, degradable or nondegradable. In this review, an overview of various natural and synthetic polymers and their possible composite scaffolds with their physicochemical properties including biocompatibility, biodegradability, morphology, mechanical strength, pore size, and porosity are discussed. The scaffolds fabrication techniques and a few commercially available biopolymers are also tabulated.

Graphene-based hybrid materials as promising scaffolds for peripheral nerve regeneration

Peripheral nerve injury (PNI) is a serious clinical health problem caused by the damage of peripheral nerves which results in neurological deficits and permanent disability. There are several factors that may cause PNI such as localized damage (car accident, trauma, electrical injury) and outbreak of the systemic diseases (autoimmune or diabetes). While various diagnostic procedures including X-ray, magnetic resonance imaging (MRI), as well as other type of examinations such as electromyography or nerve conduction studies have been efficiently developed, a full recovery in patients with PNI is in many cases deficient or incomplete. This is the reason why additional therapeutic strategies should be explored to favor a complete rehabilitation in order to get appropriate nerve injury regeneration. The use of biomaterials acting as scaffolds opens an interesting approach in regenerative medicine and tissue engineering applications due to their ability to guide the growth of new tissues, adhesion and proliferation of cells including the expression of bioactive signals. This review discusses the preparation and therapeutic strategies describing in vitro and in vivo experiments using graphene-based materials in the context of PNI and their ability to promote nerve tissue regeneration.

Biocompatible Electrospun Polycaprolactone-Polyaniline Scaffold Treated with Atmospheric Plasma to Improve Hydrophilicity

Conductive polymers (CPs) have recently been applied in the development of scaffolds for tissue engineering applications in attempt to induce additional cues able to enhance tissue growth. Polyaniline (PANI) is one of the most widely studied CPs, but it requires to be blended with other polymers in order to be processed through conventional technologies. Here, we propose the fabrication of nanofibers based on a polycaprolactone (PCL)-PANI blend obtained using electrospinning technology. An extracellular matrix-like fibrous substrate was obtained showing a good stability in the physiological environment (37 °C in PBS solution up 7 days). However, since the high hydrophobicity of the PCL-PANI mats (133.5 ± 2.2°) could negatively affect the biological response, a treatment with atmospheric plasma was applied on the nanofibrous mats, obtaining a hydrophilic surface (67.1 ± 2°). In vitro tests were performed to confirm the viability and the physiological-like morphology of human foreskin fibroblast (HFF-1) cells cultured on the plasma treated PCL-PANI nanofibrous scaffolds.

Optimizing the electrical conductivity of polyacrylonitrile/polyaniline with nickel nanoparticles for the enhanced electrostimulation of Schwann cells proliferation

Tissue engineering scaffolds made of biocompatible polymers are promising alternatives for nerve reparation. For this application, cell proliferation will be speeded up by electrostimulation, which required electrically-conductive materials. Here, a biomimicking scaffold with optimized conductivity was developed from electrospun polyacrylonitrile/electrically-conductive polyaniline (PAN/PANI) nanofibers doped with Ni nanoparticles. PAN/PANI/Ni was biocompatible for Schwann cells and exhibited a suitable tensile strength and wettability for cell proliferation. When compared with unmodified PAN/PANI, the electrical conductivity of PAN/PANI/Ni was 6.4 fold higher. Without electrostimulation, PAN/PANI and PAN/PANI/Ni exhibited similar Schwann cells' proliferation rates. Upon electrostimulation at 100 mV cm^-1 for one hour per day over five days, PAN/PANI/Ni accelerated Schwann cells' proliferation 2.1 times compared to PAN/PANI. These results demonstrate the importance of expanding the electrical conductivity of the tissue engineering scaffold to ensure optimal electrostimulation of nerve cell growth. Additionally, this study describes a straightforward approach to modulate the electrical conductivity of polymeric materials via the addition of Ni nanoparticles that can be applied to different biomimicking scaffolds for nerve healing.

Modern Porous Polymer Implants: Synthesis, Properties, and Application

Abstract

The needs of modern surgery triggered the intensive development of transplantology, medical materials science, and tissue engineering. These directions require the use of innovative materials, among which porous polymers occupy one of the leading positions. The use of natural and synthetic polymers makes it possible to adjust the structure and combination of properties of a material to its particular application. This review generalizes and systematizes the results of recent studies describing requirements imposed on the structure and properties of synthetic (or artificial) porous polymer materials and implants on their basis and the advantages and limitations of synthesis methods. The most extensively employed, promising initial materials are considered, and the possible areas of application of polymer implants based on these materials are highlighted.

Preparation and characterization of self-electrical stimuli conductive gellan based nano scaffold for nerve regeneration containing chopped short spun nanofibers of PVDF/MCM41 and polyaniline/graphene nanoparticles: Physical, mechanical and morphological studies

Conductive self -electrical stimuli bioactive scaffolds could be used the potential for peripheral nerve regeneration with the maximum efficiency. To produce such conductive self-electrical stimuli bioactive scaffolds, chopped spun piezoelectric nanofibers of polyvinylidene fluoride/mesoporous silica nanoparticle (PVDF/MCM41) are prepared and incorporated in gellan/polyaniline/graphene (gellan/PAG) nanocomposites which have been previously prepared by incorporation of polyaniline/graphene (PAG) nanoparticles in gellan gel at 80 °C. Highly conductive binary doped polyaniline/graphene nanoparticles are prepared by chemical oxidative polymerization of aniline monomer using in-suite precipitation polymerization method in presence of graphene nanoparticles and sodium dodecyl sulfate. All intermediate and final products including spun PVDF/MCM41 nanofibers, PAG nanoparticles, and gellan-gelatin gel scaffolds containing PVDF/MCM41 nano spun fibers and PAG nanoparticles are characterized using different analysis methods. Chemical and structural analyses of PAG nanoparticles and PVDF/MCM41 nanofibers have been done using FTIR and XRD methods. The morphological structure of different samples is investigated using SEM. Morphological investigation and DLS results confirm fabrication of MCM41 nanoparticle with a completely spherical shape and the average size of 50 nm of which have been dispersed in electrospun PVDF nanofibers very well. Also, the preparation of PAG nanoparticle with high conductivity is verified with morphological and conductivity tests. MTT easy and biocompatibility test results indicate potential applicability of the prepared conductive self -stimuli nano-scaffold for nerve regeneration applications.

A Review on Chitosan's Uses as Biomaterial: Tissue Engineering, Drug Delivery Systems and Cancer Treatment

Chitosan, derived from chitin, is a biopolymer consisting of arbitrarily distributed β-(1-4)-linked D-glucosamine and N-acetyl-D-glucosamine that exhibits outstanding properties- biocompatibility, biodegradability, non-toxicity, antibacterial activity, the capacity to form films, and chelating of metal ions. Most of these peculiar properties are attributed to the presence of free protonable amino groups along the chitosan backbone, which also gives it solubility in acidic conditions. Moreover, this biopolymer can also be physically modified, thereby presenting a variety of forms to be developed. Consequently, this polysaccharide is used in various fields, such as tissue engineering, drug delivery systems, and cancer treatment. In this sense, this review aims to gather the state-of-the-art concerning this polysaccharide when used as a biomaterial, providing information about its characteristics, chemical modifications, and applications. We present the most relevant and new information about this polysaccharide-based biomaterial's applications in distinct fields and also the ability of chitosan and its various derivatives to selectively permeate through the cancer cell membranes and exhibit anticancer activity, and the possibility of adding several therapeutic metal ions as a strategy to improve the therapeutic potential of this polymer.