Cheung CKH, Not C. Degradation efficiency of biodegradable plastics in subtropical open-air and marine environments: Implications for plastic pollution. THE SCIENCE OF THE TOTAL ENVIRONMENT 2024; 938:173397. [PMID: 38797407 DOI: 10.1016/j.scitotenv.2024.173397] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 03/19/2024] [Revised: 05/17/2024] [Accepted: 05/19/2024] [Indexed: 05/29/2024]
Abstract
Bioplastics are increasingly used as a solution to tackle plastic pollution problems. However, their degradability in natural environments is currently under debate. To evaluate their degradation efficiencies, we conducted in-situ degradation experiments in an open-air and two marine environments in Hong Kong. Three groups of biodegradable plastic were tested, namely (1) additive-modified low-density polyethylene (LDPE), labelled as oxo-biodegradable or photodegradable plastics, (2) polylactic acid (PLA), and (3) polyvinyl alcohol (PVA)/starch blends. Most biodegradable plastics fail to completely degrade but remain visually present after six months of exposure. Only PLA is able to demonstrate 100 % disintegration in one to three months in marine settings, suggesting that subtropical marine environments may favor PLA degradation. Biodegradable plastics that are bio-based (PLA and PVA/Starch blends) show notably larger mass losses by 23-100 % than the fossil-based ones (modified-LDPE). Our results reveal higher degradation efficiencies of PLA and PVA/Cassava starch blend in marine than open-air settings (with mass losses larger by 50 %, and by 39-41 %, respectively), potentially via biodegradation and hydrolysis. Meanwhile, modified-LDPE and PVA/Corn starch blends in general show higher degradation efficiencies in open-air than marine settings (with mass losses larger by 2 %, and by 17-33 %, respectively), potentially via abiotic oxidation. Since all tested biodegradable plastics exhibit potential fragmentation signs, further investigation is needed to characterize the behaviours of the microplastics generated. The current labelling on biodegradable bags fails to provide comprehensive information regarding their actual environmental degradation behaviours, especially considering their fragmentation risk and limited degradation exhibited in this study. This highlights the imperative for improved messaging to ensure consumers are better informed about these products.
Collapse
Affiliation(s)
- Coco Ka Hei Cheung
- Department of Earth Sciences, The University of Hong Kong, Pokfulam, Hong Kong; The Swire Institute of Marine Science, The University of Hong Kong, Pokfulam, Hong Kong.
| | - Christelle Not
- Department of Earth Sciences, The University of Hong Kong, Pokfulam, Hong Kong; The Swire Institute of Marine Science, The University of Hong Kong, Pokfulam, Hong Kong.
| |
Collapse
|
2
|
Read T, Chan CM, Chaléat C, Laycock B, Pratt S, Lant P. The effect of additives on the biodegradation of polyhydroxyalkanoate (PHA) in marine field trials. THE SCIENCE OF THE TOTAL ENVIRONMENT 2024; 931:172771. [PMID: 38670377 DOI: 10.1016/j.scitotenv.2024.172771] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 12/22/2023] [Revised: 03/12/2024] [Accepted: 04/23/2024] [Indexed: 04/28/2024]
Abstract
The persistence of conventional fossil fuel-derived plastics in marine ecosystems has raised significant environmental concerns. Biodegradable plastics are being explored as an alternative. This study investigates the biodegradation behaviour in two marine environments of melt-extruded sheets of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) bioplastic as well as blends of PHBV with a non-toxic plasticiser (triethyl citrate, TEC) and composites of PHBV with wood flour. Samples were submerged for up to 35 weeks in two subtropical marine conditions: on the sandy seabed in the sublittoral benthic zone and the sandy seabed of an open air mesocosm with pumped seawater. Rates of biodegradation, lag times and times to 95 % mass loss (T95) were determined through mass loss data and Gompertz modelling. Mechanisms of biodegradation were studied through changes in molecular weight, mechanical properties and surface features. Results reveal a rapid biodegradation rate for all PHBV samples, demonstrating a range of specific biodegradation rates relative to exposed surface area of 0.03 ± 0.01 to 0.09 ± 0.04 mg.d-1.cm-2. This rapid rate of biodegradation meant that the subtle variations in biodegradation mechanisms across different sample thicknesses and additive compositions had little effect on overall lifetimes, with the T95 for most samples being around 250-350 days, regardless of site, highlighting the robust biodegradability of PHBV in seawater. It was only the PHBV-wood flour composite that showed faster biodegradation, and that was only in the exposed ocean site. The mesocosm site was otherwise shown to be a good model for the open ocean, with very comparable biodegradation rates and changes in mechanical properties over time.
Collapse
Affiliation(s)
- Tracey Read
- School of Chemical Engineering, The University of Queensland, St Lucia, Brisbane, Queensland 4072, Australia
| | - Clement Matthew Chan
- School of Chemical Engineering, The University of Queensland, St Lucia, Brisbane, Queensland 4072, Australia
| | - Céline Chaléat
- School of Chemical Engineering, The University of Queensland, St Lucia, Brisbane, Queensland 4072, Australia
| | - Bronwyn Laycock
- School of Chemical Engineering, The University of Queensland, St Lucia, Brisbane, Queensland 4072, Australia.
| | - Steven Pratt
- School of Chemical Engineering, The University of Queensland, St Lucia, Brisbane, Queensland 4072, Australia
| | - Paul Lant
- School of Chemical Engineering, The University of Queensland, St Lucia, Brisbane, Queensland 4072, Australia
| |
Collapse
|
3
|
Lim JH, Han WB, Jang TM, Ko GJ, Shin JW, Han S, Kang H, Eom CH, Choi SJ, Rajaram K, Bandodkar AJ, Yeo WH, Hwang SW. Synthesis of shape-programmable elastomer for a bioresorbable, wireless nerve stimulator. Biosens Bioelectron 2024; 254:116222. [PMID: 38518560 DOI: 10.1016/j.bios.2024.116222] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/18/2023] [Revised: 03/01/2024] [Accepted: 03/11/2024] [Indexed: 03/24/2024]
Abstract
Materials that have the ability to manipulate shapes in response to stimuli such as heat, light, humidity and magnetism offer a means for versatile, sophisticated functions in soft robotics or biomedical implants, while such a reactive transformation has certain drawbacks including high operating temperatures, inherent rigidity and biological hazard. Herein, we introduce biodegradable, self-adhesive, shape-transformable poly (L-lactide-co-ε-caprolactone) (BSS-PLCL) that can be triggered via thermal stimulation near physiological temperature (∼38 °C). Chemical inspections confirm the fundamental properties of the synthetic materials in diverse aspects, and study on mechanical and biochemical characteristics validates exceptional stretchability up to 800 % and tunable dissolution behaviors under biological conditions. The integration of the functional polymer with a bioresorbable electronic system highlights potential for a wide range of biomedical applications.
Collapse
Affiliation(s)
- Jun Hyeon Lim
- KU-KIST Graduate School of Converging Science and Technology, Korea University, Seoul, 02841, Republic of Korea
| | - Won Bae Han
- KU-KIST Graduate School of Converging Science and Technology, Korea University, Seoul, 02841, Republic of Korea; George W. Woodruff School of Mechanical Engineering, Georgia Institute of Technology, Atlanta, GA, 30332, USA; IEN Center for Wearable Intelligent Systems and Healthcare, Georgia Institute of Technology, Atlanta, GA, 30332, USA
| | - Tae-Min Jang
- KU-KIST Graduate School of Converging Science and Technology, Korea University, Seoul, 02841, Republic of Korea
| | - Gwan-Jin Ko
- KU-KIST Graduate School of Converging Science and Technology, Korea University, Seoul, 02841, Republic of Korea
| | - Jeong-Woong Shin
- KU-KIST Graduate School of Converging Science and Technology, Korea University, Seoul, 02841, Republic of Korea
| | - Sungkeun Han
- KU-KIST Graduate School of Converging Science and Technology, Korea University, Seoul, 02841, Republic of Korea
| | - Heeseok Kang
- KU-KIST Graduate School of Converging Science and Technology, Korea University, Seoul, 02841, Republic of Korea; Center for Advanced Biomolecular Recognition, Biomedical Research Division, Korea Institute of Science and Technology (KIST), Seoul, 02792, Republic of Korea
| | - Chan-Hwi Eom
- KU-KIST Graduate School of Converging Science and Technology, Korea University, Seoul, 02841, Republic of Korea
| | - So Jeong Choi
- KU-KIST Graduate School of Converging Science and Technology, Korea University, Seoul, 02841, Republic of Korea
| | - Kaveti Rajaram
- KU-KIST Graduate School of Converging Science and Technology, Korea University, Seoul, 02841, Republic of Korea; Department of Electrical and Computer Engineering, North Carolina State University, Raleigh, NC, 27606, USA; Center for Advanced Self-Powered Systems of Integrated Sensors and Technologies (ASSIST), North Carolina State University, Raleigh, NC, 27606, USA
| | - Amay J Bandodkar
- Department of Electrical and Computer Engineering, North Carolina State University, Raleigh, NC, 27606, USA; Center for Advanced Self-Powered Systems of Integrated Sensors and Technologies (ASSIST), North Carolina State University, Raleigh, NC, 27606, USA
| | - Woon-Hong Yeo
- George W. Woodruff School of Mechanical Engineering, Georgia Institute of Technology, Atlanta, GA, 30332, USA; IEN Center for Wearable Intelligent Systems and Healthcare, Georgia Institute of Technology, Atlanta, GA, 30332, USA; Wallace H. Coulter Department of Biomedical Engineering, Georgia Tech and Emory University School of Medicine, Atlanta, GA, 30332, USA; Parker H. Petit Institute for Bioengineering and Biosciences, Institute for Materials, Institute for Robotics and Intelligent Machines, Georgia Institute of Technology, Atlanta, GA, 30332, USA
| | - Suk-Won Hwang
- KU-KIST Graduate School of Converging Science and Technology, Korea University, Seoul, 02841, Republic of Korea; Department of Integrative Energy Engineering, Korea University, Seoul, 02841, Republic of Korea; Center for Biomaterials, Biomedical Research Institute, Korea Institute of Science and Technology (KIST), Seoul, 02792, Republic of Korea.
| |
Collapse
|
4
|
La Fuente Arias CI, González-Martínez C, Chiralt A. Biodegradation behavior of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) containing phenolic compounds in seawater in laboratory testing conditions. THE SCIENCE OF THE TOTAL ENVIRONMENT 2024; 944:173920. [PMID: 38880150 DOI: 10.1016/j.scitotenv.2024.173920] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 02/15/2024] [Revised: 06/05/2024] [Accepted: 06/09/2024] [Indexed: 06/18/2024]
Abstract
Biodegradation in marine medium of PHBV films with or without 5 % wt. of phenolic compounds (catechin, ferulic acid, and vanillin) was assessed at laboratory scale. Respirometric analyses and film disintegration kinetics were used to monitor the process over a period of 162 days. Structural changes in the films were analyzed throughout the exposure period using FESEM, DSC, Thermogravimetric analyses, XRD, and FTIR spectra. Respirometric tests showed complete biodegradation of all materials during the exposure period (the biodegradation half-time ranged between 63 and 79 days) but at different rates, depending on the phenolic compound incorporated. Ferulic acid and vanillin accelerate the PHBV biodegradation, whereas catechin delayed the process. Disintegration kinetics confirmed these results and showed that degradation occurred from the surface to the interior of the films. This was controlled by the degradation rate of the polymer amorphous phase and the formation of a biomass coating on the film surface. This is the result of the compounds generated by polymer degradation in combination with excretions from microorganisms. This coating has the potential to affect the enzyme diffusion to the polymer substrate. Moreover, the cohesion forces of the amorphous phase (reflected in its glass transition temperature) affected its degradation rate, while the slower degrading crystalline fragments were released, thus contributing to the disintegration process on the film's surface. Ferulic acid, with its hydrolytic effect, enhanced degradation, as did vanillin for its plasticizing and weakening effect in the amorphous phase of polymer matrix. In contrast, catechin with cross-linking effect hindered the progress of the material degradation, considerably slowing down the process rate.
Collapse
Affiliation(s)
- Carla I La Fuente Arias
- Universitat Politècnica de València (UPV), Food Engineering Research Institute (FoodUPV), 46022, Valencia, Spain.
| | - Chelo González-Martínez
- Universitat Politècnica de València (UPV), Food Engineering Research Institute (FoodUPV), 46022, Valencia, Spain
| | - Amparo Chiralt
- Universitat Politècnica de València (UPV), Food Engineering Research Institute (FoodUPV), 46022, Valencia, Spain
| |
Collapse
|
5
|
Amin H, Ibrahim IM, Hassanein EHM. Weaponizing chitosan and its derivatives in the battle against lung cancer. Int J Biol Macromol 2024; 272:132888. [PMID: 38844273 DOI: 10.1016/j.ijbiomac.2024.132888] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/27/2023] [Revised: 05/28/2024] [Accepted: 06/02/2024] [Indexed: 06/11/2024]
Abstract
Lung cancer (LC) is a crisis of catastrophic proportions. It is a global problem and urgently requires a solution. The classic chemo drugs are lagging behind as they lack selectivity, where their side effects are spilled all over the body, and these adverse effects would be terribly tragic for LC patients. Therefore, they could make a bad situation worse, inflict damage on normal cells, and inflict pain on patients. Since our confidence in classic drugs is eroding, chitosan can offer a major leap forward in LC therapy. It can provide the backbone and the vehicle that enable chemo drugs to penetrate the hard shell of LC. It could be functionalized in a variety of ways to deliver a deadly payload of toxins to kill the bad guys. It is implemented in formulation of polymeric NPs, lipidic NPs, nanocomposites, multiwalled carbon nanotubes, and phototherapeutic agents. This review is a pretty clear proof of chitosan's utility as a weapon in battling LC. Chitosan-based formulations could work effectively to kill LC cells. If a researcher is looking for a vehicle for medication for LC therapy, chitosan can be an appropriate choice.
Collapse
Affiliation(s)
- Haitham Amin
- Department of Pharmaceutics and Pharmaceutical Technology, Faculty of Pharmacy, Al-Azhar University, Assiut 71524, Egypt.
| | - Islam M Ibrahim
- Department of Pharmacology and Toxicology, Faculty of Pharmacy, Beni-Suef University, Beni-Suef, Egypt.
| | - Emad H M Hassanein
- Department of Pharmacology and Toxicology, Faculty of Pharmacy, Al-Azhar University, Assiut 71524, Egypt.
| |
Collapse
|
6
|
Zheng J, Park K, Jang J, Son D, Park J, Kim J, Yoo JE, You S, Kim IY. Utilizing stem cell-secreted molecules as a versatile toolbox for skin regenerative medicine. J Control Release 2024; 370:583-599. [PMID: 38729435 DOI: 10.1016/j.jconrel.2024.05.009] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/04/2023] [Revised: 04/14/2024] [Accepted: 05/06/2024] [Indexed: 05/12/2024]
Abstract
Stem cells are recognized as an important target and tool in regenerative engineering. In this study, we explored the feasibility of engineering amniotic fluid-derived mesenchymal stem cell-secreted molecules (afMSC-SMs) as a versatile bioactive material for skin regenerative medicine applications in a time- and cost-efficient and straightforward manner. afMSC-SMs, obtained in powder form through ethanol precipitation, effectively contributed to preserving the self-renewal capacity and differentiation potential of primary human keratinocytes (pKCs) in a xeno-free environment, offering a potential alternative to traditional culture methods for their long-term in vitro expansion, and allowed them to reconstitute a fully stratified epithelium sheet on human dermal fibroblasts. Furthermore, we demonstrated the flexibility of afMSC-SMs in wound healing and hair regrowth through injectable hydrogel and nanogel-mediated transdermal delivery systems, respectively, expanding the pool of regenerative applications. This cell-free approach may offer several potential advantages, including streamlined manufacturing processes, scalability, controlled formulation, longer shelf lives, and mitigation of risks associated with living cell transplantation. Accordingly, afMSC-SMs could serve as a promising therapeutic toolbox for advancing cell-free regenerative medicine, simplifying their broad applicability in various clinical settings.
Collapse
Affiliation(s)
- Jie Zheng
- Department of Biotechnology, College of Life Sciences and Biotechnology, Korea University, Seoul 02841, Republic of Korea
| | - Kyoungmin Park
- Department of Biotechnology, College of Life Sciences and Biotechnology, Korea University, Seoul 02841, Republic of Korea
| | - Jihoon Jang
- Department of Biotechnology, College of Life Sciences and Biotechnology, Korea University, Seoul 02841, Republic of Korea
| | - Daryeon Son
- Department of Biotechnology, College of Life Sciences and Biotechnology, Korea University, Seoul 02841, Republic of Korea; Institute of Animal Molecular Biotechnology, Korea University, Seoul 02841, Republic of Korea
| | - Junghyun Park
- Department of Biotechnology, College of Life Sciences and Biotechnology, Korea University, Seoul 02841, Republic of Korea
| | - Jonggun Kim
- Institute of Regenerative Medicine, SL, Therapeutics Inc., Seoul 02841, Republic of Korea
| | - Jeong-Eun Yoo
- Institute of Regenerative Medicine, SL, Therapeutics Inc., Seoul 02841, Republic of Korea
| | - Seungkwon You
- Department of Biotechnology, College of Life Sciences and Biotechnology, Korea University, Seoul 02841, Republic of Korea; Institute of Animal Molecular Biotechnology, Korea University, Seoul 02841, Republic of Korea.
| | - In-Yong Kim
- Catholic High-Performance Cell Therapy Center & Department of Medical Life Science, College of Medicine, The Catholic University of Korea, Seoul 06591, Republic of Korea.
| |
Collapse
|
7
|
Tian H, Du Y, Luo X, Dong J, Chen S, Hu X, Zhang M, Liu Z, Abolfathi S. Understanding visible light and microbe-driven degradation mechanisms of polyurethane plastics: Pathways, property changes, and product analysis. WATER RESEARCH 2024; 259:121856. [PMID: 38875861 DOI: 10.1016/j.watres.2024.121856] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 12/18/2023] [Revised: 05/20/2024] [Accepted: 05/29/2024] [Indexed: 06/16/2024]
Abstract
The accumulation of polyurethane plastics (PU-PS) in the environment is on the rise, posing potential risks to the health and function of ecosystems. However, little is known about the degradation behavior of PU-PS in the environment, especially water environment. To address this knowledge gap, we investigated and isolated a degrading strain of Streptomyces sp. B2 from the surface of polyurethane coatings. Subsequently, a photoreactor was employed to simulate the degradation process of bio-based polyurethane (BPU) and petroleum-based polyurethane (PPU) under three conditions, including single microorganism (SM), single light exposure (SL), and combined light exposure/microorganism action (ML) in aqueous solution. The results indicated that PU-PS mainly relies on biodegradation, with the highest degradation rate observed after 28 d under SM condition (BPU 5.69 %; PPU 5.25 %). SL inhibited microbial growth and degradation, with the least impact on plastic degradation. Microorganisms colonized the plastic surface, secreting relevant hydrolytic enzymes and organic acids into the culture medium, providing a negative charge. The carbon chains were broken and aged through hydrogen peroxide induction or attack by oxygen free radicals. This process promoted the formation of oxidized functional groups such as OH and CO, disrupting the polymer's structure. Consequently, localized fragmentation and erosion of the microstructure occurred, resulting in the generation of secondary microplastic (MPs) particles, weight loss of the original plastic, increased surface roughness, and enhanced hydrophilicity. Additionally, BPU exhibited greater degradability than PPU, as microorganisms could utilize the produced fatty acids, which promoted their reproduction. In contrast, PPU degradation generated a large amount of isocyanate, potentially toxic to cells and inhibiting biodegradation. This study unveils the significant role of microorganisms in plastic degradation and the underlying degradation mechanisms of BPU, providing a novel strategy for polyurethane degradation and valuable information for comprehensive assessment of the behavior and fate of MPs in the environment.
Collapse
Affiliation(s)
- Hongyu Tian
- National Engineering Research Center for Efficient Utilization of Soil and Fertilizer Resources, College of Recourses and Environment, Shandong Agricultural University, Taian, Shandong 271018, China
| | - Yuping Du
- National Engineering Research Center for Efficient Utilization of Soil and Fertilizer Resources, College of Recourses and Environment, Shandong Agricultural University, Taian, Shandong 271018, China
| | - Xinyu Luo
- National Engineering Research Center for Efficient Utilization of Soil and Fertilizer Resources, College of Recourses and Environment, Shandong Agricultural University, Taian, Shandong 271018, China
| | - Jingjing Dong
- National Engineering Research Center for Efficient Utilization of Soil and Fertilizer Resources, College of Recourses and Environment, Shandong Agricultural University, Taian, Shandong 271018, China
| | - Siyu Chen
- National Engineering Research Center for Efficient Utilization of Soil and Fertilizer Resources, College of Recourses and Environment, Shandong Agricultural University, Taian, Shandong 271018, China
| | - Xiaomin Hu
- National Engineering Research Center for Efficient Utilization of Soil and Fertilizer Resources, College of Recourses and Environment, Shandong Agricultural University, Taian, Shandong 271018, China
| | - Min Zhang
- National Engineering Research Center for Efficient Utilization of Soil and Fertilizer Resources, College of Recourses and Environment, Shandong Agricultural University, Taian, Shandong 271018, China
| | - Zhiguang Liu
- National Engineering Research Center for Efficient Utilization of Soil and Fertilizer Resources, College of Recourses and Environment, Shandong Agricultural University, Taian, Shandong 271018, China.
| | - Soroush Abolfathi
- School of Engineering, University of Warwick, Coventry, CV47AL, United Kingdom
| |
Collapse
|
8
|
Xu D, Li Z, Deng Z, Nie X, Pan Y, Cheng G. Degradation profiles of the poly(ε-caprolactone)/silk fibroin electrospinning membranes and their potential applications in tissue engineering. Int J Biol Macromol 2024; 266:131124. [PMID: 38522701 DOI: 10.1016/j.ijbiomac.2024.131124] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/16/2023] [Revised: 03/14/2024] [Accepted: 03/22/2024] [Indexed: 03/26/2024]
Abstract
Degradation profiles are critical for the optimal application of electrospun polymer nanofibers in tissue regeneration, wound healing, and drug delivery systems. In this study, natural and synthetic polymers and their composites were subjected to in vivo transplantation and in vitro treatment with lipases, macrophages, and acetic acid to evaluate their degradation patterns. The effects of environmental stimulation, surface wettability, and polymer components on the degradation profiles of the electrospinning poly(ε-caprolactone)/silk fibroin (PCL/SF) nanofibers were first evaluated. In vivo degradation study demonstrated that bulk degradation, characterized by the transition from microfibers to nanofibers, and surface erosion, characterized by fusion between the microfibers or direct erosion from both ends of the microfibers, occurred in the electrospun membranes; however, bulk degradation dominated their overall degradation. Furthermore, the degradation rates of the electrospun PCL/SF membranes varied according to the composition, morphology, and surface wettability of the composite membranes. After the incorporation of silk fibroin (SF), the degradation rate of the SF/PCL composite membranes was faster, accompanied by larger values of weight loss and molecular weight (Mw) loss when compared with that of the pure poly(ε-caprolactone) (PCL) membrane, indicating a close relationship between degradation rate and hydrophilicity of the electrospinning membranes. The in vitro experimental results demonstrated that enzymes and oxidation partially resulted in the surface erosion of the PCL/SF microfibers. Consequently, bulk degradation and surface erosion coordinated with each other to enhance the hydrophilicity of the electrospinning membranes and accelerate the in vivo degradation.
Collapse
Affiliation(s)
- Dongdong Xu
- School and Hospital of Stomatology, Wenzhou Medical University, Wenzhou, Zhejiang, China
| | - Zongli Li
- School and Hospital of Stomatology, Wenzhou Medical University, Wenzhou, Zhejiang, China
| | - Zhennan Deng
- School and Hospital of Stomatology, Wenzhou Medical University, Wenzhou, Zhejiang, China
| | - Xin Nie
- School and Hospital of Stomatology, Wenzhou Medical University, Wenzhou, Zhejiang, China
| | - Yihuai Pan
- School and Hospital of Stomatology, Wenzhou Medical University, Wenzhou, Zhejiang, China.
| | - Gu Cheng
- School and Hospital of Stomatology, Wenzhou Medical University, Wenzhou, Zhejiang, China.
| |
Collapse
|
9
|
Schwab S, Nelson TF, Mecking S. Chemically Recyclable and Biodegradable Vulcanized Rubber. ACS SUSTAINABLE CHEMISTRY & ENGINEERING 2024; 12:6281-6288. [PMID: 38665800 PMCID: PMC11041115 DOI: 10.1021/acssuschemeng.3c08435] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Figures] [Subscribe] [Scholar Register] [Received: 12/21/2023] [Revised: 03/25/2024] [Accepted: 03/27/2024] [Indexed: 04/28/2024]
Abstract
The cross-linked nature of vulcanized rubbers as used in tire and many other applications prohibits an effective closed-loop mechanical or chemical recycling. Moreover, vulcanization significantly retards the material's biodegradation. Here, we report a recyclable and biodegradable rubber that is generated by the vulcanization of amorphous, unsaturated polyesters. The elastic material can be broken down via solvolysis into the underlying monomers. After removal of the vulcanized repeat units, the saturated monomers, constituting the major share of the material, can be recovered in overall recycling rates exceeding 90%. Respirometric biodegradation experiments by 13CO2 tracking under environmental conditions via the polyesters' diol monomer indicated depolymerization and partial mineralization of the vulcanized polyester rubbers.
Collapse
Affiliation(s)
- Simon
T. Schwab
- Chair of Chemical Materials Science,
Department of Chemistry, University of Konstanz, Universitätsstraße 10, 78464 Konstanz, Germany
| | - Taylor F. Nelson
- Chair of Chemical Materials Science,
Department of Chemistry, University of Konstanz, Universitätsstraße 10, 78464 Konstanz, Germany
| | - Stefan Mecking
- Chair of Chemical Materials Science,
Department of Chemistry, University of Konstanz, Universitätsstraße 10, 78464 Konstanz, Germany
| |
Collapse
|
10
|
Chai YJ, Syauqi TA, Sudesh K, Ee TL, Ban CC, Kar Mun AC, Anne Strain EM, Merican F, Rahim MA, Md Salleh K, Yin CS. Effects of poly(3-hydroxybutyrate) [P(3HB)] coating on the bacterial communities of artificial structures. PLoS One 2024; 19:e0300929. [PMID: 38635673 PMCID: PMC11025745 DOI: 10.1371/journal.pone.0300929] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 09/21/2023] [Accepted: 03/06/2024] [Indexed: 04/20/2024] Open
Abstract
The expanding urbanization of coastal areas has led to increased ocean sprawl, which has had both physical and chemical adverse effects on marine and coastal ecosystems. To maintain the health and functionality of these ecosystems, it is imperative to develop effective solutions. One such solution involves the use of biodegradable polymers as bioactive coatings to enhance the bioreceptivity of marine and coastal infrastructures. Our study aimed to explore two main objectives: (1) investigate PHA-degrading bacteria on polymer-coated surfaces and in surrounding seawater, and (2) comparing biofilm colonization between surfaces with and without the polymer coating. We applied poly(3-hydroxybutyrate) [P(3HB)) coatings on concrete surfaces at concentrations of 1% and 6% w/v, with varying numbers of coating cycles (1, 3, and 6). Our findings revealed that the addition of P(3HB) indeed promoted accelerated biofilm growth on the coated surfaces, resulting in an occupied area approximately 50% to 100% larger than that observed in the negative control. This indicates a remarkable enhancement, with the biofilm expanding at a rate roughly 1.5 to 2 times faster than the untreated surfaces. We observed noteworthy distinctions in biofilm growth patterns based on varying concentration and number of coating cycles. Interestingly, treatments with low concentration and high coating cycles exhibited comparable biofilm enhancements to those with high concentrations and low coating cycles. Further investigation into the bacterial communities responsible for the degradation of P(3HB) coatings identified mostly common and widespread strains but found no relation between the concentration and coating cycles. Nevertheless, this microbial degradation process was found to be highly efficient, manifesting noticeable effects within a single month. While these initial findings are promising, it's essential to conduct tests under natural conditions to validate the applicability of this approach. Nonetheless, our study represents a novel and bio-based ecological engineering strategy for enhancing the bioreceptivity of marine and coastal structures.
Collapse
Affiliation(s)
- Yee Jean Chai
- Centre for Global Sustainability Studies, Universiti Sains Malaysia, Minden, Penang, Malaysia
| | - Taufiq Ahmad Syauqi
- School of Biological Sciences, Universiti Sains Malaysia, Minden, Penang, Malaysia
| | - Kumar Sudesh
- School of Biological Sciences, Universiti Sains Malaysia, Minden, Penang, Malaysia
| | - Tan Leng Ee
- School of Housing, Building and Planning, Universiti Sains Malaysia, Minden, Penang, Malaysia
| | - Cheah Chee Ban
- School of Housing, Building and Planning, Universiti Sains Malaysia, Minden, Penang, Malaysia
| | - Amanda Chong Kar Mun
- Centre for Global Sustainability Studies, Universiti Sains Malaysia, Minden, Penang, Malaysia
| | - Elisabeth Marijke Anne Strain
- Institute for Marine and Antarctic Studies, University of Tasmania, Hobart, Australia
- Centre for Marine Socioecology, University of Tasmania, Hobart, Australia
| | - Faradina Merican
- School of Biological Sciences, Universiti Sains Malaysia, Minden, Penang, Malaysia
| | | | | | - Chee Su Yin
- Centre for Global Sustainability Studies, Universiti Sains Malaysia, Minden, Penang, Malaysia
| |
Collapse
|
11
|
Nzimande MC, Mtibe A, Tichapondwa S, John MJ. A Review of Weathering Studies in Plastics and Biocomposites-Effects on Mechanical Properties and Emissions of Volatile Organic Compounds (VOCs). Polymers (Basel) 2024; 16:1103. [PMID: 38675023 PMCID: PMC11054226 DOI: 10.3390/polym16081103] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/25/2024] [Revised: 04/05/2024] [Accepted: 04/11/2024] [Indexed: 04/28/2024] Open
Abstract
Polymeric materials undergo degradation when exposed to outdoor conditions due to the synergistic effects of sunlight, air, heat, and moisture. The degradation can lead to a decline in mechanical properties, fading, surface cracking, and haziness, attributed to the cleavage of the polymer chains and oxidation reactions. Accelerated weathering testing is a useful technique to evaluate the comparative photodegradation of materials within a reasonable timeframe. This review gives an overview of the different degradation mechanisms occurring in conventional plastics and bio-based materials. Case studies on accelerated weathering and its effect on the mechanical properties of conventional plastics and biocomposites are discussed. Different techniques for analysing volatile organic emissions (VOCs) have been summarized and studies highlighting the characterization of VOCs from aged plastics and biocomposites after aging have been cited.
Collapse
Affiliation(s)
- Monwabisi Cyril Nzimande
- Centre for Nanostructures and Advanced Materials, Chemicals Cluster, CSIR, Pretoria 6011, South Africa; (M.C.N.); (A.M.)
- Water Utilization and Environmental Engineering Division, Department of Chemical Engineering, University of Pretoria, Pretoria 0028, South Africa;
| | - Asanda Mtibe
- Centre for Nanostructures and Advanced Materials, Chemicals Cluster, CSIR, Pretoria 6011, South Africa; (M.C.N.); (A.M.)
| | - Shepherd Tichapondwa
- Water Utilization and Environmental Engineering Division, Department of Chemical Engineering, University of Pretoria, Pretoria 0028, South Africa;
| | - Maya Jacob John
- Centre for Nanostructures and Advanced Materials, Chemicals Cluster, CSIR, Pretoria 6011, South Africa; (M.C.N.); (A.M.)
- Department of Chemistry, Nelson Mandela University, Port Elizabeth 6031, South Africa
| |
Collapse
|
12
|
Lomakin S, Mikheev Y, Usachev S, Rogovina S, Zhorina L, Perepelitsina E, Levina I, Kuznetsova O, Shilkina N, Iordanskii A, Berlin A. Evaluation and Modeling of Polylactide Photodegradation under Ultraviolet Irradiation: Bio-Based Polyester Photolysis Mechanism. Polymers (Basel) 2024; 16:985. [PMID: 38611243 PMCID: PMC11013448 DOI: 10.3390/polym16070985] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/29/2024] [Revised: 03/25/2024] [Accepted: 04/02/2024] [Indexed: 04/14/2024] Open
Abstract
In our study, we investigated the accelerated aging process of PLA under 253.7 nm UV-C irradiation with the use of the GPC, NMR, FTIR, and DSC methods and formal kinetic analysis. The results of GPC and DSC indicated a significant degree of destructive changes in the PLA macromolecules, while spectroscopic methods NMR and FTIR showed maintenance of the PLA main structural elements even after a long time of UV exposure. In addition to that, the GPC method displayed the formation of a high molecular weight fraction starting from 24 h of irradiation, and an increase in its content after 144 h of irradiation. It has been shown for the first time that a distinctive feature of prolonged UV exposure is the occurrence of intra- and intermolecular radical recombination reactions, leading to the formation of a high molecular weight fraction of PLA decomposition products. This causes the observed slowdown of the photolysis process. It was concluded that photolysis of PLA is a complex physicochemical process, the mechanism of which depends on morphological changes in the solid phase of the polymer under UV radiation.
Collapse
Affiliation(s)
- Sergey Lomakin
- N. N. Semenov Federal Research Center for Chemical Physics Academy of Science, 119991 Moscow, Russia; (S.U.); (S.R.); (L.Z.); (O.K.); (N.S.); (A.B.)
- Emanuel Institute of Biochemical Physics, Russian Academy of Sciences, 119334 Moscow, Russia; (Y.M.); (I.L.)
| | - Yurii Mikheev
- Emanuel Institute of Biochemical Physics, Russian Academy of Sciences, 119334 Moscow, Russia; (Y.M.); (I.L.)
| | - Sergey Usachev
- N. N. Semenov Federal Research Center for Chemical Physics Academy of Science, 119991 Moscow, Russia; (S.U.); (S.R.); (L.Z.); (O.K.); (N.S.); (A.B.)
| | - Svetlana Rogovina
- N. N. Semenov Federal Research Center for Chemical Physics Academy of Science, 119991 Moscow, Russia; (S.U.); (S.R.); (L.Z.); (O.K.); (N.S.); (A.B.)
| | - Lubov Zhorina
- N. N. Semenov Federal Research Center for Chemical Physics Academy of Science, 119991 Moscow, Russia; (S.U.); (S.R.); (L.Z.); (O.K.); (N.S.); (A.B.)
| | - Evgeniya Perepelitsina
- Federal State Research Center for Chemical Physics and Medical Chemistry, Russian Academy of Sciences, 142432 Chernogolovka, Russia;
| | - Irina Levina
- Emanuel Institute of Biochemical Physics, Russian Academy of Sciences, 119334 Moscow, Russia; (Y.M.); (I.L.)
| | - Olga Kuznetsova
- N. N. Semenov Federal Research Center for Chemical Physics Academy of Science, 119991 Moscow, Russia; (S.U.); (S.R.); (L.Z.); (O.K.); (N.S.); (A.B.)
| | - Natalia Shilkina
- N. N. Semenov Federal Research Center for Chemical Physics Academy of Science, 119991 Moscow, Russia; (S.U.); (S.R.); (L.Z.); (O.K.); (N.S.); (A.B.)
| | - Alexey Iordanskii
- N. N. Semenov Federal Research Center for Chemical Physics Academy of Science, 119991 Moscow, Russia; (S.U.); (S.R.); (L.Z.); (O.K.); (N.S.); (A.B.)
| | - Alexander Berlin
- N. N. Semenov Federal Research Center for Chemical Physics Academy of Science, 119991 Moscow, Russia; (S.U.); (S.R.); (L.Z.); (O.K.); (N.S.); (A.B.)
| |
Collapse
|
13
|
Li Y, Jiao H, Zhang H, Wang X, Fu Y, Wang Q, Liu H, Yong YC, Guo J, Liu J. Biosafety consideration of nanocellulose in biomedical applications: A review. Int J Biol Macromol 2024; 265:130900. [PMID: 38499126 DOI: 10.1016/j.ijbiomac.2024.130900] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/10/2024] [Revised: 03/11/2024] [Accepted: 03/12/2024] [Indexed: 03/20/2024]
Abstract
Nanocellulose-based biomaterials have gained significant attention in various fields, especially in medical and pharmaceutical areas, due to their unique properties, including non-toxicity, high specific surface area, biodegradability, biocompatibility, and abundant feasible and sophisticated strategies for functional modification. The biosafety of nanocellulose itself is a prerequisite to ensure the safe and effective application of biomaterials as they interact with living cells, tissues, and organs at the nanoscale. Potential residual endogenous impurities and exogenous contaminants could lead to the failure of the intended functionalities or even serious health complications if they are not adequately removed and assessed before use. This review summarizes the sources of impurities in nanocellulose that may pose potential hazards to their biosafety, including endogenous impurities that co-exist in the cellulosic raw materials themselves and exogenous contaminants caused by external exposure. Strategies to reduce or completely remove these impurities are outlined and classified as chemical, physical, biological, and combined methods. Additionally, key points that require careful consideration in the interpretation of the biosafety evaluation outcomes were discussed to ensure the safety and effectiveness of the nanocellulose-based biomaterials in medical applications.
Collapse
Affiliation(s)
- Yan Li
- Biofuels Institute, School of Environment and Safety Engineering, c/o School of Emergency Management, Jiangsu University, Zhenjiang 212013, China
| | - Haixin Jiao
- Biofuels Institute, School of Environment and Safety Engineering, c/o School of Emergency Management, Jiangsu University, Zhenjiang 212013, China
| | - Hongxing Zhang
- Biofuels Institute, School of Environment and Safety Engineering, c/o School of Emergency Management, Jiangsu University, Zhenjiang 212013, China
| | - Xiangyu Wang
- Biofuels Institute, School of Environment and Safety Engineering, c/o School of Emergency Management, Jiangsu University, Zhenjiang 212013, China
| | - Yinyi Fu
- Biofuels Institute, School of Environment and Safety Engineering, c/o School of Emergency Management, Jiangsu University, Zhenjiang 212013, China
| | - Qianqian Wang
- Biofuels Institute, School of Environment and Safety Engineering, c/o School of Emergency Management, Jiangsu University, Zhenjiang 212013, China
| | - Huan Liu
- Biofuels Institute, School of Environment and Safety Engineering, c/o School of Emergency Management, Jiangsu University, Zhenjiang 212013, China
| | - Yang-Chun Yong
- Biofuels Institute, School of Environment and Safety Engineering, c/o School of Emergency Management, Jiangsu University, Zhenjiang 212013, China; Jiangsu Collaborative Innovation Center of Technology and Material of Water Treatment, Suzhou University of Science and Technology, Suzhou 215009, China
| | - Jiaqi Guo
- Jiangsu Co-Innovation Center for Efficient Processing and Utilization of Forest Resources and International Innovation Center for Forest Chemicals and Materials, Nanjing Forestry University, Nanjing 210037, China
| | - Jun Liu
- Biofuels Institute, School of Environment and Safety Engineering, c/o School of Emergency Management, Jiangsu University, Zhenjiang 212013, China; Jiangsu Collaborative Innovation Center of Technology and Material of Water Treatment, Suzhou University of Science and Technology, Suzhou 215009, China.
| |
Collapse
|
14
|
Hu L, He L, Cai L, Wang Y, Wu G, Zhang D, Pan X, Wang YZ. Deterioration of single-use biodegradable plastics in high-humidity air and freshwaters over one year: Significant disparities in surface physicochemical characteristics and degradation rates. JOURNAL OF HAZARDOUS MATERIALS 2024; 465:133170. [PMID: 38064942 DOI: 10.1016/j.jhazmat.2023.133170] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 07/18/2023] [Revised: 11/21/2023] [Accepted: 12/01/2023] [Indexed: 02/08/2024]
Abstract
More single-use plastics are accumulating in the environment, and likewise biodegradable plastics (BPs), which are being vigorously promoted, cannot escape the fate. Currently, studies on the actual degradation of BPs in open-air and freshwaters are underrepresented despite they are potentially headmost leakage and contamination sites for disposable BPs. Herein, we compared the degradation behavior of six BP materials and non-degradable polypropylene (PP) plastics over a 1-year in situ suspension in the high-humidity air, a eutrophic river, and an oligotrophic lake. Moreover, a 3-months laboratory incubation was performed to detect the release of dissolved organic carbon (DOC) from BPs. In both air and freshwaters, poly(p-dioxanone) (PPDO) degraded significantly while PP and polylactic acid (PLA) showed no signs of degradation. The average degradation rates of three poly(butylene adipate-co-terephthalate) (PBAT)-based films varied: 100% in river, 55% in lake, and 10% in air. In addition to PLA, surface chemical groups, hydrophilicity, and thermal stability of BPs changed, and microplastics were found on their surfaces. Correspondingly, BPs with faster degradation rates released relatively higher amounts of DOC. Environmental microbial and chemical characteristics may contribute to differences in BP degradation besides polymer specificity. Altogether, our results indicate the need for appropriate monitoring of BPs.
Collapse
Affiliation(s)
- Lingling Hu
- College of Environment, Zhejiang University of Technology, Hangzhou 310014, China; The Collaborative Innovation Center for Eco-Friendly and Fire-Safety Polymeric Materials (MoE), National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), State Key Laboratory of Polymer Materials Engineering, College of Chemistry, Sichuan University, Chengdu 610064, China; Shaoxing Research Institute, Zhejiang University of Technology, Shaoxing 312000, China
| | - Linlin He
- College of Environment, Zhejiang University of Technology, Hangzhou 310014, China
| | - Li Cai
- College of Environmental Science and Engineering, Donghua University, Shanghai 201620, China
| | - Yumeng Wang
- College of Environment, Zhejiang University of Technology, Hangzhou 310014, China
| | - Gang Wu
- The Collaborative Innovation Center for Eco-Friendly and Fire-Safety Polymeric Materials (MoE), National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), State Key Laboratory of Polymer Materials Engineering, College of Chemistry, Sichuan University, Chengdu 610064, China.
| | - Daoyong Zhang
- College of Environment, Zhejiang University of Technology, Hangzhou 310014, China
| | - Xiangliang Pan
- College of Environment, Zhejiang University of Technology, Hangzhou 310014, China.
| | - Yu-Zhong Wang
- The Collaborative Innovation Center for Eco-Friendly and Fire-Safety Polymeric Materials (MoE), National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), State Key Laboratory of Polymer Materials Engineering, College of Chemistry, Sichuan University, Chengdu 610064, China
| |
Collapse
|
15
|
Nik Mut NN, Na J, Jung J. A review on fate and ecotoxicity of biodegradable microplastics in aquatic system: Are biodegradable plastics truly safe for the environment? ENVIRONMENTAL POLLUTION (BARKING, ESSEX : 1987) 2024; 344:123399. [PMID: 38242301 DOI: 10.1016/j.envpol.2024.123399] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 11/05/2023] [Revised: 01/14/2024] [Accepted: 01/17/2024] [Indexed: 01/21/2024]
Abstract
Plastic products are extensively used worldwide, but inadequate management of plastic waste results in significant plastic pollution. Biodegradable plastic (BPs) offers an alternative to traditional plastics, however, not all BPs can fully degrade under natural conditions. Instead, they may deteriorate into biodegradable microplastic (BMPs) at a faster rate than conventional plastic, thereby posing an additional hazard to aquatic environments. This study provides a comprehensive overview of the fate of BPs in aquatic systems and their eco-toxicological effects on aquatic organisms such as algae, invertebrates, and fish. The findings highlight that BMPs have comparable or heightened effects compared to conventional microplastics (MPs) which physiochemical characteristic of the polymer itself or by the chemical leached from the polymeric matrix can affect aquatic organisms. While BPs is not a flawless solution to address plastic pollution, future research should prioritize investigating their production, environmental behavior, ecological impact, and whether BMPs inflict greater harm than conventional MPs.
Collapse
Affiliation(s)
- Nik Nurhidayu Nik Mut
- Division of Environmental Science and Ecological Engineering, Korea University, Seoul, 02841, Republic of Korea
| | - Joorim Na
- OJEong Resilience Institute, Korea University, Seoul, 02841, Republic of Korea.
| | - Jinho Jung
- Division of Environmental Science and Ecological Engineering, Korea University, Seoul, 02841, Republic of Korea
| |
Collapse
|
16
|
Patel R, Gómez-Cerezo MN, Huang H, Grøndahl L, Lu M. Degradation behaviour of porous poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) scaffolds in cell culture. Int J Biol Macromol 2024; 257:128644. [PMID: 38065444 DOI: 10.1016/j.ijbiomac.2023.128644] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/21/2023] [Revised: 11/16/2023] [Accepted: 12/04/2023] [Indexed: 01/27/2024]
Abstract
Exploring the degradation behaviour of biomaterials in a complex in vitro physiological environment can assist in predicting their performance in vivo, yet this aspect remains largely unexplored. In this study, the in vitro degradation over 12 weeks of porous poly(hydroxybutyrate-co-hydroxyvalerate) (PHBV) bone scaffolds in human osteoblast (hOB) culture was investigated. The objective was to evaluate how the presence of cells influenced both the degradation behaviour and mechanical stability of these scaffolds. The molecular weight (Mw) of the scaffolds decreased with increasing incubation time and the Mw reduction rate (6.2 ± 0.4 kg mol-1 week-1) was similar to that observed when incubated in phosphate buffered saline (PBS) solution, implying that the scaffolds underwent hydrolytic degradation in hOB culture. The mass of the scaffolds increased by 0.8 ± 0.2 % in the first 4 weeks, attributed to cells attachment and extracellular matrix (ECM) deposition including biomineralisation. During the first 8 weeks, the nominal compressive modulus, E⁎, of the scaffolds remained constant. However, it increased significantly from Week 8 to 12, with increments of 55 % and 42 % in normal and lateral directions, respectively, attributed to the reinforcement effect of cells, ECM and minerals attached on the surface of the scaffold. This study has highlighted, that while the use of PBS in degradation studies is suitable for evaluating Mw changes it cannot predict changes in mechanical properties to PHBV scaffolds in the presence of cells and culture media. Furthermore, the PHBV scaffolds had mechanical stability in cell culture for 12 weeks validating their suitability for tissue engineering applications.
Collapse
Affiliation(s)
- Rushabh Patel
- School of Mechanical and Mining Engineering, The University of Queensland, St Lucia, QLD 4072, Australia
| | - Maria Natividad Gómez-Cerezo
- Departamento de Química en Ciencias Farmacéuticas, Facultad de Farmacia, Universidad Complutense de Madrid, Instituto de Investigación Sanitaria Hospital, 12 de Octubre i+12, Plaza Ramón y Cajal s/n, 28040 Madrid, Spain
| | - Han Huang
- School of Mechanical and Mining Engineering, The University of Queensland, St Lucia, QLD 4072, Australia
| | - Lisbeth Grøndahl
- School of Chemistry and Molecular Biosciences, The University of Queensland, St Lucia, QLD 4072, Australia
| | - Mingyuan Lu
- School of Mechanical and Mining Engineering, The University of Queensland, St Lucia, QLD 4072, Australia.
| |
Collapse
|
17
|
Sun J, Wang X, Zheng H, Xiang H, Jiang X, Fan J. Characterization of the degradation products of biodegradable and traditional plastics on UV irradiation and mechanical abrasion. THE SCIENCE OF THE TOTAL ENVIRONMENT 2024; 909:168618. [PMID: 37977371 DOI: 10.1016/j.scitotenv.2023.168618] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 09/21/2023] [Revised: 11/12/2023] [Accepted: 11/14/2023] [Indexed: 11/19/2023]
Abstract
Biodegradable plastics are popular alternatives to traditional plastics in packaging, mulch sheets, and other applications. However, there are concerns regarding the potential for pollution as a result of their abiotic degradation. In this study, we investigated the degradation of biodegradable polybutylene adipate terephthalate/polylactic acid (PBAT/PLA) and traditional polyethylene (PE) plastic under two typical abiotic conditions: ultraviolet (UV) irradiation and mechanical abrasion (MA) for up to nine months. The physical and chemical properties of the two plastics during the degradation period were assessed. In addition, quantitative analysis of the degradation products was carried out using a new method called membrane filtration and total organic carbon determination (MF-TOCD). The results revealed that PBAT/PLA underwent a greater number of changes in surface morphology, thermal stability, and mass loss compared to PE when exposed to UV and MA during the test period. Further analysis of the released products revealed that PBAT/PLA released more products than PE. Overall, PE mainly produced microplastics (MPs) larger than 0.22 μm, whereas PBAT/PLA produced products <0.22 μm (nanoplastics and soluble molecules) on UV exposure. In contrast, when subjected to MA, PBAT/PLA produced MPs larger than 0.22 μm, and these accumulated gradually; this behavior is similar to that of PE. By combining the mass loss and the TOC data for the degradation products, we determined that long-term UV irradiation generated a large number of smaller particles from PBAT/PLA that could further degrade rather than accumulate in the environment. In summary, we established a new method to separate and characterize MPs as well as nanoplastics and soluble molecules, and provided new insights into the fate of PBAT/PLA during abiotic degradation.
Collapse
Affiliation(s)
- Jiaoxia Sun
- School of River and Ocean Engineering, Chongqing Jiaotong University, Chongqing 400074, China.
| | - Xi Wang
- School of River and Ocean Engineering, Chongqing Jiaotong University, Chongqing 400074, China
| | - Hanyue Zheng
- School of River and Ocean Engineering, Chongqing Jiaotong University, Chongqing 400074, China
| | - Hong Xiang
- School of River and Ocean Engineering, Chongqing Jiaotong University, Chongqing 400074, China
| | - Xueting Jiang
- School of River and Ocean Engineering, Chongqing Jiaotong University, Chongqing 400074, China
| | - Jianxin Fan
- School of River and Ocean Engineering, Chongqing Jiaotong University, Chongqing 400074, China
| |
Collapse
|
18
|
Tu Z, Wang L, Lu Y, Li Y, Sang L, Zhang Y, Wei Z. Rapid marine degradable poly(butylene oxalate) by introducing promotion building blocks. JOURNAL OF HAZARDOUS MATERIALS 2024; 462:132791. [PMID: 37866142 DOI: 10.1016/j.jhazmat.2023.132791] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 08/18/2023] [Revised: 10/04/2023] [Accepted: 10/13/2023] [Indexed: 10/24/2023]
Abstract
The design and development of high-performance marine-degradable plastics have long been considered a superior strategy to address marine plastic pollution. To achieve a balance between rapid marine degradability and high performance of polyester plastics, this work designed two series of poly(butylene oxalate) (PBOx) copolymers with intrinsic hydrolysis ability using poly(ethylene oxalate) (PEOx) and poly(glycolic acid) (PGA) as promotion building blocks. The synthesis process, crystallization properties, barrier performance, and mechanical properties of copolymers were comparatively investigated. Additionally, the marine degradability of copolymers received specific focus. The theoretical calculation demonstrated that the introduction of promotion blocks reduced the hydrolysis energy barrier of the copolymers. In general, the results revealed the advantages of PBEOx copolymer in satisfying practicality and better regulating marine degradability. The high gas barrier performance, suitable thermal properties, tunable mechanical properties, and rapid marine degradability endow the copolymer as a promising candidate toward sustainable and marine-degradable plastics.
Collapse
Affiliation(s)
- Zhu Tu
- State Key Laboratory of Fine Chemicals, Liaoning Key Laboratory of Polymer Science and Engineering, Department of Polymer Science and Engineering, School of Chemical Engineering, Dalian University of Technology, Dalian 116024, China
| | - Lizheng Wang
- State Key Laboratory of Fine Chemicals, Liaoning Key Laboratory of Polymer Science and Engineering, Department of Polymer Science and Engineering, School of Chemical Engineering, Dalian University of Technology, Dalian 116024, China
| | - Ying Lu
- State Key Laboratory of Fine Chemicals, Liaoning Key Laboratory of Polymer Science and Engineering, Department of Polymer Science and Engineering, School of Chemical Engineering, Dalian University of Technology, Dalian 116024, China
| | - Yang Li
- State Key Laboratory of Fine Chemicals, Liaoning Key Laboratory of Polymer Science and Engineering, Department of Polymer Science and Engineering, School of Chemical Engineering, Dalian University of Technology, Dalian 116024, China
| | - Lin Sang
- School of Automotive Engineering, Dalian University of Technology, Dalian 116024, China
| | - Yu Zhang
- Hangzhou New Base Material Technology Co., Ltd., Hangzhou 310051, China
| | - Zhiyong Wei
- State Key Laboratory of Fine Chemicals, Liaoning Key Laboratory of Polymer Science and Engineering, Department of Polymer Science and Engineering, School of Chemical Engineering, Dalian University of Technology, Dalian 116024, China.
| |
Collapse
|
19
|
Shi D, Kang Y, Jiang Z, Li X, Zhang H, Wang Q, Guo J, Jiang H, Luo Q, Ding J. Hybrid interpenetrating network of polyester coronary stent with tunable biodegradation and mechanical properties. Biomaterials 2024; 304:122411. [PMID: 38061184 DOI: 10.1016/j.biomaterials.2023.122411] [Citation(s) in RCA: 1] [Impact Index Per Article: 1.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/07/2023] [Revised: 11/20/2023] [Accepted: 11/26/2023] [Indexed: 12/30/2023]
Abstract
Poly(l-lactide) (PLLA) is an important candidate raw material of the next-generation biodegradable stent for percutaneous coronary intervention, yet how to make a polyester stent with sufficient mechanical strength and relatively fast biodegradation gets to be a dilemma. Herein, we put forward a hybrid interpenetrating network (H-IPN) strategy to resolve this dilemma. As such, we synthesize a multi-functional biodegradable macromer of star-like poly(d,l-lactide-co-ɛ-caprolactone) with six acrylate end groups, and photoinitiate it, after mixing with linear PLLA homopolymer, to trigger the free radical polymerization. The resultant crosslinked polymer blend is different from the classic semi-interpenetrating network, and partial chemical crosslinking occurs between the linear polymer and the macromer network. Combined with the tube blow molding and the postprocessing laser cutting, we fabricate a semi-crosslinked-polyester biodegradable coronary stent composed of H-IPN, which includes a physical network of polyester spherulites and a chemical crosslinking network of copolyester macromers and a part of homopolymers. Compared with the currently main-stream PLLA stent in research, this H-IPN stent realizes a higher and more appropriate biodegradation rate while maintaining sufficient radial strength. A series of polymer chemistry, polymer physics, polymer processing, and in vitro and in vivo biological assessments of medical devices have been made to examine the H-IPN material. The interventional implanting of the H-IPN stent into aorta abdominalis of rabbits and the follow-ups to 12 months have confirmed the safety and effectiveness.
Collapse
Affiliation(s)
- Daokun Shi
- State Key Laboratory of Molecular Engineering of Polymers, Department of Macromolecular Science, Fudan University, Shanghai, 200438, China
| | - Yahong Kang
- State Key Laboratory of Molecular Engineering of Polymers, Department of Macromolecular Science, Fudan University, Shanghai, 200438, China; Shanghai Key Laboratory of Interventional Medical Devices and Equipment, Shanghai MicroPort Medical Group Co., Ltd, Shanghai, 201203, China
| | - Zailai Jiang
- Shanghai Key Laboratory of Interventional Medical Devices and Equipment, Shanghai MicroPort Medical Group Co., Ltd, Shanghai, 201203, China
| | - Xin Li
- State Key Laboratory of Molecular Engineering of Polymers, Department of Macromolecular Science, Fudan University, Shanghai, 200438, China
| | - Hongjie Zhang
- State Key Laboratory of Molecular Engineering of Polymers, Department of Macromolecular Science, Fudan University, Shanghai, 200438, China
| | - Qunsong Wang
- State Key Laboratory of Molecular Engineering of Polymers, Department of Macromolecular Science, Fudan University, Shanghai, 200438, China
| | - Jingzhen Guo
- State Key Laboratory of Molecular Engineering of Polymers, Department of Macromolecular Science, Fudan University, Shanghai, 200438, China
| | - Hongyan Jiang
- Shanghai Key Laboratory of Interventional Medical Devices and Equipment, Shanghai MicroPort Medical Group Co., Ltd, Shanghai, 201203, China.
| | - Qiyi Luo
- Shanghai Key Laboratory of Interventional Medical Devices and Equipment, Shanghai MicroPort Medical Group Co., Ltd, Shanghai, 201203, China
| | - Jiandong Ding
- State Key Laboratory of Molecular Engineering of Polymers, Department of Macromolecular Science, Fudan University, Shanghai, 200438, China.
| |
Collapse
|
20
|
Athparia M, Bora N, Deka A, Sohtun P, Padhi P, Bhuyan N, Bordoloi NJ, Gogoi L, Kataki R. Non-fuel applications of bio-oil for sustainability in management of bioresources. ENVIRONMENTAL SCIENCE AND POLLUTION RESEARCH INTERNATIONAL 2023:10.1007/s11356-023-31449-w. [PMID: 38155309 DOI: 10.1007/s11356-023-31449-w] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 12/31/2022] [Accepted: 12/05/2023] [Indexed: 12/30/2023]
Abstract
Biomass valorization by thermochemical conversion method is a promising and intriguing pathway due to the flexibility of utilizing a diverse group of biomass and biowastes, specific product delivery mechanism through manipulation of process parameters, and wide applicability of the products. Pyrolysis has been viewed as an effective valorization technique to transform biowastes into pyrolytic oil, solid char, and syngas. Syngas is generally fed to the pyrolysis process to generate heat necessary for the pyrolysis process to sustain. Pyrolysis may also be a subsidiary component in a biorefinery system where it draws feedstocks from refinery process residues or the side streams of the refinery operation. In recent times, pyrolysis products have been under intense research for their usability and diverse applicability. Bio-oil's rich chemical makeup has promising potential to be used as an advanced biofuel and is considered as a storehouse of diverse chemical species ranging from green solvents to bioactive chemicals. The current review provides a state of knowledge on non-fuel uses of bio-oil and concludes that the pyrolysis process and products could be a part of the future bioeconomy if designed in a manner that biowastes are transformed into value-added products which replace products of petroleum origin.
Collapse
Affiliation(s)
- Mondita Athparia
- Biofuel Laboratory, Department of Energy, Tezpur University, Tezpur, Assam, 784028, India
| | - Neelam Bora
- Biofuel Laboratory, Department of Energy, Tezpur University, Tezpur, Assam, 784028, India
| | - Anuron Deka
- Biofuel Laboratory, Department of Energy, Tezpur University, Tezpur, Assam, 784028, India
| | - Phibarisha Sohtun
- Biofuel Laboratory, Department of Energy, Tezpur University, Tezpur, Assam, 784028, India
| | - Priyanka Padhi
- Biofuel Laboratory, Department of Energy, Tezpur University, Tezpur, Assam, 784028, India
| | - Nilutpal Bhuyan
- Biofuel Laboratory, Department of Energy, Tezpur University, Tezpur, Assam, 784028, India
- Department of Chemistry, Devi Charan Baruah Girls' College, Jorhat, 785001, India
| | - Neon Jyoti Bordoloi
- Biofuel Laboratory, Department of Energy, Tezpur University, Tezpur, Assam, 784028, India
- Department of Chemistry, Assam Down Town University, Guwahati, 781026, Assam, India
| | - Lina Gogoi
- Biofuel Laboratory, Department of Energy, Tezpur University, Tezpur, Assam, 784028, India
- Department of Environmental Science, Tezpur University, Tezpur, Assam, 784028, India
| | - Rupam Kataki
- Biofuel Laboratory, Department of Energy, Tezpur University, Tezpur, Assam, 784028, India.
| |
Collapse
|
21
|
Oudir M, Ait Mesbah Z, Lerari D, Issad N, Djenane D. Development of Eco-Friendly Biocomposite Films Based on Opuntia ficus-indica Cladodes Powder Blended with Gum Arabic and Xanthan Envisaging Food Packaging Applications. Foods 2023; 13:78. [PMID: 38201106 PMCID: PMC10778558 DOI: 10.3390/foods13010078] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 11/11/2023] [Revised: 12/15/2023] [Accepted: 12/19/2023] [Indexed: 01/12/2024] Open
Abstract
Currently, food packaging is facing a critical transition period and a major challenge: it must preserve the food products' quality and, at the same time, it must meet the current requirements of the circular economy and the fundamental principles of packaging materials eco-design. Our research presents the development of eco-friendly packaging films based on Opuntia ficus-indica cladodes (OFIC) as renewable resources. OFIC powder (OFICP)-agar, OFICP-agar-gum arabic (GA), and OFICP-agar-xanthan (XG) blend films were eco-friendlily prepared by a solution casting method. The films' properties were investigated by scanning electron microscope (SEM), Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (X-RD), and differential scanning calorimeter (DSC). Water solubility and moisture content were also determined. Morphology, thickness, molecular interactions, miscibility, crystallinity, and thermal properties, were affected by adjusting the gums (GA and XG) content and glycerol in the blend films. Moisture content increased with increasing glycerol and XG content, and when 1.5 g of GA was added. Water solubility decreased when glycerol was added at 50% and increased with increasing GA and XG content. FTIR and XRD confirmed strong intermolecular interactions between the different blend film compounds, which were reflected in the shifting, appearance, and disappearance of FTIR bands and XRD peaks, indicating excellent miscibility. DSC results revealed a glass transition temperature (Tg) below room temperature for all prepared blend films, indicating that they are flexible and soft at room temperature. The results corroborated that the addition of glycerol at 30% and the GA to the OFICP increased the stability of the film, making it ideal for different food packaging applications.
Collapse
Affiliation(s)
- Malha Oudir
- Higher School of Food Science and Agri-Food Industry, ESSAIA, Avenue Ahmed Hamidouche Route de Beaulieu, El Harrach, Alger 16200, Algeria; (M.O.); (N.I.)
- Fundamental and Applied Physics Laboratory, FUNDAPL, Faculty of Science, University of Blida 1, P.O. Box 270, Route de Soumâa, Blida 09000, Algeria;
| | - Zohra Ait Mesbah
- Fundamental and Applied Physics Laboratory, FUNDAPL, Faculty of Science, University of Blida 1, P.O. Box 270, Route de Soumâa, Blida 09000, Algeria;
| | - Djahida Lerari
- Center for Scientific and Technical Research in Physical and Chemical Analysis, CRAPC, Zone Industrielle Bou-Ismaïl, P.O. Box 384, Tipaza 42004, Algeria;
| | - Nadia Issad
- Higher School of Food Science and Agri-Food Industry, ESSAIA, Avenue Ahmed Hamidouche Route de Beaulieu, El Harrach, Alger 16200, Algeria; (M.O.); (N.I.)
| | - Djamel Djenane
- Laboratory of Food Quality and Food Safety, Mouloud Mammeri University, P.O. Box 17, Tizi Ouzou 15000, Algeria
| |
Collapse
|
22
|
Bi S, Zhang Z, Yang Z, Shen Z, Cai J, Hu J, Jin H, Qiu T, Yu P, Tan B. Protein modified cellulose nanocrystals on reinforcement and self-driven biodegradation of aliphatic polyester. Carbohydr Polym 2023; 322:121312. [PMID: 37839828 DOI: 10.1016/j.carbpol.2023.121312] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/20/2023] [Revised: 07/31/2023] [Accepted: 08/16/2023] [Indexed: 10/17/2023]
Abstract
Due to the highly environment-dependent biodegradation and uncontrolled degradation period, the long-run feasibility and effectiveness of biodegradable polymers are extensively questioned to solve plastics waste accumulation and pollution problems. This work physically incorporated lipase PS from Burkholderia cepacian on cellulose nanocrystals (CNC) and embedded it in polycaprolactone (PCL) to construct stable and controllable interfacial microenvironment between CNC and PCL for the reinforcement and controllable self-driven biodegradation. The physical adsorption of lipase PS on CNC was studied by monitoring the surface charge and particle size. FT-IR spectra confirmed the successful incorporation of lipase PS and CNC. Compared with CNC, protein-modified CNC had a higher maximum thermal decomposition temperature of 345 °C and lower interfacial tension of 11 mN/m with PCL which provided PCL composites with higher nucleation efficiency and tensile elongation of 1086 % at break. In addition, only 0.67 % embedded lipase PS completely hydrolyzed PCL membranes in <140 h. The post-compression molding at 80-100 °C had negligible influence on the lipase activity, which indicated that CNC could protect the lipase from inactivation in polymer extrusion and compression. This work also highlighted protein-modified CNC as a new technology for polymer reinforcement.
Collapse
Affiliation(s)
- Siwen Bi
- Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan, Hubei 430068, China; New Materials and Green Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, Hubei 430068, China; Hubei Longzhong Laboratory, Xiangyang, Hubei 441000, China.
| | - Zhuang Zhang
- Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan, Hubei 430068, China
| | - Zhenzhen Yang
- Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan, Hubei 430068, China; New Materials and Green Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, Hubei 430068, China
| | - Zitong Shen
- Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan, Hubei 430068, China
| | - Jiahui Cai
- Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan, Hubei 430068, China
| | - Jintao Hu
- Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan, Hubei 430068, China
| | - Haoxiang Jin
- Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan, Hubei 430068, China
| | - Tianhao Qiu
- Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan, Hubei 430068, China
| | - Peng Yu
- Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan, Hubei 430068, China; New Materials and Green Manufacturing Talent Introduction and Innovation Demonstration Base, Hubei University of Technology, Wuhan, Hubei 430068, China; Hubei Longzhong Laboratory, Xiangyang, Hubei 441000, China
| | - Bin Tan
- Department of Materials Science and Engineering, Fujian University of Technology, Fuzhou 350011, China
| |
Collapse
|
23
|
Oluwoye I, Machuca LL, Higgins S, Suh S, Galloway TS, Halley P, Tanaka S, Iannuzzi M. Degradation and lifetime prediction of plastics in subsea and offshore infrastructures. THE SCIENCE OF THE TOTAL ENVIRONMENT 2023; 904:166719. [PMID: 37673242 DOI: 10.1016/j.scitotenv.2023.166719] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 05/29/2023] [Revised: 08/25/2023] [Accepted: 08/29/2023] [Indexed: 09/08/2023]
Abstract
Engineering and civil developments have relied on synthetic polymers and plastics (including polyethylene, polypropylene, polyamide, etc.) for decades, especially where their durability protects engineering structures against corrosion and other environmental stimuli. Offshore oil and gas infrastructure and renewable energy platforms are typical examples, where these plastics (100,000 s of metric tonnes worldwide) are used primarily as functional material to protect metallic flowlines and subsea equipment against seawater corrosion. Despite this, the current literature on polymers is limited to sea-surface environments, and a model for subsea degradation of plastics is needed. In this review, we collate relevant studies on the degradation of plastics and synthetic polymers in marine environments to gain insight into the fate of these materials when left in subsea conditions. We present a new mathematical model that accounts for various physicochemical changes in the oceanic environment as a function of depth to predict the lifespan of synthetic plastics and the possible formation of plastic debris, e.g., microplastics. We found that the degradation rate of the plastics decreases significantly as a function of water depth and can be estimated quantitatively by the mathematical model that accounts for the effect (and sensitivity) of geographical location, temperature, light intensity, hydrostatic pressure, and marine sediments. For instance, it takes a subsea polyethylene coating about 800 years to degrade on ocean floor (as opposed to <400 years in shallow coastal waters), generating 1000s of particles per g of degradation under certain conditions. Our results demonstrate how suspended sediments in the water column are likely to compensate for the decreasing depth-corrected degradation rates, resulting in surface abrasion and the formation of plastic debris such as microplastics. This review, and the complementing data, will be significant for the environmental impact assessment of plastics in subsea infrastructures. Moreover, as these infrastructures reach the end of their service life, the management of the plastic components becomes of great interest to environmental regulators, industry, and the community, considering the known sizeable impacts of plastics on global biogeochemical cycles.
Collapse
Affiliation(s)
- Ibukun Oluwoye
- Curtin Corrosion Centre, Western Australian School of Mines: Minerals, Energy and Chemical Engineering, Curtin University, Perth, Australia; Graduate School of Global Environmental Studies, Kyoto University, Yoshida-Honmachi, Sakyo-ku, Kyoto, Japan.
| | - Laura L Machuca
- Curtin Corrosion Centre, Western Australian School of Mines: Minerals, Energy and Chemical Engineering, Curtin University, Perth, Australia
| | - Stuart Higgins
- Curtin University, GPO Box U1987, Perth, WA 6824, Australia
| | - Sangwon Suh
- Bren School of Environmental Science and Management, University of California, Santa Barbara, CA 93106, USA
| | - Tamara S Galloway
- College of Life and Environmental Sciences, University of Exeter, Exeter EX4 4QD, UK
| | - Peter Halley
- School of Chemical Engineering, The University of Queensland, Brisbane, Queensland 4072, Australia
| | - Shuhei Tanaka
- Graduate School of Global Environmental Studies, Kyoto University, Yoshida-Honmachi, Sakyo-ku, Kyoto, Japan
| | - Mariano Iannuzzi
- Curtin Corrosion Centre, Western Australian School of Mines: Minerals, Energy and Chemical Engineering, Curtin University, Perth, Australia
| |
Collapse
|
24
|
Deng Y, Yang P, Tan H, Shen R, Chen D. Polylactic Acid Microplastics Do Not Exhibit Lower Biological Toxicity in Growing Mice Compared to Polyvinyl Chloride Microplastics. JOURNAL OF AGRICULTURAL AND FOOD CHEMISTRY 2023; 71:19772-19782. [PMID: 38039335 DOI: 10.1021/acs.jafc.3c06576] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Indexed: 12/03/2023]
Abstract
Biomicroplastics (BMPs) will be produced during bioplastic degradation (i.e., polylactic acid), although bioplastics have been widely used for food packaging. Like conventional microplastics (MPs), BMPs would be mistakenly ingested into the body through diet or drinking water, but their health risks in vivo are poorly understood. Here, we deeply compared the toxicity difference between irregularly shaped polylactic acid (PLA-MPs, 16-350 μm) and polyvinyl chloride (PVC-MPs, 40-300 μm) MPs in growing mice. After six weeks of exposure, PLA-MP exposure resulted in more severe inhibition of the mice's weight gain than PVC-MPs did. Both PLA- and PVC-MPs significantly elevated the levels of oxidative stress. Moreover, significant changes including altered transcriptional profiles and significantly differentially expressed genes in liver and colon transcription levels were observed in the PVC- and PLA-MP groups. Compared with PVC-MPs, PLA-MPs have a stronger effect on lipid metabolism and digestive systems. PLA-MPs also caused gut microbiota dysbiosis, significantly interfering with the relative abundance of microbiota and altering microbial diversity. These findings indicated the toxicities of PLA-MPs in growing mice were not significantly reduced compared to PVC-MPs, which would also provide new insights for re-examining bioplastic safety.
Collapse
Affiliation(s)
- Yongfeng Deng
- Key Laboratory of Environmental Medicine Engineering, Ministry of Education, School of Public Health, Southeast University, Nanjing 210009, China
| | - Pan Yang
- Department of Public Health and Preventive Medicine, School of Medicine, Jinan University, Guangzhou 510632, China
| | - Hongli Tan
- State Key Laboratory of Environmental and Biological Analysis, Hong Kong Baptist University, Hong Kong SAR, 999077, China
| | - Ruqin Shen
- Key Laboratory of Environmental Medicine Engineering, Ministry of Education, School of Public Health, Southeast University, Nanjing 210009, China
| | - Da Chen
- School of Environment and Guangdong Key Laboratory of Environmental Pollution and Health, Jinan University, Guangzhou 510632, China
| |
Collapse
|
25
|
Hu H, Luan Q, Li J, Lin C, Ouyang X, Wei DQ, Wang J, Zhu J. High-Molecular-Weight and Light-Colored Disulfide-Bond-Embedded Polyesters: Accelerated Hydrolysis Triggered by Redox Responsiveness. Biomacromolecules 2023; 24:5722-5736. [PMID: 37946491 DOI: 10.1021/acs.biomac.3c00691] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/12/2023]
Abstract
Disulfide bonds have attracted considerable attention due to their reduction responsiveness, but it is crucial and challenging to prepare disulfide-bond-based polyesters by melt polycondensation. Herein, the inherently poor thermal stability of the S-S bond in melting polycondensation was overcome. Moreover, poly(butylene succinate-co-dithiodipropionate) (PBSDi) with a light color and high molecular weights (Mn values up to 84.7 kg/mol) was obtained. These polyesters can be applied via melt processing with Td,5% > 318 °C. PBSDi10-PBSDi40 shows good crystallizability (crystallinity 56-38%) and compact lamellar thickness (2.9-3.2 nm). Compared with commercial poly(butylene adipate-co-terephthalate) (PBAT), the elevated mechanical and barrier performances of PBSDi make them better packaging materials. For the degradation behavior, the disulfide monomer obviously accelerates the enzyme degradation but has a weaker effect on hydrolysis. In 0.1 mol/L or higher concentrations of H2O2 solutions, the oxidation of disulfide bonds to sulfoxide and sulfone groups can be realized. This process results in a stronger nucleophilic attack, as confirmed by the Fukui function and DFT calculations. Additionally, the greater polarity and hydrophilicity of oxidation products, proved by noncovalent interaction analysis, accelerate the hydrolysis of polyesters. Moreover, glutathione-responsive breakage, from polymers to oligomers, is confirmed by an accelerated decline in molecular weight. Our research offers fresh perspectives on the effective synthesis of the disulfide polyester and lays a solid basis for the creation of high-performance biodegradable polyesters that degrade on demand.
Collapse
Affiliation(s)
- Han Hu
- Key Laboratory of Bio-Based Polymeric Materials Technology and Application of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China
| | - Qingyang Luan
- Key Laboratory of Bio-Based Polymeric Materials Technology and Application of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China
- University of Chinese Academy of Sciences, Beijing 100049, China
| | - Jiayi Li
- State Key Laboratory of Microbial Metabolism, Joint International Research Laboratory of Metabolic & Developmental Sciences, School of Life Sciences & Biotechnology, Shanghai Jiao Tong University, Shanghai 200240, China
| | - Chen Lin
- Key Laboratory of Bio-Based Polymeric Materials Technology and Application of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China
| | - Xingyu Ouyang
- State Key Laboratory of Microbial Metabolism, Joint International Research Laboratory of Metabolic & Developmental Sciences, School of Life Sciences & Biotechnology, Shanghai Jiao Tong University, Shanghai 200240, China
| | - Dong-Qing Wei
- State Key Laboratory of Microbial Metabolism, Joint International Research Laboratory of Metabolic & Developmental Sciences, School of Life Sciences & Biotechnology, Shanghai Jiao Tong University, Shanghai 200240, China
- Zhongjing Research and Industrialization Institute of Chinese Medicine, Zhongguancun Scientifc Park, Nanyang 473006, Henan, China
- Peng Cheng Laborator, Vanke Cloud City Phase I Building 8, Xili Street, Nashan District, Shenzhen 518055, Guangdong, China
| | - Jinggang Wang
- Key Laboratory of Bio-Based Polymeric Materials Technology and Application of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China
| | - Jin Zhu
- Key Laboratory of Bio-Based Polymeric Materials Technology and Application of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, China
| |
Collapse
|
26
|
Wang Q, Li J, Wang J, Hu H, Dong Y, O'Young DL, Hu D, Zhang X, Wei DQ, Zhu J. Biobased Biodegradable Copolyesters from 2,5-Thiophenedicarboxylic Acid: Effect of Aliphatic Diols on Barrier Properties and Degradation. Biomacromolecules 2023; 24:5884-5897. [PMID: 37956178 DOI: 10.1021/acs.biomac.3c00918] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 11/15/2023]
Abstract
The demand for sustainable development has led to increasing attention in biobased polyesters due to their adjustable thermal and mechanical properties and biodegradability. In this study, we used a novel bioderived aromatic diacid, 2,5-thiophenedicarboxylic acid (TDCA) to synthesize a list of novel aromatic-aliphatic poly(alkylene adipate-co-thiophenedicarboxylate) (PAATh) copolyesters through a facile melt polycondensation method. PAAThs are random copolyesters with weight-average molecular weights of 58400 to 84200 g·mol-1 and intrinsic viscosities of 0.80 to 1.27 dL·g-1. All PAAThs exhibit sufficiently high thermal stability as well as the highest tensile strength of 6.2 MPa and the best gas barrier performances against CO2 and O2, 4.3- and 3.3-fold better than those of poly(butylene adipate-co-terephthalate) (PBAT). The biodegradability of PAAThs was fully evaluated through a degradation experiment and various experimental parameters, including residue weights, surface morphology, and molecular compositions. The state-of-the-art molecular dynamics (MD) simulations were applied to elucidate the different enzymatic degradation behaviors of PAAThs due to the effect of diols with different chain structures. The sterically hindered carbonyl carbon of the PHATh-enzyme complex was more susceptible to nucleophilic attack and exhibited a higher tendency to enter a prereaction state. This study has introduced a group of novel biobased copolyesters with their structure-property relationships investigated thoroughly, and the effect of diol components on the enzymatic degradation was revealed by computational analysis. These findings may lay the foundation for the development of promising substitutes for commercial biodegradable polyesters and shed light on their complicated degradation mechanisms.
Collapse
Affiliation(s)
- Qianfeng Wang
- Key Laboratory of Bio-based Polymeric Materials Technology and Application of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, People's Republic of China
- Department of Chemical and Environmental Engineering, Faculty of Science and Engineering, University of Nottingham Ningbo China, Ningbo 315100, People's Republic of China
| | - Jiayi Li
- State Key Laboratory of Microbial Metabolism, Joint International Research Laboratory of Metabolic and Developmental Sciences, School of Life Sciences and Biotechnology, Shanghai Jiao Tong University, Shanghai 200240, People's Republic of China
| | - Jinggang Wang
- Key Laboratory of Bio-based Polymeric Materials Technology and Application of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, People's Republic of China
| | - Han Hu
- Key Laboratory of Bio-based Polymeric Materials Technology and Application of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, People's Republic of China
| | - Yunxiao Dong
- Key Laboratory of Bio-based Polymeric Materials Technology and Application of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, People's Republic of China
| | - Drow Lionel O'Young
- Department of Chemical and Environmental Engineering, Faculty of Science and Engineering, University of Nottingham Ningbo China, Ningbo 315100, People's Republic of China
| | - Di Hu
- Department of Chemical and Environmental Engineering, Faculty of Science and Engineering, University of Nottingham Ningbo China, Ningbo 315100, People's Republic of China
| | - Xiaoqin Zhang
- Key Laboratory of Bio-based Polymeric Materials Technology and Application of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, People's Republic of China
| | - Dong-Qing Wei
- State Key Laboratory of Microbial Metabolism, Joint International Research Laboratory of Metabolic and Developmental Sciences, School of Life Sciences and Biotechnology, Shanghai Jiao Tong University, Shanghai 200240, People's Republic of China
- Zhongjing Research and Industrialization Institute of Chinese Medicine, Nanyang 473006, People's Republic of China
- Peng Cheng Laboratory, Shenzhen 518055, People's Republic of China
| | - Jin Zhu
- Key Laboratory of Bio-based Polymeric Materials Technology and Application of Zhejiang Province, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo 315201, People's Republic of China
| |
Collapse
|
27
|
Dong Y, Xie Y, Ma X, Yan L, Yu HY, Yang M, Abdalkarim SYH, Jia B. Multi-functional nanocellulose based nanocomposites for biodegradable food packaging: Hybridization, fabrication, key properties and application. Carbohydr Polym 2023; 321:121325. [PMID: 37739512 DOI: 10.1016/j.carbpol.2023.121325] [Citation(s) in RCA: 7] [Impact Index Per Article: 7.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 06/17/2023] [Revised: 08/05/2023] [Accepted: 08/21/2023] [Indexed: 09/24/2023]
Abstract
Nowadays, non-degradable plastic packaging materials have caused serious environmental pollution, posing a threat to human health and development. Renewable eco-friendly nanocellulose hybrid (NCs-hybrid) composites as an ideal alternative to petroleum-based plastic food packaging have been extensively reported in recent years. NCs-hybrids include metal, metal oxides, organic frameworks (MOFs), plants, and active compounds. However, no review systematically summarizes the preparation, processing, and multi-functional applications of NCs-hybrid composites. In this review, the design and hybridization of various NCs-hybrids, the processing of multi-scale nanocomposites, and their key properties in food packaging applications were systematically explored for the first time. Moreover, the synergistic effects of various NCs-hybrids on several properties of composites, including mechanical, thermal, UV shielding, waterproofing, barrier, antimicrobial, antioxidant, biodegradation and sensing were reviewed in detailed. Then, the problems and advances in research on renewable NCs-hybrid composites are suggested for biodegradable food packaging applications. Finally, a future packaging material is proposed by using NCs-hybrids as nanofillers and endowing them with various properties, which are denoted as "PACKAGE" and characterized by "Property, Application, Cellulose, Keen, Antipollution, Green, Easy."
Collapse
Affiliation(s)
- Yanjuan Dong
- The Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China
| | - Yao Xie
- The Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China
| | - Xue Ma
- The Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China
| | - Ling Yan
- The Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China
| | - Hou-Yong Yu
- The Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China; Department of Chemical Engineering, Waterloo Institute for Nanotechnology, University of Waterloo, 200 University Avenue West, Waterloo, Ontario, Canada.
| | - Mingchen Yang
- The Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China
| | - Somia Yassin Hussain Abdalkarim
- The Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China.
| | - Bowen Jia
- The Key Laboratory of Advanced Textile Materials and Manufacturing Technology, Ministry of Education, Zhejiang Sci-Tech University, Xiasha Higher Education Park Avenue 2 No.928, Hangzhou 310018, China
| |
Collapse
|
28
|
Picken CAR, Buensoz O, Price PD, Fidge C, Points L, Shaver MP. Sustainable formulation polymers for home, beauty and personal care: challenges and opportunities. Chem Sci 2023; 14:12926-12940. [PMID: 38023508 PMCID: PMC10664511 DOI: 10.1039/d3sc04488b] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Grants] [Track Full Text] [Figures] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/26/2023] [Accepted: 10/03/2023] [Indexed: 12/01/2023] Open
Abstract
As society moves towards a net-zero future, the need to adopt more sustainable polymers is well understood, and as well as plastics, less visible formulation polymers should also be included within this shift. As researchers, industries and consumers move towards more sustainable products there is a clear need to define what sustainability means in fast moving consumer goods and how it can be considered at the design stage. In this perspective key challenges in achieving sustainable formulation polymers are highlighted, and opportunities to overcome them are presented.
Collapse
Affiliation(s)
- Christina A R Picken
- Department of Materials, Henry Royce Institute, The University of Manchester Manchester M13 9PL UK
| | - Orla Buensoz
- Department of Materials, Henry Royce Institute, The University of Manchester Manchester M13 9PL UK
| | - Paul D Price
- Unilever R&D, Port Sunlight Laboratory Quarry Road East, Bebington, Wirral CH63 3JW UK
| | - Christopher Fidge
- Unilever R&D, Port Sunlight Laboratory Quarry Road East, Bebington, Wirral CH63 3JW UK
| | - Laurie Points
- Unilever R&D, Port Sunlight Laboratory Quarry Road East, Bebington, Wirral CH63 3JW UK
| | - Michael P Shaver
- Department of Materials, Henry Royce Institute, The University of Manchester Manchester M13 9PL UK
| |
Collapse
|
29
|
Town RM, van Leeuwen HP, Duval JFL. Effect of Polymer Aging on Uptake/Release Kinetics of Metal Ions and Organic Molecules by Micro- and Nanoplastics: Implications for the Bioavailability of the Associated Compounds. ENVIRONMENTAL SCIENCE & TECHNOLOGY 2023; 57:16552-16563. [PMID: 37856883 PMCID: PMC10620988 DOI: 10.1021/acs.est.3c05148] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Grants] [Track Full Text] [Subscribe] [Scholar Register] [Received: 07/01/2023] [Revised: 09/16/2023] [Accepted: 10/01/2023] [Indexed: 10/21/2023]
Abstract
The main driver of the potential toxicity of micro- and nanoplastics toward biota is often the release of compounds initially present in the plastic, i.e., polymer additives, as well as environmentally acquired metals and/or organic contaminants. Plastic particles degrade in the environment via various mechanisms and at different rates depending on the particle size/geometry, polymer type, and the prevailing physical and chemical conditions. The rate and extent of polymer degradation have obvious consequences for the uptake/release kinetics and, thus, the bioavailability of compounds associated with plastic particles. Herein, we develop a theoretical framework to describe the uptake and release kinetics of metal ions and organic compounds by plastic particles and apply it to the analysis of experimental data for pristine and aged micro- and nanoplastics. In particular, we elucidate the contribution of transient processes to the overall kinetics of plastic reactivity toward aquatic contaminants and demonstrate the paramount importance of intraparticulate contaminant diffusion.
Collapse
Affiliation(s)
- Raewyn M. Town
- ECOSPHERE,
Department of Biology, Universiteit Antwerpen, Groenenborgerlaan 171, 2020 Antwerpen, Belgium
| | - Herman P. van Leeuwen
- ECOSPHERE,
Department of Biology, Universiteit Antwerpen, Groenenborgerlaan 171, 2020 Antwerpen, Belgium
- Physical
Chemistry and Soft Matter, Wageningen University
& Research, Stippeneng
4, 6708 WE Wageningen, The Netherlands
| | | |
Collapse
|
30
|
Fakhri V, Su CH, Tavakoli Dare M, Bazmi M, Jafari A, Pirouzfar V. Harnessing the power of polyol-based polyesters for biomedical innovations: synthesis, properties, and biodegradation. J Mater Chem B 2023; 11:9597-9629. [PMID: 37740402 DOI: 10.1039/d3tb01186k] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 09/24/2023]
Abstract
Polyesters based on polyols have emerged as promising biomaterials for various biomedical applications, such as tissue engineering, drug delivery systems, and regenerative medicine, due to their biocompatibility, biodegradability, and versatile physicochemical properties. This review article provides an overview of the synthesis methods, performance, and biodegradation mechanisms of polyol-based polyesters, highlighting their potential for use in a wide range of biomedical applications. The synthesis techniques, such as simple polycondensation and enzymatic polymerization, allow for the fine-tuning of polyester structure and molecular weight, thereby enabling the tailoring of material properties to specific application requirements. The physicochemical properties of polyol-based polyesters, such as hydrophilicity, crystallinity, and mechanical properties, can be altered by incorporating different polyols. The article highlights the influence of various factors, such as molecular weight, crosslinking density, and degradation medium, on the biodegradation behavior of these materials, and the importance of understanding these factors for controlling degradation rates. Future research directions include the development of novel polyesters with improved properties, optimization of degradation rates, and exploration of advanced processing techniques for fabricating scaffolds and drug delivery systems. Overall, polyol-based polyesters hold significant potential in the field of biomedical applications, paving the way for groundbreaking advancements and innovative solutions that could revolutionize patient care and treatment outcomes.
Collapse
Affiliation(s)
- Vafa Fakhri
- Department of Polymer Engineering & Color Technology, Amirkabir University of Technology, P.O. Box 15875-4413, Tehran, Iran.
| | - Chia-Hung Su
- Department of Chemical Engineering, Ming Chi University of Technology, New Taipei City, Taiwan
| | - Masoud Tavakoli Dare
- Department of Polymer Engineering & Color Technology, Amirkabir University of Technology, P.O. Box 15875-4413, Tehran, Iran.
| | - Maryam Bazmi
- Department of Polymer Engineering, Science and Research Branch, Islamic Azad University, Tehran, Iran
| | - Aliakbar Jafari
- Department of Polymer Engineering & Color Technology, Amirkabir University of Technology, P.O. Box 15875-4413, Tehran, Iran.
| | - Vahid Pirouzfar
- Department of Chemical Engineering, Central Tehran Branch, Islamic Azad University, Tehran, Iran
| |
Collapse
|
31
|
Colwell J, Pratt S, Lant P, Laycock B. Hazardous state lifetimes of biodegradable plastics in natural environments. THE SCIENCE OF THE TOTAL ENVIRONMENT 2023; 894:165025. [PMID: 37348710 DOI: 10.1016/j.scitotenv.2023.165025] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 02/15/2023] [Revised: 06/18/2023] [Accepted: 06/18/2023] [Indexed: 06/24/2023]
Abstract
Plastic pollution is a critical problem that has the potential for long-lasting impact. While all plastics eventually break down to at least some degree, they can remain in different transition states, such as microplastics and nanoplastics, for extended periods of time before reaching complete mineralisation to non-hazardous end products. Each of the transition states represents different types of hazards, so it is critical to understand the factors driving the lifetimes of plastics within these states. To do this, we propose a framework for assessing plastic lifetimes in natural environments based on the flow of material through potentially hazardous states: macroplastic and mesoplastic, microplastic, nanoplastic and soluble products. State changes within this framework are underpinned by three key processes: fragmentation, depolymerisation, and bioassimilation, with the pathways for generation of the different plastic states, and the lifetimes within these states, varying widely for individual materials in different environments due to their dependence on polymer material type, form and properties, and environmental factors. The critical factors driving these processes can therefore appear complex, but molecular weight, crystallinity, oxygen and water diffusivity, and inherent polymer chain reactivity (including to enzymes) are key to our understanding. By analysing currently available data that take factors such as these into consideration, we have generated information on the most likely states in which a range of plastics with different environmental degradation behaviour may exist over time in natural environments. Polyethylene (PE), for example, should be expected to fragment and accumulate in the environment as microplastic and nanoplastic. Interestingly, the state-profile for the biodegradable plastic polylactic acid (PLA) is similar, albeit over shorter timeframes. PLA also likely fragments, but then the relatively slow process of abiotic depolymerisation results in accumulation of microplastic and nanoplastic. By contrast, the state-profile for the biodegradable plastic polyhydroxyalkanoate (PHA) would be expected to be very different. The bulk material is less susceptible to embrittlement and fragmentation as a primary path to biodegradation, since the rapid enzyme catalysed depolymerisation of exposed surfaces proceeds in conjunction with bioassimilation.
Collapse
Affiliation(s)
- John Colwell
- School of Chemical Engineering, University of Queensland, St Lucia, Australia
| | - Steven Pratt
- School of Chemical Engineering, University of Queensland, St Lucia, Australia
| | - Paul Lant
- School of Chemical Engineering, University of Queensland, St Lucia, Australia
| | - Bronwyn Laycock
- School of Chemical Engineering, University of Queensland, St Lucia, Australia.
| |
Collapse
|
32
|
Sun X, Anoopkumar AN, Madhavan A, Binod P, Pandey A, Sindhu R, Awasthi MK. Degradation mechanism of microplastics and potential risks during sewage sludge co-composting: A comprehensive review. ENVIRONMENTAL POLLUTION (BARKING, ESSEX : 1987) 2023; 333:122113. [PMID: 37379875 DOI: 10.1016/j.envpol.2023.122113] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 02/23/2023] [Revised: 06/07/2023] [Accepted: 06/24/2023] [Indexed: 06/30/2023]
Abstract
Microplastics (MPs) as a kind of emerging contaminants, widely exists in various kinds of medium, sewage sludge (SS) is no exception. In the sewage treatment process, a large number of microplastics will be deposited in SS. More seriously, microplastics in sewage sludge can migrate to other environmental media and threaten human health. Therefore, it is necessary to remove MPs from SS. Among the various restorations, aerobic composting is emerging as a green microplastic removal method. There are more and more reports of using aerobic compost to degrade microplastics. However, there are few reports on the degradation mechanism of MPs in aerobic composting, hindering the innovation of aerobic composting methods. Therefore, in this paper, the degradation mechanism of MPs in SS is discussed based on the environmental factors such as physical, chemical and biological factors in the composting process. In addition, this paper expounds the MPs in potential hazards, and combined with the problems in the present study were studied the outlook.
Collapse
Affiliation(s)
- Xinwei Sun
- College of Natural Resources and Environment, Northwest A&F University, Yangling, Shaanxi, 712 100, China
| | - A N Anoopkumar
- Centre for Research in Emerging Tropical Diseases (CRET-D), Department of Zoology, University of Calicut, Malappuram, Kerala, India
| | - Aravind Madhavan
- School of Biotechnology, Amrita Vishwa Vidyapeetham, Amritapuri, Kollam, 690525, Kerala, India
| | - Parameswaran Binod
- Microbial Processes and Technology Division, CSIR-National Institute for Interdisciplinary Science and Technology (CSIR-NIIST), Trivandrum, 695019, Kerala, India
| | - Ashok Pandey
- Centre for Innovation and Translational Research, CSIR- Indian Institute for Toxicology Research (CSIR-IITR), 31 MG Marg, Lucknow, 226 001, India; Centre for Energy and Environmental Sustainability, Lucknow, 226029, Uttar Pradesh, India; Sustainability Cluster, School of Engineering, University of Petroleum and Energy Studies, Dehradun, 248007, India
| | - Raveendran Sindhu
- Department of Food Technology, TKM Institute of Technology, Kollam, 691505, Kerala, India
| | - Mukesh Kumar Awasthi
- College of Natural Resources and Environment, Northwest A&F University, Yangling, Shaanxi, 712 100, China.
| |
Collapse
|
33
|
Alqahtani AM. Guided Tissue and Bone Regeneration Membranes: A Review of Biomaterials and Techniques for Periodontal Treatments. Polymers (Basel) 2023; 15:3355. [PMID: 37631412 PMCID: PMC10457807 DOI: 10.3390/polym15163355] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 07/25/2023] [Revised: 08/05/2023] [Accepted: 08/08/2023] [Indexed: 08/27/2023] Open
Abstract
This comprehensive review provides an in-depth analysis of the use of biomaterials in the processes of guided tissue and bone regeneration, and their indispensable role in dental therapeutic interventions. These interventions serve the critical function of restoring both structural integrity and functionality to the dentition that has been lost or damaged. The basis for this review is laid through the exploration of various relevant scientific databases such as Scopus, PubMed, Web of science and MEDLINE. From a meticulous selection, relevant literature was chosen. This review commences by examining the different types of membranes used in guided bone regeneration procedures and the spectrum of biomaterials employed in these operations. It then explores the manufacturing technologies for the scaffold, delving into their significant impact on tissue and bone regenerations. At the core of this review is the method of guided bone regeneration, which is a crucial technique for counteracting bone loss induced by tooth extraction or periodontal disease. The discussion advances by underscoring the latest innovations and strategies in the field of tissue regeneration. One key observation is the critical role that membranes play in guided reconstruction; they serve as a barrier, preventing the entry of non-ossifying cells, thereby promoting the successful growth and regeneration of bone and tissue. By reviewing the existing literature on biomaterials, membranes, and scaffold manufacturing technologies, this paper illustrates the vast potential for innovation and growth within the field of dental therapeutic interventions, particularly in guided tissue and bone regeneration.
Collapse
Affiliation(s)
- Ali M Alqahtani
- Department of Restorative Dental Sciences, College of Dentistry, King Khalid University, Al Fara, Abha 62223, Saudi Arabia
| |
Collapse
|
34
|
Tawagi E, Ung T, Cheng HLM, Santerre JP. Arrhenius-model-based degradable oligourethane hydrogels for controlled growth factor release. Acta Biomater 2023; 166:167-186. [PMID: 37207744 DOI: 10.1016/j.actbio.2023.05.024] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/16/2023] [Revised: 04/22/2023] [Accepted: 05/12/2023] [Indexed: 05/21/2023]
Abstract
Biodegradable hydrogels are growing in demand to enable the delivery of biomolecules (e.g. growth factors) for regenerative medicine. This research investigated the resorption of an oligourethane/polyacrylic acid hydrogel, a biodegradable hydrogel which supports tissue regeneration. The Arrhenius model was used to characterize the resorption of the polymeric gels in relevant in vitro conditions, and the Flory-Rehner equation was used to correlate the volumetric swelling ratio with the extent of degradation. The study found that the swelling rate of the hydrogel follows the Arrhenius model at elevated temperatures, estimating degradation time in saline solution at 37°C to be between 5 and 13 months, serving as a preliminary approximation of degradation in vivo. The degradation products had low cytotoxicity towards endothelial cells, and the hydrogel supported stromal cell proliferation. Additionally, the hydrogels were able to release growth factors and maintain the biomolecules' bioactivity towards cell proliferation. The study of the vascular endothelial growth factor (VEGF) release from the hydrogel used a diffusion process model, showing that the electrostatic attraction between VEGF and the anionic hydrogel allowed for controlled and sustained VEGF release over three weeks. In a rat subcutaneous implant model, a selected hydrogel with desired degradation rates exhibited minimal foreign body response and supported M2a macrophage phenotype, and vascularization. The low M1 and high M2a macrophage phenotypes within the implants were associated with tissue integration. This research supports the use of oligourethane/polyacrylic acid hydrogels as a promising material for delivering growth factors and supporting tissue regeneration. STATEMENT OF SIGNIFICANCE: There is a need for degradable elastomeric hydrogels that can support the formation of soft tissues and minimize long-term foreign body responses. An Arrhenius model was used to estimate the relative breakdown of hydrogels, in-vitro. The results demonstrate that hydrogels made from a combination of poly(acrylic acid) and oligo-urethane diacrylates can be designed to resorb over defined periods ranging from months to years depending on the chemical formulation prescribed by the model. The hydrogel formulations also provided for different release profiles of growth factors, relevant to tissue regeneration. In-vivo, these hydrogels had minimal inflammatory effects and showed evidence of integration into the surrounding tissue. The hydrogel approach can help the field design a broader range of biomaterials for tissue regeneration.
Collapse
Affiliation(s)
- Eric Tawagi
- Institute of Biomedical Engineering, University of Toronto, 661 University Avenue, 14th Floor, Room 1435, Toronto, ON M5G 1M1, Canada; Translational Biology & Engineering Program, Ted Rogers Centre for Heart Research, Toronto, ON, Canada
| | - Trevor Ung
- Translational Biology & Engineering Program, Ted Rogers Centre for Heart Research, Toronto, ON, Canada
| | - Hai-Ling Margaret Cheng
- Institute of Biomedical Engineering, University of Toronto, 661 University Avenue, 14th Floor, Room 1435, Toronto, ON M5G 1M1, Canada; Translational Biology & Engineering Program, Ted Rogers Centre for Heart Research, Toronto, ON, Canada; The Edward S. Rogers Sr. Department of Electrical & Computer Engineering, University of Toronto, Toronto, ON, Canada
| | - J Paul Santerre
- Institute of Biomedical Engineering, University of Toronto, 661 University Avenue, 14th Floor, Room 1435, Toronto, ON M5G 1M1, Canada; Translational Biology & Engineering Program, Ted Rogers Centre for Heart Research, Toronto, ON, Canada; Faculty of Dentistry, University of Toronto, Toronto, ON, Canada.
| |
Collapse
|
35
|
Borelbach P, Kopitzky R, Dahringer J, Gutmann P. Degradation Behavior of Biodegradable Man-Made Fibers in Natural Soil and in Compost. Polymers (Basel) 2023; 15:2959. [PMID: 37447604 DOI: 10.3390/polym15132959] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 04/05/2023] [Revised: 06/24/2023] [Accepted: 07/03/2023] [Indexed: 07/15/2023] Open
Abstract
In open environment applications, fibers are increasingly being used that are expected to biodegrade in the soil after their desired service life. Biodegradable polymer fibers are a versatile alternative to natural fibers. In this study, the degradation behavior of fibers made from polylactic acid (PLA) and a polyhydroxy alkanoate (PHA) blend with PLA, as well as a bicomponent fiber (BICO) made from polybutylene succinate (PBS) and PLA, was investigated. The fibers were stored in topsoil at 23 °C for 12 weeks. In addition, fibers were stored in compost at 58 °C for 4 weeks to investigate the degradation behavior in an industrial composting plant. Reference materials were also stored without substrate under the same temperatures and humidity conditions. Samples were taken regularly, and mechanical testing, scanning electron microscopy (SEM), gel permeation chromatography (GPC), differential scanning calorimetry (DSC), and infrared spectroscopy (IR) were used to study the degradation of the fibers. After 12 weeks in soil at ambient temperatures, the PLA and BICO fibers showed no degradation. The PHA fibers showed cracks in SEM, a decrease in molecular weight, and changes in the IR spectrum. No evidence of biological influence (bacteria or fungi) was found. Under industrial composting conditions, all fibers showed a decrease in strength and molecular weight. For the BICO and the PHA fibers, the SEM images show significant changes. Especially in the PHA fibers, fungal mycelia can be seen. The studies provide a better insight into the processes involved in the degradation behavior under different environmental conditions.
Collapse
Affiliation(s)
- Pia Borelbach
- Fraunhofer Institut für Umwelt-, Sicherheits- und Energietechnik UMSICHT, 46047 Oberhausen, Germany
| | - Rodion Kopitzky
- Fraunhofer Institut für Umwelt-, Sicherheits- und Energietechnik UMSICHT, 46047 Oberhausen, Germany
| | - Jörg Dahringer
- Indorama Ventures Fibers Germany GmbH, 86399 Bobingen, Germany
| | - Patrick Gutmann
- Indorama Ventures Fibers Germany GmbH, 86399 Bobingen, Germany
| |
Collapse
|
36
|
Pan Z, Brassart L. A reaction-diffusion framework for hydrolytic degradation of amorphous polymers based on a discrete chain scission model. Acta Biomater 2023:S1742-7061(23)00346-X. [PMID: 37343906 DOI: 10.1016/j.actbio.2023.06.021] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 02/15/2023] [Revised: 06/06/2023] [Accepted: 06/15/2023] [Indexed: 06/23/2023]
Abstract
Hydrolytic degradation of polymers involves the scission of long chain molecules, leading to molecular weight reduction and mass loss. The precise degradation response however depends on the scission probability of individual bonds along the polymer backbone. In particular, bonds near the chain ends are considered to be more susceptible to hydrolysis than inner bonds. In this paper, we incorporate a discrete chain scission model that can handle arbitrary bond scission probabilities within a continuum reaction-diffusion framework. Overall hydrolysis kinetics (including autocatalysis) is described independently of the chain scission model. By decoupling the description of the chain scission mechanism from kinetics, our framework enables the identification of the chain scission mechanism from molecular weight reduction and mass loss curves commonly reported in experimental degradation studies. We further propose a reduced continuum model which is better suited for large-scale simulations while retaining the predictive capability of the full discrete-continuum model. The model capability is illustrated in representative case studies based on experimental data from the literature for different materials and geometries. STATEMENT OF SIGNIFICANCE: Many models have been proposed to predict the evolution of molecular weight and mass loss in biodegradable polymers undergoing hydrolytic degradation. However, existing models remain limited in their ability to describe the degradation mechanism, autocatalytic kinetics and short chains diffusion simultaneously. Moreover, existing models often rely on empirical relations and a large number of fitting parameters. Here, we propose a conceptually simple discrete-continuum mathematical framework with a small number of parameters which all have a clear physical meaning. Model calibration against experimental data is simplified, and further provides insights into the degradation mechanisms at play, namely random scission, chain-end scission, or a combination of both. The framework can serve as a basis for future generalisations, including a description of evolving crystallinity, or other degradation mechanisms, such as thermal oxidation or photo-degradation.
Collapse
Affiliation(s)
- Zhouzhou Pan
- Department of Engineering Science, University of Oxford, Oxford OX1 3PJ, UK
| | - Laurence Brassart
- Department of Engineering Science, University of Oxford, Oxford OX1 3PJ, UK.
| |
Collapse
|
37
|
Thakur B, Singh J, Singh J, Angmo D, Vig AP. Biodegradation of different types of microplastics: Molecular mechanism and degradation efficiency. THE SCIENCE OF THE TOTAL ENVIRONMENT 2023; 877:162912. [PMID: 36933716 DOI: 10.1016/j.scitotenv.2023.162912] [Citation(s) in RCA: 24] [Impact Index Per Article: 24.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 11/25/2022] [Revised: 03/06/2023] [Accepted: 03/13/2023] [Indexed: 05/06/2023]
Abstract
Microplastics are widely distributed and a major pollutant in our ecosystem. Microplastics (MPs) are very small size plastic (<5 mm) present in environment, which comes from industrial, agricultural and household wastes. Plastic particles are more durable due to the presence of plasticizers and chemicals or additives. These plastics pollutants are more resistant to degradation. Inadequate recycling and excessive use of plastics lead to a large amount of waste accumulating in the terrestrial ecosystem, causing a risk to humans and animals. Thus, there is an urgent need to control microplastic pollution by employing different microorganisms to overcome this hazardous issue for the environment. Biological degradation depends upon different aspects, including chemical structure, functional group, molecular weight, crystallinity and additives. Molecular mechanisms for degradation of MPs through various enzymes have not extremely studied. It is necessary to degrade the MPs and overcome this problem. This review approaches different molecular mechanisms to degrade different types of microplastics and summarize the degradation efficiency of different types of bacteria, algae and fungal strains. The present study also summarizes the potential of microorganisms to degrade different polymers and the role of different enzymes in degradation of microplastics. To the outstanding of our awareness, this is the first article devoted to the role of microorganisms with their degradation efficiency. Furthermore, it also summarizes the role of intracellular and extracellular enzymes in biological degradation mechanism of microplastics.
Collapse
Affiliation(s)
- Babita Thakur
- Department of Microbiology, School of Bioengineering and Biosciences, Lovely Professional University, Phagwara, Punjab, India
| | - Jaswinder Singh
- Department of Zoology, Khalsa College Amritsar, Punjab, India.
| | - Joginder Singh
- Department of Microbiology, School of Bioengineering and Biosciences, Lovely Professional University, Phagwara, Punjab, India
| | - Deachen Angmo
- Department of Botanical and Environmental Sciences, Guru Nanak Dev University, Amritsar, Punjab, India
| | - Adarsh Pal Vig
- Department of Botanical and Environmental Sciences, Guru Nanak Dev University, Amritsar, Punjab, India
| |
Collapse
|
38
|
Pawlak M, Drzeżdżon J, Jacewicz D. The greener side of polymers in the light of d-block metal complexes as precatalysts. Coord Chem Rev 2023. [DOI: 10.1016/j.ccr.2023.215122] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 04/03/2023]
|
39
|
Barreira-Pinto R, Carneiro R, Miranda M, Guedes RM. Polymer-Matrix Composites: Characterising the Impact of Environmental Factors on Their Lifetime. MATERIALS (BASEL, SWITZERLAND) 2023; 16:ma16113913. [PMID: 37297046 DOI: 10.3390/ma16113913] [Citation(s) in RCA: 2] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 04/14/2023] [Revised: 05/02/2023] [Accepted: 05/15/2023] [Indexed: 06/12/2023]
Abstract
Polymer-matrix composites are widely used in engineering applications. Yet, environmental factors impact their macroscale fatigue and creep performances significantly, owing to several mechanisms acting at the microstructure level. Herein, we analyse the effects of water uptake that are responsible for swelling and, over time and in enough quantity, for hydrolysis. Seawater, due to a combination of high salinity and pressures, low temperature and biotic media present, also contributes to the acceleration of fatigue and creep damage. Similarly, other liquid corrosive agents penetrate into cracks induced by cyclic loading and cause dissolution of the resin and breakage of interfacial bonds. UV radiation either increases the crosslinking density or scissions chains, embrittling the surface layer of a given matrix. Temperature cycles close to the glass transition damage the fibre-matrix interface, promoting microcracking and hindering fatigue and creep performance. The microbial and enzymatic degradation of biopolymers is also studied, with the former responsible for metabolising specific matrices and changing their microstructure and/or chemical composition. The impact of these environmental factors is detailed for epoxy, vinyl ester and polyester (thermoset); polypropylene, polyamide and poly etheretherketone (thermoplastic); and for poly lactic acid, thermoplastic starch and polyhydroxyalkanoates (biopolymers). Overall, the environmental factors mentioned hamper the fatigue and creep performances, altering the mechanical properties of the composite or causing stress concentrations through microcracks, promoting earlier failure. Future studies should focus on other matrices beyond epoxy as well as on the development of standardised testing methods.
Collapse
Affiliation(s)
- Rui Barreira-Pinto
- Departamento de Engenharia Mecânica Faculdade de Engenharia, Universidade do Porto, Rua Dr. Roberto Frias, 4200-465 Porto, Portugal
| | - Rodrigo Carneiro
- Departamento de Engenharia Mecânica Faculdade de Engenharia, Universidade do Porto, Rua Dr. Roberto Frias, 4200-465 Porto, Portugal
| | - Mário Miranda
- Departamento de Engenharia Mecânica Faculdade de Engenharia, Universidade do Porto, Rua Dr. Roberto Frias, 4200-465 Porto, Portugal
| | - Rui Miranda Guedes
- Departamento de Engenharia Mecânica Faculdade de Engenharia, Universidade do Porto, Rua Dr. Roberto Frias, 4200-465 Porto, Portugal
- INEGI-Instituto de Engenharia Mecânica e Gestão Industrial, Rua Dr. Roberto Frias, 4200-465 Porto, Portugal
| |
Collapse
|
40
|
Mattelin V, Verfaille L, Kundu K, De Wildeman S, Boon N. A New Colorimetric Test for Accurate Determination of Plastic Biodegradation. Polymers (Basel) 2023; 15:polym15102311. [PMID: 37242886 DOI: 10.3390/polym15102311] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 04/07/2023] [Revised: 05/03/2023] [Accepted: 05/06/2023] [Indexed: 05/28/2023] Open
Abstract
As plastic waste is accumulating in both controlled waste management settings and natural settings, much research is devoted to search for solutions, also in the field of biodegradation. However, determining the biodegradability of plastics in natural environments remains a big challenge due to the often very low biodegradation rates. Many standardised test methods for biodegradation in natural environments exist. These are often based on mineralisation rates in controlled conditions and are thus indirect measurements of biodegradation. It is of interest for both researchers and companies to have tests that are more rapid, easier, and more reliable to screen different ecosystems and/or niches for their plastic biodegradation potential. In this study, the goal is to validate a colorimetric test, based on carbon nanodots, to screen biodegradation of different types of plastics in natural environments. After introducing carbon nanodots into the matrix of the target plastic, a fluorescent signal is released upon plastic biodegradation. The in-house-made carbon nanodots were first confirmed regarding their biocompatibility and chemical and photostability. Subsequently, the effectivity of the developed method was evaluated positively by an enzymatic degradation test with polycaprolactone with Candida antarctica lipase B. Finally, validation experiments were performed with enriched microorganisms and real environmental samples (freshwater and seawater), of which the results were compared with parallel, frequently used biodegradation measures such as O2 and CO2, dissolved organic carbon, growth and pH, to assess the reliability of the test. Our results indicate that this colorimetric test is a good alternative to other methods, but a combination of different methods gives the most information. In conclusion, this colorimetric test is a good fit to screen, in high throughput, the depolymerisation of plastics in natural environments and under different conditions in the lab.
Collapse
Affiliation(s)
- Valérie Mattelin
- Center for Microbial Ecology and Technology (CMET), Ghent University, 9000 Ghent, Belgium
| | - Lennert Verfaille
- Center for Microbial Ecology and Technology (CMET), Ghent University, 9000 Ghent, Belgium
| | - Kankana Kundu
- Center for Microbial Ecology and Technology (CMET), Ghent University, 9000 Ghent, Belgium
| | | | - Nico Boon
- Center for Microbial Ecology and Technology (CMET), Ghent University, 9000 Ghent, Belgium
- Center for Advanced Process Technology for Urban Resource Recovery (CAPTURE), 9000 Ghent, Belgium
| |
Collapse
|
41
|
Liu TY, Zhen ZC, Zang XL, Xu PY, Wang GX, Lu B, Li F, Wang PL, Huang D, Ji JH. Fluorescence tracing the degradation process of biodegradable PBAT: Visualization and high sensitivity. JOURNAL OF HAZARDOUS MATERIALS 2023; 454:131572. [PMID: 37148790 DOI: 10.1016/j.jhazmat.2023.131572] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 02/26/2023] [Revised: 04/30/2023] [Accepted: 05/02/2023] [Indexed: 05/08/2023]
Abstract
Biodegradable plastics have emerged as a potential solution to the mounting plastic pollution crisis. However, current methods for evaluating the degradation of these plastics are limited in detecting structural changes rapidly and accurately, particularly for PBAT, which contains worrying benzene rings. Inspired by the fact that the aggregation of conjugated groups can endow polymers with intrinsic fluorescence, this work found that PBAT emits a bright blue-green fluoresces under UV irradiation. More importantly, we pioneered a degradation evaluation approach to track the degradation process of PBAT via fluorescence. A blue shift of fluorescence wavelength as the thickness and molecular weight of PBAT film decreased during degradation in an alkali solution was observed. Additionally, the fluorescence intensity of the degradation solution increased gradually as the degradation progressed, and was found to be exponentially correlated with the concentration of benzene ring-containing degradation products following filtration with the correlation coefficient is up to 0.999. This study proposes a promising new strategy for monitoring the degradation process with visualization and high sensitivity.
Collapse
Affiliation(s)
- Tian-Yuan Liu
- National Engineering Research Center of Engineering and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; University of Chinese Academy of Sciences, Beijing 100049, China
| | - Zhi-Chao Zhen
- National Engineering Research Center of Engineering and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China
| | - Xiao-Ling Zang
- College of Chemistry and Materials Engineering, Beijing Technology and Business University, Beijing 100048, China
| | - Peng-Yuan Xu
- National Engineering Research Center of Engineering and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; University of Chinese Academy of Sciences, Beijing 100049, China
| | - Ge-Xia Wang
- National Engineering Research Center of Engineering and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China
| | - Bo Lu
- National Engineering Research Center of Engineering and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; University of Chinese Academy of Sciences, Beijing 100049, China
| | - Fei Li
- National Engineering Research Center of Engineering and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China
| | - Ping-Li Wang
- National Engineering Research Center of Engineering and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China.
| | - Dan Huang
- National Engineering Research Center of Engineering and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China.
| | - Jun-Hui Ji
- National Engineering Research Center of Engineering and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China.
| |
Collapse
|
42
|
Vieira AFC, Da Silva EHP, Ribeiro ML. Numerical Approach to Simulate the Mechanical Behavior of Biodegradable Polymers during Erosion. Polymers (Basel) 2023; 15:polym15091979. [PMID: 37177128 PMCID: PMC10181274 DOI: 10.3390/polym15091979] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 03/03/2023] [Revised: 03/31/2023] [Accepted: 04/18/2023] [Indexed: 05/15/2023] Open
Abstract
Biodegradable polymers find applications in many market segments. The ability to meet mechanical requirements within a certain time range, after which it degrades and is naturally absorbed, can be used to produce short-term use products that can be easily disposable with less environmental impact. In the segment of medical devices used in regenerative medicine, these materials are used to produce temporary implants that are naturally assimilated by the human body, avoiding a removal surgery. However, the design of these temporary devices still presents great challenges, namely in the verification of the main requirement: the lifetime of the device, associated with the progressive loss of mechanical properties, until its complete erosion and assimilation. Thus, in this study, a numerical approach is proposed to simulate the polymeric device's mechanical behavior during its hydrolytic degradation by combining the hydrolysis kinetics, that depends on mechanical factors and promotes a decrease of molecular weight and consequent decrease of mechanical performance, and erosion, when molecular weight reaches a threshold value and the polymer becomes soluble and diffuses outward, resulting in mass loss and decreasing cross-sectional area, which also contributes to the mechanical performance reduction of the device. A phenomenological approach, using the combination of continuum-based hydrolytic damage for the evolution of mechanical properties that depends on the stress field and further removal of the degraded element (to simulate mass loss) was used. Both elastoplastic and hyperelastic constitutive models were applied on this study, where the material model parameters locally depend on the molecular weight.
Collapse
Affiliation(s)
- André F C Vieira
- Center for Mechanical and Aerospace Science and Technologies (C-MAST-UBI), Universidade da Beira Interior, R. Marquês D'Ávila e Bolama, 6201-001 Covilhã, Portugal
| | - Enio H P Da Silva
- Aeronautical Engineering Department, São Carlos School of Engineering, University of São Paulo, São Carlos 13563-120, SP, Brazil
| | - Marcelo L Ribeiro
- Aeronautical Engineering Department, São Carlos School of Engineering, University of São Paulo, São Carlos 13563-120, SP, Brazil
| |
Collapse
|
43
|
Han WB, Ko GJ, Lee KG, Kim D, Lee JH, Yang SM, Kim DJ, Shin JW, Jang TM, Han S, Zhou H, Kang H, Lim JH, Rajaram K, Cheng H, Park YD, Kim SH, Hwang SW. Ultra-stretchable and biodegradable elastomers for soft, transient electronics. Nat Commun 2023; 14:2263. [PMID: 37081012 PMCID: PMC10119106 DOI: 10.1038/s41467-023-38040-4] [Citation(s) in RCA: 11] [Impact Index Per Article: 11.0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/14/2022] [Accepted: 04/13/2023] [Indexed: 04/22/2023] Open
Abstract
As rubber-like elastomers have led to scientific breakthroughs in soft, stretchable characteristics-based wearable, implantable electronic devices or relevant research fields, developments of degradable elastomers with comparable mechanical properties could bring similar technological innovations in transient, bioresorbable electronics or expansion into unexplored areas. Here, we introduce ultra-stretchable, biodegradable elastomers capable of stretching up to ~1600% with outstanding properties in toughness, tear-tolerance, and storage stability, all of which are validated by comprehensive mechanical and biochemical studies. The facile formation of thin films enables the integration of almost any type of electronic device with tunable, suitable adhesive strengths. Conductive elastomers tolerant/sensitive to mechanical deformations highlight possibilities for versatile monitoring/sensing components, particularly the strain-tolerant composites retain high levels of conductivities even under tensile strains of ~550%. Demonstrations of soft electronic grippers and transient, suture-free cardiac jackets could be the cornerstone for sophisticated, multifunctional biodegradable electronics in the fields of soft robots and biomedical implants.
Collapse
Affiliation(s)
- Won Bae Han
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Gwan-Jin Ko
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Kang-Gon Lee
- Department of Biomedical Sciences, College of Medicine, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Donghak Kim
- Center for Biomaterials, Biomedical Research Institute, Korea Institute of Science and Technology (KIST), 5 Hwarang-ro 14-gil, Seongbuk-gu, Seoul, 02792, Republic of Korea
| | - Joong Hoon Lee
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Seung Min Yang
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
- Hanwha Systems Co., Ltd., 188 Pangyoyeok-ro, Bundang-gu, Seongnam-Si, Gyeonggi-do, 13524, Republic of Korea
| | - Dong-Je Kim
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Jeong-Woong Shin
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Tae-Min Jang
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Sungkeun Han
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Honglei Zhou
- Department of Engineering Science and Mechanics, The Pennsylvania State University, University Park, PA, 16802, USA
| | - Heeseok Kang
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Jun Hyeon Lim
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Kaveti Rajaram
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Huanyu Cheng
- Department of Engineering Science and Mechanics, The Pennsylvania State University, University Park, PA, 16802, USA
| | - Yong-Doo Park
- Department of Biomedical Sciences, College of Medicine, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea
| | - Soo Hyun Kim
- Center for Biomaterials, Biomedical Research Institute, Korea Institute of Science and Technology (KIST), 5 Hwarang-ro 14-gil, Seongbuk-gu, Seoul, 02792, Republic of Korea
| | - Suk-Won Hwang
- KU-KIST Graduate School of Converging Science and Technology, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea.
- Center for Biomaterials, Biomedical Research Institute, Korea Institute of Science and Technology (KIST), 5 Hwarang-ro 14-gil, Seongbuk-gu, Seoul, 02792, Republic of Korea.
- Department of Integrative Energy Engineering, Korea University, 145 Anam-ro, Seongbuk-gu, Seoul, 02841, Republic of Korea.
| |
Collapse
|
44
|
Eck M, Bernabeu L, Mecking S. Polyethylene-Like Blends Amenable to Abiotic Hydrolytic Degradation. ACS SUSTAINABLE CHEMISTRY & ENGINEERING 2023; 11:4523-4530. [PMID: 37008182 PMCID: PMC10052336 DOI: 10.1021/acssuschemeng.2c07537] [Citation(s) in RCA: 3] [Impact Index Per Article: 3.0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Figures] [Subscribe] [Scholar Register] [Received: 12/20/2022] [Revised: 03/06/2023] [Indexed: 06/19/2023]
Abstract
Long-chain aliphatic polyester-18,18 (PE-18,18) exhibits high density polyethylene-like material properties and, as opposed to high density polyethylene (HDPE), can be recycled in a closed loop via depolymerization to monomers under mild conditions. Despite the in-chain ester groups, its high crystallinity and hydrophobicity render PE-18,18 stable toward hydrolysis even under acidic conditions for one year. Hydrolytic degradability, however, can be a desirable material property as it can serve as a universal backstop to plastic accumulation in the environment. We present an approach to render PE-18,18 hydrolytically degradable by melt blending with long-chain aliphatic poly(H-phosphonate)s (PP). The blends can be processed via common injection molding and 3D printing and exhibit HDPE-like tensile properties, namely, high stiffness (E = 750-940 MPa) and ductility (εtb = 330-460%) over a wide range of blend ratios (0.5-20 wt % PP content). Likewise, the orthorhombic solid-state structure and crystallinity (χ ≈ 70%) of the blends are similar to HDPE. Under aqueous conditions in phosphate-buffered media at 25 °C, the blends' PP component is hydrolyzed completely to the underlying long-chain diol and phosphorous acid within four months, as evidenced by NMR analyses. Concomitant, the PE-18,18 major blend component is partially hydrolyzed, while neat PE-18,18 is inert under identical conditions. The hydrolysis of the blend components proceeded throughout the bulk of the specimens as confirmed by gel permeation chromatography (GPC) measurements. The significant molar mass reduction upon extended immersion in water (M n(virgin blends) ≈ 50-70 kg mol-1; M n(hydrolyzed blends) ≈ 7-11 kg mol-1) resulted in embrittlement and fragmentation of the injection molded specimens. This increases the surface area and is anticipated to promote eventual mineralization by abiotic and biotic pathways of these HDPE-like polyesters in the environment.
Collapse
|
45
|
Tian R, Li K, Lin Y, Lu C, Duan X. Characterization Techniques of Polymer Aging: From Beginning to End. Chem Rev 2023; 123:3007-3088. [PMID: 36802560 DOI: 10.1021/acs.chemrev.2c00750] [Citation(s) in RCA: 4] [Impact Index Per Article: 4.0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 02/22/2023]
Abstract
Polymers have been widely applied in various fields in the daily routines and the manufacturing. Despite the awareness of the aggressive and inevitable aging for the polymers, it still remains a challenge to choose an appropriate characterization strategy for evaluating the aging behaviors. The difficulties lie in the fact that the polymer features from the different aging stages require different characterization methods. In this review, we present an overview of the characterization strategies preferable for the initial, accelerated, and late stages during polymer aging. The optimum strategies have been discussed to characterize the generation of radicals, variation of functional groups, substantial chain scission, formation of low-molecular products, and deterioration in the polymers' macro-performances. In view of the advantages and the limitations of these characterization techniques, their utilization in a strategic approach is considered. In addition, we highlight the structure-property relationship for the aged polymers and provide available guidance for lifetime prediction. This review could allow the readers to be knowledgeable of the features for the polymers in the different aging stages and provide access to choose the optimum characterization techniques. We believe that this review will attract the communities dedicated to materials science and chemistry.
Collapse
Affiliation(s)
- Rui Tian
- State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing 100029, China
| | - Kaitao Li
- State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing 100029, China
| | - Yanjun Lin
- State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing 100029, China
- School of Chemical Engineering, Qinghai University, Xining 810016, China
| | - Chao Lu
- State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing 100029, China
- Green Catalysis Center, College of Chemistry, Zhengzhou University, Zhengzhou 450001, China
| | - Xue Duan
- State Key Laboratory of Chemical Resource Engineering, Beijing University of Chemical Technology, Beijing 100029, China
| |
Collapse
|
46
|
Liu TY, Xu PY, Lu B, Zhen ZC, Zheng WZ, Dong YC, Li X, Wang GX, Ji JH. Enhanced degradation of poly(ethylene terephthalate) by the addition of lactic acid / glycolic acid: composting degradation, seawater degradation behavior and comparison of degradation mechanism. JOURNAL OF HAZARDOUS MATERIALS 2023; 446:130670. [PMID: 36580787 DOI: 10.1016/j.jhazmat.2022.130670] [Citation(s) in RCA: 6] [Impact Index Per Article: 6.0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Subscribe] [Scholar Register] [Received: 11/09/2022] [Revised: 12/08/2022] [Accepted: 12/23/2022] [Indexed: 06/17/2023]
Abstract
The degradability improvement of poly(ethylene terephthalate) (PET), one of the most widely used but non-degradable disposable packaging material, is of great significance. However, the balance between degradability and mechanical properties remains a huge challenge. Herein, simple hydroxy acids, lactic acid (LA) and glycolic acid (GA) as easy hydrolysis sites were introduced into non-degradable PET via melt polycondensation. A series of high molecular weight poly(ethylene terephthalate-co-L‑lactide) (PETL) and poly(ethylene terephthalate-co-glycolate) (PETG) copolyesters were synthesized with an excellent tensile strength greater than 50 MPa, much higher than that of most commercially available degradable polymers. The introduction of hydroxy acid endows PET with significantly improved composting and seawater degradation performance. Furtherly, the degradation rate of PETG with hydrophilic GA unit was faster than that of PETL, and the mineralization rate of PETG80 reaches 22.0%. The density of functional theory (DFT) calculation revealed that adding hydroxy acid to the PET molecular chain reduced the energy barrier of the hydrolysis reaction. The molecular polarity index (MPI) analysis furtherly confirmed that the higher affinity between the GA unit and water may be the primary reason for the faster degradation of PETG.
Collapse
Affiliation(s)
- Tian-Yuan Liu
- National Engineering Research Center of Engineering Plastics and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; University of Chinese Academy of Sciences, Beijing 100049, China
| | - Peng-Yuan Xu
- National Engineering Research Center of Engineering Plastics and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; University of Chinese Academy of Sciences, Beijing 100049, China
| | - Bo Lu
- National Engineering Research Center of Engineering Plastics and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; Hainan Degradable Plastics Technology Innovation Center, Haikou 571137, China
| | - Zhi-Chao Zhen
- National Engineering Research Center of Engineering Plastics and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; Hainan Degradable Plastics Technology Innovation Center, Haikou 571137, China
| | - Wei-Zhen Zheng
- National Engineering Research Center of Engineering Plastics and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; University of Chinese Academy of Sciences, Beijing 100049, China
| | - Yan-Chao Dong
- National Engineering Research Center of Engineering Plastics and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; University of Chinese Academy of Sciences, Beijing 100049, China
| | - Xiao Li
- National Engineering Research Center of Engineering Plastics and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; University of Chinese Academy of Sciences, Beijing 100049, China
| | - Ge-Xia Wang
- National Engineering Research Center of Engineering Plastics and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; Hainan Degradable Plastics Technology Innovation Center, Haikou 571137, China.
| | - Jun-Hui Ji
- National Engineering Research Center of Engineering Plastics and Ecological Plastics, Technical Institute of Physics and Chemistry, Chinese Academy of Sciences, Beijing 100190, China; Hainan Degradable Plastics Technology Innovation Center, Haikou 571137, China.
| |
Collapse
|
47
|
Li MQ, Luo ZX, Yu XY, Tian GQ, Wu G, Chen SC, Wang YZ. Ring-Opening Polymerization of a Seven-Membered Lactone toward a Biocompatible, Degradable, and Recyclable Semi-aromatic Polyester. Macromolecules 2023. [DOI: 10.1021/acs.macromol.2c02172] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Indexed: 03/17/2023]
Affiliation(s)
- Mao-Qin Li
- The Collaborative Innovation Center for Eco-Friendly and Fire-Safety Polymeric Materials (MoE), National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), State Key Laboratory of Polymer Materials Engineering, College of Chemistry, Sichuan University, Chengdu 610064, China
| | - Zi-Xuan Luo
- The Collaborative Innovation Center for Eco-Friendly and Fire-Safety Polymeric Materials (MoE), National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), State Key Laboratory of Polymer Materials Engineering, College of Chemistry, Sichuan University, Chengdu 610064, China
| | - Xiao-Yan Yu
- The Collaborative Innovation Center for Eco-Friendly and Fire-Safety Polymeric Materials (MoE), National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), State Key Laboratory of Polymer Materials Engineering, College of Chemistry, Sichuan University, Chengdu 610064, China
| | - Guo-Qiang Tian
- The Collaborative Innovation Center for Eco-Friendly and Fire-Safety Polymeric Materials (MoE), National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), State Key Laboratory of Polymer Materials Engineering, College of Chemistry, Sichuan University, Chengdu 610064, China
| | - Gang Wu
- The Collaborative Innovation Center for Eco-Friendly and Fire-Safety Polymeric Materials (MoE), National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), State Key Laboratory of Polymer Materials Engineering, College of Chemistry, Sichuan University, Chengdu 610064, China
| | - Si-Chong Chen
- The Collaborative Innovation Center for Eco-Friendly and Fire-Safety Polymeric Materials (MoE), National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), State Key Laboratory of Polymer Materials Engineering, College of Chemistry, Sichuan University, Chengdu 610064, China
| | - Yu-Zhong Wang
- The Collaborative Innovation Center for Eco-Friendly and Fire-Safety Polymeric Materials (MoE), National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), State Key Laboratory of Polymer Materials Engineering, College of Chemistry, Sichuan University, Chengdu 610064, China
| |
Collapse
|
48
|
Li NY, Qu JH, Yang JY. Microplastics distribution and microbial community characteristics of farmland soil under different mulch methods. JOURNAL OF HAZARDOUS MATERIALS 2023; 445:130408. [PMID: 36455321 DOI: 10.1016/j.jhazmat.2022.130408] [Citation(s) in RCA: 7] [Impact Index Per Article: 7.0] [Reference Citation Analysis] [Abstract] [Key Words] [MESH Headings] [Track Full Text] [Subscribe] [Scholar Register] [Received: 09/27/2022] [Revised: 11/10/2022] [Accepted: 11/14/2022] [Indexed: 06/17/2023]
Abstract
The widespread use of plastic film in agricultural production has resulted in the accumulation of large amounts of residual plastic film in the soil, and most of the plastic residuals eventually break up into microplastics (MPs). However, the effects of different film mulching methods on the soil ecosystems are largely unexplored. Therefore, we investigated the MPs distribution and the physicochemical properties and microbial community structure in the farmland soil tillage layer covered with different mulching method of film. The results indicate that the film mulching method had no significant effect on the soil pH and organic matter content, however, the respiration intensity of the soil covered with mulching film (MF) (60.11-84.99 μg/g) and shed film (SF) (56.10-65.68 μg/g) was significantly higher than that covered with shed film & mulching film (SMF) (17.25-39.16 μg/g). The MPs abundance in the soil covered with MF (1367 particles/kg soil) was significantly higher than that covered with SF (800 particles/kg soil) and slightly higher than that with SMF (1000 particles/kg soil). The small-sized (0-0.5 mm) MPs abundance was increased with the tillage layer depth (0-20 cm), while the large-sized (1-5 mm) MPs abundance was the opposite. In addition, in the soil covered with agricultural film, the dominant phylum and genera of the bacteria were Proteobacteria (relative abundance was 64.06 %) and Pseudomonas (13.16 %), respectively. In the soil without agricultural film application as a control treatment, the diversity of the soil bacterial community was higher than that in the soil covered with agricultural film, and the relative abundances of the top 10 genera were all less than 5 %. Overall, this study provides essential information for understanding the effects of different film mulching methods on the agricultural systems. Overall, this study provides essential information for understanding the effects of different film mulching methods on the distribution of MPs and the biogeochemical properties of farmland soils.
Collapse
Affiliation(s)
- Na-Ying Li
- College of Architecture and Environment, Sichuan University, Chengdu 610065, China; Key Laboratory of Environment Remediation and Ecological Health (Zhejiang University), Ministry of Education, China
| | - Jia-Hui Qu
- College of Architecture and Environment, Sichuan University, Chengdu 610065, China
| | - Jin-Yan Yang
- College of Architecture and Environment, Sichuan University, Chengdu 610065, China; Key Laboratory of Environment Remediation and Ecological Health (Zhejiang University), Ministry of Education, China.
| |
Collapse
|
49
|
Klabukov I, Tenchurin T, Shepelev A, Baranovskii D, Mamagulashvili V, Dyuzheva T, Krasilnikova O, Balyasin M, Lyundup A, Krasheninnikov M, Sulina Y, Gomzyak V, Krasheninnikov S, Buzin A, Zayratyants G, Yakimova A, Demchenko A, Ivanov S, Shegay P, Kaprin A, Chvalun S. Biomechanical Behaviors and Degradation Properties of Multilayered Polymer Scaffolds: The Phase Space Method for Bile Duct Design and Bioengineering. Biomedicines 2023; 11:biomedicines11030745. [PMID: 36979723 PMCID: PMC10044742 DOI: 10.3390/biomedicines11030745] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 01/30/2023] [Revised: 02/21/2023] [Accepted: 02/22/2023] [Indexed: 03/06/2023] Open
Abstract
This article reports the electrospinning technique for the manufacturing of multilayered scaffolds for bile duct tissue engineering based on an inner layer of polycaprolactone (PCL) and an outer layer either of a copolymer of D,L-lactide and glycolide (PLGA) or a copolymer of L-lactide and ε-caprolactone (PLCL). A study of the degradation properties of separate polymers showed that flat PCL samples exhibited the highest resistance to hydrolysis in comparison with PLGA and PLCL. Irrespective of the liquid-phase nature, no significant mass loss of PCL samples was found in 140 days of incubation. The PLCL- and PLGA-based flat samples were more prone to hydrolysis within the same period of time, which was confirmed by the increased loss of mass and a significant reduction of weight-average molecular mass. The study of the mechanical properties of developed multi-layered tubular scaffolds revealed that their strength in the longitudinal and transverse directions was comparable with the values measured for a decellularized bile duct. The strength of three-layered scaffolds declined significantly because of the active degradation of the outer layer made of PLGA. The strength of scaffolds with the PLCL outer layer deteriorated much less with time, both in the axial (p-value = 0.0016) and radial (p-value = 0.0022) directions. A novel method for assessment of the physiological relevance of synthetic scaffolds was developed and named the phase space approach for assessment of physiological relevance. Two-dimensional phase space (elongation modulus and tensile strength) was used for the assessment and visualization of the physiological relevance of scaffolds for bile duct bioengineering. In conclusion, the design of scaffolds for the creation of physiologically relevant tissue-engineered bile ducts should be based not only on biodegradation properties but also on the biomechanical time-related behavior of various compositions of polymers and copolymers.
Collapse
Affiliation(s)
- Ilya Klabukov
- Department of Regenerative Medicine, National Medical Research Radiological Centre of the Ministry of Health of the Russian Federation, 249031 Obninsk, Russia
- Department of Urology and Operative Nephrology, Peoples Friendship University of Russia (RUDN University), 117198 Moscow, Russia
- Obninsk Institute for Nuclear Power Engineering, National Research Nuclear University MEPhI, 115409 Obninsk, Russia
- Correspondence:
| | - Timur Tenchurin
- National Research Centre “Kurchatov Institute”, 1, Akademika Kurchatova pl., 123182 Moscow, Russia
| | - Alexey Shepelev
- National Research Centre “Kurchatov Institute”, 1, Akademika Kurchatova pl., 123182 Moscow, Russia
| | - Denis Baranovskii
- Department of Regenerative Medicine, National Medical Research Radiological Centre of the Ministry of Health of the Russian Federation, 249031 Obninsk, Russia
- Department of Urology and Operative Nephrology, Peoples Friendship University of Russia (RUDN University), 117198 Moscow, Russia
| | - Vissarion Mamagulashvili
- National Research Centre “Kurchatov Institute”, 1, Akademika Kurchatova pl., 123182 Moscow, Russia
| | - Tatiana Dyuzheva
- Department of Hospital Surgery, Sklifosovsky Institute of Clinical Medicine, Sechenov First Moscow State Medical University (Sechenov University), 119435 Moscow, Russia
| | - Olga Krasilnikova
- Department of Regenerative Medicine, National Medical Research Radiological Centre of the Ministry of Health of the Russian Federation, 249031 Obninsk, Russia
| | - Maksim Balyasin
- Research and Educational Resource Center for Cellular Technologies, Peoples Friendship University of Russia (RUDN University), 117198 Moscow, Russia
| | - Alexey Lyundup
- Research and Educational Resource Center for Cellular Technologies, Peoples Friendship University of Russia (RUDN University), 117198 Moscow, Russia
- N.P. Bochkov Research Centre for Medical Genetics, 115478 Moscow, Russia
| | - Mikhail Krasheninnikov
- Research and Educational Resource Center for Cellular Technologies, Peoples Friendship University of Russia (RUDN University), 117198 Moscow, Russia
- Lomonosov Institute of Fine Chemical Technologies, Russian Technological University MIREA, 119454 Moscow, Russia
| | - Yana Sulina
- Department of Obstetrics and Gynecology, Sechenov First Moscow State Medical University (Sechenov University), 119435 Moscow, Russia
| | - Vitaly Gomzyak
- National Research Centre “Kurchatov Institute”, 1, Akademika Kurchatova pl., 123182 Moscow, Russia
| | - Sergey Krasheninnikov
- National Research Centre “Kurchatov Institute”, 1, Akademika Kurchatova pl., 123182 Moscow, Russia
| | - Alexander Buzin
- National Research Centre “Kurchatov Institute”, 1, Akademika Kurchatova pl., 123182 Moscow, Russia
- Laboratory of the Structure of Polymer Materials, Enikolopov Institute of Synthetic Polymer Materials RAS, 117393 Moscow, Russia
| | - Georgiy Zayratyants
- Department of Pathology, Moscow State University of Medicine and Dentistry, Delegatskaya st., 20, p. 1, 127473 Moscow, Russia
| | - Anna Yakimova
- Department of Regenerative Medicine, National Medical Research Radiological Centre of the Ministry of Health of the Russian Federation, 249031 Obninsk, Russia
| | - Anna Demchenko
- N.P. Bochkov Research Centre for Medical Genetics, 115478 Moscow, Russia
| | - Sergey Ivanov
- Department of Regenerative Medicine, National Medical Research Radiological Centre of the Ministry of Health of the Russian Federation, 249031 Obninsk, Russia
| | - Peter Shegay
- Department of Regenerative Medicine, National Medical Research Radiological Centre of the Ministry of Health of the Russian Federation, 249031 Obninsk, Russia
- Department of Urology and Operative Nephrology, Peoples Friendship University of Russia (RUDN University), 117198 Moscow, Russia
| | - Andrey Kaprin
- Department of Regenerative Medicine, National Medical Research Radiological Centre of the Ministry of Health of the Russian Federation, 249031 Obninsk, Russia
- Department of Urology and Operative Nephrology, Peoples Friendship University of Russia (RUDN University), 117198 Moscow, Russia
| | - Sergei Chvalun
- National Research Centre “Kurchatov Institute”, 1, Akademika Kurchatova pl., 123182 Moscow, Russia
- Laboratory of the Structure of Polymer Materials, Enikolopov Institute of Synthetic Polymer Materials RAS, 117393 Moscow, Russia
| |
Collapse
|
50
|
Relationship between failure strain, molecular weight, and chain extensibility in biodegradable polymers. J Mech Behav Biomed Mater 2023; 139:105663. [PMID: 36657195 DOI: 10.1016/j.jmbbm.2023.105663] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 10/03/2022] [Revised: 01/02/2023] [Accepted: 01/05/2023] [Indexed: 01/07/2023]
Abstract
Prior to degradation, biocompatible polymers exhibit ductile behaviour and yield stress offers a suitable design approach. However, as degradation proceeds the material transitions to a brittle failure mode, suggesting a more conservative design approach is necessary. Here, we predict the evolving ductility of biodegrading polymers, concentrating on the relationship between molecular weight and failure strain, εf, in poly (lactic acid). Several datasets are chosen from literature to explore the relationship, with an overview of the experimental techniques provided. Failure criteria are proposed and examined alongside these datasets: the first assumes εf is related to the finite chain extensibility of an average chain; the second introduces an exponential empirical trend; the third proposes a modified extensibility criterion (based on the first criterion) that considers the entire molecular weight distribution; and the fourth offers an alternative to the third by considering the effect of chain scissions. Combining the failure criteria with a previously introduced time-dependent kinetic scission model provides results as a function of degradation duration. The predictions obtained can offer insight into material failure, particularly at advanced stages of degradation.
Collapse
|