Retention of Candida albicans on acrylic resin and silicone of different surface topography

Bacterial adhesion and surface properties of computer-aided design-computer-aided manufacturing restorative materials

PURPOSE

This study aimed to evaluate the surface properties and bacterial adhesion of computer-aided design-computer-aided manufacturing (CAD-CAM) restorative materials.

METHODS

Four CAD-CAM resin-based blocks (Vita Enamic, Shofu block HC, Cerasmart [CS] and Lava Ultimate [LU]) and a leucite-reinforced glass ceramic block (IPS Empress CAD) were used in the present study. Specimens prepared with dimensions of 10 × 10 × 1 mm were polished. Surface characteristics were assessed with hydrophobicity and surface free energy (SFE) analysis. Surface roughness was measured using a profilometer, and elemental and topographic evaluations were performed with SEM-EDX analysis. After being kept in artificial saliva for 1 h, Streptococcus mutans (S. mutans) and Streptococcus mitis (S. mitis) were incubated separately in 5% CO2 atmosphere at 37°C for 24 h. The adhered bacteria were counted as ×108 CFU/mL.

RESULTS

Surface roughness, contact angle and SFE measurement values were found to be in the range of 0.144-0.264 Ra, 28.362°-70.074° and 39.65-63.62 mN/m, respectively. The highest adhered amount of S. mutans was found in CS and the lowest in LU, while there was no significant difference between the amounts of adhered S. mitis.

CONCLUSION

Despite differences in the surface properties of the materials used for the study, the materials exhibited identical properties with respect to bacterial adhesion.

Assessing the suitability of fused deposition modeling to produce acrylic removable denture bases

OBJECTIVE

To study the feasibility of using poly methyl methacrylate (PMMA) filament and fused deposition modeling (FDM) to manufacture denture bases via the development of a study that considers both conventional and additive-based manufacturing techniques.

MATERIALS AND METHODS

Five sample groups were compared: heat and cold cured acrylic resins, CAD/CAM milled PMMA, 3D-printed PMMA (via FDM), and 3D-printed methacrylate resin (via stereolithography, SLA). All groups were subjected to mechanical testing (flexural strength, impact strength, and hardness), water sorption and solubility tests, a tooth bonding test, microbiological assessment, and accuracy of fit measurements. The performance of sample groups was referred to ISO 20795-1 and ISO/TS 19736. The data was analyzed using one-way ANOVA.

RESULTS

Samples manufactured using FDM performed within ISO specifications for mechanical testing, water sorption, and solubility tests. However, the FDM group failed to achieve the ISO requirements for the tooth bonding test. FDM samples presented a rough surface finish which could ultimately encourage an undesirable high level of microbial adhesion. For accuracy of fit, FDM samples showed a lower degree of accuracy than existing materials.

CONCLUSIONS

Although FDM samples were a cost-effective option and were able to be quickly manufactured in a reproducible manner, the results demonstrated that current recommended testing regimes for conventionally manufactured denture-based polymers are not directly applicable to additive-manufactured denture base polymers. Therefore, new standards should be developed to ensure the correct implementation of additive manufacturing techniques within denture-based fabrication workflow.

Impact of multiscale surface topography characteristics on Candida albicans biofilm formation: From cell repellence to fungicidal activity

While there has been significant research conducted on bacterial colonization on implant materials, with a focus on developing surface modifications to prevent the formation of bacterial biofilms, the study of Candida albicans biofilms on implantable materials is still in its infancy, despite its growing relevance in implant-associated infections. C. albicans fungal infections represent a significant clinical concern due to their severity and associated high fatality rate. Pathogenic yeasts account for an increasing proportion of implant-associated infections, since Candida spp. readily form biofilms on medical and dental device surfaces. In addition, these biofilms are highly antifungal-resistant, making it crucial to explore alternative solutions for the prevention of Candida implant-associated infections. One promising approach is to modify the surface properties of the implant, such as the wettability and topography of these substrata, to prevent the initial Candida attachment to the surface. This review summarizes recent research on the effects of surface wettability, roughness, and architecture on Candida spp. attachment to implantable materials. The nanofabrication of material surfaces are highlighted as a potential method for the prevention of Candida spp. attachment and biofilm formation on medical implant materials. Understanding the mechanisms by which Candida spp. attach to surfaces will allow such surfaces to be designed such that the incidence and severity of Candida infections in patients can be significantly reduced. Most importantly, this approach could also substantially reduce the need to use antifungals for the prevention and treatment of these infections, thereby playing a crucial role in minimizing the possibility contributing to instances of antimicrobial resistance. STATEMENT OF SIGNIFICANCE: In this review we provide a systematic analysis of the role that surface characteristics, such as wettability, roughness, topography and architecture, play on the extent of C. albicans cells attachment that will occur on biomaterial surfaces. We show that exploiting bioinspired surfaces could significantly contribute to the prevention of antimicrobial resistance to antifungal and chemical-based preventive measures. By reducing the attachment and growth of C. albicans cells using surface structure approaches, we can decrease the need for antifungals, which are conventionally used to treat such infections.

Adhesion of Candida Albicans to digital versus conventional acrylic resins: a systematic review and meta-analysis

BACKGROUND

The present systematic review and meta-analysis investigated the available evidence about the adherence of Candida Albicans to the digitally-fabricated acrylic resins (both milled and 3D-printed) compared to the conventional heat-polymerized acrylic resins.

METHODS

This study followed the guidelines of the Preferred Reporting Items for Systematic Review and Meta-analyses (PRISMA). A comprehensive search of online databases/search tools (Web of Science, Scopus, PubMed, Ovid, and Google Scholar) was conducted for all relevant studies published up until May 29, 2023. Only in-vitro studies comparing the adherence of Candida albicans to the digital and conventional acrylic resins were included. The quantitative analyses were performed using RevMan v5.3 software.

RESULTS

Fourteen studies were included, 11 of which were meta-analyzed based on Colony Forming Unit (CFU) and Optical Density (OD) outcome measures. The pooled data revealed significantly lower candida colonization on the milled digitally-fabricated compared to the heat-polymerized conventionally-fabricated acrylic resin materials (MD = - 0.36; 95%CI = - 0.69, - 0.03; P = 0.03 and MD = - 0.04; 95%CI = - 0.06, - 0.01; P = 0.0008; as measured by CFU and OD respectively). However, no differences were found in the adhesion of Candida albicans between the 3D-printed digitally-fabricated compared to the heat-polymerized conventionally-fabricated acrylic resin materials (CFU: P = 0.11, and OD: P = 0.20).

CONCLUSION

The available evidence suggests that candida is less likely to adhere to the milled digitally-fabricated acrylic resins compared to the conventional ones.

Effect of Denture Wearing on Occurrence of Fungal Isolates: An Original Study

The present study aimed to evaluate the effect of denture wearing on the occurrence of fungal isolates in the oral cavity before and after complete denture insertion. Fifty completely edentulous patients were selected. Swab samples were collected intraorally before the fabrication of complete dentures from the palatal mucosal surface and after complete denture fabrication (1 and 7 days after denture insertion). Further, these samples were inoculated and incubated. Results showed that in 48 patients, no isolate of fungus before denture insertion was found. In two subjects, results were false positive (contamination from the environment), and in six patients, there was an increase in growth, but not much significant increase of growth was seen (mild growth of fungus only after denture insertion). One of the major findings of this study was that the overall occurrence of fungal isolates (before and after denture insertion) in the oral cavity was not significant.

Cryptocarya moschata extract decreases single and mixed biofilms on acrylic resins

OBJECTIVE

This study proposed to assess the effect of Cryptocarya moschata extract on single and mixed biofilms formed on denture base and reline acrylic resin.

MATERIALS AND METHODS

Single and mixed biofilms of Candida albicans and Streptococcus mutans were formed on the samples and treated with C. moschata extract; Nystatin solution at 100,000 IU/mL or Penicillin antibiotic solution at 100,000 IU/mL; or PBS solution. Antimicrobial activity was analyzed by counting colony-forming units, metabolism assay, assessment of protein components of the biofilm matrix, and of cell viability using confocal laser scanning microscopy (CLSM). Data were submitted to ANOVA and Tukey's post-test (α = 0.05).

RESULTS

Cryptocarya moschata extract reduced cell viability of C. albicans and S. mutans single and mixed biofilms formed on samples. For all types of biofilms in the C. moschata group, there was a log reduction of the biofilm, proven by the Alamar Blue assay. Analyzing the extracellular matrix protein components, groups treated with the extract exhibited a lower level of fluorescence compared to the PBS groups. Reduction in thickness biofilm and viable cells was perceptible in the C. moschata group when assessing through CLSM.

CONCLUSION

Cryptocarya moschata extract reduced the single and mixed biofilms of C. albicans and S. mutans on acrylic resins.

Effects of disinfection with a vinegar-hydrogen peroxide mixture on the surface characteristics of denture acrylic resins

OBJECTIVE

This study aimed to investigate changes in the surface characteristics of two denture resins when disinfected with a vinegar-hydrogen peroxide (VHP) mixture.

MATERIALS AND METHODS

Microwave-polymerized or 3D printed acrylic resin disks were immersed for 900 min (simulating 90 daily uses) in the following solutions (N = 10): water; 0.5% sodium hypochlorite; hydrogen peroxide and water dilution (1:1 ratio); vinegar and water dilution (1:1 ratio); and VHP mixture. Surface roughness, Knoop microhardness, surface free energy, and scanning electron microscopic images were assessed before and after the immersions. Results were compared using the 2-way ANOVA for repeated measures and Tukey test, at 5% significance.

RESULTS

Surface roughness and microhardness did not differ (P > .05) among the solutions and times. Surface free energy and its dispersive component increased (P < .05) for all solutions. All solutions, except for water and VHP mixture, degraded microtopography.

CONCLUSIONS

The VHP mixture was not deleterious to conventional and 3D-printed resin surfaces.

CLINICAL RELEVANCE

Conventional and 3D printed resin dentures can be disinfected with a VHP mixture in a 1:1 ratio because this mixture does not substantially affect the surface characteristics after 90 daily immersions. On the contrary, sodium hypochlorite, hydrogen peroxide, and vinegar solutions, even in low concentrations, should be used with caution for denture disinfection because they may alter the resin microtopography over time.

Antifungal effects of eugenol on Candida albicans adherence to denture polymers

Background

The study's objective is to assess the adherence of C. albicans in different types of denture polymers and the effectiveness of eugenol and commercialized denture cleansers in the removal of C. albicans. Three types of denture base polymers (Lucitone® 199 (High-Impact PMMA), Impact® (conventional PMMA) and Eclipse® (UDMA)) and two hard denture reline materials (Kooliner® and Tokuyama® Rebase II Fast) were used in this study.

Methods

Three hundred samples were prepared (6 × 2 mm disc shape) and divided into five groups of denture polymers (n = 60) and further subjected into five treatment groups (Polident®, Steradent, distilled water, eugenol 5-minutes, and eugenol 10-min). Three samples were extracted from each treatment group for baseline data (n = 12). Baseline data were used to calculate the initial number of C. albicans adherence. A 0.5 ml immersion solution from each specimen was cultured on YPD agar and incubated for 48 h at 37 °C. Visible colonies were counted using a colony counter machine (ROCKER Galaxy 230).

Results

The result showed that the denture base polymer significantly affected the initial adherence (p = 0.007). The removal of C. albicans was also considerably affected by the denture base polymers and denture cleansers (p < 0.05). Lucitone®, Tokuyama®, and Kooliner® denture base polymers immersed for 3 min in eugenol showed the best results of removal.

Discussion

This study's overall results showed that all denture polymers used as denture bases had an effect on C. albicans initial adherence and removal from the denture base, and eugenol is comparable to commercialised denture cleansers in reducing the number of attached C. albicans on denture base polymers.

Antifungal Efficacy of Ocimum Basilicum Essential Oil in Tissue Conditioner Against Candida Albicans: An In vitro Study

Tissue conditioner is used to condition inflamed mucosa induced by denture stomatitis. However, the drawback of the aging tissue conditioner is increased surface roughness, thus enhance microbial adhesion. Ocimum basilicum is known for its antimicrobial effects but its use in liners has not been investigated. Aims: This study aimed to determine the antifungal efficacy of ocimum basilicum essential oil (OBEO) when incorporated into tissue conditioner against C. albicans and the effect on the properties.

Subject and Methods

The antimicrobial activities were determined using disc diffusion, minimum inhibitory concentration (MIC) and minimum fungicidal concentration (MFC). After incorporation into tissue conditioner, the color difference and surface roughness were evaluated after one day. The surface morphology and the antibiofilm activity were assessed on day 1 and day 14.

Results

The zone of inhibition of OBEO on Sabouraud Dextrose agar was significantly wider than nystatin and deionized water (P=0.000) with the MIC and MFC values were 1.25% and 5%. Both OBEO concentrations incorporated into tissue conditioner, there was no significant difference of color changes in the light-dark character (P=0.102) and surface roughness (P=0.920) when compared to the control group. As for adherence at days 1 and 14, both concentrations of OBEO in tissue conditioner show significantly reduced adherence of C. albicans compared to the control group (P=0.000).

Conclusion

OBEO exhibited significantly better antifungal activity against C. albicans when compared to nystatin and deionized water and resulted in no significant color changes, better surface roughness and lesser adherence of C. albicans toward the tissue conditioner.

Effect of Effervescent Denture Cleansers on 3D Surface Roughness of Conventional Heat Polymerized, Subtractively, and Additively Manufactured Denture Base Resins: An In Vitro Study

PURPOSE

To compare the change in surface roughness of denture bases fabricated using three different techniques (additive manufacturing, subtractive manufacturing, and conventional heat-polymerizing) when immersed in two commonly available denture cleansers.

MATERIALS AND METHODS

One hundred and seventeen disc-shaped denture base specimens (39/group), were fabricated by subtractive manufacturing (Wieland), additive manufacturing (NextDent Denture 3D+), and conventional heat-polymerizing (Meliodent) techniques, following the manufacturers' instructions. Specimens were randomly divided into 3 groups and immersed in two effervescent denture cleansing solutions and distilled water to simulate 180 days of denture cleansing. A 3D optical noncontact surface profilometer was used to record the surface roughness of the tested denture base materials before and after immersion. Two-way ANOVA, followed by Bonferroni post hoc test, was used to assess the effects of denture cleansers on surface roughness of tested denture base resins.

RESULTS

When immersed in Fixodent and Fittydent effervescent denture cleansing solutions, the highest change in absolute surface roughness (∆Sa, in μm) was observed in additively manufactured denture base material (0.181 ±0.018 and 0.079 ±0.008), followed by heat-polymerized denture base material (0.149 ±0.012 and 0.059 ± 0.011), while subtractively manufactured denture base material showed the least change (0.110 ±0.026 and 0.038 ±0.007), respectively. There was a difference in the extent of change in surface roughness between the denture cleansers. The change in surface roughness was much higher with the Fixodent denture cleanser as compared to the Fittydent denture cleanser.

CONCLUSION

Subtractively manufactured denture base resin displayed the lowest change while additively manufactured denture base resin displayed the highest change in surface roughness in both denture cleansers, but the extent of change in surface roughness was variable.

Efficacy of Denture Cleansers on Microbial Adherence and Surface Topography of Conventional and CAD/CAM-Processed Denture Base Resins

This study assessed the efficacy of five denture cleansers on the microbial adherence and surface topography of conventional and CAD/CAM denture base resins. Acrylic resin discs were fabricated using conventional, milling, and 3D printing methods (N = 180). The discs were contaminated with dual species of Candida albicans and Streptococcus mutans biofilm for 72 h and then disinfected with either of the denture cleansers (Fittydent cleansing tablets, 2% Chlorhexidine gluconate, 0.2% Chlorhexidine gluconate, 0.5% sodium hypochlorite, and 1% sodium hypochlorite (n = 10). Distilled water served as the control group. The colony-forming units of the microorganisms were calculated, followed by post-treatment surface roughness. Data were statistically analyzed using one-way ANOVA, paired t-test, and post hoc Tukey HSD test (α = 0.05). Among the denture cleansers, 2% Chlorhexidine gluconate, 0.5% sodium hypochlorite, and 1% sodium hypochlorite had the best cleansing effect on the resin discs and demonstrated zero growth of colonies for both the species. Comparing the material groups, the 3D-processed discs showed higher colony-forming units followed by the conventional and CAD/CAM milled group. The highest surface roughness was demonstrated by the 3D-printed discs (0.690 ± 0.08 μm), followed by the conventional (0.493 ± 0.11 μm) and the milled groups (0.301 ± 0.08 μm). The tested chemical denture cleansers affected the Candida albicans and Streptococcus mutans adhesion compared to control discs immersed in distilled water. The clinician may recommend to their patient to use 2% chlorhexidine gluconate for the disinfection of CAD/CAM PMMA denture base materials.

Determining growth inhibition of Candida albicans biofilm on denture materials after application of an organoselenium-containing dental sealant

STATEMENT OF PROBLEM

Denture stomatitis is a chronic inflammatory condition caused by the formation of Candida albicans biofilm on denture bases. It is associated with aggravating intraoral pain, itching, and burning sensations. It can also potentiate cardiovascular diseases and aspiration pneumonia. The problem has thus far eluded efficient, toxic-free, and cost-effective solutions.

PURPOSE

The purpose of this in vitro study was to investigate the effectiveness of organoselenium to inhibit the formation of C. albicans biofilm on the surface of acrylic resin denture base materials when it is either incorporated into the acrylic resin material or coated on the denture surface as a light-polymerized surface sealant.

MATERIAL AND METHODS

Sixty heat-polymerized polymethyl methacrylate disks were fabricated and assigned to 4 groups (n=15): disks coated with a light-polymerized organoselenium-containing enamel surface sealant (DenteShield), disks impregnated with 0.5% organoselenium (0.5% selenium), disks impregnated with 1% organoselenium (1% selenium), and disks without organoselenium (control). C. albicans biofilm was grown on each disk which had been placed in a well of the microtiter plate containing 1-mL brain heart infusion broth inoculated with C. albicans. The plates were incubated aerobically at 37 °C for 48 hours. A confocal laser scanning microscope was used to determine the biofilm thickness, biomass, and live/dead cell ratio. Biofilm morphology was examined with scanning electron microscopy, whereas microbial viability was quantified by the spread plate method. The data were analyzed by using ANOVA and Tukey-Kramer multiple comparisons (α=.05).

RESULTS

The microbial viability, biofilm thickness, biofilm biomass, and live/dead cell ratio were lower (P<.001) on disks in the test groups (DenteShield, 0.5% selenium, 1% selenium) when compared with the control group, with these variables being lowest in the 0.5% selenium and 1% selenium groups. The 0.5% selenium and 1% selenium groups did not differ significantly from each other in any of the variables (P>.05). Scanning electron microscope images showed inhibition of both biofilm growth and yeast to hyphae transition in the DenteShield, 0.5% selenium, and 1% selenium groups, with visible disruption of the biofilm morphology.

CONCLUSIONS

The present study demonstrated that organoselenium, whether incorporated into or coated on the surface of an acrylic resin denture base material, has the potential to inhibit Candida albicans biofilm growth on denture surfaces and as such can be clinically useful for the prevention of denture stomatitis.

Effect of cigarette smoke and denture cleansers on the surface properties and color stability of CAD-CAM and conventional denture base resins

This study aimed to evaluate the hardness, roughness, and color stability of heat- and microwave-polymerized polymethyl methacrylate (PMMA), polyamide, and CAD-CAM PMMA resins when exposed to cigarette smoke (CS) and immersed in a denture cleanser (DC). Specimens of each resins were divided into four subgroups (n=10). The DC and CS+DC specimens were immersed in a DC; the CS and CS+DC specimens were exposed to CS; and the control (C) specimens were kept in distilled water. Hardness, roughness, and color measurements were performed. DC and CS significantly affected the roughness and color of all resins (p<0.05). However, these did not affect the hardness of the CAD-CAM PMMA resin (p>0.05). The CAD-CAM PMMA resin presented the lowest roughness, highest hardness, and lowest ΔE₀₀ values. While the roughness of all resins exposed to CS when immersed in DC decreased, the ΔE₀₀ values of the conventional PMMAs also decreased. Although this decreases were not significant, it may be advisable to use DC for smokers to decrease discoloration and roughness especially for conventional PMMAs resins.

Changes in the Surface Texture of Thermoplastic (Monomer-Free) Dental Materials Due to Some Minor Alterations in the Laboratory Protocol-Preliminary Study

Contemporary thermoplastic monomer-free prosthetic materials are widely used nowadays, and there are a great variety available on the market. These materials are of interest in terms of the improvement of the quality features of the removable dentures. The aim of this study is to establish how minimal changes in the laboratory protocol of polyamide prosthetic base materials influence the surface texture. Two polyamide materials intended for the fabrication of removable dentures bases were used-Perflex Biosens (BS) and VertexTM ThermoSens (TS). A total number of 20 coin-shaped samples were prepared. They were injected under two different modes-regular, as provided by the manufacturer, and modified, proposed by the authors of this study. Scanning electronic microscopy (SEM) under four magnifications-×1000, ×3000, ×5000, and ×10,000-was conducted. With minimal alterations to the melting temperature (5 °C) and the pressure (0.5 Bar), in Biosens, no changes in terms of surface improvement were found, whereas in ThermoSens, the surface roughness of the material significantly changed in terms of roughness reduction. By modifying the technological mode during injection molding, a smoother surface was achieved in one of the studied materials.

Adherence Of Candida Albicans to Five Long-Term Silicone-Based Denture Lining Materials Bonded to CAD-CAM Denture Base

PURPOSE

Knowledge about quantifying the number as well as the retention and adhesion of Candida albicans blastoconidia to silicone denture liners is limited. Thus, the aim of this in vitro study was to explore the adherence of Candida albicans to the surface of five long-term silicone-based soft denture lining materials, using artificial saliva.

MATERIALS & METHODS

A total of 50 specimens (10 × 10 × 3 mm) of five long-term resilient liners (Molloplast-B; GC Reline Soft; Elite Soft Relining; Tokuyama Sofreliner S; Ufigel SC), bonded to a computer-aided design and computer-aided manufacturing denture base, were prepared. The specimens were inoculated and incubated in artificial saliva for 1h and 24h with a standardized (2.8 × 10⁶ cfu/ml) Candida albicans suspension. At the end of the incubation period, the specimens were stained with acridine orange and observed, using fluorescence microscopy.

RESULTS

After 1h and in 24h, Molloplast B demonstrated significantly earlier adherence of Candida albicans cells compared to the other chairside materials (p<0.001 and p<0.001, respectively), where the mean number of cells also increased in the frontal parts. Regarding the rate of Candida albicans proliferation from 1h to 24 hours within the materials, there was an increase in all materials (Molloplast B: p<0.001; GC Reline Soft: p = 0.220; Elite Soft Relining: p = 0.032; Tokuyama Sofreliner S: p = 0.001; Ufigel Sc: p = 0.001). The Ufigel Sc showed a significant 2.5-fold increase at 24h.

CONCLUSIONS

Long-term silicone denture liners accumulate a significant amount of Candida albicans blastoconidia and their coverage by them increases progressively over time. This article is protected by copyright. All rights reserved.

The denture microbiome in health and disease: an exploration of a unique community

The United Nations suggests the global population of denture wearers (an artificial device that acts as a replacement for teeth) is likely to rise significantly by the year 2050. Dentures become colonized by microbial biofilms, the composition of which is influenced by complex factors such as patient’s age and health, and the nature of the denture material. Since colonization (and subsequent biofilm formation) by some micro‐organisms can significantly impact the health of the denture wearer, the study of denture microbiology has long been of interest to researchers. The specific local and systemic health risks of denture plaque are different from those of dental plaque, particularly with respect to the presence of the opportunist pathogen Candida albicans and various other nonoral opportunists. Here, we reflect on advancements in our understanding of the relationship between micro‐organisms, dentures, and the host, and highlight how our growing knowledge of the microbiome, biofilms, and novel antimicrobial technologies may better inform diagnosis, treatment, and prevention of denture‐associated infections, thereby enhancing the quality and longevity of denture wearers.

Impact of Surface Changes and Microbial Adhesion on Mucosal Surface Finishing of Resin Denture Bases by Shot Blast Polishing Using Viscoelastic Media

Surface changes and microbiological effects following shot blast polishing with viscoelastic media of the mucosal surface of resin denture bases were examined. Average surface roughness (Ra) and the depth of surface removal of specimens were measured over time, and the clinical number of microbial adhesions on the mucosal surface of dentures was clinically assessed. The results obtained showed no changes in Ra after 20 s of polishing, Ra of <0.2 µm, and a depth of surface removal < 20 µm. This method of finishing did not affect the fit of the mucosal surface of the dentures. Furthermore, the adhesion of microorganisms to the mucosal surface of dentures was significantly suppressed. Shot blast polishing with viscoelastic media is useful for finishing the mucosal surface of resin denture bases.

The Effects of Incorporating Ag-Zn Zeolite on the Surface Roughness and Hardness of Heat and Cold Cure Acrylic Resins

One of the most widely used materials for the fabrication of prosthetic dental parts is acrylic resin. Its reasonable mechanical and physical properties make it a popular material for a wide range of dental applications. Recently, many attempts have been made to improve the mechanical and biological properties of this material, such as by adding fibres, nanoparticles, and nanotubes. The current study aimed to evaluate the effects of adding an antimicrobial agent, Ag-Zn zeolite, on the surface roughness and hardness of the denture base resins. Ag-Zn zeolite particles were chemically prepared and added at different concentrations (0.50 wt.% and 0.75 wt.%) to the heat cure (HC) and cold cure (CC) acrylic resins. Zeolite particles were characterized and confirmed using X-ray diffraction (XRD) and Energy-Dispersive X-ray Spectroscopy (EDX) attached with a Scanning Electron Microscope (SEM). Sixty disk shape specimens (40 mm diameter and 2 mm thickness) were fabricated from the HC and CC resins with and without the zeolite. All the specimens were divided into two main groups based on the acrylic resins, then each was subdivided into three groups (n = 10) according to the concentration of the Ag-Zn zeolite. A surface roughness and a hardness tester were used to measure the surface finish and hardness of the specimens. The analysed data showed that the surface roughness values significantly decreased when 0.50 wt.% and 0.75 wt.% zeolite were incorporated in the HC resin specimens compared to the control group. However, this reduction was not significant in the case of CC resin, while the surface hardness was significantly improved after incorporating 0.50 wt.% and 0.75 wt.% zeolite for both the CC and HC resins. Incorporating Ag-Zn zeolite with acrylic resin materials could be beneficial for improving their surface finish and resistance to surface damage as defined by the higher hardness.

Hydrophobicity of denture base resins: A systematic review and meta-analysis

Objectives:

The aim of this article is to review the factors that attract Candida albicans to denture base resin (DBR) and to verify the influence of different surface treatments, chemical modification, or structural reinforcements on the properties of DBR.

Materials and Methods:

Searches were carried out in PubMed, Scopus, WOS, Google Scholar, EMBASE, and J-stage databases. The search included articles between 1999 and 2020. This study followed the Preferred Reporting Items for Systematic Reviews and Meta-Analyses statement. The keywords used during the search were “Candida albicans,” “Denture base,” “PMMA,” “Acrylic resin,” “Surface properties,” “hydrophobicity/hydrophilicity,” “contact angle,” and “surface free energy.” English full-text articles involving in-vitro studies with different acrylic resin modifications were included, whereas abstracts, dissertations, reviews, and articles in languages other than English were excluded. A meta-analysis was performed where appropriate.

Results:

Out of the 287 articles, 21 articles conformed to inclusion criteria. Sixteen articles were subjected to meta-analysis using random-effects model at 95% confidence interval. Results showed that DBR coatings/plasma coatings were effective methods to modify surface properties with estimated contact angle (CA) of 59.37° [95% confidence interval (CI): 53.69, 65.04]/55.87° (95% CI: 50.68, 61.06) and surface roughness (R_a) of 0.55 µm (95% CI: 0.52, 0.58)/0.549 µm (95% CI: 0.5, 0.59), respectively. Antifungal particle incorporation into poly(methylmethacrylate) DBR also produced similar effects with an estimated R_a of 0.16 µm (95% CI: 0.134, 0.187).

Conclusion:

The three properties responsible for C. albicans adhesion to DBR were R_a, CA, and surface free energy in terms of hydrophobicity. Therefore, the correlations between the hydrophobicity of DBR and C. albicans adhesion should be considered during future investigations for Candida-related denture stomatitis.

The Influence of Decontamination Procedures on the Surface of Two Polymeric Liners Used in Prosthodontics

Polymeric liners are materials commonly used in prosthodontics to reshape denture surfaces contacting the soft tissues of the oral cavity. The aim of the study was to determine the impact of different cleaning methods on two polymeric materials used in prosthodontics as non-adhesive permanent liners. The material for the research consisted of samples made from Mollosil Plus (Detax, Ettlingen, Germany)-direct polysiloxan liner; and Plastitanium (Pressing Dental, San Marino, Republic of San Marino)-an injection-molded liner. A total of 198 samples were made, 99 of each assessed material. They were exposed to different cleaning methods-a toothbrush, a toothbrush and soap, a toothbrush and toothpaste (BlendaMed, Procter&Gamble, Cincinnati, OH, USA), a toothpaste and denture cleaning paste (Protefix Hygiene Denture Paste, Queisser Pharma, Germany), denture cleansing tablets (Protefix Hygiene Cleaning Tablets, Queisse Pharma, Germany), and a disinfecting spray (Aftermat, Port Jefferson Station, New York City, NY, USA)-for 1 min, 5 min, 10 min, and 15 min. The image acquisition was performed with scanning electron microscopy and samples were analyzed for the homogeneity of their surfaces-the presence of holes, grooves, precipitate, and small and large separating pieces of the material marking departures from this homogeneity. For each type of damage, one point was given. Continuous data from two groups were compared with Mann-Whitney U testing. Due to a small sample size and distribution of variables other than normal, to compare more than two groups, Kruskal-Wallis testing with post hoc analysis (Dunn test with Bonferroni correction) was used. Categorical data were compared with the chi-square test and the Fisher's exact test. The Mollosil Plus material should be decontaminated with the use of a toothbrush or toothbrush with soap, while Plastitanium material should be disinfected. Plastitanium samples are more susceptible to damage during the decontamination procedures than Mollosil Plus.

Promoting Candida zemplinina adhesion on oak chips: A strategy to enhance esters and glycerol content of Montepulciano d'Abruzzo organic wines

In this study cell surface hydrophobicity and the ability to adhere on abiotic surfaces (polystyrene plates, stainless steel and oak chips) of 10 Candida zemplinina strains were assessed. Moreover, the impact of C. zemplinina cells adhered on oak surface on fermentation kinetics and volatile profile of Montepulciano d'Abruzzo organic wines was evaluated. All strains showed a hydrophobic nature with a certain affinity for the apolar solvents tested (hexadecane and decane). In agreement with this data strains were able to adhere on abiotic surfaces in a strain dependent way. On polystyrene plates all strains mainly grew as planktonic cells. On stainless steel surfaces sessile cells ranged from 2.6 Log CFU/mL (SB2) to 4.1 Log CFU/mL (SB8), while on oak chips were about 2 log higher ranging from 4.3 Log CFU/mL (SB8) to 6.1 Log CFU/mL (SB10). Candida zemplinina sessile state resulted in an increase of glycerol (from 6.98 g/L to 11.92 g/L) and esters amount (from 55.47 g/L to 91.5 mg/L), and a reduction of ethanol content (from 14.13% to 9.12% v/v). As for esters, methyl vanillate, ethyl isobutyrate, and ethyl isovalerate were present only when C. zemplinina was adhered on oak chips. This study revealed that changes of concentrations in esters and glycerol content reflected the fermentation bioactivity of yeast cells attached on oak chips. Surface-adhered behaviours should be considered in the improvement of strategies for the development of high-quality organic wines and eventually obtain novel wine styles.

Use of Photosensitizer, Glutaraldehyde, alcohol and Ultrasonics in disinfection of polished and rough surfaces of self-curing polymethyl methacrylate denture base material

AIM

To assess the effectiveness of chemical, ultrasonic and photodynamic therapy (PDT) mediated disinfection against in-vitro biofilms colonized with C. albicans, S. oralis, and S. aureus on surfaces of PMMA (polymethylmethacrylate) denture base material.

MATERIALS AND METHODS

Fifty plates of PMMA were prepared with two different surface topography (rough and polished) analyzed by profilometry. Provenance culture (ATCC) of C. albicans, S. oralis, and S. aureus were inoculated on specimens and exposed to disinfection. The disinfection included Rosebengal (RB) 5 μM activated by a red LED, 2% glutaraldehyde, 70% Isopropyl alcohol, ultrasonic disinfection, and saline solution as a control. The antimicrobial efficacy was assessed by subsequently calculating viable counts after disinfection. The data were analyzed using analysis of variance (ANOVA) and Tukey's Post Hoc test.

RESULTS

The unpolished surface demonstrated the highest average surface roughness As 5.32±0.36 (μm) and root mean square roughness Rr 7.22±0.81 (μm) compared to the polished surface. Intergroup comparison demonstrated polished and rough PMMA plate disinfected with rose bengal, glutaraldehyde and alcohol-based disinfection exhibited comparable reduction against C. albicans and S. oralis CFU/mL (log10) (p>0.05). Whereas, this reduction was significantly higher on the rough and polished surface of PMMA when disinfected using ultrasounds for 30 sec (p<0.05). Rose Bengal was the most effective method of disinfection against S. aureus both on polished (0.17±0.13) and rough (0.44±0.22) denture plates (p<0.05).

CONCLUSION

The ultrasonic disinfection was most effective in reducing viable microbial counts. RB mediated PDT exhibited a more substantial reduction of the colonies of S.aureus.

Antifungal Activity of Denture Base Resin Containing Nanozirconia: In Vitro Assessment of Candida albicans Biofilm

Objective

To evaluate the antimicrobial effects of different concentrations of zirconium dioxide nanoparticles (nano-ZrO₂) reinforcement of poly(methyl) methacrylate (PMMA) on surface roughness and C. albicans biofilm.

Methods

20 heat-polymerized acrylic resin discs were conventionally made and divided into 4 groups (n = 5) according to nano-ZrO₂ concentration: control (0% filler) and 3 experimental groups (2.5% (Z2.5), 5.0% (Z5.0), and 7.5% (Z7.5)). An optical profilometer was used for surface roughness evaluation, followed by Candida adherence assay. Specimens were sterilized, then immersed in cultured yeast (C. albicans), and incubated at 37°C for 48 hours. After that, discs were rinsed before extracting the clustered pellets of Candida. The attached C. albicans was counted using the direct method after spreading on agar media and incubating for 48 hours. Statistical analysis was performed using one-way ANOVA and Tukey's post hoc test at α = 0.05.

Results

Surface roughness was significantly increased with all modified groups compared with control (P < 0.01), which showed the lowest roughness value (0.027 ± 0.004 μm). There was no significant difference in the roughness value among reinforced groups (2.5, 5.0, and 7.5%) (P > 0.05), with Z7.5 showing the highest roughness value (0.042 ± 0.004 μm). Candida count was reduced as the nano-ZrO₂ increased but not significantly (P=0.15).

Conclusions

The addition of different concentrations of nano-ZrO₂ particles to PMMA increased the surface roughness compared with control; in contrast, insignificant reduction of C. albicans biofilm was detected.

Ultraviolet C as a method of disinfecting medical silicone used in facial prostheses: An in vitro study

STATEMENT OF PROBLEM

Hygiene and disinfection are important factors for preserving facial prostheses and supporting tissue health. However, a method that does not accelerate degradation or color change is necessary.

PURPOSE

The purpose of this in vitro study was to evaluate the effectiveness of irradiation with ultraviolet C light-emitting diode (UV-C LED) light in the disinfection and initial color stability of the silicone (A-588-1; Factor II) used in facial prostheses.

MATERIAL AND METHODS

One hundred and twenty specimens were made, contaminated by multispecies biofilm, and divided into 5 groups (n = 24) with different treatments: control, distilled water, 0.12% chlorhexidine, UV-C LED light, and dimethyl sulfoxide (DMSO) as the negative control. Cell viability was measured by the methyl tetrazolium salt method. Statistical analysis was performed by generalized linear models. Additional descriptive analysis was performed for color analysis by using 16 silicone specimens made with light and dark intrinsic coloring in 4 groups (controls and treatments n=4) submitted to UV-C LED light. The ΔE of the specimens was obtained by CIEDE200.

RESULTS

The results of cell viability demonstrated a statistically significant difference among the groups (P<.001), with a microbial reduction after UVC-LED exposure compared with the control group. Regarding the color, the groups presented an average ΔE (light 0.205 and dark 0.308) compatible with visually imperceptible changes (light < 0.7 and dark < 1.2).

CONCLUSIONS

Irradiation with UV-C LED light decreased the in vitro microbial cell viability of the medical silicone used in facial prostheses, demonstrating initial color stability.

Surface morphology and in vitro leachability of soft liners modified by the incorporation of antifungals for denture stomatitis treatment

OBJECTIVE

To evaluate the surface morphology and in vitro leachability of temporary soft linings modified by the incorporation of antifungals in minimum inhibitory concentrations (MIC) for Candida albicans biofilm.

METHODOLOGY

Specimens of soft lining materials Softone and Trusoft were made without (control) or with the addition of nystatin (Ny), miconazole (Mc), ketoconazole (Ke), chlorhexidine diacetate (Chx), or itraconazole (It) at their MIC for C. albicans biofilm. The surface analyses were performed using Confocal laser scanning microscopy after 24 h, 7 days, or 14 days of immersion in distilled water at 37ºC. In vitro leachability of Chx or Ny from the modified materials was also measured using Ultraviolet visible spectroscopy for up to 14 days of immersion in distilled water at 37ºC. Data (μg/mL) were submitted to ANOVA 1-factor/Bonferroni (α=0.05).

RESULTS

Softone had a more irregular surface than Trusoft. Morphological changes were noted in both materials with increasing immersion time, particularly, in those containing drugs. Groups containing Chx and It presented extremely porous and irregular surfaces. Both materials had biexponential release kinetics. Softone leached a higher concentration of the antifungals than Trusoft (p=0.004), and chlorhexidine was released at a higher concentration than nystatin (p<0.001).

CONCLUSIONS

The surface of the soft lining materials changed more significantly with the addition of Chx or It. Softone released a higher concentration of drugs than Trusoft did, guiding the future treatment of denture stomatitis.

Effect of a vinegar-hydrogen peroxide mixture on the surface properties of a cobalt-chromium alloy: A possible disinfectant for removable partial dentures

STATEMENT OF PROBLEM

A vinegar-hydrogen peroxide mixture has been reported to be effective in eliminating Candida albicans and Staphylococcus aureus from acrylic resin, and its action has been reported to be comparable with that of sodium hypochlorite or peracetic acid. However, the effects of this mixture on cobalt-chromium alloys remain unknown.

PURPOSE

The purpose of this in vitro study was to evaluate the surface roughness, Knoop microhardness, surface free energy, and wettability of a cobalt-chromium alloy when exposed to a vinegar-hydrogen peroxide mixture.

MATERIAL AND METHODS

Fifty specimens of cobalt-chromium alloy were fabricated and immersed for 900 minutes, simulating 3 months of a daily 10-minute immersion in the following chemical agents (n=10): distilled water (W); 0.5% sodium hypochlorite (H); 3% hydrogen peroxide and water dilution in 1:1 ratio (HP); white-wine vinegar and water dilution in 1:1 ratio (V); and vinegar and hydrogen peroxide mixture in 1:1 ratio (VHP). Surface roughness, Knoop microhardness, surface free energy, and wettability were measured with single blinding before and after immersions. Data were statistically analyzed by using 2-way repeated measures ANOVA (α=.05).

RESULTS

The vinegar-hydrogen peroxide mixture did not affect the surface roughness or Knoop microhardness. However, 0.5% sodium hypochlorite significantly increased the roughness and decreased microhardness. Surface free energy and wettability increased after immersions, regardless of the types of solution.

CONCLUSIONS

Immersion in a vinegar-hydrogen peroxide mixture did not affect the surface characteristics of a cobalt-chromium alloy.

Nanoscale Surface Roughness Influences Candida albicans Biofilm Formation

The microbial contamination of surfaces presents a significant challenge due to the adverse effects associated with biofilm formation, particularly on implantable devices. Here, the attachment and biofilm formation of the opportunistic human pathogen, Candida albicans ATCC 10231, were studied on surfaces with decreasing magnitudes of nanoscale roughness. The nanoscale surface roughness of nonpolished titanium, polished titanium, and glass was characterized according to average surface roughness, skewness, and kurtosis. Nonpolished titanium, polished titanium, and glass possessed average surface roughness (S_a) values of 350, 20, and 2.5 nm; skewness (S_skw) values of 1.0, 4.0, and 1.0; and (S_kur) values of 3.5, 16, and 4, respectively. These unique characteristics of the surface nanoarchitecture were found to play a key role in limiting C. albicans attachment and modulating the functional phenotypic changes associated with biofilm formation. Our results suggest that surfaces with a specific combination of surface topographical parameters could prevent the attachment and biofilm formation of C. albicans. After 7 days, the density of attached C. albicans cells was recorded to be 230, 70, and 220 cells mm^-2 on nonpolished titanium, polished titanium, and glass surfaces, respectively. Despite achieving a very low attachment density, C. albicanscells were only observed to produce hyphae associated with biofilm formation on nonpolished titanium surfaces, possessing the highest degree of surface roughness (S_a = 350 nm). This study provides a more comprehensive picture of the impact of surface architectures on C. albicans attachment, which is beneficial for the design of antifungal surfaces.

How microbes read the map: Effects of implant topography on bacterial adhesion and biofilm formation

Microbes have remarkable capabilities to attach to the surface of implanted medical devices and form biofilms that adversely impact device function and increase the risk of multidrug-resistant infections. The physicochemical properties of biomaterials have long been known to play an important role in biofilm formation. More recently, a series of discoveries in the natural world have stimulated great interest in the use of 3D surface topography to engineer antifouling materials that resist bacterial colonization. There is also increasing evidence that some medical device surface topographies, such as those designed for tissue integration, may unintentionally promote microbial attachment. Despite a number of reviews on surface topography and biofilm control, there is a missing link between how bacteria sense and respond to 3D surface topographies and the rational design of antifouling materials. Motivated by this gap, we present a review of how bacteria interact with surface topographies, and what can be learned from current laboratory studies of microbial adhesion and biofilm formation on specific topographic features and medical devices. We also address specific biocompatibility considerations and discuss how to improve the assessment of the anti-biofilm performance of topographic surfaces. We conclude that 3D surface topography, whether intended or unintended, is an important consideration in the rational design of safe medical devices. Future research on next-generation smart antifouling materials could benefit from a greater focus on translation to real-world applications.

Antagonistic effect of isolated and commercially available probiotics on the growth of Candida albicans on acrylic resin denture surfaces

STATEMENT OF PROBLEM

Biofilms can be retained on dental prostheses leading to the development of infections. The indiscriminate use of antifungal drugs can result in the development of microorganisms that are resistant to these antimicrobial agents. Whether probiotics are a suitable alternative for reducing the prevalence of oral candidiasis is unclear.

PURPOSE

The purpose of this in vitro study was to evaluate the influence of 6 different live strains of probiotics and 2 commercially available probiotic supplements used for inhibiting the growth of Candida albicans biofilm in heat-polymerized acrylic resin denture base material and to determine whether biofilm byproducts modify the surface of specimens.

MATERIAL AND METHODS

Biofilms of C. albicans were formed on acrylic resin specimens in the presence of probiotics and quantified by colony-forming units (CFUs), and the surface roughness (Ra) of the specimens was assessed before and after the formation of biofilms. The CFU and roughness data were analyzed by analysis of variance and the Tukey HSD test (α=.05).

RESULTS

A significant decrease in the number (CFU/mL) of C. albicans cells was found when they were cultured with 4 probiotics: B. lactis (P=.045), B. longum (P<.001), L. casei (P<.001), and L. helveticus (P<.001) and with the commercially available probiotic Prolive (P=.05). The Ra of specimens decreased after exposure to different microbial biofilms (P≤.05) except in 3 experimental groups.

CONCLUSIONS

In general, the tested probiotics had an antagonistic effect on the growth of C. albicans, and the surface of acrylic resin was altered after exposure to biofilm byproducts.

Nanometals in Dentistry: Applications and Toxicological Implications-a Systematic Review

Nanotechnology is a vital part of health care system, including the dentistry. This branch of technology has been incorporated into various fields of dentistry ranging from diagnosis to prevention and treatment. The latter involves application of numerous biomaterials that help in restoration of esthetic and functional dentition. Over the past decade, these materials were modified through the incorporation of metal nanoparticles (NP) like silver (Ag), gold (Au), titanium (Ti), zinc (Zn), copper (Cu), and zirconia (Zr). They enhanced antimicrobial, mechanical, and regenerative properties of these materials. However, lately, the toxicological implications of these nanometal particles have been realized. They were associated with cytotoxicity, genotoxicity altered inflammatory processes, and reticuloendothelial system toxicity. As dental biomaterials containing metal NPs remain functional in oral cavity over prolonged periods, it is important to know their toxicological effects in humans. With this background, the present systematic review is aimed to gain an insight into the plausible applications and toxic implications of nano-metal particles as related to dentistry.

Impact of various finishing and polishing techniques and composite materials on Candida albicans biofilm formation

Candida albicans biofilms are commonly associated with severe oral infections. In dentistry, prosthetic and restorative materials are potential structures for the adhesion of C. albicans facilitating the formation of Candida biofilm and infection. Three composite resins (Charisma Classic, Sonic Fill, Estelite ∑ Quick) and two finishing-polishing systems (Biscover LV, Dental Finishing Disc) were evaluated for Candida biofilm formation. A Candida biofilm assay showed that both the resin and the finishing/polishing procedures affect Candida biofilm formation. Specifically, Candida biofilm formation was significantly lower in Sonic Fill resin than both Charisma Classic and Estelite ∑ Quick (P = .021). The type of finishing and polishing procedure also significantly affected the Candida biofilm formation to composite material (P < .001). Candida biofilm formation was more advanced after Biscover LV procedure than Dental Finishing Disc procedure.

Effects of statherin on the biological properties of titanium metals subjected to different surface modification

The failure of dental implants is usually caused by bacteria infection, poor bioactivity and biocompatibility. It is a common phenomenon clinically. Statherin, a salivary protein, plays a crucial role of mediator between materials and cells/bacteria. However, the conformation of statherin might be changed by the implants in vivo. In this study, we investigated the effects of statherin on the bioactivities, antibacterial abilities and biocompatibilities of the titanium metals and the reaction mechanism. We found that the conformation of statherin was mainly influenced by surface composition, surface structure, surface roughness, surface hydrophilia and Ti-OH groups of materials. Statherin could decrease the cell biocompatibility of the titanium metals including pure titanium (PT), anodic oxidation (AO), sandblasting and etching (SLA) and plasma spraying hydroxyapatite (HA) coating in HGF cell experiments, regulate the bio-mineralization ability of HA coating in SBF, and enhance the antibacterial properties of PT and HA coating. This study revealed that surface properties of materials could change the conformation of statherin, which influenced the bioactivities, antibacterial properties and biocompatibilities of the materials in return.

The accuracy of the prediction models for surface roughness and micro hardness of denture teeth

The paper aimed to compare the performance of artificial neural network (ANN) model with the results of in vitro experiments. For these experiments, maxillary molars of four different denture teeth were subjected to tea, coffee, cola, cherry juice, distilled water. Vickers microhardness and surface roughness values were measured. Subsequently, ANN model for the prediction of microhardness and surface roughness of different denture teeth were examined. A back-propagation ANN has been used to develop a model relating to the amount of microhardness and surface roughness. The independent variables of the model are distilled water, tea, filtered coffee, cola, cherry juice, time and denture teeth. Microhardness and surface roughness were chosen as the dependent variables. According to the results, a neural network architecture having one input layer with ten neurons, two hidden layers with six neurons, one output layer with two neurons and an epoch size of 48 gives better prediction. Prediction models for dental materials could also be supportive for in vitro studies.

Mechanical and Surface Properties of Resilient Denture Liners Modified with Chitosan Salts

Chitosan (CS) and its derivatives show antibacterial and antifungal properties and could help treat and prevent denture stomatitis (DS). Mechanical and surface properties of resilient denture liners were evaluated when modified with CS salts. CS-hydrochloride (CS-HCl) and CS-glutamate (CS-G) were added to resilient denture liners Ufi Gel P and Coe-Soft at four different concentrations (0.1%, 0.2%, 0.4%, 1% w/w) from which specimens were produced, as well as a control group of each material with no added CS salt. Ten specimens per group (Ø 35 mm, height 6 mm) were manufactured. They were stored in distilled water at 37 °C for a total of 30 days (d). Shore A hardness (SHA) and surface roughness (Ra) were evaluated after 24 h (T1), 7 d (T2), 14 d (T3) and 30 d (T4). Kruskal-Wallis and U-test (Bonferroni-Holm adjusted) were used for statistical analysis (p ≤ 0.05). Ra increased significantly once CS salts were added. SHA increased significantly for some groups, but all specimens fulfilled requirements set by ISO 10139-2:2016. Modification with CS salts does not influence the mechanical properties of the modified resilient denture liners in a clinically relevant manner. Despite the increased roughness, the concept is suitable for further studies. Especially antimicrobial/antibiofilm studies are needed.

Nano CuAl2O4 spinel mineral as a novel antibacterial agent for PVDF membrane modification with minimized copper leachability

The employment of copper-containing antibacterial agents for membrane modification can constrain undesirable bacterial adhesion and growth in an effective and economical way. However, copper ion may be leached out and cause further toxicity after applying those materials for membrane processes. Therefore, in this study, nano CuAl₂O₄ spinel was synthesized as a novel copper-containing material which was expected to have good antibacterial activity and simultaneously stabilize copper ions by its intrinsic structure. The obtained nano spinel was applied for membrane modification via both doping and coating methods. Results show that the addition of nano CuAl₂O₄ spinel during doping process can change polyvinylidene fluoride (PVDF) membrane properties (crystallization, tensile strength, porosity, pore size distribution, permeate flux and bovine serum albumin (BSA) rejection) obviously, but no obvious change was observed for the coated membrane except increased hydrophilicity and permeate flux. Most importantly, the amount of bacteria attachment was found to reduce significantly (˜68%) on the membrane coated with nano spinel, which indicates the successful application of nano CuAl₂O₄ spinel as a novel antibacterial agent for membrane modification without extra concern of copper toxicity.

Improving Polymethyl Methacrylate Resin Using a Novel Titanium Dioxide Coating

PURPOSE

The objective of this study was to improve the surface characteristics of poly (methyl methacrylate) (PMMA) by developing a novel, thin film coating process and to characterize the resulting coated surface.

MATERIALS AND METHODS

An atomic layer deposition (ALD) technique was developed to deposit a titanium dioxide (TiO₂ ) nano-thin film on PMMA. The surface wettability for both coated and uncoated PMMA was determined by measuring water contact angle. Wear resistance was assessed using a mechanical tooth-brushing device with a 50 g load for 6000 strokes after 5 months of water storage. A denture cleanser challenge test was performed by using sonication in 3.8% sodium perborate for 1 hour with aged specimens. X-ray photoelectron spectroscopy (XPS) was used before and after the brushing test and challenge test to analyze the PMMA surface chemical composition. The mechanical strength of coated and uncoated PMMA was measured using a three-point bending test. Surface microbial interactions were also evaluated by assessing Candida albicans biofilm attachment.

RESULTS

Nano-TiO₂ coating (30 nm thick) was successfully deposited on PMMA at 65°C. After coating, water contact angle decreased from 70° to less than 5°. After brushing test, the coating remained intact. XPS analysis revealed no loss of TiO₂ from coated specimens following brushing and denture cleanser sonication for 1 hour. There was no statistically significant difference in mechanical strength (MPa) (mean ± SD) between PMMA (139.4 ± 11.3) and TiO₂ -PMMA (160.7 ± 37.1) (p = 0.0995). C. albicans attachment decreased by 63% to 77% on the coated PMMA surface.

CONCLUSIONS

ALD is a promising technique to modify surface properties of PMMA and resulted in a stable adherent thin film. By depositing a TiO₂ coating, PMMA surface properties may lead to significantly reduced microorganism adhesion and easier pathogen removal from PMMA. For patients who wear dentures, reducing the oral microbial biofilm burden using a TiO₂ -coated PMMA surface could positively impact their oral and systemic health.

The antibacterial and anticancer properties of zinc oxide coated iron oxide nanotextured composites

Core-shell α-Fe₂O₃-ZnO structures of different nanotextured morphology were synthesized through wet chemical routes using different solvents like ethanol, ethanolamine, water and acetaldehyde. Morphological tuning using different solvents resulted in the formation of different shapes, such as disc, spindle, rod and sphere (abbreviated as FZ-ND, FZ-NSP, FZ-NR and FZ-NS, respectively). Structural, morphological and compositional characterization of these nanoparticles (NPs) has been carried out. Antibacterial efficacy of the synthesized NPs was checked against Gram negative V. cholerae N16961 (VcN16961) and Gram positive S. aureus bacteria by recording optical density (OD) at different time points. Among the NPs tested, FZ-NSP was found to be the most effective against VcN16961, while FZ-NR showed maximum efficacy against S. aureus, implying the importance of nanotextured surface as well as the morphology in the manifestation of antibacterial activity. The kinetics of growth for both the bacteria has been modelled using logistic approach. Cytotoxicity was evaluated through MTT (3-(4,5-dimethyl-2-thiazolyl)-2,5-diphenyltetrazolium bromide) assay against human breast adenocarcinoma cell line (MCF-7), human hepatocarcinoma cell line (HepG2) and against normal human embryonic kidney cell line (HEK-293). The lesser toxicity of α-Fe₂O₃-ZnO towards HEK-293 and the potent anticancer activity against MCF-7 and HepG2 cells underline its applicability as anticancer agent. With continued improvement of nanotechnology, this study may pave the way for designing and construction of various morphologically diverse, nanotextured materials with desired functional attributes.

The effects of adding various ratios of zirconium oxide nanoparticles to poly(methyl methacrylate) on physical and mechanical properties

The aim of the present study is to evaluate the transverse strength, modulus of elasticity, surface roughness, hardness, and water sorption/solubility of nanoparticle zirconium oxide (nano-ZrO₂) added to heat-cured poly(methyl methacrylate) (PMMA) after thermocycling. The specimens were divided into four groups according to the ratio of nano-ZrO₂ addition to heat-cured PMMA; group 1: 5% nano-ZrO₂; group 2: 10% nano-ZrO₂; group 3: 20% nano-ZrO₂, and group 4 (control): PMMA without nano-ZrO₂. A statistically significant decrease in transverse strength was observed by all additional rates of nano-ZrO₂ compared with group 4 (control; P < 0.025). When hardness results were evaluated, groups 1 and 2 showed statistically higher values compared with groups 3 and 4 (P < 0.025). The surface roughness of group 3 was statistically higher than the other groups (P < 0.025), but it was within the clinically acceptable limits. As the nano-ZrO₂ addition rate increased, water sorption/solubility values of the specimens also increased. Although nano-ZrO₂ addition had an adverse effect on some mechanical and physical properties of heat-cured PMMA, it increased hardness values, implying that the addition of nano-ZrO₂ would contribute positively to some mechanical properties of PMMA denture base material when nano-ZrO₂ was homogeneously distributed in PMMA.

Kinetics of antifungal activity of home-generated ozonated water on Candida albicans

Background and Purpose:

Candida-associated denture stomatitis is one of the most common forms of oral candidiasis among denture wearers. Regarding this, the aim of the present study was to evaluate the antifungal effects of home-generated ozonated water on the adhesion of the C. albicans attached to the surface of the denture base acrylic resins.

Materials and Methods:

For the purpose of the study, different concentrations of C. albicans were added to the tubes containing acrylic resin blocks, and then incubated for 2 h at 35°C. The samples were assigned into three groups, each of which contained 42 samples, including normal saline (NS) solution as the negative control, nystatin (N) solution as the positive control, and ozonated water as the test group. The samples were washed and placed in an ultrasonic bath. Subsequently, the saline solution was cultured on Sabouraud dextrose agar. The concentrations of Candida were evaluated during the contact times.

Results:

The test group (i.e., ozonated water) with 114 colony-forming units (CFU) showed a significant reduction of Candida colonies, compared to the NS group with 2,172 CFU. The 120- and 1-minute incubation with ozonated water showed the highest and lowest effects on the viability of Candida adhered to the acrylic resin, respectively.

Conclusion:

Based on the findings, home-generated ozonated water can be applied to remove the Candida attached to the surface of the denture plates.

Properties of an acrylic resin after immersion in antiseptic soaps: Low-cost, easy-access procedure for the prevention of denture stomatitis

Denture stomatitis triggered by Candida species requires better preventive measures. This study evaluated the physical and biological properties of a denture base acrylic resin after immersion in antiseptic soaps. Acrylic resin specimens were prepared and stored in distinct solutions for 0, 7, 14, 21, and 28 days. The solutions were as follows: DW: distilled water at 37°C (control group); DS: cycles of daily immersion in Dettol soap for 8 hours at room temperature, followed by immersion in distilled water for 16 hours at 37°C; PS: cycles of daily immersion in Protex soap, as described for the previous group; LS: cycles of daily immersion in Lifebuoy soap, as described for the DS group. The parameters evaluated at each time point were the following: biofilm formation capacity by Candida albicans and reduction of preformed fungal biofilms, cytotoxicity, surface roughness, hardness, and color change. For the fungal adhesion phase, the type of soap had a statistically significant effect (p = 0.0292), but after 24 hours, no differences were found between solutions or between storage times. Regarding the efficacy of biofilm reduction, there was a significant difference when the groups were compared to each other (p = 0.014). Dettol and Lifebuoy eliminated the preformed biofilm on the specimens. Moreover, all the soaps were classified as non-cytotoxic (on HaCaT cell line) because there was no difference in cell viability between the different groups, except after 21 days, when a decrease in cell viability occurred, regardless of the type of soap. Regarding the roughness, there was no statistically significant difference (p > 0.05) between the groups. Lifebuoy decreased resin hardness regardless of storage time (p = 0.003). After 21 and 28 days of storage, there was an increase in hardness value, regardless of the type of soap. The specimens’ color, according to the National Bureau of Standards values, ranged from 0.27 to 0.58 (i.e., imperceptible or mild color changes). In general, the disinfectant soaps were not able to prevent biofilm formation, but all the soaps were effective in reducing the preformed biofilm. In addition, all soaps were non-cytotoxic and did not change surface roughness, hardness (except Lifebuoy), and color (except Lifebuoy). Therefore, immersion in two antiseptic soaps (Protex and Dettol) may be a cheap and easy procedure for preventing denture stomatitis.

Impact of surface topography on biofilm formation by Candida albicans

Candida albicans is a fungal pathogen that causes serious biofilm-based infections. Here we have asked whether surface topography may affect C. albicans biofilm formation. We tested biofilm growth of the prototypical wild-type strain SC5314 on a series of polydimethylsiloxane (PDMS) solids. The surfaces were prepared with monolayer coatings of monodisperse spherical silica particles that were fused together into a film using silica menisci. The surface topography was varied by varying the diameter of the silica particles that were used to form the film. Biofilm formation was observed to be a strong function of particle size. In the particle size range 4.0-8.0 μm, there was much more biofilm than in the size range 0.5-2.0 μm. The behavior of a clinical isolate from a clade separate from SC5314, strain p76067, showed results similar to that of SC5314. Our results suggest that topographic coatings may be a promising approach to reduce C. albicans biofilm infections.

Effect of incorporation of surface pre-reacted glass ionomer filler in tissue conditioner on the inhibition of Candida albicans adhesion

We investigated the effects of incorporation of surface pre-reacted glass ionomer (S-PRG) filler in tissue conditioner (TC) on Candida albicans adhesion. We prepared specimens containing 0, 5, 10, or 20 wt% of S-PRG filler, and measured the amount of C. albicans on the surface using a colony forming unit (CFU) assay and scanning electron microscopic images. In addition, we measured the consistency, penetration depth, and surface roughness (Ra). CFU values for 10 and 20 wt% were significantly lower than that for the control (p<0.05). Hyphal density on the surface was greater in the control. The 10 and 20 wt% specimens showed significantly higher consistency and Ra, lower penetration depth ratio than control (p<0.05). These results suggest that incorporation of S-PRG filler may reduce C. albicans adhesion onto TC surface; however, the optimal amount of filler is dictated by the influence of filler incorporation on mechanical and surface characters of TC.

Antifungal Efficacy and the Mechanical Properties of Soft Liners against Candida albicans after the Incorporation of Garlic and Neem: An In vitro Study

Objectives:

To evaluate the in vitro growth inhibition of Candida albicans, in the soft-liner material and Shore A hardness from resin-based denture soft lining materials modified by neem or garlic incorporation.

Materials and Methods:

Resin discs were prepared with poly methyl methacrylate (PMMA) and soft liners incorporated with varying concentrations of neem or garlic. For antifungal activity, resin discs were placed on agar plates inoculated with C. albicans and were evaluated after 2, 4, and 7 days using the streaking method. The hardness of the PMMA was evaluated with the use of Shore A at 2, 4, and 7 days. Data were statistically processed by SPSS software (IBM Company, Chicago, USA) using Kruskal–Wallis test, and post hoc comparisons were done using Dunn's test. P <0.05 was considered statistically significant.

Results:

Neem and garlic added to PMMA soft liner had an inhibitory effect on C. albicans. Both the neem and garlic when added showed positive results against C. albicans when compared to the control group. The soft liner hardness increased statistically by time but not for the different plant extract concentrations.

Conclusions:

Within the limitations of this in vitro study, it was found that neem and garlic can be used as an additive to tissue conditioner to reduce the adherence of C. albicans without significantly affecting the hardness of the heat-polymerized acrylic resin.

Development of antibacterial denture cleaner for brushing containing tea tree and lemongrass essential oils

We evaluated effectiveness of tea tree oil (TO) and lemongrass oil (LO) for removal of Candida biofilm from denture base resin and their influence on that surface. Biofilm of C. albicans was formed on resins, and immersed in various concentrations of each oil and distilled water (DW). The biofilm removal effect was determined by incubating specimens in RPMI medium containing Alamar blue (AB) and measuring absorbance. Wear test was also conducted, and surface condition of resins was determined using laser scanning microscope and digital microscope. Specimens immersed in the TO and LO solutions tended to have a lower AB value at higher concentrations and longer soaking times. Use of these agents resulted in less surface roughness as compared to DW. Our results suggest that TO and LO were valid to remove biofilm attached to resin with lower levels of abrasion, and these are effective for use in denture cleaner.

Superficial and Inner Examination of a Microwave-Irradiated Dental Acrylic Resin and Its Metal-Polymer Interface

The aim of this study is to conduct an extended surface and cross-section characterization of a denture base acrylic resin subjected to 500, 650, and 750 W microwave irradiation for 2, 3, and 5 min to assess its morphological modifications. A commercial heat-cured powder was polymerized according to the manufacturer's specifications and distributed into 20 circular samples. A stainless-steel wire was partially embedded in half of the discs, in order to investigate the metal-polymer interface. High-resolution scanning electron microscopy (SEM) imaging, white light interferometry, roughness measurements and Fourier transform infrared spectrometry were employed for morphological and structural evaluation of the irradiated polymer. Superficial adaptation was discovered after 5 min exposure at 500 W, 650 W, and 750 W, revealing significant roughness correction for 750 W. SEM characterization revealed the inner alteration of the resin for the 750 W protocol and a metal-polymer gap developed regardless of the irradiation conditions. The considerable temperature fluctuations that the samples were subject to during the experiments did not essentially change the poly(methyl-methacrylate) bond structure.

Effect of Monopoly-coating Agent on the Surface Roughness of a Tissue Conditioner Subjected to Cleansing and Disinfection: A Contact Profilometric In vitro Study

Introduction

Tissue conditioners are used to improve the health of the soft tissues of denture-bearing areas. However, leaching of plasticizers from tissue conditioners results in deterioration, which necessitates frequent replacement. The life of these liners varies, but it can be extended by the use of a coating material.

Aim

To evaluate the surface roughness of a tissue conditioner with monopoly coating, subjected to denture cleanser and disinfectant.

Materials and Methods

Sixty disk-shaped specimens of Visco-gel were made and divided into six groups of 10 each (control 1 [C1], control 2 [C2], control 3 [C3], group 1 [M1], group 2 [M2], and group 3 [M3]). Specimens of the control group were not coated with monopoly, while the specimens of the groups 1, 2, and 3 were coated with monopoly. Specimens of C1 and M1 were immersed in distilled water. Specimens of C2, C3, M2, and M3 were immersed into solution of denture cleanser for 8 h at room temperature and immersed in distilled water for the remainder of the 24-h period. C3 and M3 specimens were treated with disinfectant for 10 min before testing the surface roughness. The surface roughness was measured on 1^st, 3^rd, 5^th, 7^th, and 14^th day, using a contact profilometer. Student's paired t-test was used to compare the mean Ra values within each group. In the present study, P < 0.05 was considered as the level of significance.

Results

The mean surface roughness values of M1, M2, and M3 groups were less than C1, C2, and C3, respectively. Among all the groups, M1 showed the least surface roughness values.

Conclusion

Monopoly-coating agent prevents the deterioration and reduces the surface roughness of the tissue conditioner.