Injectable and Sprayable Polyphenol-Based Hydrogels for Controlling Hemostasis

Multifunctional sprayable carboxymethyl chitosan/polyphenol hydrogel for wound healing

The use of facile methods to synthesize environmentally friendly and multifunctional hydrogel dressings is still a major challenge in development. Herein, Turkish gall extract (TGE) and carboxymethyl chitosan (CMCS) were combined and sprayed using a dual syringe to form a multifunctional TGE-CMCS hydrogel (TC gel) in one step through abundant hydrogen bonding between functional groups as a green approach. TC gel showed rapid gelation at 19.0 ± 2.9 s. Apart from the advantage of being able to adapt to different wound shapes, TC gel retained the antioxidant, antibacterial, hemostatic and anti-inflammatory properties of TGE. In vitro antibacterial experiments showed that TC-gel eliminated 98.27 ± 0.79 % of Staphylococcus aureus and 98.87 ± 1.08 % of Escherichia coli. Compared with TGE or CMCS alone, TC gel accelerates skin wound healing due to its three-dimensional network structure and continuous release of active components at the wound site, enhancing re-epithelialization, improving collagen deposition, and increasing angiogenesis. The wound healing rate of full-thickness skin defect rats treated with TC gel was 93.98 ± 0.63 % on the 10th day. These results suggest that TC gel combined with a facile and scalable manufacturing method is a promising multifunctional wound dressing for clinical wound management.

Fabrication and hemostasis evaluation of a carboxymethyl chitosan/sodium alginate/Resina Draconis composite sponge

Hemostasis is the first step of emergency medical treatment. It is particularly important to develop rapid-acting and efficacious hemostatic materials. Carboxymethyl chitosan (CMCS), sodium alginate (SA) and Resina Draconis (RD) were composited uniformly by polyelectrolyte blending. Their composite sponges (CMCS/SA/RD) were prepared by freeze-induced phase separation. CMCS/SA/RD sponges were characterized by Fourier transform infrared spectroscopy and scanning electron microscopy, and their blood absorption and hemolysis ratio were analyzed. The hemostatic effect of the composite sponges was evaluated by coagulation in vitro and in vivo. The composite sponges had a porous network structure. The water absorption ratio was >8000 %, and hemolysis ratio was <5 %. CMCS/SA/RD-II and CMCS/SA/RD-III composite sponges shortened the coagulation time in vitro by 11.33 s and 9.66 s, the hepatic hemostasis time by 13.8 % and 23.3 %, and the hemostasis time after mouse-tail amputation by 28.9 % and 23.9 %, respectively. A preliminary study on its coagulation mechanism showed that CMCS/SA/RD had significant effects on erythrocyte adsorption, platelet adhesion, and shortening of the activated partial thromboplastin time.

Enhancing regenerative medicine with self-healing hydrogels: A solution for tissue repair and advanced cyborganic healthcare devices

Considering the global burden related to tissue and organ injuries or failures, self-healing hydrogels may be an attractive therapeutic alternative for the future. Self-healing hydrogels are highly hydrated 3D structures with the ability to self-heal after breaking, this property is attributable to a variety of dynamic non-covalent and covalent bonds that are able to re-linking within the matrix. Self-healing ability specially benefits minimal invasive medical treatments with cell-delivery support. Moreover, those tissue-engineered self-healing hydrogels network have demonstrated effectiveness for myriad purposes; for instance, they could act as delivery-platforms for different cargos (drugs, growth factors, cells, among others) in tissues such as bone, cartilage, nerve or skin. Besides, self-healing hydrogels have currently found their way into new and novel applications; for example, with the development of the self-healing adhesive hydrogels, by merely aiding surgical closing processes and by providing biomaterial-tissue adhesion. Furthermore, conductive hydrogels permit the stimuli and monitoring of natural electrical signals, which facilitated a better fitting of hydrogels in native tissue or the diagnosis of various health diseases. Lastly, self-healing hydrogels could be part of cyborganics - a merge between biology and machinery - which can pave the way to a finer healthcare devices for diagnostics and precision therapies.

Hybrid Hydrogels for Immunoregulation and Proangiogenesis through Mild Heat Stimulation to Accelerate Whole-Process Diabetic Wound Healing

Intense and persistent oxidative stress, excessive inflammation, and impaired angiogenesis severely hinder diabetic wound healing. Bioactive hydrogel dressings with immunoregulatory and proangiogenic properties have great promise in treating diabetic wounds. However, the therapeutic effects of dressings always depend on drugs with side effects, expensive cytokines, and cell therapies. Herein, a novel dynamic borate-bonds crosslinked hybrid multifunctional hydrogel dressings with photothermal properties are developed to regulate the microenvironment of diabetic wound sites and accelerate the whole process of its healing without additional medication. The hydrogel is composed of phenylboronic acid-modified chitosan and hyaluronic acid (HA) crosslinked by tannic acid (TA) through borate bonds and Prussian blue nanoparticles (PBNPs) with photothermal response characteristics are embedded in the polymer networks. The results indicate hydrogels show inherent broad-spectrum antioxidative activities through the integrated interaction of borate bonds, TA, and PBNPs. Meanwhile, combined with the regulation of macrophage phenotype by HA, the inflammatory microenvironment of diabetic wounds is transformed. Moreover, the angiogenesis is then enhanced by the mild photothermal effect of PBNPs, followed by promoted epithelialization and collagen deposition. In summary, this hybrid hydrogel system accelerates all stages of wound repair through antioxidative stress, immunomodulation, and proangiogenesis, showing great potential applications in diabetic wound management.

Advances in Hydrogels of Drug Delivery Systems for the Local Treatment of Brain Tumors

The management of brain tumors presents numerous challenges, despite the employment of multimodal therapies including surgical intervention, radiotherapy, chemotherapy, and immunotherapy. Owing to the distinct location of brain tumors and the presence of the blood-brain barrier (BBB), these tumors exhibit considerable heterogeneity and invasiveness at the histological level. Recent advancements in hydrogel research for the local treatment of brain tumors have sought to overcome the primary challenge of delivering therapeutics past the BBB, thereby ensuring efficient accumulation within brain tumor tissues. This article elaborates on various hydrogel-based delivery vectors, examining their efficacy in the local treatment of brain tumors. Additionally, it reviews the fundamental principles involved in designing intelligent hydrogels that can circumvent the BBB and penetrate larger tumor areas, thereby facilitating precise, controlled drug release. Hydrogel-based drug delivery systems (DDSs) are posited to offer a groundbreaking approach to addressing the challenges and limitations inherent in traditional oncological therapies, which are significantly impeded by the unique structural and pathological characteristics of brain tumors.

Trends in polysaccharide-based hydrogels and their role in enhancing the bioavailability and bioactivity of phytocompounds

Over the years, polysaccharides such as chitosan, alginate, hyaluronic acid, k-carrageenan, xanthan gum, carboxymethyl cellulose, pectin, and starch, alone or in combination with proteins and/or synthetic polymers, have been used to engineer an extensive portfolio of hydrogels with remarkable features. The application of polysaccharide-based hydrogels has the potential to alleviate challenges related to bioavailability, solubility, stability, and targeted delivery of phytocompounds, contributing to the development of innovative and efficient drug delivery systems and functional food formulations. This review highlights the current knowledge acquired on the preparation, features and applications of polysaccharide/phytocompounds hydrogel-based hybrid systems in wound management, drug delivery, functional foods, and food industry. The structural, functional, and biological requirements of polysaccharides and phytocompounds on the overall performance of such hybrid systems, and their impact on the application domains are also discussed.

Antibacterial adhesive based on oxidized tannic acid-chitosan for rapid hemostasis

Currently, bacterial infections and bleeding interfere with wound healing, and multifunctional hydrogels with appropriate blood homeostasis, skin adhesion, and antibacterial activity are desirable. In this study, chitosan-based hydrogels were synthesized using oxidized tannic acid (OTA) and Fe3+ as cross-linkers (CS-OTA-Fe) by forming covalent, non-covalent, and metal coordination bonds between Fe3+ and OTA. Our results demonstrated that CS-OTA-Fe hydrogels showed antibacterial properties against Gram-positive bacteria (Staphylococcus aureus)and Gram-negative bacteria (Escherichia coli), low hemolysis rate (< 2 %), rapid blood clotting ability, in vitro (< 2 min), and in vivo (90 s) in mouse liver bleeding. Additionally, increasing the chitosan concentration from 3 wt% to 4.5 wt% enhanced cross-linking in the network, leading to a significant improvement in the strength (from 106 ± 8 kPa to 168 ± 12 kPa) and compressive modulus (from 50 ± 9 kPa to 102 ± 14 kPa) of hydrogels. Moreover, CS-OTA-Fe hydrogels revealed significant adhesive strength (87 ± 8 kPa) to the cow's skin tissue and cytocompatibility against L929 fibroblasts. Overall, multifunctional CS-OTA-Fe hydrogels with tunable mechanical properties, excellent tissue adhesive, self-healing ability, good cytocompatibility, and fast hemostasis and antibacterial properties could be promising candidates for biomedical applications.

Self-healing, antioxidant, and antibacterial Bletilla striata polysaccharide-tannic acid dual dynamic crosslinked hydrogels for tissue adhesion and rapid hemostasis

Biomaterials capable of achieving effective sealing and hemostasis at moist wounds are in high demand in the clinical management of acute hemorrhage. Bletilla striata polysaccharide (BSP), a natural polysaccharide renowned for its hemostatic properties, holds promising applications in biomedical fields. In this study, a dual-dynamic-bonds crosslinked hydrogel was synthesized via a facile one-pot method utilizing poly(vinyl alcohol) (PVA)-borax as a matrix system, followed by the incorporation of BSP and tannic acid (TA). Chemical borate ester bonds formed around borax, coupled with multiple physical hydrogen bonds between BSP and other components, enhanced the mechanical properties and rapid self-healing capabilities. The catechol moieties in TA endowed the hydrogel with excellent adhesive strength of 30.2 kPa on the surface of wet tissues and facilitated easy removal without residue. Benefiting from the synergistic effect of TA and the preservation of the intrinsic properties of BSP, the hydrogel exhibited outstanding biocompatibility, antibacterial, and antioxidant properties. Moreover, it effectively halted acute bleeding within 31.3 s, resulting in blood loss of 15.6 % of that of the untreated group. As a superior hemostatic adhesive, the hydrogel in this study is poised to offer a novel solution for addressing future acute hemorrhage, wound healing, and other biomedical applications.

Advancing homogeneous networking principles for the development of fatigue-resistant, low-swelling and sprayable hydrogels for sealing wet, dynamic and concealed wounds in vivo

Effective sealing of wet, dynamic and concealed wounds remains a formidable challenge in clinical practice. Sprayable hydrogel sealants are promising due to their ability to cover a wide area rapidly, but they face limitations in dynamic and moist environments. To address this issue, we have employed the principle of a homogeneous network to design a sprayable hydrogel sealant with enhanced fatigue resistance and reduced swelling. This network is formed by combining the spherical structure of lysozyme (LZM) with the orthotetrahedral structure of 4-arm-polyethylene glycol (4-arm-PEG). We have achieved exceptional sprayability by controlling the pH of the precursor solution. The homogeneous network, constructed through uniform cross-linking of amino groups in protein and 4-arm-PEG-NHS, provides the hydrogel with outstanding fatigue resistance, low swelling and sustained adhesion. In vitro testing demonstrated that it could endure 2000 cycles of underwater shearing, while in vivo experiments showed adhesion maintenance exceeding 24 h. Furthermore, the hydrogel excelled in sealing leaks and promoting ulcer healing in models including porcine cardiac hemorrhage, lung air leakage and rat oral ulcers, surpassing commonly used clinical materials. Therefore, our research presents an advanced biomaterial strategy with the potential to advance the clinical management of wet, dynamic and concealed wounds.

Sprayable self-assembly multifunctional bioactive poly(ferulic acid) hydrogel for rapid MRSA infected wound repair

The repair of methicillin-resistant staphylococcus aureus (MRSA) infected wounds remains a serious challenge. Development of multifunctional bioactive hydrogels has shown promising potential in treating MRSA wound. Ferulic acid has special bioactivities including antioxidant antiinflammation antibacterial capacities but limited in lack of engineering strategy for efficient treatment of MRSA infected wound. Herein, we developed a multifunctional bioactive poly(ferulic acid) copolymer (FPFA) for treating MRSA infected wound. FPFA could be self-assembled into hydrogel under body temperature and demonstrated the injectable, sprayable, self-healing, anti-inflammatory, antioxidant, and angiogenic activity. FPFA hydrogel also showed the good cytocompatibility, efficiently enhanced the endothelial cell migration, scavenged intracellular reactive oxygen species (ROS), inhibited the expression of inflammatory factors and enhanced the in vitro angiogenesis. The MRSA-infected wound model showed that FPFA could significantly inhibit the MRSA infection and excess inflammation, reinforce the angiogenesis, accelerate wound healing and skin tissue regeneration.

Gelatin-based dynamic response antioxidant, anti-inflammatory multifunctional hydrogel for enhanced diabetic wound repair

Diabetic wound therapy presents significant challenges in the clinical environment, where persistent bleeding, disturbed inflammatory regulation, impaired cellular proliferation, and impaired tissue remodeling are major features of diabetic wound healing. However, current treatment strategies need to be considered in the context of the dynamic and complex needs of chronic wound healing. Here, multifunctional dynamic boronic acid cross-linked hydrogels were prepared by the reaction of gelatin (Gel) inoculated with 5-carboxy 3-nitrophenylboronic acid (NPBA) and Epigallocatechin gallate (EGCG) to achieve rapid gelation at pH = 7.4, EGCG could interact electrostatically with cationic antimicrobial peptides (AMP) to achieve the effective loading of AMP in the hydrogels. This hydrogel can be injected and adhered to skin defects in diabetic patients to provide a barrier and rapid hemostasis. In a high glucose microenvironment, the rapid release of AMP effectively kills bacteria, while the responsive release of EGCG eliminates reactive oxygen species (ROS) and promotes macrophage M2 polarization. In addition, the hydrogel had excellent biocompatibility and degradability properties, degraded completely after 3 days of subcutaneous injection, and was non-toxic in H&E staining of major organs and serum liver function indices in mice. This multifunctional injectable hydrogel accelerates diabetic skin wound repair and is a promising dressing for the precise treatment of diabetic wounds.

Progress in injectable hydrogels for the treatment of incompressible bleeding: an update

Uncontrollable haemorrhage from deep, noncompressible wounds remains a persistent and intractable challenge, accounting for a very high proportion of deaths in both war and disaster situations. Recently, injectable hydrogels have been increasingly studied as potential haemostatic materials, highlighting their enormous potential for the management of noncompressible haemorrhages. In this review, we summarize haemostatic mechanisms, commonly used clinical haemostatic methods, and the research progress on injectable haemostatic hydrogels. We emphasize the current status of injectable hydrogels as haemostatic materials, including their physical and chemical properties, design strategy, haemostatic mechanisms, and application in various types of wounds. We discuss the advantages and disadvantages of injectable hydrogels as haemostatic materials, as well as the opportunities and challenges involved. Finally, we propose cutting-edge research avenues to address these challenges and opportunities, including the combination of injectable hydrogels with advanced materials and innovative strategies to increase their biocompatibility and tune their degradation profile. Surface modifications for promoting cell adhesion and proliferation, as well as the delivery of growth factors or other biologics for optimal wound healing, are also suggested. We believe that this paper will inform researchers about the current status of the use of injectable haemostatic hydrogels for noncompressible haemorrhage and spark new ideas for those striving to propel this field forward.

Drug-Releasing Tannic Acid-Mediated Adhesive PEG Hydrogel for Porous Titanium Implants

Porous titanium implants are commonly utilized for orthopedic surgery because they can mimic the mechanical properties and porous structure of human bone. However, the bioinertness of titanium (Ti) has been reported to obstruct biointegration processes, resulting in slower bone repair. Here, we propose a localized drug delivery system on Ti surfaces using adhesive hydrogel to enhance biological-Ti interactions. The hydrogel was fabricated from polyethylene glycol (PEG), which was cross-linked by the complex of tannic acid (TA) and 1,4-phenylenediboronic acid (PDBA) and stabilized by bovine serum albumin (BSA). The hydrogel was formed and attached to a Ti plate to investigate stability, biodegradability, controlled drug release, and biocompatibility. The stability and biodegradability of the hydrogel could be tuned by adjusting the concentrations of BSA and TA. The hydrogel lasted and remained adhered to the Ti surface after being submerged in PBS for at least 15 days. The controlled release of strontium ranelate (SrRan) and the release mechanism depended on the amount of TA since it was found to govern the hydrogel integrity and pore size. Additionally, in vitro biocompatibility was validated using L929 fibroblast and MC3T3-E1 osteoblast cells that showed greater than 70% viability. The adhesive hydrogel was further studied by injecting it into a 3D-printed Ti-scaffold that contained a porous structure mimicking natural human bone. The hydrogel completely filled and adhered to the inner porous structure of the scaffold. The biodegradation and drug release of the hydrogel in the scaffold occurred at a slower rate, suggesting sustainable drug release that is suitable for bone cell regeneration. The overall results in biodegradability, controlled drug release, and biocompatibility demonstrate the great potential of the drug-releasing TA-mediated adhesive PEG hydrogel as a Ti-enhancing biomaterial that supports osseointegration.

A self-healable and bioadhesive acacia gum polysaccharide-based injectable hydrogel for wound healing acceleration

The present study aimed at developing an injectable hydrogel based on acacia gum (AG) for wound healing acceleration. The hydrogels were synthetized through metal-ligand coordination mediated by Fe3+ and characterized in terms of gelation time, gel content, initial water content, swelling capacity, water retention ratio, and porosity. Moreover, FTIR, XRD and TGA analyses were performed for the hydrogels and allantoin (Alla) loaded ones. Furthermore, bioadhessiveness, and self-healing as well as antibacterial, toxicity and wound healing potentials of the hydrogels were evaluated. The hydrogels displayed fast gelation time, high swelling, porosity, and bioadhessiveness, as well as antioxidant, self-healing, antibacterial, blood clotting, and injectability properties. FTIR, XRD and TGA analyses confirmed hydrogel synthesis and drug loading. The Alla-loaded hydrogels accelerated wound healing by decreasing the inflammation and increasing the cell proliferation as well as collagen deposition. Hemocompatibility, cell cytotoxicity, and in vivo toxicity experiments were indicative of a high biocompatibility level for the hydrogels. Given the advantages of fast gelation, injectability and beneficial biological properties, the use of Alla-loaded hydrogels could be considered a new remedy for efficient wound healing.

Sprayable Ti3C2 MXene hydrogel for wound healing and drug release system

Wound healing is a critical process that facilitates the body's recovery from injuries and helps prevent infections, thereby maintaining overall tissue and organ functionality. However, delayed wound healing owing to various factors can lead to bacterial infections and secondary complications. In this study, a ciprofloxacin (CIP)-loaded MXene/sodium alginate (SA) hydrogel was fabricated to inhibit bacterial infections and enhance wound healing. The hydrogel was formulated in a sprayable state by blending CIP-loaded MXene (CIP-MX) with SA. This hydrogel was found to exhibit excellent photothermal conversion capability and biocompatibility under near-infrared (NIR) irradiation. In addition, the hydrogel enabled controlled drug release based on NIR irradiation, ultimately enabling improved antibacterial activity. Based on the in vitro and in vivo experiments, the CIP-loaded MXene/SA hydrogel (CIP-MX@Gel) accelerated wound healing. Overall, the CIP-MX@Gel has excellent potential as an effective wound healing material.

Biomimetic Hemostatic Powder Derived from Coacervate-Immobilized Thermogelling Copolymers

Intrinsic hemostasis is an innate body response to prevent bleeding based on the sol-gel transition of blood. However, it is often inadequate for exceptional situations, such as acute injury and coagulation disorders, which typically require immediate medical intervention. Herein, we report the preparation of an efficient hemostatic powder, composed of tannic acid (TA), poly(ethylene glycol) (PEG), and poly(d,l-lactide-co-glycolide)-b-poly(ethylene glycol)-b-poly(d,l-lactide-co-glycolide) triblock copolymer (TB), for biomimetic hemostasis at the bleeding sites. TA has a high affinity for biomolecules and cells and can form coacervates with PEG driven by hydrogen bonding. TB enhances the mechanical strength and provides thermoresponsiveness. The hemostatic powder can rapidly transit into a physical and biodegradable seal on wet substrates under physiological conditions, demonstrating its promise for the generation of instant artificial clots. Importantly, this process is independent of the innate blood clotting process, which could benefit those with blood clotting disorders. This biomimetic hemostatic powder is an adaptive topical sealing agent for noncompressible and irregular wounds, which is promising for biomedical applications.

Biologically Derived Nanoarchitectonic Coatings for the Engineering of Hemostatic Needles

Bleeding after venipuncture could cause blood loss, hematoma, bruising, hemorrhagic shock, and even death. Herein, a hemostatic needle with antibacterial property is developed via coating of biologically derived carboxymethyl chitosan (CMCS) and Cirsium setosum extract (CsE). The rapid transition from films of the coatings to hydrogels under a wet environment provides an opportunity to detach the coatings from needles and subsequently seal the punctured site. The hydrogels do not significantly influence the healing process of the puncture site. After hemostasis, the coatings on hemostatic needles degrade in 72 h without inducing a systemic immune response. The composition of CMCS can inhibit bacteria of Gram-negative Escherichia coli and Gram-positive Staphylococcus aureus by destroying the membrane of bacteria. The hemostatic needle with good hemostasis efficacy, antibacterial property, and safety is promising for the prevention of bleeding-associated complications in practical applications.

Nanoarchitectonics of tannic acid based injectable hydrogel regulate the microglial phenotype to enhance neuroplasticity for poststroke rehabilitation

BACKGROUND

Stroke is the second leading cause of mortality and disability worldwide. Poststroke rehabilitation is still unsatisfactory in clinics, which brings great pain and economic burdens to stroke patients. In this study, an injectable hydrogel in which tannic acid (TA) acts as not only a building block but also a therapeutic drug, was developed for poststroke rehabilitation.

METHODS

TA is used as a building block to form an injectable hydrogel (TA gel) with carboxymethyl chitosan (CMCS) by multivalent hydrogen bonds. The morphology, rheological properties, and TA release behavior of the hydrogel were characterized. The abilities of the TA gel to modulate microglial (BV2 cells) polarization and subsequently enhance the neuroplasticity of neuro cells (N2a cells) were assessed in vitro. The TA gel was injected into the cavity of stroke mice to evaluate motor function recovery, microglial polarization, and neuroplasticity in vivo. The molecular pathway through which TA modulates microglial polarization was also explored both in vitro and in vivo.

RESULTS

The TA gel exhibited sustainable release behavior of TA. The TA gel can suppress the expression of CD16 and IL-1β, and upregulate the expression of CD206 and TGF-β in oxygen and glucose-deprived (OGD) BV2 cells, indicating the regulation of OGD BV2 cells to an anti-inflammatory phenotype in vitro. This finding further shows that the decrease in synaptophysin and PSD95 in OGD N2a cells is effectively recovered by anti-inflammatory BV2 cells. Furthermore, the TA gel decreased CD16/iNOS expression and increased CD206 expression in the peri-infarct area of stroke mice, implying anti-inflammatory polarization of microglia in vivo. The colocalization of PSD95 and Vglut1 stains, as well as Golgi staining, showed the enhancement of neuroplasticity by the TA gel. Spontaneously, the TA gel successfully recovered the motor function of stroke mice. The western blot results in vitro and in vivo suggested that the TA gel regulated microglial polarization via the NF-κB pathway.

CONCLUSION

The TA gel serves as an effective brain injectable implant to treat stroke and shows promising potential to promote poststroke rehabilitation in the clinic.

A Mechanically Resilient and Tissue-Conformable Hydrogel with Hemostatic and Antibacterial Capabilities for Wound Care

Hydrogels are used in wound dressings because of their tissue-like softness and biocompatibility. However, the clinical translation of hydrogels remains challenging because of their long-term stability, water swellability, and poor tissue adhesiveness. Here, tannic acid (TA) is introduced into a double network (DN) hydrogel consisting of poly(vinyl alcohol) (PVA) and poly(acrylic acid) (PAA) to realize a tough, self-healable, nonswellable, conformally tissue-adhesive, hemostatic, and antibacterial hydrogel. The TA within the DN hydrogel forms a dynamic network, enabling rapid self-healing (within 5 min) and offering effective energy dissipation for toughness and viscoelasticity. Furthermore, the hydrophobic moieties of TA provide a water-shielding effect, rendering the hydrogel nonswellable. A simple chemical modification to the hydrogel further strengthens its interfacial adhesion with tissues (shear strength of ≈31 kPa). Interestingly, the TA also can serve as an effective hemostatic (blood-clotting index of 58.40 ± 1.5) and antibacterial component, which are required for a successful wound dressing. The antibacterial effects of the hydrogel are tested against Escherichia coli and Staphylococcus aureus. Finally, the hydrogel is prepared in patch form and applied to a mouse model to test in vivo biocompatibility and hemostatic performances.

Colorimetric pH-responsive and hemostatic hydrogel-based bioadhesives containing functionalized silver nanoparticles

Here we develop and characterize a dual-cross-linked pH-responsive hydrogel based on the carboxyethyl chitosan-oxidized sodium alginate (CAO) containing silver nanoparticles (Ag NPs) functionalized with tannic acid/red cabbage (ATR). This hybrid hydrogel is formed via covalent and non-covalent cross-linking. The adhesive strength measured in contact with cow skin and compression strength is measured more than 3 times higher than that of CAO. Importantly, the incorporation of 1 ​wt% ATR into CAO significantly enhances the compression strength of CAO from 35.1 ​± ​2.1 ​kPa to 97.5 ​± ​2.9 ​kPa. Moreover, the cyclic compression tests confirm significantly higher elastic behavior of CAO after the addition of ATR-functionalized NPs to CAO. The CAO/ATR hydrogel is pH-sensitive and indicated remarkable color changes in different buffer solutions. The CAO/ATR also shows improved hemostatic properties and reduced clotting time compared to the clotting time of blood in contact with CAO hydrogel. In addition, while CAO/ATR is effective in inhibiting the growth of both Gram-positive and Gram-negative bacteria, CAO is only effective in inhibiting the growth of Gram-positive bacteria. Finally, the CAO/ATR hydrogel is cytocompatible with L929 fibroblasts. In summary, the resulting CAO/ATR hydrogel shows promising results in designing and constructing smart wound bioadhesives with high cytocompatibility, antibacterial properties, blood coagulation ability, and fast self-healing properties.

Mussel-inspired nanoparticle composite hydrogels for hemostasis and wound healing

Uncontrolled hemorrhage caused by trauma can easily lead to death. Efficient and safe hemostatic materials are an urgent and increasing need for hemostatic research. Following a trauma, wound healing is induced by various cellular mechanisms and proteins. Hemostatic biomaterials that can not only halt bleeding quickly but also provide an environment to promote wound healing have been the focus of research in recent years. Mussel-inspired nanoparticle composite hydrogels have been propelling the development of hemostatic materials owing to their unique advantages in adhesion, hemostasis, and bacteriostasis. This review summarizes the hemostatic and antimicrobial fundamentals of polydopamine (PDA)-based nanomaterials and emphasizes current developments in hemorrhage-related PDA nanomaterials. Moreover, it briefly discusses safety concerns and clinical application problems with PDA hemostatic nanomaterials.

Polyphenols Coordinated with Cu (II) in an Aqueous System Build Ion-Channel Coatings on Hair Surfaces

Recently, developments in the field of cosmetics have led to a renewed interest in hair dyeing. However, damage to the hair during the dyeing process has increased hesitation in attempting hair dyeing. As a result, hair dyes with minimal side effects have been in constant demand, and are being developed. In this study, natural-extract polyphenols, pyrogallol, and gallic acid are coordinated by CuCl₂ in a NaCl aqueous solution to form an oligomer, which creates an ion-channel coating on the hair surface to protect it. This work attempts to develop fast, simple, and damage-free hair-dye ingredients based on pyrogallol and gallic acid. The morphology and elements of polyphenols coated on hair are characterized. The results reveal that the hair is dyed with the polyphenol-based dye reagent successfully. Moreover, the thickness of the dyed hair continuously rises ten times after dyeing. The tensile strength of the dyed hair is also measured, showing an upward and downward trend. These results reflect the fact that pyrogallol and gallic acid are considered to be the essential and functional polyphenols, and can build ion blocks on hair, which can create new multifunctional coating materials.

Chitosan-Based Hemostatic Hydrogels: The Concept, Mechanism, Application, and Prospects

The design of new hemostatic materials to mitigate uncontrolled bleeding in emergencies is challenging. Chitosan-based hemostatic hydrogels have frequently been used for hemostasis due to their unique biocompatibility, tunable mechanical properties, injectability, and ease of handling. Moreover, chitosan (CS) absorbs red blood cells and activates platelets to promote hemostasis. Benefiting from these desired properties, the hemostatic application of CS hydrogels is attracting ever-increasing research attention. This paper reviews the recent research progress of CS-based hemostatic hydrogels and their advantageous characteristics compared to traditional hemostatic materials. The effects of the hemostatic mechanism, effects of deacetylation degree, relative molecular mass, and chemical modification on the hemostatic performance of CS hydrogels are summarized. Meanwhile, some typical applications of CS hydrogels are introduced to provide references for the preparation of efficient hemostatic hydrogels. Finally, the future perspectives of CS-based hemostatic hydrogels are presented.

Tannic acid-crosslinked O-carboxymethyl chitosan hydrogels for enhanced antibacterial activity and rapid hemostasis

Bacterial infection and massive blood loss are major challenges for global public health. Herein, a series of tannic acid encapsulated O-carboxymethyl chitosan (CMC) based hydrogels were prepared using a facile approach for both hemorrhage control and effective anti-bacterium. The results indicated that the tannic acid-cosslinked CMC hydrogels had excellent mechanical property, swelling ability as well as great cytocompatibility. Comparably, with increasing tannic acid loading, the bleeding control and antibacterial performance against both E. coli and S. aureus were improved simultaneously, especially for the 5% tannic acid-cosslinked CMC hydrogel. Moreover, the prepared CMC hydrogel loading with tannic acid could induce hemocytes and platelets aggregation, promote the blood clotting and achieve bleeding control in vivo due to the interconnected fibrous web structure and the chemical activation (the phenol group of tannic acid). Thus, the resultant CMC hydrogel enabled the maintenance of high bioavailability of tannic acid and synchronization with the interconnected fibrous structure of CMC hydrogels, which was expected to be a promising candidate for robust and safe hemostatic dressings.

Hyaluronic acid and chitosan-based injectable and self-healing hydrogel with inherent antibacterial and antioxidant bioactivities

Injectable dressings offering intrinsic antibacterial activity and antioxidation are required, because persistent bacterial infection and oxidative damage are common issues associated with chronic non-healing wounds. Herein, a versatile QCS-l-TA-l-OHA hydrogel is fabricated using ubiquitous nature derived biological macromolecules, quaternized chitosan (QCS), tannic acid (TA) and oxidant hyaluronic acid (OHA), driving by multiple dynamic interactions under physiological conditions. The hydrogel can serve as multiple functional wound dress with injectable and self-healing capabilities coupling with attractive antibacterial activity and antioxidation. The biocompatible and self-biodegradable hydrogel augments free radical scavenging capacity, antibacterial, angiogenesis, mature granulation tissue and collagen disposition, enabling fast wound healing of rat skin full-thickness incision model. This study highlights a wound dressing platform of hyaluronic acid and chitosan based injectable and self-healing hydrogel with inherent antibacterial and antioxidant bioactivities, thereby avoiding the use of antibiotics or antioxidant agents.

Polysaccharide-Based Adhesive Antibacterial and Self-Healing Hydrogel for Sealing Hemostasis

Adhesive hydrogels have been considered as one of the most ideal materials for wound dressing. However, most existing adhesive hydrogels still have disadvantages such as low mechanical properties, poor biological activity (antibacterial and hemostatic ability), and low biocompatibility, which largely limit their application. Thus, it is highly desired to prepare a hydrogel-based wound dressing with good self-healing, ideal adhesive properties, rapid hemostasis, and excellent wound infection prevention activity. In this study, a simple method was presented to prepare a PAM-Lignin-CS-Laponite-SA hydrogel for wound dressing. The obtained hydrogel displayed excellent self-healing ability and repeatable adhesive performance, benefiting from the introduction of hydrogen bonding and electrostatic interactions inside the hydrogel network. In addition, the PAM-Lignin-CS-Laponite-SA hydrogel also exhibited low cell cytotoxicity, good antibacterial activity, and outstanding hemostatic properties. In conclusion, the PAM-Lignin-CS-Laponite-SA hydrogel demonstrated good tissue adhesion, excellent self-healing ability, effective bleeding control, and good antibacterial activity to prevent wound infection, which provides a new idea for developing a multifunctional hydrogel-based tissue adhesive hemostatic dressing.

Polysaccharides-Based Injectable Hydrogels: Preparation, Characteristics, and Biomedical Applications

Polysaccharides-based injectable hydrogels are a unique group of biodegradable and biocompatible materials that have shown great potential in the different biomedical fields. The biomolecules or cells can be simply blended with the hydrogel precursors with a high loading capacity by homogenous mixing. The different physical and chemical crosslinking approaches for preparing polysaccharide-based injectable hydrogels are reviewed. Additionally, the review highlights the recent work using polysaccharides-based injectable hydrogels as stimuli-responsive delivery vehicles for the controlled release of different therapeutic agents and viscoelastic matrix for cell encapsulation. Moreover, the application of polysaccharides-based injectable hydrogel in regenerative medicine as tissue scaffold and wound healing dressing is covered.

PEG-mediated hybrid hemostatic gauze with in-situ growth and tightly-bound mesoporous silicon

Pre-hospital control of bleeding is critical to save lives, however the development of hemostatic agents with efficient and safe performance is still a challenge. In this study, a hybrid hemostatic gauze (MG-PEG) with in-situ growth and tightly bound mesoporous silicon (MSN) was prepared by template method for hemorrhage control. This material integrated meso-porosity, blood coagulation and stability into flexible gauze fiber. The PEG in MG-PEG was not only used as template for the in-suit MSN growth, but also acted as joint connection between the gauze fibers and MSN. The MSN particles were firmly bound to the surface of gauze fibers with extremely low leakage after 3 min of sonication and displayed a comparable coagulant activity to untreated sample. The results of animal experiments confirmed that MG-PEG possessed superior hemostatic performance over silicates-based inorganic hemostasis-Combat Gauze, in terms of higher coagulant activity (in vivo clotting time <200 s), minimized loss of active components (liquids OD was only 3 % of CG), well biocompatibility (hemolysis ratio < 5 %, no cytotoxicity) and wider indications range for practical application.

Design of biopolymer-based hemostatic material: Starting from molecular structures and forms

Uncontrolled bleeding remains as a leading cause of death in surgical, traumatic, and emergency situations. Management of the hemorrhage and development of hemostatic materials are paramount for patient survival. Owing to their inherent biocompatibility, biodegradability and bioactivity, biopolymers such as polysaccharides and polypeptides have been extensively researched and become a focus for the development of next-generation hemostatic materials. The construction of novel hemostatic materials requires in-depth understanding of the physiological hemostatic process, fundamental hemostatic mechanisms, and the effects of material chemistry/physics. Herein, we have recapitulated the common hemostatic strategies and development status of biopolymer-based hemostatic materials. Furthermore, the hemostatic mechanisms of various molecular structures (components and chemical modifications) are summarized from a microscopic perspective, and the design based on them are introduced. From a macroscopic perspective, the design of various forms of hemostatic materials, e.g., powder, sponge, hydrogel and gauze, is summarized and compared, which may provide an enlightenment for the optimization of hemostat design. It has also highlighted current challenges to the development of biopolymer-based hemostatic materials and proposed future directions in chemistry design, advanced form and clinical application.

•

Biopolymers possess sound biocompatibility, biodegradability and bioactivity for the design of hemostatic materials.

•

Molecular structure designs including component and chemical modification are summarized from a microscopic perspective.

•

Design of various forms of hemostatic materials is discussed and compared synthetically from a macroscopic perspective.

Punicalagin-Loaded Alginate/Chitosan-Gallol Hydrogels for Efficient Wound Repair and Hemostasis

For recently devised wound-healing materials, a variety of acute application systems with sustainable therapeutic effects on wound sites have been suggested. For example, hydrogel-type healing agents with porous structures and high drug encapsulation efficiencies have been developed for wound repair. However, challenges remain about the poor mechanical and adhesive properties of hydrogels. Herein, we propose a punicalagin (PC)-containing wound-healing hydrogel in adhesive form that is mechanically stable and has sustainable wound-healing therapeutic efficiency. The APC hydrogel, composed of alginate (ALG), PC, and chitosan–gallol (CHI–G), exhibits significant mechanical and self-healing properties, thus indicating that PC increases cross-linking in ALG/CHI–G as macromolecule. The PC-containing mechanically enhanced hydrogel demonstrates high tissue adhesiveness. Sustainable PC release for 192 h, which indicates high therapeutic effect of the released PC, and great blood compatibility are evaluated based on rapid blood coagulation and minimal hemolysis. The cytocompatibility and wound-healing abilities of the PC-containing APC hydrogel are greater than those of the non-PC hydrogel, as verified by cell compatibility and wound scratch assays. These results indicate that a suitable concentration of PC-containing hydrogel with sustainable moisture condition and PC release may inspire further polyphenol-agent-containing hydrogels as wound-healing agents with structural stability and therapeutic efficiency.

Tannic acid: a versatile polyphenol for design of biomedical hydrogels

Tannic acid (TA), a natural polyphenol, is a hydrolysable amphiphilic tannin derivative of gallic acid with several galloyl groups in its structure. Tannic acid interacts with various organic, inorganic, hydrophilic, and hydrophobic materials such as proteins and polysaccharides via hydrogen bonding, electrostatic, coordinative bonding, and hydrophobic interactions. Tannic acid has been studied for various biomedical applications as a natural crosslinker with anti-inflammatory, antibacterial, and anticancer activities. In this review, we focus on TA-based hydrogels for biomaterials engineering to help biomaterials scientists and engineers better realize TA's potential in the design and fabrication of novel hydrogel biomaterials. The interactions of TA with various natural or synthetic compounds are deliberated, discussing parameters that affect TA-material interactions thus providing a fundamental set of criteria for utilizing TA in hydrogels for tissue healing and regeneration. The review also discusses the merits and demerits of using TA in developing hydrogels either through direct incorporation in the hydrogel formulation or indirectly via immersing the final product in a TA solution. In general, TA is a natural bioactive molecule with diverse potential for engineering biomedical hydrogels.

Engineered Hemostatic Biomaterials for Sealing Wounds

Hemostatic biomaterials show great promise in wound control for the treatment of uncontrolled bleeding associated with damaged tissues, traumatic wounds, and surgical incisions. A surge of interest has been directed at boosting hemostatic properties of bioactive materials via mechanisms triggering the coagulation cascade. A wide variety of biocompatible and biodegradable materials has been applied to the design of hemostatic platforms for rapid blood coagulation. Recent trends in the design of hemostatic agents emphasize chemical conjugation of charged moieties to biomacromolecules, physical incorporation of blood-coagulating agents in biomaterials systems, and superabsorbing materials in either dry (foams) or wet (hydrogel) states. In addition, tough bioadhesives are emerging for efficient and physical sealing of incisions. In this Review, we highlight the biomacromolecular design approaches adopted to develop hemostatic bioactive materials. We discuss the mechanistic pathways of hemostasis along with the current standard experimental procedures for characterization of the hemostasis efficacy. Finally, we discuss the potential for clinical translation of hemostatic technologies, future trends, and research opportunities for the development of next-generation surgical materials with hemostatic properties for wound management.

Metal Ion-Directed Functional Metal-Phenolic Materials

Metal ions are ubiquitous in nature and play significant roles in assembling functional materials in fields spanning chemistry, biology, and materials science. Metal-phenolic materials are assembled from phenolic components in the presence of metal ions through the formation of metal-organic complexes. Alkali, alkali-earth, transition, and noble metal ions as well as metalloids interacting with phenolic building blocks have been widely exploited to generate diverse hybrid materials. Despite extensive studies on the synthesis of metal-phenolic materials, a comprehensive summary of how metal ions guide the assembly of phenolic compounds is lacking. A fundamental understanding of the roles of metal ions in metal-phenolic materials engineering will facilitate the assembly of materials with specific and functional properties. In this review, we focus on the diversity and function of metal ions in metal-phenolic material engineering and emerging applications. Specifically, we discuss the range of underlying interactions, including (i) cation-π, (ii) coordination, (iii) redox, and (iv) dynamic covalent interactions, and highlight the wide range of material properties resulting from these interactions. Applications (e.g., biological, catalytic, and environmental) and perspectives of metal-phenolic materials are also highlighted.

Antibacterial, wearable, transparent tannic acid-thioctic acid-phytic acid hydrogel for adhesive bandages

Making a hydrogel-based first-aid bandage with green resources, desirable biocompatibility, universal adhesive properties, low cost and simple production is a long-standing research aspiration. Considering this, three naturally existing organic acids, namely tannic acid, thioctic acid and phytic acid, were used to construct a novel adhesive gel (TATAPA hydrogel) for epidermal tissue bandage applications. This hydrogel could be synthesized under mild conditions with no need for a freeze-thawing shaping procedure, and was transparent, moldable and stretchable with good stability under continuous water immersion. In lap-shear tests, the TATAPA hydrogel could adhere to various hydrophilic and hydrophobic surfaces. Moreover, in the case of skin tissue adhesion, the hydrogel could be easily peeled off from the skin, meeting wearability requirements. Rheological tests showed that the hydrogel possessed thermal sensitive properties derived from multi-supramolecular interactions. The methicillin-resistant Staphylococcus aureus (MRSA)-infected burn wound test demonstrated that the hydrogel had desirable antibacterial activity and was beneficial for wound healing. A femoral artery bleeding assay was also used to reveal that the TATAPA hydrogel could be directly pasted onto the bleeding site for hemostasis. Overall, this hydrogel demonstrates potential as a surgical bioadhesive for a broad range of medical applications.

Hot Melt Super Glue: Multi-Recyclable Polyphenol-Based Supramolecular Adhesives

We report the rapid and facile synthesis of hot melt super glue (HMSG) via the formation of adhesive supramolecular networks between catechol or pyrogallol hydroxyl groups (-OH) of polyphenols and repeat units (-CH₂ CH₂ O-) of poly(ethylene glycol) (PEG) based on hydrogen bonds. The adhesion strength of HMSG, processed by heating-cooling of polyphenols and PEG without additional solvents, can be tuned up to 8.8 MPa via changing the molecular weight of PEG and the ratio of hydrogen bonding donors and receptors. The advantages of the reported HMSG lie in the ease and scalability of the assembly process, rapid adhesion on various substrates with excellent processability, resistance of low temperature and organic solvents, and recyclable adhesion strength. The solvent-free HMSG represents a promising adhesive supramolecular network to expand the versatility and application of polyphenol-based materials. This article is protected by copyright. All rights reserved.

A low-swelling and toughened adhesive hydrogel with anti-microbial and hemostatic capacities for wound healing

Hydrogel-based wound dressings with tissue adhesion abilities are widely used for wound closure. However, currently developed hydrogel adhesives are still poor at continuing to seal wounds while bleeding is ongoing. Herein, we demonstrate an antibacterial and hemostatic hydrogel adhesive with low-swelling properties and toughness for wound healing. The hydrogel was composed of Pluronic F127 diacrylate, quaternized chitosan diacrylate, silk fibroin, and tannic acid, and it was not only able to maintain good tissue adhesion abilities in a moist environment but it also showed guaranteed tissue adhesion and mechanical strength after absorbing water due to its low-swelling and toughness properties. Furthermore, in vitro and in vivo tests demonstrated that the hydrogel also had antibacterial, antioxidant, and hemostatic properties, which could promote tissue regeneration. All these findings demonstrate that this hydrogel with multifunctional properties is a promising material for clinical wound healing applications.

Sprayable Hydrogel for Biomedical Applications

Polymeric hydrogels have extraordinary potential to be utilized for biomedical applications. Recently, sprayable hydrogels have received increasing attention for their biocompatibility, degradability, tunable mechanical properties and rapid spray-filming abilities. In...

Polymeric Materials for Hemostatic Wound Healing

Hemorrhage is one of the greatest threats to life on the battlefield, accounting for 50% of total deaths. Nearly 86% of combat deaths occur within the first 30 min after wounding. While external wound injuries can be treated mostly using visual inspection, abdominal or internal hemorrhages are more challenging to treat with regular hemostatic dressings because of deep wounds and points of injury that cannot be located properly. The need to treat trauma wounds from limbs, abdomen, liver, stomach, colon, spleen, arterial, venous, and/or parenchymal hemorrhage accompanied by severe bleeding requires an immediate solution that the first responders can apply to reduce rapid exsanguinations from external wounds, including in military operations. This necessitates the development of a unique, easy-to-use, FDA-approved hemostatic treatment that can deliver the agent in less than 30 s and stop bleeding within the first 1 to 2 min at the point of injury without application of manual pressure on the wounded area.

Polymorphic transient glycolipid assemblies with tunable lifespan and cargo release

HYPOTHESIS

In living systems, dynamic processes like dissipative assembly, polymorph formation, and destabilization of hydrophobic domains play an indispensable role in the biochemical processes. Adaptation of biological self-assembly processes to an amphiphilic molecule leads to the fabrication of intelligent biomaterials with life-like behavior.

EXPERIMENTS

An amphiphilic glycolipid molecule was engineered into various dissipative assemblies (vesicles and supramolecular nanotube-composed hydrogels) by using two activation steps, including heating-cooling and shear force in method-1 or boric acid/glycolipid complexation and shear force in method-2. The influence of number of activation steps on vesicle to nanotube phase transitions and activation method on the properties of hydrogels were investigated, where the morphological transformations and destabilization of hydrophobic domains resulted from a bilayer to a higher-order crystal structure.

FINDINGS

Hydrophobic and hydrophilic cargos encapsulated in the dissipative assemblies (vesicles and injectable hydrogels) can be released in a controlled manner via changing the activation method. The reported adaptive materials engineered by dual activation steps are promising self-assembled systems for programmed release of loaded cargos at a tunable rate.

Recent advances in materials for hemostatic management

Traumatic hemorrhage can be a fatal event, particularly when large quantities of blood are lost in a short period of time. Therefore, hemostasis has become a crucial part of emergency treatment. For small wounds, hemostasis can be achieved intrinsically depending on the body's own blood coagulation mechanism; however, for large-area wounds, particularly battlefield and complex wounds, materials delivering rapid and effective hemostasis are required. In parallel with the constant progress in science, technology, and society, advances in hemostatic materials have also undergone various iterations by integrating new ideas with old concepts. There are various natural and synthetic hemostatic materials, including hemostatic powders, adhesives, hydrogels, and tourniquets, for the treatment of severe external trauma. This review covers the differences among the currently available hemostatic materials and comprehensively describes the hemostatic effects of different materials based on the underlying mechanisms. Finally, solutions for current issues related to trauma bleeding are discussed, and the prospects of hemostatic materials are proposed.

Multifunctional wound dressing for rapid hemostasis, bacterial infection monitoring and photodynamic antibacterial therapy

Wound management is a major global issue, and there is a growing challenge to develop more effective hemostatic dressings to control bleeding and prevent pathogen infections. In this study, a multifunctional wound dressing was developed to meet the clinical need. The hemostatic layer of wound dressing can quickly stop the bleeding. Meanwhile, the detection layer is used for real-time fluorescence monitoring of the bacterial colonization. When infection occurs, wound dressing is further subjected to illumination for in-situ photodynamic antibacterial treatment. In the rabbit ear artery hemostasis model, the hemostasis time of the wound dressing was 1 s. The detection limit of the wound dressing was 1.4 × 10⁵ CFU/cm² for Escherichia coli, 5.9 × 10⁵ CFU/cm² for Staphylococcus aureus, and 3.8 × 10⁶ CFU/cm² for Pseudomonas aeruginosa, respectively. Compared with the control group, an enhanced wound closure (up to 97.3%) were observed in mice treated with the wound dressing. In vitro and in vivo experiment results suggested that the wound dressing was effective in killing pathogenic bacterial and exhibited good biological compatibility, and induced no inflammatory reaction. The proposed design prevents massive bleeding and wound infection, and further promotes wound healing. STATEMENT OF SIGNIFICANCE: In this work, we developed a multifunctional wound dressing, capable of rapid hemostasis, colorimetric monitoring of bacterial infection, and in situ photodynamic antibacterial. The hemostatic layer can quickly stop the bleeding due to its large specific surface area and adsorption pore size for platelet at bleeding site. Meanwhile, the detection layer can intelligently monitor the bacterial infection and respond to report bacterial infection by emitting fluorescence. When infection occurs, wound dressing can be used for in-situ photodynamic antibacterial treatment. In vitro and in vivo results showed that the wound dressing was biocompatible, prevented massive bleeding and wound infection, and further promoted wound healing.

Stretchable and Bioadhesive Gelatin Methacryloyl-Based Hydrogels Enabled by in Situ Dopamine Polymerization

Hydrogel patches with high toughness, stretchability, and adhesive properties are critical to healthcare applications including wound dressings and wearable devices. Gelatin methacryloyl (GelMA) provides a highly biocompatible and accessible hydrogel platform. However, low tissue adhesion and poor mechanical properties of cross-linked GelMA patches (i.e., brittleness and low stretchability) have been major obstacles to their application for sealing and repair of wounds. Here, we show that adding dopamine (DA) moieties in larger quantities than those of conjugated counterparts to the GelMA prepolymer solution followed by alkaline DA oxidation could result in robust mechanical and adhesive properties in GelMA-based hydrogels. In this way, cross-linked patches with ∼140% stretchability and ∼19 000 J/m³ toughness, which correspond to ∼5.7 and ∼3.3× improvement, respectively, compared to that of GelMA controls, were obtained. The DA oxidization in the prepolymer solution was found to play an important role in activating adhesive properties of cross-linked GelMA patches (∼4.0 and ∼6.9× increase in adhesion force under tensile and shear modes, respectively) due to the presence of reactive oxidized quinone species. We further conducted a parametric study on the factors such as UV light parameters, the photoinitiator type (i.e., lithium phenyl-2,4,6-trimethylbenzoylphosphinate, LAP, versus 2-hydroxy-4'-(2-hydroxyethoxy)-2-methylpropiophenone, Irgacure 2959), and alkaline DA oxidation to tune the cross-linking density and thereby hydrogel compliance for better adhesive properties. The superior adhesion performance of the resulting hydrogel along with in vitro cytocompatibility demonstrated its potential for use in skin-attachable substrates.

In vitroassessment of green polyhydroxybutyrate/chitosan blend loaded with kaempferol nanocrystals as a potential dressing for infected wounds

Despite the major medical advancements in recent decades, treating infected wounds successfully remains a challenge. In this research, a functional blend of Polyhydroxybutyrate (PHB) and Chitosan (Cs) was developed for wound infection mitigation with tailored biological and physicochemical properties. Water insoluble kaempferol (KPF) was pre-formulated to water soluble KPF nanocrystals (KPF-NCs) with fine particle size of 145 ± 11 nm, and high colloidal stability (-31 ± 0.4 mV) to improve its drug transdermal delivery. PHB-Cs-KPF-NCs (1:2 ratio) film owned the best physical properties in terms of high breathability, thermal stability and mechanical strength (33 ± 1 MPa). Besides, XRD and FTIR findings indicated the interaction between Cs, PHB and KPF, reducing the film crystallinity. The scanning electron microscopy of the film displayed a highly interconnected porous morphology. KPF-NCs were integrated in PHB-Cs matrix with a marked encapsulation efficiency of 96.6%. The enhanced drug-loading film showed a sustain release pattern of KPF-NCs over 48 h. Interestingly, the developed blend possessed an impressive blood clotting capacity within 20 min. Furthermore, we presented a new naturally-sourced mixture of Cs+KPF-NCs with powerful antibacterial effects against MDRStaphylococcus aureusandAcentibacter baumanniiat very low concentrations. The membrane evidenced a remarkable antibacterial naturein vitrowith almost 100% cell viability reduction against the study strains after 48 h. By virtue of these advantages, this green blend is highly proposed for optimal wound care.

Polyphenol-Containing Nanoparticles: Synthesis, Properties, and Therapeutic Delivery

Polyphenols, the phenolic hydroxyl group-containing organic molecules, are widely found in natural plants and have shown beneficial effects on human health. Recently, polyphenol-containing nanoparticles have attracted extensive research attention due to their antioxidation property, anticancer activity, and universal adherent affinity, and thus have shown great promise in the preparation, stabilization, and modification of multifunctional nanoassemblies for bioimaging, therapeutic delivery, and other biomedical applications. Additionally, the metal-polyphenol networks, formed by the coordination interactions between polyphenols and metal ions, have been used to prepare an important class of polyphenol-containing nanoparticles for surface modification, bioimaging, drug delivery, and disease treatments. By focusing on the interactions between polyphenols and different materials (e.g., metal ions, inorganic materials, polymers, proteins, and nucleic acids), a comprehensive review on the synthesis and properties of the polyphenol-containing nanoparticles is provided. Moreover, the remarkable versatility of polyphenol-containing nanoparticles in different biomedical applications, including biodetection, multimodal bioimaging, protein and gene delivery, bone repair, antibiosis, and cancer theranostics is also demonstrated. Finally, the challenges faced by future research regarding the polyphenol-containing nanoparticles are discussed.

A reduced polydopamine nanoparticle-coupled sprayable PEG hydrogel adhesive with anti-infection activity for rapid wound sealing

There is a growing demand to develop sprayable hydrogel adhesives with rapid-forming and antibacterial abilities to instantly seal open wounds and combat pathogen infection. Herein, we propose to design a polydopamine nanoparticle (PDA NP) coupled PEG hydrogel that can quickly solidify via an amidation reaction after spraying as well as tightly binding PDA NPs to deliver reactive oxygen species (ROS) and induce a photothermal effect for bactericidal activity, and provide a hydrophilic surface for antifouling activity. The molecular structure of the 4-arm-PEG-NHS precursor was regulated to increase its reactivity with 4-arm-PEG-NH2, which thus shortened the gelation time of the PEG adhesive to 1 s to allow a fast solidification after being sprayed. The PEG-NHS precursor also provided covalent binding with tissue and PDA NPs. The reduced PDA NPs have redox activity to convey electrons to oxygen to generate ROS (H2O2), thus endowing the hydrogel with ROS dependent antibacterial ability. Moreover, NIR irradiation can accelerate the ROS release because of the photothermal effect of PDA NPs. In vitro tests demonstrated that H2O2 and the NIR-photothermal effect synergistically induced a fast bacterial killing, and an in vivo anti-infection test also proved the effectiveness of PEG-PDA. The sprayable PEG-PDA hydrogel adhesive, with rapid-forming performance and a dual bactericidal mechanism, may be promising for sealing large-scale and acute wound sites or invisible bleeding sites, and protect them from pathogen infection.

Sustained Release Systems for Delivery of Therapeutic Peptide/Protein

Peptide/protein therapeutics have been significantly applied in the clinical treatment of various diseases such as cancer, diabetes, etc. owing to their high biocompatibility, specificity, and therapeutic efficacy. However, due to their immunogenicity, instability stemming from its complex tertiary and quaternary structure, vulnerability to enzyme degradation, and rapid renal clearance, the clinical application of protein/peptide therapeutics is significantly confined. Though nanotechnology has been demonstrated to prevent enzyme degradation of the protein therapeutics and thus enhance the half-life, issues such as initial burst release and uncontrollable release kinetics are still unsolved. Moreover, the traditional administration method results in poor patient compliance, limiting the clinical application of protein/peptide therapeutics. Exploiting the sustained-release formulations for more controllable delivery of protein/peptide therapeutics to decrease the frequency of injection and enhance patient compliance is thus greatly meaningful. In this review, we comprehensively summarize the substantial advancements of protein/peptide sustained-release systems in the past decades. In addition, the advantages and disadvantages of all these sustained-release systems in clinical application together with their future challenges are also discussed in this review.

Chitosan coated pH-responsive metal-polyphenol delivery platform for melanoma chemotherapy

The safe and effective drug delivery system is important for cancer therapy. Here in, we first constructed a delivery system Cabazitaxel(Cab)@MPN/CS between metal-polyphenol (MPN) and chitosan (CS) to deliver Cab for melanoma therapy. The preparation process is simple, green, and controllable. After introducing CS coating, the drug loading was improved from 7.56 % to 9.28 %. Cab@MPN/CS NPs released Cab continuously under acid tumor microenvironment. The zeta potential of Cab@MPN/CS NPs could be controlled by changing the ratio of Cab@MPN and CS solutions. The positively charged Cab@MPN/CS accelerate B16F10 cell internalization. After internalized, Cab@MPN/CS NPs could escape from lysosomes via the proton sponge effect. The permeability of CS promotes the penetration of Cab@MPN/CS to the deeper B16F10 tumor spheroids. In vivo results showed that Cab@MPN/CS NPs have a longer retention time in tumor tissues and significantly inhibit tumor growth by up-regulating TUNEL expression and down-regulating KI67 and CD31 expression. Thus, this delivery system provides a promising strategy for the tumor therapy in clinic.